A microwave radiation-enhanced Fe–C/persulfate system for the treatment of refractory organic matter from biologically treated landfill leachate

In this study, a microwave (MW) radiation enhanced Fe–C/PS system was used to treat refractory organic matter in biologically-treated landfill leachate. The effects of important influencing factors on the refractory organic matter in biologically treated landfill leachate were explored, and the main reactive oxygen species produced in the system were verified. The mechanism by which humus was degraded was investigated by analyzing effectiveness of organics removal in different systems, and comparative analysis was conducted on the Fe–C materials before and after the reaction. The results showed that degradation capacity and reaction rate of the system could be improved with an increase in the Fe–C/PS dosage and MW power, while initial acidic conditions were also conducive to the degradation of organic matter. Under the conditions of an Fe–C of 1 g L−1, PS dosage of 30 mM, MW power of 240 W, and reaction time of 10 min, the UV254, TOC, and CN removal efficiencies were 51.48%, 94.56%, and 51.59%, respectively. In the MW/Fe–C/PS system, a large amount of and a small amount of ˙OH were generated by the thermal activation of PS to remove organic matter. The removal efficiency of organic matter could be further improved via the homogeneous catalytic oxidation and heterogeneous adsorption catalytic oxidation of Fe–C materials. In addition, the MW/Fe–C/PS system was effective for removing refractory organic matter from the leachates from four typical treatment systems: DTRO, SAARB, MBR, and NF. The MW/Fe–C/PS system has the potential to be widely applied for the treatment of landfill leachate.


Introduction
With rapid economic and social development and the acceleration of urbanization, municipal solid waste (MSW) output in China is increasing at an annual rate of 8-10%, 1 which has inevitably led to the continuous production of landll leachate. Landll leachate, as a complex and refractory highconcentration organic wastewater, 2,3 can cause secondary pollution of the environment, thereby endangering human health and disrupting the balance of ecosystems. 4,5 Biological and advanced membrane treatments are currently the preferred leachate treatment processes in China, 6-9 with the typical system being pretreatment + anaerobic + membrane bioreactor (MBR) + nanoltration (NF) + reverse osmosis (RO). Organic pollutants in the landll leachate can be effectively removed using this process, but there are broader changes in the water quality and quantity of landll leachate over time. Landll leachate typically has the characteristics of a high ammonia nitrogen concentration, 10,11 high organic matter content, 12,13 an unbalanced carbon-nitrogen ratio, 14,15 and poor biodegradability. 16,17 Traditional biological methods have proven relatively ineffective at removing organic matter from landll leachate alone, which together with the poor removal of ammonia nitrogen, total nitrogen, and humus has restricted the stability and efficiency of landll leachate treatment. 8 The semi-aerobic aged-refuse biolter (SAARB) is a low-cost and easy-to-operate pretreatment technology for landll leachate. 18,19 It uses natural ventilation to form an "aerobicanoxic-anaerobic" internal environment, enabling the organic matter in leachate to be degraded through "adsorptionexchange-degradation". 20 It has a strong removal effect for nitrogenous pollutants, as well as a strong buffering performance on the changes of leachate water quality. However, the effluent from a SAARB (denoted as SAARB leachate) cannot meet the relevant discharge standards due to its high concentration of refractory pollutants, and therefore further advanced treatment needs to be carried out on the SAARB leachate. 21,22 In contrast, advanced oxidation technology can generate highly chemically reactive free radicals through various physical or chemical reactions (e.g., photoelectric, acoustic, and magnetic reactions), enabling the refractory organic pollutants in wastewater to be rapidly degraded. [23][24][25][26] Persulfate (PS), a strong oxidant that is relatively convenient for storage and transportation, can generate SO À 4 , which has a high redox potential (E 0 ¼ 2.6 V), via different activation methods. [27][28][29][30] Its advantage over the cOH lies in its greater stability and longer half-life, 31 and it has therefore become widely applied in the in situ remediation of soil and groundwater, 32,33 as well as the treatment of landll leachate. 12,34,35 Persulfate is relatively stable at room temperature with a slow SO À 4 generation rate, resulting in a low degradation efficiency of organic matter. Many studies have attempted to improve the activation rate of PS and remove refractory organic matter by means of thermal activation, 36 light activation, 37,38 alkali activation, 39 and transition metal activation. [40][41][42] Some studies have found that Fe-C materials can effectively activate PS because of their favorable adsorption and catalytic activity. 43,44 However, when treating wastewater with a high concentration of difficult pollutants and complex components, the contaminated sediment will hinder the effective contact between the heterogeneous catalyst and the oxidant, thereby affecting the treatment effect. Microwaves (MW) radiation provides a means of activation with both thermal and non-thermal effects. 45,46 They can efficiently promote the activation efficiency of PS and reduce the activation energy and molecular bond strength required for system reaction by virtue of their thermal effects. In addition, their nonthermal effects can not only promote the activation of the oxidant, but also facilitate the regeneration of the lter and maintain the long-lasting surface reactivity. Therefore, the heterogeneous advanced oxidation system has a strong application potential. Few studies have been conducted on the enhancement of an Fe-C/PS system by MW radiation, especially in terms of the removal efficiency and degradation mechanism of refractory organic matter in SAARB leachate.
In this study, an MW-enhanced and Fe-C-activated PS advanced oxidation system (MW/Fe-C/PS) was used to treat refractory organic matter in landll leachate following treatment with a SAARB. First, the inuence of different factors (PS dosage, Fe-C dosage, MW power, and initial pH value) on refractory organic matter in the leachate was investigated. Second, the efficiency of an MW/Fe-C/PS system was analyzed by a comparison of the effectiveness of organic matter removal in different systems and through a three-dimensional (3D) excitation and emission matrix (EEM) analysis. Third, the degradation mechanism of an MW/Fe-C/PS system was analyzed in an alcohol quenching experiment and the physical properties of the Fe-C materials were characterized before and aer the reaction. Finally, an MW/Fe-C/PS system was used to treat the leachate resulting from several typical treatments, conrming the applicability and effectiveness of the MW/Fe-C/ PS system to treat landll leachate.

Landll leachates and chemicals
Landll leachate was collected from a large anaerobic landll site in southwest China. The leachate was alkaline and dark brown, having the characteristics of a typical aged landll leachate. The wastewater used in the experiment was the effluent resulting from the pretreatment of landll leachate by a SAARB. Detailed information of the SAARB was reported by previous studies. 18,19 The SAARB effluent was light brown, with an initial pH of 8.01, total organic carbon (TOC) content of 190 mg L À1 , an absorbance at wavelength 254 nm (UV 254 ) of 4.39 cm À1 , and a color number (CN) of 0.1755.
Potassium persulfate, concentrated sulfuric acid (H 2 SO 4 ), sodium hydroxide (NaOH), tert-butyl alcohol (TBA), and ethyl alcohol (EtOH) were all at analytical grade and were purchased from Chron Chemicals (Chengdu, China). An Fe-C ller was purchased from Puyinworun Environmental Co. Ltd. (Shandong, China). And Fe-C was crushed and screened by passing through a 100-mesh standard sieve for experimental use. A microwave-chemical reactor (MCR-3 type) was purchased from a Yuezhong Equipment Co. Ltd. (Shanghai, China).

Experimental methods
A 100 mL volume of leachate from an aged-refuse biolter was transferred to a 250 mL round-bottom ask. H 2 SO 4 and NaOH were used for pH adjustment. A preset amount of Fe-C and potassium persulfate was added and mixed evenly with a stirrer. Then, the mixture was immediately placed into a MW chemical reactor for reaction (10 min). A condensing device was operated during the reaction to reduce the evaporation of the solution. Aer the reaction was completed, the solution was immediately placed into an ice water bath to cool to room temperature in order to cease the reaction, and then ltered through a 0.45 mm ber lter membrane. The ltered water sample was tested, and a parallel experiment was then set up repeating the above steps.

Analysis methods
2.3.1. Analysis of water quality indicators. Water quality indicators were analyzed using standard methods. 47 The pH value was determined by the glass electrode method, TOC was determined by a total organic carbon analyzer (TOC-L CPH CN200, Shimadzu, Kyoto, Japan). The relative content of humus in the SAARB leachate was characterized by UV 254 . 48 Chromaticity was expressed by the CN, which was calculated as follows: 49,50 Samples were diluted to a certain multiple with secondary reverse osmosis ultrapure water and then analyzed by a spec-trouorometer (Aqualog-UV-800C, HORIBA, Kyoto, Japan). The xed excitation wavelength and emission wavelength were both 200-550 nm, with a scanning interval of 5 nm and a scanning speed of 2400 nm min À1 .
2.3.2. Material characterization. Before and aer the reaction, CuKa was used as the radiation source for Fe-C materials. In addition, the tube current was 40 mA and the tube voltage was 30 kV, with a scanning range of 10-80 and a scanning mode of q/2q, continuous scanning. The characterization was conducted using scanning electron microscopy (SEM: 5900LV, Jeol, Tokyo, Japan), X-ray Diffraction (XRD: XD-2, Puxi, Beijing, China), energy dispersive spectroscopy (EDS: Evo18, ZEISS Jena, Germany), and X-ray photoelectron spectroscopy (XPS: Thermo Fisher Scientic, Waltham, MA, USA).

Results and discussion
3.1. Inuencing factors 3.1.1. PS dosage. As shown in Fig. 1(a), the UV 254 , TOC, and CN removal efficiencies in the leachate all displayed an upward trend with an increase in the PS dosage. When the PS dosage was 30 mM, the removal efficiencies of UV 254 , TOC, and CN were 51.48%, 51.59%, and 85.31%, respectively. With an increase in the PS dosage, the concentration of reactive oxygen species produced in the system with a high oxidation performance increased. Over time, increasing amounts of SO À 4 and cOH were produced when PS was activated by contact with the surface of zero-valent iron, iron oxide, and iron oxyhydroxide in the Fe-C system. With an increase in the PS dosage, the solution pH decreased, the concentration of dissolved ferric ions increased, and more SO À 4 was generated by the homogeneous activation of PS; thus, increasing the organic matter removal efficiency. However, with a continuous increase in PS dosage, the removal efficiency tended to become stable. This was due to the concentration of organic matter in the system decreasing rapidly, which reduced the probability of contact. Additionally, the generated SO À 4 was easily annihilated by reaction with excess active components, such as S 2 O 8 2À , 51,52 Fe(II), 53,54 and SO À 4 , 55 which reduced the oxidation utilization rate of PS; thus, restricting the growth of the organic matter removal efficiency.
3.1.2. Fe-C dosage. As shown in Fig. 1(b), the organic matter removal efficiency in the leachate gradually increased with the increase in the Fe-C dosage. When the Fe-C dosage was 2 g L À1 , the UV 254 and TOC removal rates increased to 47.77% and 55.40%, respectively. The Fe-C materials had a well-developed porous structure and large specic surface area, which could adsorb and accumulate a small amount of organic matter by van der Waals attraction, and the marginal unsaturated carbon atoms could also provide equally active sites to adsorb nonpolar compounds in wastewater. 56 An increase in the dosage not only increased the adsorption capacity of organic matter, but also improved the contact probability between organic matter and surface activated free radicals. With an increase in the dosage of Fe-C materials, the contact area involved in PS surface catalysis was larger and the Fe 2+ concentration released by the reduction of iron increased. This accelerated the generation of SO À 4 ; therefore, reducing the concentration of organic pollutants. Furthermore, the pH value of the effluent decreased with an increase in the Fe-C dosage, which also indicated that the addition of Fe-C could promote the production of SO À 4 . Therefore, a large number of organic substances could be degraded and converted into acidic intermediate substances, resulting in a decrease in the pH value.
3.1.3. MW power. As shown in Fig. 1(c), the organic matter removal efficiency in the SAARB leachate also increased significantly with an increase in the MW output power. When the power increased from 80 to 400 W, the UV 254 , TOC, and CN removal efficiencies in the SAARB effluent increased by 49.11%, 48.70%, and 92.09%, respectively. This was because an increase in MW power not only facilitated a rapid temperature rise in the system, 30,57 but also promoted the decomposition of PS to produce SO À 4 . At the same time, the reaction temperature increased with the increased MW output power. Through these thermal and non-thermal effects, the activation energy and molecular chemical bond strength of the reaction in the system was effectively reduced, the oxidation reaction efficiency was improved, and the organic matter could then be degraded more easily. 58 However, with a continuous increase in MW output power, organic matter removal increased slowly, which may be attributed to the fact that PS was fully activated within 10 min at a MW power of 240 W, and the oxidation removal of organic matter by free radicals reached a maximum. Therefore, an increase in MW power led to only a slight increase in the organic matter removal efficiency. This was also demonstrated by the rapid decrease in the pH value of the effluent at 240 W, which then tended to remain unchanged.
3.1.4. Initial pH value. As shown in Fig. 1(d), the removal of organic matter by the system under acidic conditions was signicantly better than that under alkaline conditions. With an initial pH of 7, the UV 254 , TOC, and CN removal rates in the effluent were 45.54%, 53.80%, and 96.92%, respectively. The electrode reaction was promoted and the corrosion of Fe-C was accelerated under acidic conditions, 59 and therefore, the oxidation-reduction, electrocoagulation, occulation, and adsorption processes operated effectively. When the pH value of the reaction system increased, there was a larger amount of cOH in the system, which reacted with Fe 2+ /Fe 3+ to form ironcontaining precipitates. The existence of these precipitates in the solution could affect the mass transfer effect and the attack of organic matter by SO À 4 , while PS could be activated efficiently in the system. However, with an increase in the pH value, the probability of the decomposition of PS to SO À 4 increased, and the oxidation of organic matter by SO À 4 and cOH was further inhibited. Therefore, the removal of organic matter from the SAARB effluent by the MW/Fe-C/PS system was most effective under acidic conditions.

Comparison of the organic removal efficiency of different oxidation systems enhanced by MW
The organic matter removal effect of Fe-C alone, PS alone, and the Fe-C/PS, MW/Fe-C, MW/PS, and MW/Fe-C/PS systems during the treatment of landll leachate (i.e., SAARB effluent) were compared to determine the mechanism by which humus was degraded in each system. To investigate the activation effect of MW radiation, Fe-C materials, and their combined action on PS and the degradation of humus, an analysis of the removal effects of different leachate treatment systems was conducted using the SAARB effluent. The results are shown in Fig. 2. 3.2.1. Organic removal efficiency. As shown in Fig. 2(a), it was found that Fe-C alone, PS alone, and the Fe-C/PS system resulted in a relatively poor degradation of organic matter in the landll leachate (i.e., SAARB leachate). In the Fe-C system alone, a small amount of organic matter could be adsorbed by van der Waals attraction because the material had a welldeveloped porous structure and large specic surface area. The unsaturated carbon atoms at the edges also provided equally active sites to adsorb nonpolar compounds in the wastewater. In the PS system alone, PS did not easily decompose at room temperature, 60 and only a small amount of SO À 4 was generated to degrade some of the organic matter. In the Fe-C/PS system at room temperature, the pH of the solution was still alkaline due to the ineffective hydrolysis of PS, which was higher than the isoelectric point of the catalyst. It was therefore difficult for the catalyst surface to adsorb oxidant on the active sites, and iron ions could not be easily dissolved out. This promoted the activation of PS to a limited extent and slightly improved the organic matter removal efficiency.
Microwaves can reduce the activation energy and molecular bond strength required for the reaction in the system, 58 and at the same time they increase the reaction temperature, so that some organic matter can be thermally decomposed. However, they cannot directly degrade the humus and other refractory organic matter, and therefore the UV 254 removal efficiency of the MW system alone was only 4.78%. When MW radiation was introduced into the Fe-C, PS, and Fe-C/PS systems as a means of enhanced activation, the UV 254 and TOC removal efficiencies in each system increased to different degrees. This can be explained by the fact that MW radiation can cause magnetic materials, such as Fe-C materials, to rapidly accumulate energy and heat up. The chemical bonds in the attached organic matters can be broken, or they can even be mineralized and leave the internal pore space, increasing the potential for physical adsorption. This can also improve the activity of isoactive sites, increase the pace of chemical adsorption, and promote the direct oxidation of organic matter by Fe 0 , surface iron oxide, and Fe 2+ ; thus, increasing the removal of organic matter in the Fe-C system to a certain extent. Microwave radiation can rapidly increase the temperature of the system, and thermal activation is an effective way to activate PS to produce SO À 4 . 57,58 Aer heating by MW radiation, the activation rate of PS was greatly improved, and the organic matter removal efficiency in the system was signicantly improved. With the addition of MW radiation to the Fe-C/PS system, organic matter removal was further improved. The CN removal efficiency in the leachate reached 93.29%, while the UV 254 and TOC removal rates reached maximum values of 52.16% and 51.59%, respectively. With the optimization of the Fe-C adsorption performance, more organic matter was adsorbed and degraded, which further improved the organic matter removal efficiency.
3.2.2. 3D-EEM spectra. A number of studies have shown that different types of organic matter are distributed in different uorescence regions in the 3D-EEM spectrum. 50,61 As shown in Fig. 2(b), two main emission regions were identied in the leachate analyzed in this study. (1) A uorescence region in the range of F1 ¼ (Ex/Em ¼ 235-255 nm/410-450 nm) that represented the fulvic acid-like substances in the ultraviolet region, and was mainly caused by low-molecular-weight organic matter with a high uorescence frequency. 18 (2) A uorescence region in the range of F2 ¼ (E x /E m ¼ 310-360 nm/370-450 nm) that represented the fulvic-like substances in the visible light region, and was mainly caused by relatively stable aromatic organic matter with a large molecular weight. 50 According to Table S1, † the SAARB leachate mainly contained two kinds of substances: fulvic-like substances in the ultraviolet region and fulvic-like substances in the visible light region. The peak intensities of fulvic-like substances in the ultraviolet region and the visible light region in the SAARB leachate were 1398 and 938.1, respectively. Under different process conditions, the peaks of these two regions decreased to varying degrees, and the fulvic-like substances removal efficiencies in the ultraviolet and visible light regions in the MW/ Fe-C and MWPS systems were less than 20%, indicating that their removal effect on organic matter in the leachate was weak.
However, the fulvic-like substances removal efficiencies in the ultraviolet and visible light regions by the PS system alone were 52.22% and 21.09%, respectively, indicating that although the activation efficiency of the PS system alone was low at room temperature, the SO À 4 produced could effectively attack organic matter, breaking the chains and reducing the molecular weight. However, the mineralization (i.e., complete degradation) of organic matter was limited. In the Fe-C/PS system, the activation of PS by Fe-C increased the fulvic-like substances removal efficiencies in the ultraviolet and visible light regions to 61.59% and 34.70%, respectively. In the MW/PS and MW/Fe-C/ PS systems, the fulvic-like substances removal efficiencies in the ultraviolet and visible light regions reached 94.48% and 94.43%, respectively, and blue-shi clearly occurred in the uorescence peak position, indicating that the degree of molecular condensation and molecular weight of dissolved organic matter in the leachate were greatly reduced. Fulvic-like substances in the ultraviolet and visible light regions were effectively degraded into small-molecule organic matter, i.e., the humication degree of organic matter was reduced. This also indicated that the thermal activation of PS was the main process that effectively reduced the humication degree in the MW/Fe-C/PS system. On this basis, the adsorption-oxygen coupling process of Fe-C materials, in which they adsorb and catalyze PS and then oxidize organic matter, can further contribute to the reduction of humication degree of the treated SAARB leachate.

Identication of reactive oxygen species
Reactive oxygen species such as SO À 4 and cOH were produced during the degradation of organic matter by activated PS. The mechanism by which organic matter in the leachate was degraded by the MW/Fe-C/PS system was further investigated, and the major reactive oxygen species in the reaction process were veried. Two radical quenchers (TBA and EtOH) were added to the system in radical quenching experiments under the conditions of an Fe-C concentration of 1 g L À1 , PS dosage of 30 mM, MW output power of 240 W, and reaction time of 10 min.
As shown in Fig. 3, with the addition of TBA, the organic matter removal efficiency decreased slightly, and the inhibition effect was not obvious. With the addition of EtOH, there was an obvious decrease in the CN removal efficiency, and when n(EtOH):n(PS) ¼ 10, the removal efficiency decreased by 22.72%. These results indicated that both TBA and EtOH inhibited the removal of organic matter from the SAARB leachate in the MW/Fe-C/PS system to some extent, but the removal of organic matter was only marginally inhibited aer adding TBA. The addition of EtOH rapidly inhibited the degradation of organic matter in leachate in the oxidation system, indicating that EtOH had a stronger inhibition effect on the system than TBA. 58 Generally, TBA is oen used as a trapping agent for cOH, while EtOH is oen used as a trapping agent for both cOH and SO À 4 , 15,52 proving that SO À 4 and cOH existed simultaneously in the MW/Fe-C/PS system. The removal of organic matter was predominantly attributed to SO À 4 and was supplemented by cOH, indicating that Fe-C combined with MW radiation can effectively activate PS to produce SO

Transformation of Fe-C materials in the MW/Fe-C/PS system
The Fe-C materials were characterized by XRD, SEM, EDS, and XPS before and aer the reaction to investigate property changes of Fe-C materials, as well as the morphology, species, and relative content of each element in the Fe-C materials before and aer the reaction. Results are shown in Fig. 4.
3.4.1. XRD analysis. Fig. 4(a) shows the XRD patterns of the Fe-C materials before and aer the reaction. From a comparison with powder diffraction le (PDF) standards, the 2q peak coincided with Fe(PDF#65-5150) at 43.13 and 49.96 , and with C(PDF#50-0927) at 26.52 , 36.03 , and 43.32 , indicating that there was a large amount of elemental Fe and C prior to the Fe-C reaction. At the same time, there were obvious 2q peaks at 30.16 , 35.51 , 57.13 , 62.70 , and 89.93 before the reaction, indicating the presence of iron oxide and iron oxyhydroxide in the Fe-C materials. Many typical peaks were still present in the Fe-C materials aer the reaction, indicating that the Fe-C materials still contained elemental Fe and C aer the reaction. In addition, the 2q peaks at 30.16 , 35.51 , and 57.13 increased, indicating that in this system, Fe 0 formed iron oxides (such as Fe 3 O 4 ) aer the reaction.
3.4.2. SEM-EDS analysis. Fig. 4(b and c) show the SEM and EDS patterns of Fe-C materials before and aer the reaction, which enabled the changes in the surface morphology of Fe-C materials to be characterized. It can be seen from Fig. 4(b) that before the treatment of the SAARB leachate, the surface of the Fe-C material was relatively rough, the grain sizes were uneven and scattered, and there was a specic pore structure. The EDS pattern revealed a large Fe, O, and C content near the 0-2 keV interval, indicating that iron oxide was the main component in the large grains. There was a large Fe content in the 6-8 keV interval, indicating that Fe in small grains was mainly attached to the surface of C. It can be seen from Fig. 4(c) that Fe-C material could easily form iron corrosion products in an aerobic environment. From the peaks of C, O, and Fe in the EDS pattern and the decrease in their content aer the reaction, it was inferred that as the reaction progressed, part of the Fe was detached from the surface of the main crystal phase, and iron oxide and elemental Fe on the surface of the material were electrochemically corroded.
3.4.3. XPS analysis. Fig. 4(d) shows the XPS full scanning spectrum of Fe-C materials before and aer the reaction, enabling the morphology, species, and relative content of various elements in the Fe-C materials to be investigated. It can be seen from the gure that there were three typical characteristic peaks in the material, i.e., C 1s, O 1s, and Fe 2p, indicating that the Fe-C materials were mainly composed of C, O, and Fe. By analyzing and comparing the peak patterns before and aer the reaction of Fe-C materials it was found that the peak values of C and Fe displayed an upward trend, while the peak values of O displayed a downward trend. To better analyze the existing state, species, and relative contents of C, O, and Fe, O 1s, C 1s, and Fe 2p high resolution spectra of Fe-C materials were further analyzed. The results are illustrated in Fig. 4(e-g).
It can be seen from the peak diagram of O 1s that the binding energies corresponded to O 2 c À , cOH, and H 2 O at 529.40, 530.78, and 532.14 eV, respectively. As can be seen from Table S2, † the relative contents of O 2 c À and cOH increased to 1.88% and 23.15%, respectively, aer the reaction, implying that C played a role in adsorption and skeleton support during the removal of organic matter. The Fe and iron oxides loaded on the C skeleton played a leading role and could effectively participate in the reaction to form Fe(III), which could complex with organic functional groups on the carbon surface to achieve the removal of pollutants.
It can be seen from the C 1s peak diagram that the binding energies at 283.93, 284.59, 285.55, and 288.04 eV corresponded to C-C, C-O, C]O, and O]C]O bonds, respectively. It can be seen from Table S2 † that the contents of the C-C, C]O and O]C]O bonds were reduced aer the reaction, indicating that the Fe-C materials could destroy the oxygen-containing functional groups aer the reaction, and the C-C content was reduced from 21.96% to 8.68%, indicating that C has a strong adsorption effect on organic matter and participates in the removal of organic matter during the reaction. In addition, the relative content of C-O increased from 41.32% to 66.18% due to the adsorption of unsaturated bonds.
It can be seen from the Fe 2p peak diagram that the binding energies at 710.36, 712.72, 717.78, and 723.32 corresponded to Fe 0 , Fe(II), Fe(III), and Fe 3 O 4 , respectively. According to Table  S2, † the relative contents of Fe(II) and Fe 3 O 4 both decreased, while the contents of both Fe 0 and Fe(III) increased, indicating that Fe(II) could destroy the molecular structure of organic matter in this reaction system, reducing macromolecular organic matter to small molecular organic matter and transforming it into Fe 0 and Fe(III). The relative content of Fe 3 O 4 displayed a decreasing trend before and aer the reaction, which indicated that the Fe(III) contained in the reaction also participated in the formation of organic complex precipitates and formed a transformation chain of iron with different valence states. Therefore, the Fe-C materials aer the reaction still had a certain oxidation-reduction ability.

Wide applicability
Landll leachate is a high-concentration wastewater containing a variety of organic and inorganic substances. Treatment techniques need to be buffered against changes in the composition and concentration of contaminants given that the composition of different leachates varies greatly. The MW/Fe-C/PS system, as an advanced oxidation treatment technology with SO À 4 as the main reactive oxygen species, could play a unique role in effectively degrading most pollutants and adapting to the treatment needs of various types of wastewater, with a range of different compositions, by adjusting the reaction conditions to control the action intensity of oxidants. The effect of this system on the removal of refractory organic matter from different types of landll leachate was studied, and a reliability analysis was conducted to determine the effectiveness of an MW-Fe-C/PS system for the treatment of landll leachate containing different pollutants and other high concentration organic wastewaters.
Leachates from four typical treatment systems, disk tubereverse osmosis (DTRO), SAARB, MBR, and NF, were used as the research objects. For the SAARB and MBR, leachate effluents were treated by the SAARB and a two-stage biological nitrogen removal system, respectively, and the biodegradability was substantially reduced and the proportion of refractory organic matter was high. The DTRO and NF leachates were the concentrated (retentate) solutions of biologically treated effluent that were produced aer treatment by DTRO or NF membranes, respectively. The concentration of refractory organic matter was further enriched, and the concentrations of organic matter in each leachate were different (see Table 1 for details). Under the conditions of an Fe-C concentration of 1 g L À1 , MW output power of 240 W, and reaction time of 10 min, the PS dosage (oxidant) was varied (PS DTRO ¼ 10 mM; PS SAARB ¼ 30 mM; PS MBR ¼ 60 mM; PS NF ¼ 180 mM), and the MW/Fe-C/PS system was used to treat each of the four leachates.
3.5.1. Organic matter removal performance. The organic matter removals from the four leachates treated with the MW/ Fe-C/PS system and the humus degradation revealed by 3D-EEM are shown in Fig. 5. When the MW/Fe-C/PS system was used to treat the DTRO, SAARB, MBR, and NF leachates, as shown in Fig. 5(a), it was found that organic matter in the system was both removed effectively. The MW/Fe-C/PS system removed more than 40% of the UV 254 , 50% of the TOC, and more than 90% of the CN from the DTRO, SAARB, MBR, and NF leachates. The best results were obtained for the MBR leachate, with UV 254 , TOC, and CN removal efficiencies of 78.90%, 83.94%, and 99.41%, respectively. The results conrmed that the MW/Fe-C/PS system could decompose organic pollutants in various landll leachates in a stable and efficient manner.
The removal performance of MW/Fe-C/PS system on four leachates containing substances with different humication degree was further evaluated. As shown in Fig. 5(b), the four leachates from SAARB, MBR, DTRO, and NF had obvious peaks at F1 and F2, and the relative intensity of these two luminescent regions was signicantly different in different water samples. As shown in Table S3, † the relative intensity ranges of the F1 and F2 peaks for the four leachates were 659-1266 and 460.5-1533 respectively, among which the maximum relative intensities of F1 and F2 were 1266 (MBR) and 1533 (NF), respectively. It is generally believed that the lower the humication degree of organic matter, the lower the benzene-ring content, the lower the condensation degree of aromatic compounds, and the shorter the uorescence excitation corresponding to the peak of humic-like substances. All four leachates contained fulvic-like substances in the ultraviolet region and fulvic-like substances in the visible light region, but there were differences in the composition and concentration of benzene-ring and aromatic refractory pollutants. The relative intensity of these two uorescent regions in the four leachates treated by the MW/Fe-C/PS system decreased to a large extent, and the peak position of the uorescence peaks occurred blue-shi. The removal efficiencies of fulvic-like substances in the ultraviolet region and fulvic-like substances in the visible light region reached over 90% for the SAARB and MBR leachates, which indicated that the degree of molecular condensation and molecular weight of aromatic compounds in the leachates decreased greatly, while the degree of humication had increased. These results indicate that the MW/Fe-C/PS system has a wide practicability and feasibility for the treatment of landll leachate.

Proposed reaction mechanism of MW/Fe-C/PS system
The reaction mechanism was proposed and illustrated in Fig. 6.
In the MW/Fe-C/PS system, the system temperature rose rapidly under the action of MW radiation and the PS was thermally activated. At the same time, Fe-C itself has a certain adsorption capacity, reduction capability, and catalytic property, which can activate PS on the surface of the catalyst (heterogeneous catalysis) and in the solution (homogeneous catalysis). Both the SO À 4 generated by PS activation and the cOH generated by its chain reaction were used to remove organic matter. 3.6.1. Thermal activation of PS. Under the action of MW radiation, the temperature of the system rose rapidly. Aer the PS adsorbed on the catalyst surface and solution absorbed heat energy, the O-O bond was broken to form SO À 4 , which can react with H 2 O/OH À to further generate a small amount of HOc. Both SO À 4 and HOc are highly oxidative reactive oxygen species with an unsaturated electronic structure, which can react with the time of 10 min, the UV 254 , TOC, and CN removal efficiencies from leachate were 51.48%, 94.56%, and 51.59%, respectively.
(3) In the MW/Fe-C/PS system, the organic matter in the SAARB leachate was mainly degraded by the high-efficiency activation of PS by the thermal effect of MW radiation and the homogenous and heterogeneous activation of iron species, while the adsorption-oxidation coupling system of Fe-C further improved the degradation efficiency of organic matter.
(4) The MW/Fe-C/PS system has a strong removal effect on the refractory organic matter from the SAARB, MBR, DTRO, and NF leachates. Therefore, the MW/Fe-C/PS system has the potential to be widely applied for the treatment of landll leachate.

Conflicts of interest
There are no conicts to declare.