Self-assembled silk fibroin hydrogels: from preparation to biomedical applications

Silk fibroin (SF) from Bombyx mori silkworm has been used as a textile fiber for centuries. In addition, for decades, SF has been used as a suture material. SF’s unique properties, such as exceptional host tissue response, appropriate mechanical properties, tunable degradation, simple processing method, and low cost, make it an attractive biomaterial. Accordingly, SF-based hydrogels have attracted much interest in the past years for biomedical applications. The tendency of SF chains to associate and form physical networks has been exploited very frequently in the last decade to prepare self-assembled SF hydrogels. This review describes the methods to prepare self-assembled SF hydrogels focusing on gelation mechanisms and biomedical applications thereof. The advantages and limitations of the methods used to induce SF assembly were discussed. In addition, the use of self-assembled SF hydrogels in interpenetrating network systems and the 3D printing applications were reviewed.


Introduction
The cocoons of silkworms have evolved over millions of years to protect the larvae from predators as they metamorphose into moths.The cocoon silks spun by the domestic silkworm Bombyx mori (B.mori) have been used in textiles for thousands of years. 1 Silk has long been a vital textile stock due to its unique feel, luster, dyeability, tensile strength, and elasticity.In recent years its applications substantially increased,

Ozgun Can Onder
Ozgun Can Onder is a senior researcher at the Eindhoven University of Technology.Ozgun studied Chemistry and Molecular Biology at Bogazici University and trained as a synthetic chemist.Ozgun obtained his PhD in 2018 from Koc University, specializing in the preparation of polyester-based foams.He also participated in industrial projects related to the synthesis and characterization of polyurethanes and gained an understanding of the structure-morphology-properties relationships.Between 2018 and 2022, he worked at the Slovenian National Institute of Chemistry as a researcher, where he developed macroporous polypeptide-based biomaterials, mentored graduate students, and collaborated with industrial partners for EU-funded projects.

Syeda Rubab Batool
Syeda Rubab Batool completed her Doctor of Pharmacy from Baqai Medical University, Pakistan, in 2013.After that, she moved to Koc University, Turkey, where she completed her PhD in Biomedical Sciences and Engineering in 2021.Her current research focuses on the preparation of innovative biomaterials and stimuli-responsive hydrogels for various biomedical, tissue engineering, and regenerative medicine applications.
especially in the biomedical and cosmetics sectors.Nearly 1000 metric tons of B. mori silk are produced and processed annually. 2he silk fibroin (SF) isolated from B. mori cocoons is a widely investigated, natural silk protein used for numerous biomedical applications due to its biocompatibility, biodegradability, and mechanical stability.In addition, it is also advantageous to use silk for biomedical applications because of the available large-scale processing infrastructure of traditional silk textile industries.Regenerated SF has been approved by the U.S. Food and Drug Administration (FDA) for clinical use in biomedical applications. 3,4ydrogels are water-swollen three-dimensional viscoelastic macromolecular networks, crosslinked through either covalent bonds or non-covalent interactions such as electrostatic interactions, hydrogen bonding, hydrophobic association, and multivalent coordination. 5,6Hydrogels have attracted extensive attention due to their versatility in composition, preparation, and resulting tunable properties such as swelling capacity, an interfacial affinity for target compounds, stimuli response, degradability, viscoelasticity, and network architecture. 7,8Polymeric hydrogels have been used as functional materials in a variety of applications.Biomedical applications can benefit from the properties above, as hydrogels resemble biological tissues because of their porosity, high water content, and tissue-like elasticity. 9,10Therefore, biocompatible hydrogels have emerged as promising biomaterials in a variety of biomedical applications such as tissue engineering, 11 and biosensing. 12They are also used as biointerface materials 13 and drug delivery systems. 14F hydrogels have recently received significant attention in the biomedical field.They have been used in various applications, including bone-filling materials, sustained delivery systems, and three-dimensional cell culture carriers as shown in Fig. 1. [15][16][17] For the preparation of SF hydrogels, several chemical and physical crosslinking methodologies have been developed.SF chains in aqueous solutions tend to associate and form physical 3D networks, leading to the formation of self-assembled hydrogels.The physical crosslinking approach is quite useful for biomedical applications because it is cheaper, safer, and the use of toxic chemical agents is not required.In addition, the complete removal of residual chemical crosslinkers after purification is not a concern.Furthermore, shear-thinning platforms can be developed for minimally invasive operations by utilizing the tendency of SF chains to associate in aqueous solutions.9][20] However, there is no comprehensive review article on self-assembled SF hydrogels to the best of our knowledge.This report aims (i) to overview the strategies to prepare self-assembled SF hydrogel-based biomaterials, (ii) to investigate the principles of SF gelation in aqueous solutions, and (iii) to describe the applications of selfassembled SF hydrogels in the biomedical sector.For this purpose, we will start with a quick explanation of the cocoon formation process and chemical composition of cocoons.Then we will overview the regeneration process of SF.The methods used to induce the association of SF chains will be reviewed.The use of self-assembled SF hydrogels in interpenetrating network systems and bioink formulations for 3D printing applications will be discussed.

Overview of the cocoon formation process
B. mori is the domestic silk moth that feeds on the mulberry plants.These moths live for only several weeks.During that span, moths pass through four development stages: egg, larva, pupa, and adult, as presented in Fig. 2A.The life cycle begins when the female silk moth lays eggs.The eggs hatch into larvae that feed on the mulberry leaves.At this stage, the larva spins silk threads around itself and forms a cocoon to protect itself from predators while continuing its development into a pupa.In the pupa stage, the silk cocoon can be collected by placing the pupa in boiling water, so that the silk thread can be used for industrial applications.
During the development of larvae, the silk gland grows to be an organ over 15 cm long.Silk fibers are produced through unique biomolecular machinery contained in these glands.The silk glands of B. mori exist as two tubular structures (Fig. 2B).According to its morphology and function, the silk gland contains three compartments: the anterior silk gland, middle silk gland, and posterior silk gland. 21First, SF components are secreted into the posterior gland as an aqueous solution during cocoon production.These components are fibroin heavy chain (350 kDa), fibroin light chain (25 kDa), and P25 glycoprotein (30 kDa).A disulfide bond links fibroin heavy and light chains in a 1-1 ratio.The formed heavy-light chain complex also binds glycoprotein P25 in a ratio of 6-1 via hydrophobic interactions to form a high molecular mass elementary unit. 22This fibroin unit is then transferred from the posterior to the middle gland.In the middle gland, glue-like sericin proteins are produced.As fibroin passes through the middle gland, it is coated via sericins. 23Sericin-coated fibroin then flows through the narrow anterior silk gland duct.The viscosity of the fibroin solution increases as it passes through the anterior gland.At the end of the anterior gland, the tubules come together to form a spinneret, from which silk fibers are pulled via larval head movement.The spinneret consists of a silk press and a duct where the fiber exits through a pore.The combined actions of strain and shear, together with the dehydration and induction of the ions, induce the conversion of viscous fibroin solution into a solid filament at the spinneret. 24A fully grown cocoon comprises a single fiber 1300-1500 m long and 10-20 mm in diameter. 25The soluble silk proteins exist in a metastable state within silk glands, and chains adopt disordered conformations.During fiber formation, the protein chains undergo major structural rearrangements, and chains are transformed from largely disordered states to b-sheet-rich conformations, serving as the underlying basis for the high strength of silk fibers. 26

Chemical composition of the cocoons
In general, as produced cocoons are composed of fibroin (470 wt%) and sericin (25-30 wt%) proteins. 28The sericin proteins located outside the fibroin proteins act as the glue that brings the two fibroin units together.The chemical composition of these proteins was characterized extensively.The primary structure of a heavy chain consists of two flanking hydrophilic blocks at C-and N-terminals. 29In between are hydrophobic blocks intertwined by small hydrophilic domains.The hydrophobic domains are mainly composed of dipeptide units in the form of GX where X can be alanine, serine, tyrosine, valine, or threonine.The most common repeat units include GAGAGS, GAGAGY, and GAGAGVGY.The presence of these repeat units is very critical for the self-organization of SF chains into the well-defined b-sheet crystalline structures. 30Overall, the heavy chain comprises 45.9% glycine, 30.3% alanine, 12.1% serine, 5.3% tyrosine, 1.8% valine, and only 4.7% of the other 15 amino acids. 31The proportion of hydrophobic residues in the heavy chain is approximately 79%.The heavy chains of SF materials are generally responsible for the extraordinary mechanical performance, as they can self-assemble into discrete b-sheet crystallites.
The light chain has a standard amino acid composition and a non-repetitive sequence.It contains a very different amino acid composition of 15% aspartate, 14% alanine, 11% glycine, and 11% serine. 32Light chains do not play a significant role during the self-assembly of SF chains because of their small size and the lack of repetitive sequences.So far, light chain amino acid sequences are not observed in the b-sheet domains of SF.The sericin proteins have a wide range of molecular weights between 40-400 kDa.Sericin chains are mainly composed of serine (25%), glycine (18%), aspartic acid (18%), and threonine (7%) amino acids. 33Sericins are soluble in water due to a high content of hydrophilic amino acids.

Regeneration of fibroin from the cocoons
For a long time, sericin has been considered to induce allergic and immunological reactions in humans. 34However, it was demonstrated that, sericin does not cause these reactions itself. 35Instead, the immune response is induced only when sericin and fibroin molecules are used together. 36,37Therefore, all sericin should be removed from fibroin intended for biological applications.This removal step is called degumming.Since the hydrophilicity of sericin is much more excellent than fibroin, it can be selectively removed from the cocoons.Various degumming conditions are reported in the literature.For example, selective dissolution of sericin can be conducted in alkali (e.g., sodium carbonate), acids (e.g., citric acid), or high concentration denaturant solutions (e.g., urea), or proteases. 38he most commonly used degumming method is alkali treatment.This process most commonly involves boiling cocoons in an aqueous sodium carbonate for 10-60 min. 39Silk fibroin regeneration process was presented schematically in Fig. 3A.
After degumming, the cocoons are rinsed with water several times and dried.Fibroin in the cocoon is found in the b-sheet structure, which is stabilized by the intermolecular hydrogen bonds and hydrophobic interactions.Because of the strong intermolecular interactions, fibroin cannot be solubilized in the water right away.To solubilize fibroin in aqueous solutions, chaotropic reagents are used to disrupt the hydrogen bonds View Article Online between fibroin chains (e.g., LiBr, LiSCN, CaCl 2 -ethanol). 40ost commonly, extracted dry cocoons are dissolved in 9.3 M LiBr aqueous solution at 60 1C.After that, the solution is filtered or centrifuged.Filtered solution or the supernatant are dialyzed continuously for several days in distilled water to remove the salts and low molecular weight impurities.Depending on the conditions, the resulting fibroin solution (usually a few weight percent) is stable at 4 1C for several weeks.To obtain higher concentrations of fibroin, reverse dialysis can be performed.For example, an aqueous solution of polyethylene glycol (PEG) could be used instead of pure water during dialysis. 41[47] 1.4 Characteristics of SF as biomaterials SF derived from the B. mori, as a natural protein biopolymer, has been widely studied in biomedical applications, mainly due to its mechanical performance, tunable degradation ability, and its biocompatibility with various biological tissues such as skin and cartilage. 48,49he proper balance of breaking strength, modulus, and elongation makes SF ductile and tough. 50Naturally produced SF fiber has a high ultimate tensile strength of 300-740 MPa.It also has a large breaking strain and high toughness exceeding those of synthetic fibers such as Kevlar.The strength-to-density ratio of silk is up to ten times higher than steel. 51Considering these outstanding mechanical features, the high tensile strength of silk fiber is suitable for suture, while its flexibility is appropriate for preparing load-bearing applications.The strength and stiffness of silk are dictated mainly by b-sheet crystallites due to intermolecular hydrogen bonds, van der Waals forces, and hydrophobic interactions.These contribute significantly to the stability of the structure.Whereas the toughness of the material is attributed to the presence of a semi-amorphous matrix.Therefore, collectively, the semiamorphous matrix and b-sheet crystallites govern the mechanical behavior of SF-based materials. 52s a protein-based biomaterial, silk fibroin degrades in vitro and in vivo by proteolytic enzymes such as protease XIV, a-chymotrypsin, proteinase K, papain, and collagenase. 53uring the enzymatic degradation, the hydrophilic amorphous domains degrade firstly.These domains include the C-termini, N-termini, linker segments in the heavy chain, and the light chain.Subsequently, the more crystalline domains with packed structures start to degrade. 54SF-based materials with higher b-sheet contents degrade slower.In addition, the degradation time of SF depends on some other factors such as external pressure, concentration, treatment conditions, and characteristics of the implanted site. 55The degradation behavior of natural fibers is also different from regenerated silk materials.The degradation rate of the natural fibers is much slower due to their compact semicrystalline structure with a highly oriented fibrous network. 56The biodegradation of SF can be investigated both in vitro and vivo.In vitro, it can be studied based on mass loss, morphological changes, and analysis of degraded by-products. 57In vivo, (i) mechanical characteristics tests following implantation in animal models for a specific time, (ii) structural integrity analysis via histological examinations, (iii) fluorescent staining and various biochemical assays can be used to study silk biodegradability. 58n terms of biodegradability, the use of SF in biomedical applications has several advantages compared to other synthetic and natural polymers.Even though the use of biodegradable polyesters such as PLA, PCL, PGA is approved by FDA for biomedical applications, [59][60][61][62] the release of acidic by-products during their degradation is an issue of concern.However, there are no such issues associated with silk degradation.Because the enzymatic degradation of SF leads to the formation of smaller polypeptides and eventually amino acids, which are easily absorbed or metabolized in vivo.Unlike other natural polymers such as gelatin and collagen, SF-based materials can retain their mechanical strength over a long time in vivo, which is advantageous in tissue engineering applications where slow degradation and load-bearing capacity are required. 63The degradation of SF occurs via surface erosion, unlike that of biodegradable polyesters, which undergo bulk hydrolysis degradation. 64Owing to its slow loss of mechanical strength, non-toxic by-products, and controllable degradation rate, SF presents distinct benefits for biomedical applications compared with other synthetic or natural polymers.
Apart from its robust mechanical properties and biodegradability, degummed SF has excellent biocompatibility.In some studies, the presence of outer sericin coating was found to cause immunogenic reactions.Therefore, removing sericin via a degumming process is an essential step for SF processing.SF is an FDA-approved biomaterial and is widely used as a suture material.There are various SF-based commercial products in the market such as Seri s and SeriACLTM s . 65n previous years, many in vitro and in vivo studies confirmed the biocompatibility of SF-based materials.For example biocompatibility of SF-based materials was confirmed by different research groups in vitro by using various cell cultures such as osteoblasts, epithelial cells, fibroblasts, keratinocytes, mesenchymal stem cells (MSCs), and hepatocytes. 66ong-term in vivo biocompatibility of biomaterials based on SF is also assessed by various research groups.For example, after implantation of the silk fibroin films seeded with autologous rat (MSCs) in Lewis rats, a very low inflammatory potential was observed.Histological and immunohistochemical evaluation after 6 weeks revealed the presence of circumferentially oriented fibroblasts, few blood vessels, macrophages at the implant-host interface, and the absence of giant cells.In addition, the inflammatory tissue reaction was less pronounced around the fibroin films compared to collagen or PLA films. 67n another study, various SF scaffolds were implanted subcutaneously or intramuscularly in nude or Lewis rats.In order to investigate the acute and long-term immunogenic potential, gross observations, histological and immunohistochemical evaluations, and real-time PCR analyses were conducted throughout 52 weeks.And, it was found that all the scaffolds were well tolerated throughout the study without any abnormalities. 68n addition to implantable systems, the biocompatibility of injectable systems was also investigated.As an example, the biocompatibility of SF hydrogels was studied in a rabbit critical-sized distal femur defect model over 12 weeks.It was revealed that the injected SF hydrogels did not elicit an immunological reaction and promoted bone remodeling and maturation.Surprisingly, the defects treated by SF hydrogel were more similar to the native bone than that for PLGA-treated defects. 69

Self-assembled SF hydrogels
Fibroin molecules in the regenerated aqueous solution are primarily found in helical and random-coil conformations.However, this conformation is metastable because of the tendency of fibroin chains to associate and form b-sheet structures in aqueous solutions. 70The less stable helical and random-coil conformations of fibroin are also called Silk I.The more stable b-sheet-rich conformation of fibroin is called Silk II. 71With time, the conformation of fibroin molecules transforms from random-coil to b-sheet, then the b-sheet structures aggregate to form physical crosslinks that organize into hydrogels (Fig. 3B).Gelation kinetics is a function of several parameters, including temperature, pH, concentration, and the presence of residual chaotropic reagents (due to incomplete dialysis).The regenerated solution cannot be stored indefinitely, after some point it can inevitably form a gel due to self-assembly and organization of SF chains.However, it is known that at 4 1C, the regenerated solution can be stored for several weeks depending on the fibroin concentration. 39ogueira et al. have studied the effect of dialysis time and temperature on the gelation kinetics of the regenerated fibroin solution. 70They used a CaCl 2 -ethanol system to solubilize fibroin, and they conducted dialysis at different temperatures to remove CaCl 2 -ethanol.They monitored the residual Ca 2+ concentration and recorded the sol-gel transition time.The presence of Ca ions in the fibroin solution decreased the tendency of association.As the Ca 2+ concentration decreased during dialysis, intermolecular interactions between chains became more and more favorable, and at some point, the gelation took place.It was found that the gelation time gradually decreased with increasing temperature.When the temperature was increased from 10 to 25 1C, the gelation time was decreased from 22 to 3 days.This decrease in gelation time is due to the enhanced fibroin association at higher temperatures due to increased mobility of SF chains.It was also found that when the temperature increased from 10 to 25 1C, the residual concentration of Ca ions increased from 5.70 to 11.09 mg mL À1 at the time of gelation.Despite a significantly higher Ca 2+ concentration at 25 1C, the gelation time was only three days which is significantly lower than the gelation time at 10 1C (22 days).Therefore, it was evident that the effect of temperature on gelation kinetics is higher than that of residual Ca 2+ concentration.Therefore, it can be concluded that the duration and temperature of the dialysis process are critical parameters during the regeneration process.Moreover, dialysis should be stopped before the solution gels if further processing of the fibroin solution is desired, which is generally the case.
Ma et al. studied the biomineralization of Calcite crystals within SF hydrogels. 72For this purpose, 5, 10, 15, and 25 wt% regenerated fibroin solutions were prepared.Then, CaCl 2 was dissolved in each solution at a concentration of 20 mM.The obtained solutions were incubated at 60 1C.Even though the exact gelation time of each solution was not explicitly mentioned, it was said that after 20 h, hydrogels were obtained in all solutions.Obtained hydrogels were immersed in Na 2 CO 3 solutions for 12 h to induce the mineralization of CaCO 3 crystals.Furthermore, the effect of fibroin concentration on the morphology of the crystals was analyzed.
Jin et al. studied the biomineralization of hydroxyapatite in fibroin hydrogels for bone tissue engineering applications. 73hey prepared 5 wt% fibroin solutions with varying Ca 2+ concentrations of 0, 10, 30, and 80 mM.Then, the solutions were incubated at 60 1C for 24 h to induce gelation.The obtained hydrogels were immersed in Na 2 HPO 4 solution at pH 8.5 to promote crystallization and growth of hydroxyapatite crystals.They investigated the effect of phosphate concentration and mineralization time on osteoblast proliferation and physicochemical properties of hydrogels.
Li et al. utilized a freeze-thawing approach to speed up the thermal gelation of fibroin solutions. 74They prepared 1, 2, and 4 wt% fibroin solutions.Then, the solutions were frozen at À7 1C to induce the association of fibroin chains.The solutions were frozen for 6, 24, or 48 h.After thawing the solutions at room temperature, the sol-gel transition of the solutions was optically monitored.It was found that the gelation of 24 h frozen 1 and 2 wt% solutions was observed after 12 and 6 h, respectively.They analyzed the effect of freezing time on gelation rate for 2 wt% fibroin solutions.When the freezing time was decreased to 6 h, the gelation was significantly slowed down, and it took more than two days for the system to gel.When the solution was frozen for 48 h, the frozen solution became insoluble after thawing due to a more significant association of the chains.For the 4 wt% solution, the frozen gel also became water-insoluble.It was suggested that slightly associated chains form during freezing, which can act as potential nucleation sites and facilitate the nucleation and growth of b-sheet crystals, resulting in a decrease in gelation time of the solutions.Due to extensive association, the frozen solutions became water-insoluble and failed to form a gel when the concentration was greater than 2 wt%, or the freezing time was greater than 24 h.Therefore, this method is limited to fibroin solutions with concentrations less than 2 wt%.
In all the examples provided above, the thermal gelation of SF via self-assembly was observed.Regenerated fibroin molecules exhibit strong intra-and intermolecular interactions, facilitating their self-assembly into antiparallel b-sheets and ultimately leading to physical gelation of the solution.However, as seen from the examples above, the thermal gelation process can take several hours to days, depending on SF concentration, solution compositions, and storage conditions.This long duration can limit its applications.Therefore, several strategies were developed to speed up the physical gelation of fibroin via selfassembly of SF chains as summarized in Fig. 4B.

pH-Induced self-assembly
The isoelectric point (pI) is the pH of a solution at which the net primary charge of a protein becomes zero. 75Above pI, protein molecules attain a net negative charge, and electrostatic repulsion of the chains can occur, which may decrease the tendency of intermolecular association. 76It is known that lowering the pH from neutral toward the pI reduces the electrostatic repulsion and may expose hydrophobic groups of the proteins.These changes can lead to enhanced protein-protein interactions and induce self-assembly.
In their studies, Hirabayashi et al. studied the effect of pH on the gelation rate of 3 wt% fibroin solutions at 20 1C. 77It was found that, when the pH was decreased from 6 to 4, the number of days required for the gelation was decreased from 8 to 1. Ayub et al. also studied the effect of pH on the gelation rate of 3 wt% fibroin solutions at 20 1C.It was found that when the pH was between 6 and 13, the gelation time was around 7-8 days.However, when the pH was between 2 and 4, the gelation took place within one day.It was also reported that when the pH was above 13 or below 1.5, gelation did not take place. 78The reason for failing to form a gel was explained by the extensive repulsion between fibroin chains.However, the hydrolysis of peptide bonds might also contribute to the failure of gelation in these very acidic or basic aqueous solutions.pI of silk fibroin is around 3.8; therefore, when the pH is decreased near pI, carboxylate anions become protonated, decreasing the fibroin chains' net charge.The resulting increased tendency for association leads to the faster gelation of fibroin solutions in these studies.
Nagarkar et al. investigated the mechanism of sol-gel transition of fibroin solutions upon lowering the pH below its pI.They performed rheology and light scattering experiments.Upon lowering the pH from 8.2 to 2.0, 20 nm-sized aggregates consisting of an association of 3-4 fibroin chains formed immediately.With time, these aggregates increased both in size and mass.Moreover, at the time of gelation, the aggregates rapidly agglomerated to form a heterogeneous structure.It was found that the gelation proceeds in two steps.Initially, there is a gradual increase in light scattering and elasticity until the gelation point is reached.Then, these parameters start to increase rapidly, suggesting a nucleation and growth mechanism. 79ini et al. used fibroin hydrogels as scaffolds to promote the healing of critically sized cancellous defects. 69Fibroin hydrogels were obtained by decreasing the pH of the regenerated fibroin solution to 3.8 and incubating the solution overnight at 50 1C.It was found that the hydrogels did not cause any inflammation, and stimulation of b1 growth factors was achieved.After 12 weeks, complete healing of defects in the trabecular bone of rabbits was achieved.It was also found that fibroin hydrogels significantly improved bone remodeling and maturation compared to the synthetic poly(lactic acid)-PEG hydrogels.
Kambe et al. assessed the use of SF hydrogels as implants to treat ischemic tissue disorders. 80They produced fibroin hydrogels with or without vascular inducing peptide (VIP).During preparation, they mixed aqueous solutions of SF and VIP with citrate buffer at pH 3.0.After incubation at 37 1C overnight, hydrogels were obtained.After the subcutaneous implantation of SF hydrogels in rats for several weeks, it was revealed that endothelial cells successfully migrated through the hydrogels, leading to the infiltration of macrophage and fibroblast cells.With time, macrophage and fibroblasts degraded the fibroin network and produced collagen.Thus, the fibroin hydrogel was gradually replaced by the regenerated tissue.For the hydrogels containing VIP, it was observed that the cell infiltration was accelerated, and the number of blood vessels in the regenerated tissue was doubled compared to the native fibroin gels.

Additive-induced self-assembly
Gelation time of the aqueous fibroin solutions was decreased from several days to less than a day by reducing the pH below its pI.However, it is still quite long; therefore, various additiveinduced self-assembly approaches were undertaken to improve the gelation kinetics of SF solutions.
2.2.1 Alcohol-induced.It was found that the addition of alcohols to the SF solution decreases the gelation time even further.It was proposed that the addition of alcohols which are miscible with water, dehydrates the fibroin chains and accelerates the formation of b-sheet domains by allowing chain-chain interactions.After the gelation is completed, the alcohol is exchanged with water to obtain hydrogels since the network becomes insoluble in water after extensive b-sheet formation. 81,82umata et al. studied the effect of fibroin concentration and ethanol content of the solution on the gelation behavior by rheometry. 83They prepared a stock solution of fibroin at 6.3 wt% concentration.Then, they mixed this solution with different volumes of ethanol.Furthermore, they obtained a series of solutions with decreasing fibroin concentration and increasing ethanol content.To determine the gelation point, they analyzed the time evolution of storage modulus G 0 and the loss modulus G 00 of the obtained solutions.In Table 1, the gelation time of each solution is presented.It was observed that, as the ethanol content of the solution increases, gelation time decreases significantly.For example, gelation time was decreased from around 24 h to 5 s when the ethanol content was increased from 10 to 50% (v/v).However, when the ethanol content was increased further, the gelation time started to level off and increase, presumably due to decreased fibroin concentration.
Kaewprasit et al. systematically investigated the effect of different alcohol types such as monohydric (methanol, ethanol, propanol, and butanol) and polyhydric alcohols (1,3-propanediol, and glycerol) on the SF gelation at 25 1C (Fig. 5A). 84They used 5 wt% fibroin solutions, and the alcohol content of the solutions was fixed at 10 wt%.The gelation of the system was monitored by optical density analysis.The gelation of fibroin in the absence of alcohol occurred around 7-8 days.This time was remarkably shortened by alcohol addition.For monohydric alcohols, the gelation time of solutions containing methanol, ethanol, and propanol was around 9.1, 8.7, and 8.2 h, respectively.Interestingly, the addition of butanol resulted in significantly faster gelation (0.7 h).As the polarity of alcohol decreases, the extent of hydrophobic interactions between alcohol and fibroin chains increases, leading to faster chain association.In the case of polyhydric alcohols, presumably due to their higher polarities, the gelation time increased significantly compared to their monohydric counterparts.In their another study, Kaewprasit et al. prepared a series of SF hydrogels via alcohol-induced self-assembly. 85Methanol, butanol, and glycerol were used as triggers to induce self-assembly.They conducted cell attachment and proliferation tests with L929 cell lines on hydrogels produced with different alcohol types.Firstly, all the hydrogels were found to be non-toxic.L929 cells were found to attach to the hydrogel surface one day after the seeding and start spreading.The proliferation and differentiation of the fibroblasts were also achieved within five days throughout the hydrogel scaffolds.
Moares et al. prepared self-assembled SF hydrogels via ethanol-induced self-assembly. 86They investigated the gel formation process in solutions with different ethanol contents.It was found that the gelation time decreased with increasing ethanol content.Without ethanol, it took 72 h for the regenerated fibroin solution to form a gel at 37 1C.The addition of ethanol significantly decreased the gelation time.Depending on the ethanol content, gelation of the solutions took place between 8 min and 7 h.The drug release profile of the hydrogels was also studied by using diclofenac sodium as a model compound.The drug compound was both soluble in water and ethanol.And it was loaded either by dissolving it in the regenerated fibroin solution directly or in ethanol prior to the induction of self-assembly.It was found that the presence of drug molecules did not alter the gelation kinetics significantly.A sustained release profile was obtained for hydrogels loaded in both ways.
Li et al. prepared curcumin functionalized SF hydrogels for enhancing adipogenic differentiation of bone marrow-derived human mesenchymal stem cells (hBMSC). 87Curcumin is a natural phenolic compound obtained from Curcuma longa.
In various studies, it has been shown that curcumin has antioxidant, anti-inflammatory, and anticarcinogenic effects.To prepare the composite material, curcumin was dissolved in ethanol, and the resulting solution was mixed with the regenerated SF solution.Then the mixture was incubated overnight to obtain hydrogels.Curcumin was distributed homogenously in the SF matrix.The strong binding of curcumin molecules to the hydrophobic b-sheet domains of SF resulted in the entrapment and stabilization of curcumin molecules.Therefore, the curcumin release from the SF matrix was very low, and the composites retained the high antioxidant ability for at least one month.It was found that the SF film-associated curcumin significantly inhibited the proliferation of hBMSC while promoting adipogenic differentiation.The effect was dose-dependent, with a critical curcumin concentration of 0.125-0.250mg mL.However, the presence of free curcumin in the cell culture medium inhibited both the proliferation and the adipogenesis of hBMSCs at a concentration range of 5-10 mM, which is almost 1000 times higher than the released curcumin from the composites.These findings showed that the curcumin delivery mode differentially affects the adipogenic differentiation of hBMSC, thus providing a tool to functionalize biomaterial scaffolds with antioxidants for tissue regeneration.Ribeiro et al. prepared SF-nanohydroxyapatite (nano-HA) composite hydrogels for bone tissue engineering. 88The regenerated fibroin solutions were found to gel within 67 and 48 h, at 37 and 50 1C, respectively.This time was too long to prepare nanocomposites without hydroxyapatite aggregation.Therefore, ethanol was used to disperse nano-HA and facilitate the gelation via self-assembly.During the composite preparation, the use of 70% ethanol was found to be optimum.Because, at higher ethanol concentrations, fibroin precipitation was observed.At lower ethanol concentrations, hydroxyapatite deposition was observed due to increased gelation time.To prevent deposition, gelation should be achieved within 15 min.Aggregation was observed when hydroxyapatite content is greater than 15% relative to SF.Therefore, the composites were prepared with 10 and 15% hydroxyapatite.The incorporation of hydroxyapatite decreased the swelling degree of SF hydrogel.And compressive properties of the hydrogels were improved with increased hydroxyapatite content.The metabolic and alkaline phosphatase activities of osteoblastic cells were improved by incorporating hydroxyapatite into the SF matrix, making this composite a promising material for bone tissue engineering.
Rojas et al. prepared SF-porphyrin composite hydrogels for photodynamic therapy applications. 89Ethanol was used to induce SF hydrogelation.Porphin was dissolved in ethanol, and this solution was mixed with the regenerated SF solution to produce composite hydrogels.Rheological studies were performed with hydrogels with and without porphyrin.It was found that the presence of porphyrin did not interfere with the gel formation.In addition, the encapsulation of porphyrins in the self-assembled polypeptide network prevented their aggregation, thereby significantly increasing the generation of singlet oxygen.It was also shown that porphyrins could diffuse out of the hydrogel and permeate the outer skin layers.Therefore, these composite hydrogels are suitable platforms for the sustained release of photosensitizers for photodynamic therapy applications.
Tomoda et al. produced a controlled-release device composed of SF microparticles embedded in SF hydrogel. 90First, they produced SF microparticles by an atomization method.Then dye molecules were incorporated into the microparticles by adsorption.The loaded microparticles were then mixed with regenerated SF solution.After treatment with 1-1 ethanol solution, gelation of the system was achieved.They studied the kinetics of dye release from the loaded microparticles and hydrogels containing loaded microparticles.It was found that the dye release from the microparticles reached equilibrium in approximately 90 min.Whereas for the hydrogels containing the loaded microparticles, the release persisted for 900 min, exhibiting a release 10 times longer.The dye release from the microparticles followed a Fickian diffusion mechanism.However, SF hydrogels containing SF microparticles followed an anomalous diffusion mechanism, showing that the release was correlated with the network degradation.Therefore, the used strategy holds the potential for developing prolongedrelease devices, especially for drugs and bioactive compounds.
2.2.2 Surfactant-induced.The use of surfactants was also found to induce the self-assembly of fibroin molecules in solution. 92Wu et al. used sodium dodecyl sulfate (SDS) as a gelling agent to produce fibroin hydrogels. 93It was found that the gelation can be induced by SDS in minutes, based on hydrophobic interactions and electrostatic effects (Fig. 6).Such interactions induce the unfolding, self-assembly, and association of fibroin chains, thus leading to the gelation of the mixture.In the absence of SDS, gelation of 4 wt% fibroin solution took place at 37 1C in 8 days.With increasing SDS concentration, the gelation time significantly decreased.The fastest gelation (15 min) was observed when the SDS concentration was between 8-12 mM.However, with a further increase in SDS concentration, the gelation process slowed down.For example, the fibroin solution formed a gel in 40 min at 33 mM SDS.With increased surfactant concentration, hydrophobic interactions between the tails of the surfactant molecules and hydrophobic Gly-Ala repeats of fibroin chains can trigger faster fibroin unfolding and association into mixed micellar nanoparticles and clusters.These structures serve as the nucleation sites of the gel skeleton.The subsequent assembly of fibroin molecules into stable b-sheet structures may lead to the formation of b-sheet-rich hydrogel networks.Due to the accumulation of negatively charged micelles, electrostatic repulsions occur at higher surfactant concentrations, hindering the formation of hydrophobic microdomains and decreasing the gelation rate.The release rate of SDS from the fibroin hydrogels was very slow and below the lethal oral dose for humans, owing to the strong hydrophobic interactions between surfactant and fibroin molecules.
Sun et al. prepared fibroin hydrogels using a cationic surfactant, Dodecyltrimethylammonium bromide (DTAB), as a gelation agent and studied the antimicrobial activity of the hydrogels. 94In the absence of surfactant, gelation of fibroin solution took place over 10 days at 37 1C.Upon surfactant addition, the gelation took place within an hour.To assess the antibacterial activity, zone of inhibition tests were performed with Escherichia coli and Staphylococcus aureus bacteria.The inhibition zone increased with the DTAB content of the hydrogels for both bacteria types, and virgin hydrogels failed to produce an inhibition zone.
Park et al. studied the effect of various surfactant types on the gelation of fibroin solution through self-assembly. 95They used neutral Triton X-100, anionic sodium dodecylbenzene sulfonate (SDBS), and several cationic alkyl ammonium bromide surfactants.In the absence of any surfactant, the fibroin gelation took place within 70 h.In the presence of neutral surfactant, the gelation time was gradually decreased with increasing surfactant concentration up to 50 mM.At 50 mM surfactant, the solution dodecyltrimethyl ammonium bromide (DTAB), and hexadecyltrimethyl ammonium bromide (HTAB).HTAB is the most hydrophobic one among these three, and it was not soluble in the fibroin solution beyond 20 mM.The aggregate formation was observed at concentrations lower than 20 mM instead of gelation.Fibroin chains have an overall negative charge at neutral pH values, and the strong electrostatic interactions between surfactant and fibroin molecules are believed to cause this precipitation.In the case of DTAB, which has a shorter alkyl tail, at concentrations higher than 20 mM, aggregate formation was observed.However, below 20 mM, gelation took place, but aggregate formation and phase separation of the solution were also observed.When OTAB was used, which has the shortest alkyl chain, above 20 mM gelation was accompanied by aggregation and phase separation.Below 20 mM, gelation was achieved without aggregate formation or phase separation.However, the gelation time was very long, around 60 h.In the study mentioned previously, the authors obtained different results when the DTAB surfactant was used to induce gelation.This might be due to the difference in SF concentrations and the purity of the fibroin solution after the dialysis process.Anionic surfactants were the mostly used surfactants to induce fibroin gelation in general.
Zhang et al. used anionic sodium N-lauroyl sarcosinate (SNS) surfactant to produce SF hydrogels. 96It is an amino acid-based surfactant, and it is widely used in a variety of cosmetic and medical applications.They systematically studied the effects of fibroin concentration, surfactant concentration, and temperature on gelation behavior via optical density measurements.The native SF solution took 8-10 days to form a gel at 37 1C.At increased SNS concentrations, the gelation time decreased.A distinct reduction appeared at SNS levels below 4 g L À1 , while a steady curve was observed for SNS concentrations above 4 g L À1 .The shortest gelation time (20 min) was observed when the SNS concentration was 3-5 g L À1 , and the SF concentration was 10-15 g L À1 .And, at a given fibroin and SNS concentration, the gelation time decreased with increasing temperature.L929 cells were cultured on the surface of hydrogels for seven days.The cells grew and proliferated steadily on the surfaces.However, it was observed that the viability of cells was lower in hydrogels containing SNS compared to native fibroin gels due to the low oral toxicity of SNS.
Dubey et al. used sophorolipid (SL) as a gelling agent. 91SLs are carbohydrate-based amphiphilic biosurfactants derived from the non-pathogenic yeast Candida bombicola.SLs have several advantages over other surfactants.SLs are natural compounds derived using a completely biological process.Thus, SLs have improved biocompatibility and reduced environmental impact.The addition of SL to fibroin solution accelerated SF's gelation near physiological pH, and gelation time was reduced from a few weeks to a few hours (Fig. 5B).Fibroin hydrogels thus obtained were lyophilized to form 3D scaffolds.Moreover, it was shown that L929 cells were successfully adhered to and proliferated on these constructs.
In their follow-up study, Dubey et al. investigated the mechanism of SL-induced gelation of fibroin solutions. 97SLs are extracellularly produced by the yeast as a mixture that comprises two forms: acidic and lactonic form.When the carboxylic end of the fatty acid tail remains free, it is known as acidic SL (ASL), whereas internal esterification of this carboxylic group with the 4 0 OH of the sugar molecule results in a closed ring structure, that is, lactonic SL (LSL).It was found that upon mixing fibroin solution and SL, the gelation time and mechanism differed depending upon the type of ASL and LSL content of the sophorolipid.For example, when the fibroin solution was mixed with ASL, the gelation started after 10 h, prior to which both the components were found to exist in the solution without any interaction.The shift in equilibrium between the ASL micelles and non-associated molecules led to the diffusiondependent onset of gelation.However, in the presence of LSL, the fibroin gelation was faster.NMR studies confirmed that the reason for faster gelation was the preferential binding of LSL to fibroin chains, leading to the unfolding of the protein and eventual formation of b-sheets.
Li et al. produced SF hydrogels with improved mechanical properties. 98They used SDS as the surfactant to induce gelation, and the compressive and tensile modulus of the hydrogels were as high as 3.0 and 3.3 MPa when the fibroin concentration was about 15 wt%.It was shown that the mechanical properties mainly depended on the fibroin concentration, while the type and concentration of the surfactant had little effect.They also prepared virgin fibroin hydrogel and ethanol-induced fibroin hydrogel and compared their conformation and morphology with SDS-induced one.It was found that, although the total b-sheet content in the hydrogel almost did not change, the surfactant speeded up the formation of b-sheet structures, more importantly, confined their size.This confinement resulted in smaller average pore size and a more homogenous morphology, which were thought to contribute to the enhanced mechanical properties.In the same study, they also used neutral and cationic surfactants.In the presence of SDS, the gelation time was 35 min.When Triton neutral surfactant was used, the gelation time increased to 2 h.In the presence of cationic surfactants, gelation was not observed.Instead, aggregation or precipitation took place.Through in situ nanoparticle formation, they produced Fe 3 O 4 -loaded fibroin hydrogels.With this material, they efficiently catalyzed H 2 O 2 -related reactions.
Phosphorylglycerols are negatively charged amphipathic lipids.They are biologically important as pulmonary surfactants in mammals and as membrane components in microorganisms.They can induce conformational changes in several proteins, such as a-lactalbumin, and b-lactoglobulin.Laomeephol et al. used a natural sodium salt (DMPG), to induce fibroin assembly. 100lectrostatic and hydrophobic interactions between the DMPG and SF chains induced the structural transition of SF chains to b-sheet, and consequently, a rapid gel formation was observed within 50 min.The gelation time was controlled by varying the lipid concentration.To assess the potential of the hydrogels as cell carriers, several mammalian cell lines, including L929, NIH/3T3, SaOS-2, and CaSki, were encapsulated into the hydrogel.The SFbased hydrogels supported the normal growth of fibroblasts, corroborating their cytocompatibility.In addition, inhibition in View Article Online the growth of cancer-derived cell lines was observed.Therefore, these DMPG-induced fibroin hydrogels were shown to be suitable for 3D platforms for biomedical applications, such as cell therapies and tissue regeneration.2.2.3 PEG-induced.Due to toxicity issues of alcohols and surfactants, these additives need to be extracted prior to their use in biomedical applications.To overcome this issue, Wang et al. explored the use of low-molecular-weight poly(ethylene glycol) (PEG) to induce SF self-assembly (Fig. 7). 101PEG300 and PEG400 are commercially available and FDA-approved compounds for oral, topical, and parenteral drug administration.In that study, they investigated the PEG-SF gelation kinetics via optical density and rheology measurements.Their preliminary screening studies showed that only low-molecular-weight PEGs (o1500 Da) induced SF gelation.PEGs with higher molecular weights caused the formation of aggregates in the forms of fibers and particles.Therefore, they focused on SF gelation induced by low-molecular-weight PEGs, especially PEG300 and 400, due to their viability as pharmaceutical-grade additives and the mixing efficiency and gel homogeneity.They kept the concentrations of PEG300 and 400 in SF hydrogels below 45%.Thus, toxicity would not be a concern because it is known that the highest concentration of PEG 300 and 400 used in drug formulations for parental injection can approach 50% without any toxic effects.PEG300 and 400 can induce fast and controllable SF gelation.Gelation was controlled to take place within 30 min for SF at both low (2-5%) and high concentrations (8-15%) by varying the concentration of PEGs.This enabled in situ preparation of SF hydrogels for clinical applications where thin needle injection is needed.The PEG-SF hydrogels exhibited high content of crystalline b-sheet structure.PEG is a highly hydrophilic molecule that binds water.The presence of PEG in the SF solution may force the hydrophobic domains on the SF molecules to assemble due to the excluded volume effect and further form crystalline b-sheets.PEG-SF gels injected subcutaneously in rats, showed a minimal inflammatory response and slow degradation (420 days for 5% gel), indicating that the gel may be suitable for drug delivery and tissue regeneration needs.Cytotoxicity of PEG-SF hydrogel was assessed using hMSCs.PEG-SF gels were unfavorable for initial hMSCs attachment and proliferation, likely due to the initial presence of a high concentration of PEG.However, the gels supported cell functions over longer time frames as the PEG dissipated from the hydrogel.This is an interesting observation because, for many medical applications, acute inflammation initiated by the binding of protein and recruitment of macrophages and fibroblasts occurs in the first few days after material implantation.
The same group further investigated the anti-adhesion ability of PEG-SF hydrogels. 102They evaluated the adhesion prevention of these hydrogels after laminectomies in New Zealand rabbits.Laminectomy is a standard operation in spine surgery to reduce spinal cord and nerve pressure.However, scar tissues often form in the spinal canal and adhere to the dura surface, resulting in low back pain post-surgery.For this reason, anti-adhesion materials are needed to isolate the surface of dura from the surrounding tissues physically.They demonstrated that the hydrogels reduced scar tissue formation around the dura and thus reduced epidural adhesion in rabbit models.The hydrogels fully degraded within 8 weeks postsurgery, but the adhesion prevention effect persisted past 8 weeks.The unique material properties of SF and the local, temporal release of PEG were thought to be responsible for this effective adhesion prevention.
The most used additives for the induction of SF assembly were summarized in this section.In addition, tannic acid, [103][104][105] peptide gelators, [106][107][108] carbon dioxide, 109,110 and various copolymers 111,112 were also employed as additives for the preparation of self-assembled SF hydrogels in various biomedical applications.

Shear-induced self-assembly
Shear forces are known to stretch polymer chains in solution. 113he stretching of the chains can dissociate intramolecular interactions and make chains more available for intermolecular interactions.Shear-induced gelation has been reported for amphiphilic or associating polymers in poor solvents. 114For associating polymers, increased intermolecular interactions between self-associating chains that undergo non-Gaussian stretching due to flow were argued to lead to shear-induced gelation.The SF protein is an amphiphilic block copolymer that consists of segments with predominantly hydrophobic domains that are phase-separated in the nanometer scale to enable solubilization in water.Therefore, in the regenerated fibroin solution, the chains are found in a metastable state.The shear gradient may cause the unfolding of SF molecular Fig. 7 Gelation process after mixing equal volume of SF and PEG400 solutions at room temperature.Reproduced with permission from Elsevier. 101

Review
Materials Advances domains and the formation of macromolecule clusters rich in b-sheet content due to increased exposure of hydrophobic domains to water.The subsequent increase in the concentration and overall lifetime of inter-cluster crosslinks and the physical entanglements between dangling fibroin chains could eventually lead to a percolation-like transition into a permanent, physical hydrogel network.Sonication-and vortexinduced self-assembly of fibroin solutions have emerged as practical and gentle methods for preparing SF hydrogels.2.3.1 Sonication-induced.Ultrasonication generates high shear forces via acoustic cavitation, which occurs when highpower ultrasound is coupled with liquids. 115As a result of this cavitation, the media may experience extreme local effects such as heating, high pressure, and high strain rates.These physical phenomena have been exploited in various applications, including self-assembly and gelation of N-isopropylacrylamide/acrylic acid copolymer, 116 organic fluids with metalated peptides, 117 and synthetic self-assembling peptides. 118Aside from peptides, proteins such as human serum albumin and myoglobin have been studied with sonication to characterize their aggregation and self-assembly behavior related to disease states.
Sonication-induced gelation method of SF solutions was firstly introduced by Wang et al. 119 It was shown that the solgel transition of fibroin solution was accelerated by ultrasonication as illustrated in Fig. 8. Since its introduction, this method has found extensive use for various biomedical applications because of several advantages compared to other methods to induce self-assembly.The gelation time can be controlled from minutes to hours based on the sonication parameters such as energy output, duration, and SF concentration.In the time frame between the end of sonication and the onset of gelation, cells or biomolecules such as drugs and growth factors can be mixed with the fibroin solution, and after the gelation, 100% encapsulation can be achieved. 120,121his approach is sufficiently gentle to maintain cell viability during encapsulation and avoids the use of harsh chemical treatments. 122,123It allows accurate cell seeding and homogenous distribution of cells throughout the hydrogel.The use of harsh chemical treatments is avoided.Very importantly, injection into the target tissue or site is possible as shown in Fig. 9.
In their pioneering study, Wang et al. investigated the effects of sonication parameters, fibroin concentration, ion type, and pH on gelation kinetics of fibroin solutions. 119They used 1, 2, 6, and 20% (w/v) fibroin solutions, and sonication was performed at 20% amplitude for 5, 10, or 30 s. Gelation time decreased with increasing concentration and duration of sonication, except for the 20% case where the gelation was slower compared to 6% due to the solution's high viscosity, which may hinder the propagation of sound waves.For example, gelation time decreased from around 40 h to less than an hour, when sonication time increased from 5 to 30 s for 6% SF solution.It was also found that lower concentrations of K + ions (20-50 mM) and low pH (4) accelerated gelation, whereas the presence of Ca 2+ ions and higher concentrations of K + ions slowed down the gelation process.The mechanical properties of the gels were improved with increasing concentration.For instance, the modulus rose from 500 to 1500 kPa, when concentration increased from 4 to 12%.Cell culture studies were performed using hMSCs.Hydrogels with less than 4% fibroin concentration were found to be too weak to be manipulated during the cell culture studies.Sonicated fibroin solutions at 4, 8, and 12% (w/v) were mixed with hMSCs.Proliferation and differentiation of the cells were assessed by histological analysis and DNA quantification.The cells grew rapidly and proliferated over 21 days in the 4% hydrogel.However, the survival was lower in the gels with higher concentrations, likely due to limitations in the mass transport due to decreased mesh size of the hydrogel. 124F hydrogels produced via this method are popular biomaterials for bone and cartilage tissue engineering applications.Ding et al. used fibroin hydrogels as scaffolds to deliver rat bone marrow stem cells into bone defects. 1254 wt% fibroin solutions were sonicated at 25% amplitude for 30 s.Then, cell suspensions at different final concentrations of 1.0 Â 10 5 , 1.0 Â 10 6 , and 1.0 Â 10 7 cells per mL were mixed with sonicated fibroin solution before gel formation.The osteogenic potential of the as-obtained cell/fibroin constructs was investigated by in vitro and in vivo studies.The 1.0 Â 10 7 group exhibited the highest ALP activity, the most calcium deposition, and the strongest osteogenic-related gene expression in vitro.That group also showed a clear increase in bone formation in vivo with superior performance with respect to both new bone

Materials Advances Review
volume and trabecular number in the defect area.More importantly, only in the 1.0 Â 10 7 group, the function of the encapsulated stem cells guaranteed a continuous bone formation process in the long term.In their another study, the same group utilized fibroin hydrogels as a delivery vehicle for rabbit maxillary sinus floor augmentation. 1265 wt% fibroin solutions were sonicated at 25% amplitude for 30 s. Then the solutions were mixed with (i) vascular endothelial growth factor (VEGF165), (ii) bone morphogenic protein-2 (BMP-2), and (iii) both.Prior to gelation, the solutions were injected into elevated cavities.It was found that SF gel alone did not promote sufficient bone formation alone in the rabbit model.Nevertheless, angiogenic and osteogenic factors released from SF gel promoted tissue invasion and new bone formation.At the same time, the delivery of a single angiogenic agent was not sufficient for bone regeneration.Roohaniesfahani et al. studied the effects of simultaneous release of Mg, Sr, and Si ions from injectable SF hydrogels to treat bone defects in mouse models. 127For this purpose, a triphasic ceramic, MSM-10, was used as a delivery agent.Ceramic powders were manually mixed with 4 wt% SF solutions at various concentrations.The solutions were sonicated at 45% amplitude and 25 Hz frequency.The sonication time was adjusted to achieve gelation within 5-10 min.Because faster gelation (o5 min) was impractical for handling and longer gelation (410 min) resulted in phase separation of MSM-10 particles and SF.The presence of Mg, Sr, and Si ions significantly increased the gelation time of SF solutions and decreased the b-sheet content of the resulting gels.However, the presence of those ions improved the injectability and in vitro osteogenic properties of the gels.The implantation of ceramic/SF hydrogels into subcutaneous defects of mouse models showed reduced immune reaction and increased neovascularization compared to pure SF hydrogels.
Yodmuang et al. prepared SF microfiber-reinforced SF hydrogels as scaffolds for cartilage repair. 1284 wt% SF solutions were sonicated at 12% amplitude for 15 s and then mixed with SF fibers and chondrocytes.In addition, SF fiber-reinforced agarose gels were also prepared for comparison since agarose has been labeled as the gold-standard biomaterial for in vitro cartilage tissue formation.It was found that, while the addition of microfibers significantly increased the moduli of SF hydrogels, it contributed to a lesser extent for agarose hydrogels, likely due to weaker interfacial bonding between the SF microfibers and agarose.Fiber-reinforced SF hydrogels exhibited a 50% improvement in equilibrium modulus and a 60% increase in dynamic modulus at day 42 compared with SF hydrogels without fibers.In addition, higher glycosaminoglycan staining around the fibers was revealed after histological evaluation of fiber-reinforced SF hydrogels.This suggested that newly synthesized proteoglycan was localized to SF microfibers.In contrast, glycosaminoglycan staining was not localized to SF microfibers in fiber-reinforced agarose hydrogels since SF microfibers failed to form a physical bond with the agarose matrix.Excellent chondrocyte compatibility, glycosaminoglycan and collagen matrix deposition make these materials a feasible alternative to agarose for cartilage tissue engineering.
Self-assembled SF hydrogels have also found use in brain repair and regeneration applications.Nieto et al. examined the short-and long-term compatibility of injectable SF hydrogels in the striatum of mouse brains. 129Their preliminary studies showed that a gelation time of 10 min after sonication is required to inject the solution into the target area successfully.Therefore, several sonication conditions were screened by changing the amplitude, sonication time, number of sonication pulses, and concentration.Desired gelation time was obtained when 2 wt% fibroin solutions were subjected to two sonication pulses of 30 s at 60% amplitude.In vivo studies indicated that the animals reasonably tolerated the striatal injection of SF.Because, similar to the saline group, the survival rate exceeded 90%.After the injection, fibroin hydrogels exhibited acceptable biocompatibility with the brain tissue.The gradual degradation of hydrogel resulted in minor immune system activation.After two weeks, hydrogel deposits did not elicit immune reactions or behavioral deficits at all.The degradation of SF was also histologically confirmed in the brain parenchyma of rats one month after intracerebral injection due to the action of brain proteases or myeloid cells and microglia.One month after transplantation, cognitive and sensorimotor deficits were not evident by behavioral or electrophysiological analysis.Overall, the analysis of cell death, inflammatory response, and brain function examined by behavioral tests and electrophysiological analysis confirmed the tolerability of SF by the brain tissue.
Osama et al. explored the use of self-assembling SF hydrogels as a matrix for the minimally invasive delivery of MSCs to the brain. 130In that study, they tried to optimize the conditions for efficient delivery of MSCs.To induce self-assembly, fibroin solutions (1-5 wt%) were exposed to 3 to 6 sonication cycles on ice (one cycle consisted of 30 s on and 30 s off) at 30% amplitude.1% hydrogel was found to be too soft for the application.Increasing SF concentration improved the stiffness of the gels.2, 3, and 4 wt%, hydrogels exhibited matrix elasticity similar to the brain tissue.With these hydrogels, cell viability tests were performed in vitro.An initial drop in MSC viability was observed for all the gels.Then it stabilized on day 3 and then steadily increased over the remaining culture period (14 days).They also investigated the effect of the addition time of the cells to the sonicated solution, and it was found that a more homogeneous distribution of cells was obtained when cells were mixed with the solution just 10 min after sonication, where the mixture was still a solution.In their another study, the same group explored the use of self-assembling fibroin hydrogels as injectable platforms for regeneration in the stroke cavity.In vivo studies were performed with rats.It was found that the hydrogels demonstrated stability throughout the study (7 weeks), excellent space-filling and conformity, and excellent biocompatibility with minimum immune response.The gels also interacted with the glial scar and supported endogenous cell proliferation after the experimental stroke.
Self-assembled SF hydrogels produced via sonication have been used as sustained delivery platforms in various biomedical applications.Guziewicz et al. developed a system for the sustained delivery of monoclonal antibodies. 131It was found that protein stability was maintained during encapsulation.After encapsulation, some of the loaded hydrogels were lyophilized.The impact of lyophilization was evaluated by comparing antibody release rates between lyogels and the parent hydrogel material.Lyophilization of antibody-loaded SF hydrogels significantly improved long-term antibody release properties over the parent hydrogel material due to enhanced interactions between SF and antibody molecules after water removal.
Han et al. investigated the effect of delivery of microRNA-675 (miRNA-675), originating from the long non-coding RNA H19, to prevent aging-induced vascular dysfunction in mouse hindlimb. 133hey explored the use of a combination of exosomes and SF hydrogel as a delivery platform.miRNA-675 is known to promote skeletal muscle regeneration and inhibit cardiomyocyte hypertrophy.However, naked miRNA is susceptible to degradation by RNase in the extracellular environment.In order to avoid the loss of miRNA during delivery, stem cell-derived exosomes were used to deliver miRNA-675.To induce self-assembly, 4 wt% SF solutions were sonicated three times for 30 s at 30% amplitude.To the freshly sonicated solution, exosome solution was added, and the mixture was kept at 37 1C to allow for gelation.It was shown that mice treated with miRNA-675 exosomes encapsulated in SF hydrogel showed significantly enhanced blood perfusion compared to miRNA-675 exosomes alone.The improved effects resulted from the enhanced retention and stability of miRNA-675 by exosomes and SF hydrogel.Thus, SF hydrogel-based delivery of exosomes represented an effective way to achieve sustained delivery of miRNA for tissue protection.
Zheng et al. incorporated 3-mercaptopropionic acid (MPA)coated CdTe quantum dots (QD) into SF hydrogels via physical adsorption and entrapment. 134The fluorescence of the QDs remained stable for more than 96 h in PBS buffer or when subcutaneously injected into mice.The cytotoxicity of QDs was significantly reduced when the QDs were incorporated into SF hydrogels.This system was useful for tracking the degradation and distribution of SF biomaterials and can be used as a potential diagnostic tool.He et al. investigated the use of nanographene oxide (NGO) and lanthanide-doped rare-earth up-conversion nanoparticles (UCNPs) loaded SF hydrogels for tumor upconversion luminescence (UCL) imaging and photothermal therapy.NGO absorbs near-infra-red (NIR) radiation and transforms it into thermal energy.Therefore, it Mater.Adv., 2022, 3, 6920-6949 | 6935 has been widely used in photothermal therapy applications.Furthermore, UCNPs can act as luminescent nanoprobes.These two compounds were mixed with sonicated SF solution, and the resulting hybrid hydrogels showed outstanding UCL imaging properties and a photothermal therapy effect under NIR laser irradiation.The in vivo studies presented excellent suppression of tumor growth in the 4T1 tumor-bearing mice.Therefore, this system was shown to hold great potential for combining tumor imaging and antitumor therapy for clinical applications.
2.3.2Vortex-induced.The self-assembly of SF solutions is accelerated when a shear force is applied through a vortex shaker.In this way, SF gels can be obtained from simple equipment, unlike ultrasonication, without contacting the solution with a probe.Yucel et al. introduced vortex-induced hydrogelation of SF solutions. 135It was found that the gelation kinetics can be controlled by changing the vortex time, solution temperature, and fibroin concentration.This is important since the gelation should take place within a time frame enabling homogenous distribution of cells or biomolecules.It was also shown that these vortex-induced hydrogels show shear-thinning behavior and can be injected through needles.In addition, the stiffness of the hydrogels recovered immediately after the removal of applied shear.This enables the applicability of these materials for homogeneous three-dimensional cell encapsulation, homogeneous delivery in vivo, and localization of hydrogel/cell scaffolds at the injection site.
Davis et al. used self-assembled SF hydrogels as transplantation devices to treat type-1 diabetes. 136For this purpose, isolated pancreatic islet cells were mixed with freshly vortexed SF solutions, and the mixture was allowed to gel for 2 h at 37 1C.In addition, to enhance islet cell graft survival and function, islets were encapsulated along with extracellular proteins (laminin and collagen IV) and mesenchymal stromal cells.It was found that, after a 7 day in vitro encapsulation, islets remained viable and maintained insulin secretion in response to glucose stimulation.And when islets were encapsulated with collagen IV or laminin, the insulin secretion was increased on day 2 and day 7, respectively.A 3.2-fold synergistic improvement in islet insulin secretion was observed when islets were co-encapsulated with stromal cells and ECM proteins.Furthermore, encapsulated islets had increased gene expression of functional genes; insulin I, insulin II, glucagon, somatostatin, and PDX-1, and lower expression of the de-differentiation genes cytokeratin 19 and vimentin compared to non-encapsulated cells.Therefore, the suitability of self-assembled SF hydrogels was demonstrated for co-encapsulation of various cell types and biomolecules for the treatment of type 1 diabetes.
Managing infection in ischemic, avascular, and necrotic tissues is a significant challenge because drug penetration into abscesses is limited by the lack of vascularity and the dense capsule wall.Therefore, high plasma concentrations of antibiotics are required to overcome this penetration barrier.Moreover, this is problematic due to dose-limiting tissue toxicities and high inter-individual variability in abscess permeability.Kojic et al. proposed an alternative treatment for focal infections, which is based on laser-mediated heating of Au-NP suspended in an injectable and degradable SF hydrogel. 137The use of Au-NP-loaded hydrogels was first evaluated in vitro.The effects of power and duration of laser application on temperature change and bactericidal performance were assessed for various nanoparticle concentrations.Then, in vitro studies were performed with mice infected with S. aureus.It was found that even single 10 min laser treatment of a subcutaneous infection in mice preserved the general tissue architecture while achieving a bactericidal effect.In addition, this procedure allows for case-specific treatment by controlling the nanoparticle concentration, laser exposure, and power.The self-assembled SF hydrogel was found to be very useful for this treatment since, apart from its biocompatibility and biodegradability, it prevented nanoparticle aggregation and ensured spatial stabilization at the injection site.

Self-assembly induced by the concentration-dilution method
As we have seen so far, the self-assembly of fibroin chains was accelerated via several methods, resulting in the formation of hydrogels.The as-obtained structure is not water-soluble, and this process is irreversible due to the hydrophobicity of the hierarchically assembled structure.Kaplan et al. developed a so-called ''concentration-dilution method'' to make this assembly process reversible. 138In the first step, the freshly prepared 6 wt% SF solution was concentrated at 60 1C up to 20 wt%.During this process, metastable nanoparticles were formed.After that, the solution was diluted below 2 wt% to induce disassembly.After incubation at 60 1C, the diluted solution was transformed into a hydrogel.Dynamic oscillatory studies proved that the solution and hydrogel states were entirely reversible and could be recycled many times.It was found that solutions produced this way had a higher zeta potential (above À50 mV) than previous SF materials, which tend to be below À30 mV.Due to their amphiphilic nature, the fibroin molecules can form micelles or aggregates in water.It was thought that these structures can migrate to the surface of the assemblies to reduce the free energy of the SF-water system, thus resulting in the increase in negative charge on the surface of the assemblies.It was proposed that b-sheet-rich nanofibers provide enough hydrophobicity for hydrogel formation, while high electrostatic repulsion restrains physical crosslinks, a combination of which allows a reversible sol-gel behavior.More importantly, hydrogels obtained in this way could still flow, unlike typical self-assembled SF hydrogels, due to the restricted aggregation of b-sheet domains.And these hydrogels were found the retain flowability for long times.Unlike selfassembled SF hydrogels, where physical crosslinking kinetics need to be tuned carefully for a suitable injection, these thixotropic SF nanofiber hydrogels can flow on demand once injected and solidify rapidly after shearing is ceased.These features can prevent unwanted leakage from the target site due to insufficient gelation rates.Therefore, the thixotropic property of these hydrogels resulted in better injectability when compared with other forms of injectable self-assembled SF hydrogels where there is a tight time window for the injection.This interesting self-assembly behavior was exploited for various applications by various groups. 139,140u et al. used this methodology to prepare a fibroin-based injectable and local delivery platform for cancer treatment. 141 wt% regenerated fibroin solution was first concentrated to above 20 wt% slowly over 24 h at 60 1C to form metastable nanoparticles and then diluted to 0.5 wt%.The diluted SF solutions were incubated for 24 h at 60 1C to induce nanofiber hydrogel formation.Then, doxorubicin (DOX) was directly dissolved into the SF hydrogel to yield DOXloaded hydrogel.These thixotropic SF hydrogels allowed tunable pH-responsive and sustained DOX delivery.The sustained and tunable release of DOX continued over 8 weeks from these hydrogels and provided long-term control of cytotoxicity of cancer cells.Injection in a breast cancer model showed that the hydrogels improved anticancer capacity, suggesting that this approach is promising for localized chemotherapies.
Ding et al. prepared SF-hydroxyapatite hydrogels as injectable platforms for regenerating irregular bone defects. 142First, SF-coated HA nanoparticles were prepared via an aqueous precipitation reaction using SF as a template and a surface stabilizer.The 6 wt% regenerated fibroin solution was slowly concentrated to 20 wt% over 24 h at 60 1C to form metastable nanoparticles and then diluted to 2 wt% with distilled water.The diluted SF solution was incubated for 24 h at 60 1C to induce the formation of nanofiber hydrogel.These thixotropic SF nanofiber hydrogels and initially prepared SF-coated HA nanoparticles were blended to form injectable nanoscale systems with a homogeneous distribution of HA.The ratio of HA nanoparticles and SF nanofibers was tuned to achieve mechanical properties and organic-inorganic compositions similar to those of natural bone while retaining the ability to be injected.The composite hydrogels supported improved osteogenesis compared to that of SF nanofiber hydrogels.The optimized SF-HA hydrogels demonstrated good cytocompatibility and osteogenic differentiation capacity in vitro and supported bone formation in vivo, suggesting its potential to be used in bone tissue engineering and regeneration.
The same group further extended this work to improve osteogenesis activity. 143Desferrioxamine (DFO) is known to simultaneously induce the secretion of multiple angiogenesisrelated factors and cytokines to facilitate more stable vascularization in bone regeneration.Bone morphogenetic protein-2 (BMP-2) is known to enhance osteoinduction.SF nanofibers and HA nanoparticles were used as nanocarriers to load DFO and BMP-2, forming injectable composite hydrogels with multiple angiogenic and osteogenic cues.It was found that the angiogenesis and osteogenesis capacity could be regulated independently by tuning the release behaviors of DFO and BMP-2 to achieve microenvironments for bone tissue regeneration.Both in vitro and in vivo results revealed that these hydrogels created suitable niches to accelerate the regeneration of vascularized bone compared with other SF-based hydrogels reported.

Self-assembled SF in interpenetrating network hydrogels
An interpenetrating polymer network (IPN) is a combination of two different polymers, at least one of which is synthesized or crosslinked in the immediate presence of the other. 144These networks are at least partially interlaced on a molecular scale but not covalently bonded to each other and cannot be separated unless chemical bonds are broken.In this way, the properties and structures of different polymers are combined into a new hybrid material.Because of this combination of favorable properties, IPN hydrogels have been used in numerous applications, including drug delivery, wound healing, and tissue engineering. 145Due to its favorable physico-chemical properties and self-assembly behavior, SF was used along with various biopolymers such as gelatin, collagen, hyaluronic acid, and PNIPAM to prepare IPN hydrogels for various applications as listed in Table 2. 146,147

SF-Gelatin IPN hydrogels
Gelatin is obtained by breaking the triple-helix conformation of collagen into single-stranded macromolecules.Upon cooling below 30 1C in an aqueous environment, its chains undergo a thermally induced reversible transformation from random-coil to triple-helix conformation. 164This introduces physical crosslinks, which induce gelation at sufficiently high gelatin concentrations.At temperatures near body temperature, 37 1C, its chains attain random-coil conformations, thus exhibiting unacceptably weak mechanical properties, and even can be dissolved away.To improve its mechanical and biological properties, SF was blended with gelatin, and IPN hydrogels were prepared (Fig. 10).
In their preliminary studies, Gil et al. prepared physical gelatin-SF IPN hydrogels. 148For this purpose, 4 wt% gelatin and SF aqueous solutions were mixed at varying ratios at 40 1C.Then, the mixtures were cast in Petri dishes and kept at 10 1C to induce gelatin triple-helix formation.After that, the mixtures were dried under vacuum, and films were obtained containing 0, 10, 25, 40, and 60 wt% SF.After that, the dried films were immersed in a 3-1 methanol-water solution to induce the assembly of fibroin chains and form b-sheet structures, which resulted in the formation of a second physically crosslinked network.As-obtained films were immersed in water at 5 1C to induce swelling.DSC analysis was performed to discern the relative importance of the triple-helix conformation of gelatin and the b-sheet conformation of SF on the thermal properties of IPN hydrogels.For the hydrogels containing 0, 10, 25, and 40 wt% SF, the helix-coil transition temperature of gelatin was around 34 1C.When SF content was increased to 60 wt%, transition temperature was increased to 46 1C.In the case of hydrogel containing 75 wt% SF, no transition was observed in the DSC analysis.This suggests that most of the crystallized SF network effectively alters the extent to which the gelatin chains rearrange.Since SF in b-sheet conformation is more hydrophobic than gelatin, at sufficiently high concentrations, they may shield gelatin chains from water molecules, thereby restricting their mobility and ability to accomplish conformational change.By performing DSC cooling scans, it was also found that in the presence of an established SF crystalline network, the helix-coil conformational transition of gelatin is thermally reversible between ambient and body temperature.Complementary dynamic rheological measurements were also performed to reveal the effect of the SF physical network on the mechanical properties of the IPN hydrogels.The formation of fibroin b-sheet crystals increased the dynamic elastic modulus of the hydrogels and stabilized the hydrogels to much higher temperatures than the corresponding untreated gels.Even when the hydrogels were heated above the gel-sol transition, they did not liquefy and remained intact.It was also found that the introduction of the b-sheet forming SF network; (i) improved the thermal stability of blends at elevated temperatures and (ii) enhanced the mechanical properties, such as tensile modulus, elongation, and tensile strength.
In a follow-up study, they analyzed the swelling and protein release kinetics of these IPN hydrogels at varying compositions and temperatures below and above the helix-coil transition of gelatin. 149It was found that the swelling degree was significantly higher at 37 1C than 20 1C, indicating that the randomcoil conformation of gelatin permitted greater water sorption.It was also found that the IPN hydrogels underwent slight mass loss at 20 1C.However, at 37 1C, gelatin molecules were slowly released into the surrounding medium.Therefore, at 37 1C, the b-sheet crystals of SF were solely responsible for stabilizing the hydrogel.Due to their tailorable composition-and temperaturedependent swelling and release properties, these IPN hydrogels are thought to be attractive biomaterials for thermally responsive biomedical and pharmaceutical applications.
Xiao et al. synthesized a series of gelatin-SF IPN hydrogels with tunable features for potential biomedical applications. 151o form the gelatin 3D network, this time, they performed chemical crosslinking instead of physical crosslinking via the formation of triple-helix structures.For this purpose, they functionalized gelatin chains with methacrylate groups (Gel-MA).Then regenerated SF solution was mixed with Gel-MA solution at various concentrations to obtain compositions containing 0, 8, 14, and 25 wt% SF.These solutions were then poured into PDMS molds, and photo-crosslinking was performed under UV radiation to produce semi-IPN hydrogels.Then, the resulting gels were detached from the molds and treated with aqueous methanol solution to trigger the physical association of fibroin chains to form full-IPN hydrogels.Swelling properties of both semi-and full-IPN hydrogels were studied, and it was found that the introduction of SF chains decreased the swelling degree of semi-IPN gels compared to pure chemically crosslinked Gel-MA gels.After the methanol treatment, the swelling degree was significantly decreased compared to semi-IPN hydrogels since the formation of the b-sheet fibroin network increases the hydrophobicity of the system.The mechanical properties of the gels were studied by compression tests.Before the methanol treatment, for all compositions, the modulus was around 5 kPa.After the treatment, the modulus significantly increased and became 15, 30, and 75 kPa, for IPNs containing 8, 14, and 25 wt% SF, respectively.The enzyme-mediated degradation profiles of full-IPN hydrogels were investigated using collagenase solutions in vitro.The presence of b-sheet domains of SF decreased the degradation rate.An almost complete degradation was observed for the pure Gel-MA sample after 48 h.However, for the IPN samples, the degradation rate decreased significantly, around 25% weight loss was observed after 72 h.It was speculated that the presence of b-sheet structures could act as water-insoluble backbones, thus hindering the permeation of collagenase into the hydrogel.For the full-IPN samples, cell culture studies were performed using NIH-3T3 fibroblasts.It was found that the sample containing 8 wt% SF was the most suitable for cell spreading and proliferation.However, at higher contents of SF, the cell-biomaterial interactions became worse, and the cell proliferation rate decreased.In another study, Xiao and coworkers utilized a similar approach to prepare gelatin-SF IPN hydrogels.However, this time they used sonication to induce the assembly of fibroin chains instead of alcohol treatment (Fig. 11).It was found that obtained hydrogels display high swelling degrees, excellent compressive properties, and resistance to enzymatic degradation.Cell culture studies were performed with osteoblast cells.The cell attachment and viability studies demonstrated that the synthesis process was not toxic for cells, and the cell growth behavior in the hydrogels could be tuned by adjusting the ratio of fibroin to Gel-MA.
In their studies, Park et al. produced gelatin-SF IPN hydrogels using a different approach to crosslink gelatin chains. 152hey first treated an aqueous mixture of gelatin and SF with microbial transglutaminase that forms crosslinks between glutamine and lysine amino acids in gelatin molecules.Then, the physical assembly of SF chains was induced by immersing the hydrogel in aqueous ethanol.The resulting IPN hydrogel was swollen in water and lyophilized, and the second layer of the IPN was formed by repeating the dual crosslinking procedure again.The obtained IPN hydrogels were found to be highly elastic and tough.Compressive studies revealed that IPN hydrogels were much stiffer than pure SF or pure gelatin hydrogels.It was also found that adding another layer of the IPN further enhanced the mechanical properties.The obtained gels were non-cytotoxic and allowed adhesion and proliferation of human dermal fibroblasts.

SF-Collagen IPN hydrogels
Collagen is the major structural component of the extra-cellular matrix (ECM) found in connective tissues and internal organs. 165here are at least 28 members belonging to the collagen superfamily; however, Type I collagen is one of the most abundant molecules in the body.It assembles into fibers that form the structural and mechanical matrix of bone, skin, tendons, cornea, blood vessel walls, and other connective tissues.Collagen I has a typical chain composition of GPX, where X is any amino acid other than glycine, proline, or hydroxyproline. 166It is soluble in slightly acidic buffers and typically associates after neutralization by adjusting the pH around 7.5.As a result, Collagen I can assemble into a triple-helical structure, which can be hierarchically bundled and physically crosslinked in the form of fibrous networks. 167The mechanical properties of these physically assembled collagen hydrogels are very low.In order to obtain hydrogels with desired physical and biological properties, several groups produced collagen-SF IPN hydrogels.
Buitrago et al. produced SF-collagen IPN hydrogels as cell encapsulating platforms. 156During preparation, neutralization at pH 7.0 was performed to induce the association of collagen chains; and sonication was used to trigger SF self-assembly as presented in Fig. 12.In their preliminary experiments, collagen and SF were not subjected to any treatments, and the blended solution did not gel as expected.When collagen was neutralized but SF was not sonicated, a very unstable and weak gel was obtained.When SF was sonicated, but collagen was not neutralized, coagulation of SF was observed without gelation.Only when both the collagen neutralization and the SF sonication were applied, the gelation took place.Hydrogels with controlled compressive moduli were obtained by tuning the SF/collagen ratio and their concentration, which are considered to find a wide range of applications for soft and hard tissues.In addition, the hydrogels were able to be molded easily into various shapes and display elasticity, which is difficult to achieve in the case of pure SF gels (too brittle) or collagen gels (easily losing water then yielded).It was shown that hBMSCs were successfully encapsulated during the gelation process.The encapsulated cells rapidly anchored and spread throughout the network.In addition, shrinkage of the hydrogel was not observed during culture studies.This is a significant improvement since substantial cell-mediated contraction is generally observed for pure collagen gels.
Khoo and coworkers prepared SF-collagen IPN hydrogels as biomaterials to elucidate breast cancer migration. 157Firstly, regenerated SF solution was sonicated at low amplitude to prevent quick gelation during preparation.After sonication, the collagen solution was added, and the solution pH was adjusted to 7.4 by adding sodium hydroxide to trigger collagen Fig. 11 The schematic diagram of the preparation of the SF-GelMA IPN hydrogels.Reproduced with permission from Elsevier. 153ssembly and then lightly vortexed.IPN hydrogels were obtained after incubation.By changing the concentration of SF while keeping the collagen concentration constant, the compressive modulus of gels was tuned between 30 and 300 Pa.It was found that the invasion of breast cancer cells depended on both SF concentration and pore size.The maximum invasion was observed at intermediate SF concentration, which produced gels with a loss modulus of 100 Pa.At higher SF concentrations, the invasion decreased due to decreased pore size of the IPN network.It was further shown that the cancer cells could be biased toward mesenchymal migration by treatment with exogenous human epidermal growth factor since it increases cell contractility and enhances cell-matrix adhesions.Whereas, after treatment with taxol, the cancer cells were biased toward amoeboid migration since it disrupts cytoskeletal function by stabilizing microtubules.

SF-Hyaluronic acid IPN hydrogels
Hyaluronic acid (HA) is a naturally occurring, non-immunogenic glycosaminoglycan that plays a vital role in cell-ECM interactions, wound healing, inflammation and angiogenesis. 168HA is highly hydrophilic, thus can provide the hydration of tissues.However, its poor biomechanical performance and rapid degradation limit its applications.Therefore, HA-SF IPN hydrogels were prepared to expand the range of properties and hence applications available to both SF and HA individually.In this way, the hydrophilicity of HA can be combined with the strength and slow degradation of SF in a single material.
Tavsanli et al. prepared mechanically robust and stretchable HA-SF IPN hydrogels. 154For this purpose, hydroxyl groups of HA were functionalized with methacrylate units at different degrees between 4 and 25 mol%.First, polymerization of methacrylated HA (MeHA) was performed in the presence of SF at 50 1C.Under these conditions, physical association of SF chains might be expected.However, no gel formation was observed in MeHA and SF aqueous solutions, which is ascribed to the steric hindrance effect of SF chains.Therefore, N,Ndimethyl acrylamide monomer was included in the reaction system as a spacer to connect methacrylated pendant groups of HA chains.The reaction was performed at 50 1C for two days to produce composite hydrogels.FTIR and XRD analyses confirmed the formation of b-sheet domains in the SF network.It is known that SF chains can self-assemble to form these domains even in the absence of any trigger, such as sonication or alcohol addition, at high temperatures.This procedure takes more time, but it would not be problematic in this case since a long time is already required for the chemical crosslinking of HA pendant groups.It was found that the presence of a physical SF network significantly enhanced the mechanical strength and toughness of MeHA hydrogels by providing a pathway for energy dissipation under load.Furthermore, mechanical and swelling properties of the IPN hydrogels were controlled by varying the methacrylation degree of MeHA and concentration of the polymers.
In their studies, Xiao et al. produced cell-laden IPN hydrogels based on SF and MeHA. 155They developed a one-pot, biocompatible approach for synthesizing cell-laden IPN hydrogels via sonication and photocrosslinking (Fig. 13).Methacrylation was achieved by reacting HA with methacrylic anhydride at pH 8. Then SF and MeHA solutions were mixed at room temperature to obtain prepolymer solutions.Then the prepolymer solution was sonicated and exposed to UV radiation sequentially to produce IPN hydrogels.For the cell encapsulation, sterilized prepolymer solution was sonicated and immediately mixed with the cultured MC3T3-E1 mouse preosteoblast cells.Then, the suspension was UV crosslinked and incubated at 37 1C.The sol-gel transition time of SF was regulated by adjusting the ultrasonic energy inputs, such as amplitude and time, to allow for further processing and cell encapsulation.The obtained IPN hydrogels were found to possess significantly enhanced mechanical strength compared to the neat SF hydrogels.Moreover, the introduction of the HA network increased the water content of the gels.Cellular fluorescence staining revealed that the osteoblasts could successfully attach to the IPN network.In addition, the cell viability analyses indicated that the synthetic process was biocompatible, and the IPN hydrogel supported the proliferation and spreading of osteoblast cells throughout the hydrogel Fig. 12 Schematic illustration of the formation of physically crosslinked collagen-SF IPN.Reproduced with permission from Elsevier. 156etwork, showing that these gels are promising biomaterials for regenerative medicine.

SF-Poly(N-isopropylacrylamide) IPN hydrogels
Poly(N-isopropylacrylamide) (PNIPAM) is one of the most widely studied temperature-responsive polymers.PNIPAM chains in aqueous solutions exhibit a coil to globule transition when the temperature increases above a lower critical solution temperature (LCST) of 32 1C. 169Correspondingly, in PNIPAM hydrogels, a volume transition takes place around this temperature.The fact that the LCST of PNIPAM lies close to body temperature and can easily be tuned above and below 37 1C renders PNIPAM-based materials very suitable for biomedical applications.PNIPAM hydrogels provide reversible expansion/ contraction in aqueous environments upon thermal stimulus; however, these systems suffer from slow swelling/deswelling response, weak mechanical properties, and limited biocompatibility.To address these concerns, PNIPAM-SF hydrogels were prepared by various research groups.
In their studies, Gil et al. prepared PNIPAM-SF IPN hydrogels and investigated their viscoelastic and swelling/deswelling properties. 161For this purpose, aqueous NIPAAM and SF solutions were mixed at different proportions, and free radical polymerization was performed in the presence of N,N 0 -Methylenebis(acrylamide) crosslinker for 1 day at 10 1C.Then, the obtained semi-IPN gels were immersed in methanol solution to induce the association of SF chains to form a full-IPN.The viscoelastic properties of both semi-and full-IPN hydrogels (before/after methanol treatment) were investigated by dynamic shear oscillation measurements.For the semi-IPN hydrogels, both storage and loss moduli were decreased with the increasing SF content.Whereas, for the full-IPN hydrogels, the moduli values were increased with the SF content, indicating the effect of the physical SF network on the viscoelastic properties.The volume phase transition behavior of semi-and full-IPN hydrogels towards changes in the temperature and ionic strength was analyzed by swelling tests.It was found that the introduction of a physical SF network did not interfere with the volume phase transition of the PNIPAM network.Deswelling kinetics were determined by measuring the swelling degree first at 20 1C (swollen), then at various time intervals after placing them at 45 1C.With increasing SF content deswelling rate was initially increased, exhibited a maximum at 30 wt%, then started to decline.The rate increase in lower SF contents was ascribed to the reduced skin layer effects due to the ability of the physical SF network to act as water-draining channels.As the SF content increases, the tendency of PNIPAM chains to associate via hydrophobic interactions decreases above the transition temperature.This resulted in a decrease in the deswelling rate since the mobility of the PNIPAM network is responsible for the gel contraction above LCST.The introduction of the SF physical network brings about two effects, and there is a trade-off between them.This was thought to be the reason for the decreased deswelling rate at higher SF contents.
Kaplan and coworkers produced macroporous PNIPAM-SF IPN hydrogels and explored their potential as biocompatible actuating devices. 162Aqueous NIPAAM and SF solutions were mixed at different proportions, and free radical polymerization was performed in the presence of N,N 0 -methylenebis-(acrylamide), and N,N,N 0 ,N 0 -tetramethylethylenediamine crosslinkers for one day at room temperature.The formation of macropores was induced by freeze-drying.The dried gels were dipped in methanol solution to trigger the self-assembly of SF chains to create a physical network.The swelling degree of At 20 1C, it was found to be constant regardless of IPN composition.However, at 45 1C, the swelling degree decreased with increasing SF content.The incorporation of the SF network enhanced the mechanical properties and actuating force.The swelling/deswelling behavior of IPN gels was studied.The introduction of the SF physical network enhanced both swelling and deswelling rates due to reduced skin layer formation.For example, the sample containing 30 wt% SF showed rapid and stable shrinking and swelling at a constant rate by switching the temperature at 40 s intervals between 20 and 45 1C.This shows the applicability of these IPN hydrogels as dynamic soft materials for various sensing and related functions.

Other self-assembled SF containing IPN hydrogels
Luo et al. prepared IPN hydrogels composed of hydroxypropyl methylcellulose (HPMC) and SF. 160HPMC is a cellulose derivative characterized by its LCST of 62 1C.To prepare the hydrogels, aqueous solutions of HPMC and SF were mixed in different proportions (HPMC/SF w/w, 9/1, 7/3, 5/5) at room temperature.Then, gelation of the mixtures was induced by storing them for 2 h at 70 1C.Aqueous solutions of HPMC are known to gel when the temperature is increased above its LCST, due to dehydration and increasing hydrophobic interactions between pendant groups.Even though no secondary treatment was performed to induce self-assembly of SF chains, the SF chains were aggregated to form b-sheet domains while being kept at 70 1C for 2 h.It was speculated that the exposure of hydrophobic side chains of HPMC, induced by heating above its LCST, drives the association of SF chains via hydrophobic interactions.The morphologies of the hydrogels with different proportions were investigated by confocal laser scanning microscopy.In the 9/1 sample, both networks were able to mix homogeneously.However, with increasing SF content, the degree of phase separation increased.Compressive analyses showed that all samples display elastomeric behavior.The 9/1 sample exhibited the most robust mechanical performance among all.It was the toughest sample with high flexibility and excellent elasticity due to the lack of significant phase separation.In vitro cytotoxicity tests were performed with L929 mouse fibroblasts cells.There was no significant difference in cell viability between the 9/1 hydrogel and the pristine SF hydrogel, with survival rates over 95%.These results demonstrated that the 9/1 IPN hydrogel holds great promise for biomedical applications where both high strength and biocompatibility are required.
Kim et al. prepared cellulose-SF IPN hydrogels. 159Cellulose is the greatest renewable natural source of organic materials.Cellulose is insoluble in conventional solvents because of the strong H-bonding intermolecular interactions.Therefore, a LiBr aqueous solution was used to dissolve cellulose.Firstly, aqueous LiBr solutions of cellulose and SF were mixed at 120 1C for 2 min.The obtained mixture was cooled down to 70 1C, where gelation of cellulose took place.After that, methanol treatment was performed to induce the association of SF chains, resulting in the formation of IPN structure.Obtained gels were dipped in water to remove LiBr salts and methanol.Morphologies of the hydrogels were characterized by SEM after freeze-drying.Both cellulose and cellulose-SF samples were composed of long, interconnected nanofibrils which form a 3D network.The introduction of the SF network increased the specific surface area from 199 to 236 m 2 g À1 .While the porosity and swelling ratio of the gels were significantly reduced with increasing SF content, all the gels possessed a high water-uptake value.By adjusting the cellulose/SF proportion, the enzymatic degradation rate was controlled.The introduction of the SF network improved cell adhesion and proliferation, making these IPN systems valuable candidates for tissue engineering applications.
Zhao et al. produced tough IPN hydrogels composed of SF and poly(acrylamide-co-stearyl acrylate). 163Their unique approach includes the introduction of SDS surfactant, heat-induced SF b-sheet formation, and photoinitiated polymerization of the acrylamide (AM)-stearyl acrylate (SA) network as shown in Fig. 14.Firstly, SDS with variable contents was introduced to the mixture of SA and AM monomers.During the formation of micelles for 2 h at 40 1C, the hydrophobic SA monomers and hydrophilic AM monomers lie respectively inside and outside of the micelles.Afterwards, SF was introduced under stirring.Initially, a physical SF network was formed with b-sheet crosslinks around the shells of the micelles with hydrophobic cores due to the hydrophobic nature of the b-sheet structure.Then, photo-polymerization was performed to synthesize the second network, which has a structure similar to amphiphilic block polymers such that hydrophobic poly(SA) blocks lie in micelles, and hydrophilic poly(AM) blocks stay outside the micelles.The as-prepared IPN hydrogels were found to be mechanically weak due to the absorption of the large amount of water by the hydrophilic poly(AM) network, which can destroy the b-sheet domains.Therefore, an SDS immersion post-treatment was performed to prevent the breakdown of hydrogels by promoting the hydrophobic interactions and electrostatic repulsive forces.The stability of post-treated RSF IPN hydrogels also significantly increased.Mechanical properties of both single network hydrogels and IPN hydrogels were studied by tensile tests.It was found that SF single network hydrogel was too brittle to be clamped during the measurement.Moreover, poly(AM-co-SA) single network hydrogel was too soft.In comparison, all IPN hydrogels exhibited better mechanical properties with both high strength and large elongation at break.The tensile strength of equilibrium IPN hydrogels was between 0.26 and 0.44 MPa, depending on the SDS content.The optimal SDS content was found to be around 1/16 (SDS/AM molar ratio) for the highest tensile strength.This IPN hydrogel also displayed the greatest fracture strain and tensile elongation of 800%.The toughness of these IPN hydrogels was attributed to the presence of both the rigid RSF/SDS network and the soft poly(SA-co-AM) network.The elongation at break values of these IPN hydrogels was greater than the ones in previous works.Such physically interacted IPN hydrogels with robust mechanical and biocompatible features are expected to broaden the applications of SF in biomedical fields.
Yang et al. prepared chitin/SF IPN hydrogels for bile duct restoration application. 158First chitin/SF blend solutions were prepared by mixing each solution at 0 1C at predetermined amounts.Then epichlorohydrin was added to form a crosslinked chitin network.After gelation took place, the samples were taken out from the molds and dipped in ethanol solution to induce the formation of a physical SF network.The obtained IPN hydrogels were found to have high compressive strength (1.36 MPa) and toughness (0.71 MJ m À2 of fracture energy) which is required to be used as a bile duct cannula at the wound site.The IPN hydrogels effectively reduced bile leakage and accelerated the regeneration of the extrahepatic bile duct.In addition, the composite cannula also performed intriguing responsive degradation behavior in different bile concentrations.In the case of bile leakage, they were able to provide a low-bile ambience favor for fibroblast growth.This could be eliminated quickly in enterocoelia in the case of no leakage.These results indicate that chitin/SF IPN hydrogels can be used for the clinical treatment and prevention of postoperative biliary leakage.

Self-assembled SF hydrogels in bioink formulations for 3D printing
3D bioprinting is an extended application of additive manufacturing that involves building a tissue or organ layer-by-layer using a bottom-up approach. 170,1713D bioprinting aims to mimic the natural cellular architecture by depositing materials and cells together to restore the structure and functionality of complex tissues.In 3D bioprinting, cells or biomolecules are printed directly onto a substrate in a specific pattern such that the cells can hold together to form the required 3D construct.These biological printable materials are called bioinks.Bioinks are core to 3D bioprinting technology by providing a stable and biocompatible environment in which cells can proliferate and differentiate. 172Traditional inks used for 3D printing are mainly designed for non-biological applications.Therefore, the processing conditions are not suitable for cells. 173For example, 3D printing of thermoplastics including acrylonitrile butadiene styrene and polylactic acid (PLA), requires high temperatures, which are biologically deleterious.
Hydrogels are widely applied as bioinks for cell encapsulation for 3D bioprinting.An ideal bioink consists of ECM-like features supporting cell and tissue growth and appropriate mechanical strength. 174Since cells require mild environments, processing and crosslinking of bioink during printing should be compatible.Decellularized ECM (dECM), synthetic and natural polymers are commonly used materials for 3D bioprinting.Although synthetic polymers have advantages due to their consistency in composition.Their use in biomedical applications is often limited due to the need for organic solvents for processing and limited bio-instructive features.In contrast, natural polymers are quite hydrophilic and contain inherent biological properties and functions that resemble the ECM.SF has been widely investigated and used in bioink formulations due to its biocompatibility, cytocompatibility, remarkable mechanical strength, and biodegradability. 175,176More importantly, the physical association of SF chains in aqueous solutions renders SF very useful in bioink formulations since the use of ultraviolet light or deleterious chemical crosslinkers can be avoided during gelation.In their studies, Ghosh et al. performed 3D printing of regenerated SF solution by directwriting into a coagulating alcohol bath (86% methanol), such that the deposited fibers underwent b-sheet crystallization to form complex 3D micro-periodic architectures with diameters as low as 5 mm. 177However, the methanol bath cannot be used for the deposition of alive cells.Das and coworkers observed that during the printing process, upon applying shear, clogging of micronozzle was observed due to the association of SF chains induced by shear stress, obstructing a smooth flow of the printed filaments. 178It was found that printing SF solution alone without additives is very challenging.Therefore, to develop suitable bioink formulations, SF molecules were used along with non-toxic molecules that induce the self-assembly of SF chains and act as bulking agents.
Kaplan et al. developed SF-based bioinks for 3D printing. 179Several non-toxic polyols such as glycerol, 1,3-propanediol, 1,2,6-hexanetriol, adonitol, or erythritol were used to induce SF assembly.Furthermore, gelatin was used as a bulking agent to facilitate faster layer stacking and print height retention without contributing to the crystallization of SF chains.Bioink formulations containing 10% gelatin/5% SF/1% glycerol (w/v) produced the most robust structures, while SF alone without any additives were the weakest.In their follow-up study, Kaplan and coworkers used the same SF/gelatin/glycerol system to prepare 3D printed soft tissue constructs. 180They optimized the formulation by modulating concentrations of each component to generate materials under optimal printing conditions.These formulations were designed to yield under extrusion forces, undergo rapid gelation upon deposition, be biocompatible in vivo, and show volume retention over time.It was found that a gelatin concentration above 10% (w/v) was optimal for printing in physiological conditions, and a ratio of 1 : 1 of SF to gelatin was needed to maintain a homogenous stable structure.This bioink formulation was used to print patient-specific cheek geometry to reconstruct soft tissue resected due to reconstructive surgical procedures such as tumor removal.The in vivo response of the printed implants was tested in a mouse model.They retain their shape for up to 3 months with minimal inflammatory response and tissue integration.
Huang et al. also used a similar approach and prepared bioinks composed of SF, gelatin, and glycerol. 181For this purpose, SF and gelatin were mixed at a fixed ratio of 1/2 (w/w), and glycerol was added at a fixed ratio of 5/1 (w/w) SF to glycerol to induce the association of SF chains.Bacterial cellulose nanofibers (BCNF) were also included in the composition to improve the structural resolution and enhance the mechanical properties of composite hydrogel scaffolds.Following 3D printing of the bioink, freeze-drying was performed to introduce hierarchical porosity to the material via phase separation. 182,183It was found that the tensile strength of the printed sample increased significantly with the addition of BCNFs in the bioink.In vitro and in vivo biological studies were performed with L929 cell lines.This demonstrated that the hierarchical pore structure was beneficial to tissue ingrowth.The pores ranging from 10 to 20 mm served as hosts for cellular infiltration, while the pores with a diameter from 300 to 600 mm ensured sufficient mass transfer and nutrient supply.
Singh et al. prepared bioink formulations composed of SF and gelatin. 184Instead of using glycerol to induce the association of SF chains, they blended SF from B. mori and Philosamia ricini (P.ricini) to form a self-blended hydrogel in a crosslinkerfree approach (Fig. 15).They have chosen this approach not only to induce b-sheet formation but also because of the unique properties of SF from P. ricini.For instance, its primary structure contains the cell-binding arginine-glycine-aspartic acid (RGD) units and poly(alanine) sequences, which impart enhanced mechanical properties.The components were blended at various concentrations to rheologically and structurally optimize the formulation and improve the printing efficiency.In that way, anatomical structures such as the human ear were printed with good fidelity and adequate resolution.The obtained constructs supported the growth and proliferation of encapsulated chondrocytes leading to the cartilaginous ECM formation, indicated by the high sulfated glycosaminoglycan and collagen levels, and upregulation of chondrogenic gene expression with minimal hypertrophy of chondrocytes.
Zheng et al. studied the use of SF-PEG hydrogels as selfstanding bioinks for 3D printing for tissue engineering. 173s mentioned previously, mixing PEG with SF induces the assembly of SF chains leading to its gelation.They explored the use of non-cellularized SF-PEG gels (PEG removed after printing) and cellularized SF-PEG hydrogels without PEG removal (Fig. 16).The gels with a SF concentration greater than 5% (w/v) showed better shape fidelity during printing, especially after the 3D printed constructs were incubated in phosphatebuffered saline (PBS) over 24 h.However, when the concentration was 10%, the gel was too stiff to be injected through the nozzle.Therefore, 7.5% (w/v) concentration was selected for the remainder of the study.To determine the amount of PEG that can be used safely, cytotoxicity studies were performed with hMSCs.When PEG concentration was 0.1% and 0.5%, the total cell metabolic activity was similar to that of the controls.At 1%, the cell metabolic activity was significantly retarded.When the PEG concentration increased to 2% and 5%, cells stopped growing completely.Animal studies were performed by subcutaneous implantation of 7.5% bioink gels in mice.The cells survived and proliferated in the gel matrix for at least 6 weeks post-implantation, revealing the suitability of these materials for tissue engineering applications.
In order to improve biological activity, Li et al. produced growth factor-loaded SF-based bioinks for cartilage tissue engineering. 185Platelet-rich plasma (PRP) was used as an autologous resource of growth factors.The inks were prepared by mixing an equal volume of 80% PEG solution with 10% SF solution, along with an appropriate PRP to obtain final 12.5%, 25%, and 50% (v/v) PRP concentrations.It was revealed that the obtained structures possess proper internal pore structure, good biomechanical properties, and a suitable degradation rate for cartilage regeneration.The cell culture studies were performed by using rabbit chondrocytes.Hematoxylin and eosin staining showed that the 50% PRP group formed cartilage-like lacunae structures at four weeks.Safranin-O and Masson's trichrome staining showed cartilage-specific ECM deposition, especially in 25% and 50% PRP groups.Immunohistochemistry revealed that the production of collagen II was higher in the 50% PRP group than in other constructs.These findings suggested that the samples containing 50% PRP could find uses in cartilage tissue engineering.
In their study, Zhang et al. used a similar approach to develop bioink formulations containing dECM and TGF-b3 growth factor for cartilage tissue engineering. 186For this purpose, SF and dECM were blended at various amounts to obtain final concentrations of 0-7.5% and 0-3%, respectively.The obtained mixtures were then mixed with an equal volume of 80% PEG400 to induce gelation.It was found that for an optimum printing, the concentrations of SF and dECM should be greater than 2.5 and 2.0%, respectively.When the dECM concentration was above 3% and SF concentration was above 7.5%, the bioink was highly viscous and required higher printing pressures that might decrease the viability of the encapsulated cells.Whereas, when the dECM concentration was below 2% and SF concentration was below 2.5%, the resulting low viscosity caused issues during printing due to sagging or collapse.After optimizing the formulation, the BMSCs were encapsulated within the bioink, and 3D printed.The chondrogenic differentiation of BMSCs in the constructs was assessed by the mRNA levels of several markers such as SOX-9, collagen I and II, and aggrecan via rt-PCR.After 28 days, the expression levels of these markers significantly increased, suggesting a successful differentiation of BMSCs.The chondrogenesis potential of the constructs was further assessed in vivo.3D printed scaffolds were transplanted into nude mice in the subcutaneous region.The deposition of collagen and glycosaminoglycans was shown by Masson's trichrome, safranin-O and immunohistological staining.Also, characteristic cartilage Fig. 16 Preparation and 3D printing of bioink composed of SF and PEG.Reproduced with permission from Wiley-VCH, copyright 2017. 173

Materials Advances Review
Mater.Adv., 2022, 3, 6920-6949 | 6945 lacunas and round chondrocyte-like cells were observed after 28 days.They further extended this study and prepared bilayered structures consisting of decellularized extracellular matrix (dECM), PCL, and SF for osteochondral repair. 187For this purpose, two types of bioinks were prepared using cartilage dECM (DCM) and bone dECM (DBM).For each bioink, regenerated SF and PEG were added to the corresponding dECM.Then, BMSCs were encapsulated in both bioinks.To fabricate the bone layer, PCL was first extruded to print the outline, and then the DBM/SF bioink was printed to fill the space.Then, DCM/SF bioink was printed as the cartilage layer on top of the bone layer.First, the delivery capacity of growth factors and the potential of constructs for chondrogenesis or osteogenesis were measured in vitro.In vivo experiments demonstrated that the scaffolds loaded with growth factors promoted osteochondral regeneration in the rabbit knee joint model.This shows the suitability of these bilateral materials for applications in osteochondral regeneration.

Concluding remarks and future perspectives
SF is emerging as an essential protein biomaterial of broad biomedical applicability.It is already an established textile fiber, and nearly 1000 metric tons of silk are produced and processed annually.SF-based systems are useful for applications where slow biodegradation and good mechanical properties are critically required.In addition, it is economically advantageous to use silk for biomedical applications because of the available large-scale processing infrastructure of traditional silk textile industries.Over the past decades, SF-based hydrogels have emerged as valuable platforms for various biomedical applications spanning from cell culture and tissue engineering to controlled drug delivery.
SF chains in aqueous solutions have a great tendency to selfassemble and form 3D physical networks.This physical crosslinking process is very suitable for biomedical applications because it is cheaper and safer, and the use of toxic chemical agents is not required.Also, the presence of residual chemical crosslinkers after purification is not a concern.In addition, shear-thinning platforms can be developed for minimally invasive operations by utilizing the tendency of SF chains to associate in aqueous solutions.The progress described here has demonstrated the feasibility of using self-assembled SF hydrogels in biomedical applications.The methods used to produce self-assembled SF hydrogels were summarized along with their pros and cons.
Despite the progress made, there is still room for improvements regarding the preparation of physical SF hydrogels.The degumming procedures and batch-to-batch variations of SF must be considered for making reasonable comparisons between different studies.A deeper understanding of the detailed physical gelation mechanisms may help researchers in the future to produce SF hydrogels with greater mechanical strength and modulus.The functionality of the SF-based hydrogels should be improved in the future to increase their role in drug delivery, bioelectronics, and regenerative medicine applications.In order to expand the use of SF-based hydrogels from basic biomedical research into clinical practice, a significant effort should be made to develop construction processes that offer slight batch-to-batch variations in an eco-friendly and time-saving way.

a
Polymer Performance Materials Group, Department of Chemical Engineering and Chemistry, Eindhoven University of Technology, 5600 MB Eindhoven, The Netherlands.E-mail: ozgnondr@gmail.comb School of Engineering and Technology, National Textile University, 37610 Faisalabad, Pakistan

Fig. 2 (
Fig. 2 (A) The life cycle of B. mori.(B) B. mori silk gland organization.Reproduced with permission from Elsevier. 27(C) Chemical structure of common repeat unit of SF.

Fig. 4 (
Fig. 4 (A) The structure of SF at different scales.(B) Chart representing the usage of methods to prepare self-assembled SF hydrogels.

Table 1
Gelation time of different fibroin solutions.Reprinted with permission from ref. 83.Copyright 2011 American Chemical Society