Low temperature scalable synthetic approach enabling high bifunctional electrocatalytic performance of NiCo2S4 and CuCo2S4 thiospinels

Ternary metal sulfides are currently in the spotlight as promising electroactive materials for high-performance energy storage and/or conversion technologies. Extensive research on metal sulfides has indicated that, amongst other factors, the electrochemical properties of the materials are strongly influenced by the synthetic protocol employed. Herein, we report the electrochemical performance of uncapped NiCo2S4 and CuCo2S4 ternary systems prepared via solventless thermolysis of the respective metal ethyl xanthate precursors at 200 and 300 °C. The structural, morphological and compositional properties of the synthesized nanoparticles were examined by powder X-ray diffraction (p-XRD), transmission electron microscopy (TEM), high-resolution TEM, scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) techniques. Electrochemical studies indicate that NiCo2S4 nanoparticles synthesized at 300 °C exhibit superior energy storage characteristics with a high specific capacitance of ca. 2650 F g−1 at 1 mV s−1, as compared to CuCo2S4 nanoparticles, which showcased a specific capacitance of ca. 1700 F g−1 at the same scan rate. At a current density of 0.5 A g−1, NiCo2S4 and CuCo2S4 nanoparticles displayed specific capacitances of 1201 and 475 F g−1, respectively. In contrast, CuCo2S4 nanoparticles presented a higher electrocatalytic activity with low overpotentials of 269 mV for oxygen evolution reaction (OER), and 224 mV for the hydrogen evolution reaction (HER), at 10 mA cm−2. The stability of the catalysts was examined for 2000 cycles in which a negligible change in both OER and HER activities was observed.


Introduction
Designing energy storage devices and conversion technologies based on clean and renewable energy is critical for sustainable energy development. Supercapacitors have demonstrated high functional capability in terms of power density, lifecycle, and charge-discharge rate and have therefore received great attention as efficient energy storage devices. 1 Responding to the projected high energy consumptions, recent studies have mainly focused on improving device energy density and rate capability. 2 The hydrogen production via the electrochemical splitting of water is another intensively investigated strategy of renewable energy storage and/or conversion. 3 While the approach presents a simple way of producing high purity hydrogen, its practical application is impeded by the large overpotential involved. 3,4 To attain faster reaction kinetics and scale-up hydrogen production, the process requires the use of earth-abundant, cost-effective and highly efficient electrocatalysts. 5 On this account, numerous electroactive materials have been investigated for both energy storage and energy conversion applications. Transition metal nitrides, 6 transition metal dichalcogenides, 7 hybrids of metals and metal phosphides/metal nitrides, 8 carbon nanomaterials, their doped derivatives, and composites, 9 and ternary thiospinels, 1b,10 are examples of advanced materials which have demonstrated remarkable performance. NiCo 2 S is a normal thiospinel with remarkable electrochemical performance. 1b, 11 This superior performance is believed to be due to the high conductivity of the material, which is attributed to its metallic character. 11 Since the rst report by Chen et al., 12 a large number of studies on the use of NiCo 2 S 4 in supercapacitors, 13 batteries, 14 dye-sensitized solar cells, 15 oxygen reduction/evolution reactions, 16 and hydrogen generation reactions 17 have been carried out. Recently, CuCo 2 S 4 , another member of the ternary thiospinels, has been reported for its potential in energy storage/conversion applications. 18 Similar to NiCo 2 S 4 , CuCo 2 S 4 , has a normal thiospinel crystal structure with copper and cobalt ions occupying the tetrahedral and octahedral sites, respectively. 19 It is paramagnetic and metallic, with unique electronic properties. For instance, it exhibits a low resistivity (10 À4 U), and s-wave superconductivity at low temperature. 20 Specically, CuCo 2 S 4 has mainly been studied as an electrode material for lithium-ion batteries, 18c sodium-ion batteries, 18b and supercapacitors. 18e Limited studies on the electrocatalytic activity of CuCo 2 S 4 in oxygen reduction/ evolution reactions, 18d and hydrogen generation reactions 18a are known. Both bulk and nanostructured NiCo 2 S 4 /CuCo 2 S 4 based materials have been studied. It has been shown that, nano-engineering of the electrodes/electrocatalysts enhances the electrochemical performance of the materials. 1b, 21 The synthetic protocol employed in nanomaterials preparation is among the key factors determining the nal structure and resultant properties of the materials. 1b, 22 Years of extensive research on nanoscience and nanotechnology has provided us with numerous synthetic approaches, with solution-based techniques dominating the eld. 23 A characteristic feature of nanomaterials synthesized in solution is the presence of surface adsorbed ligands which provide particle stabilization via electrostatic or steric repulsive interactions. Long-chain amines, carboxylates, thiols, and phosphines are some of the commonly employed ligands. 24 While capping ligands are indispensable during nanoparticles synthesis, studies have shown that the presence of these ligands on the surface of a nanoparticle may, in some cases, act as impurities, blocking the particle's active sites and diminish the material's end application, particularly catalysis. For example, Ung et al. 25 studied the effect of various amine and carboxylate ligands on the electrocatalytic activity of CoP towards hydrogen generation in which the uncapped CoP nanocrystals demonstrated higher activity than the capped nanocrystals. Lu et al. 26 examined the electrocatalytic activity of Ag nanorods for oxygen reduction reaction in which the surfactant-free nanorods displayed higher activity than the nanorods capped with polyvinylpyrrolidone. In another study, Henckel et al. 27 investigated the role of dodecylamine, as a surfactant, on the hydrogen generation activity of WSe 2 . Removing the ligand from the catalytic sites of the material was observed to improve the kinetics of the reaction. The synthesis of nanomaterials free of capping ligands is therefore crucial for their catalytic performance. Several techniques for the removal of the capping ligands aer nanomaterials synthesis have been developed. [26][27][28] However, most of these techniques are laborious, expensive, and sometimes alter the shape and stability of the particles. 29 The melt method is a recently described approach of synthesis which allows the preparation of nanomaterials in the absence of any passivating ligands. 30 This provides the possibility of synthesizing nanomaterials with abundant active sites for enhanced electrochemical performance. Unlike solutionbased techniques, nanomaterials are synthesized via solventfree, surfactant-free thermolytic decomposition of their corresponding molecular precursors. 30,31 The approach is therefore simple, inexpensive and eco-friendly. Herein, we report the synthesis of uncapped NiCo 2 S 4 and CuCo 2 S 4 nanoparticles via the melt approach using respective metal ethyl xanthate precursors. The efficiency of the synthesized ternary systems for supercapacitance and water splitting applications has been examined. To the best of our knowledge, this is the rst study investigating the electrochemical properties of the two systems synthesized using the melt approach.

Instrumentation
Elemental analysis of the complexes was performed on a Perki-nElmer automated model 2400 series II CHNS/O analyzer. Thermogravimetric analysis was done from 30 to 600 C at 10 C min À1 using a PerkinElmer Pyris 6 under N 2 gas ow. p-XRD analysis was performed using a Bruker AXS D8 diffractometer equipped with a nickel-ltered Cu Ka radiation (l ¼ 1.5418Å) at 40 kV, 40 mA, at room temperature. The diffraction patterns were recorded in the high angle 2q range of 10-70 at a scan speed of 0.2 s per step and an increment of 0.01314. TEM and HRTEM analyses of the synthesized ternary systems were carried out using a JEOL 1400 TEM and JEOL 2100 HRTEM, respectively. Samples were prepared by placing a drop of the particles dilute solution on Formvar-coated grids (150 mesh) for TEM and holey carbon grids for HRTEM. The samples were allowed to dry completely at room temperature, viewed at accelerating voltages of 120 kV and 200 kV for TEM and HRTEM, respectively. Images were captured digitally using a Mega view III camera; stored and measured using so imaging systems iTEM soware (TEM) and Gatan camera with Gatan soware (HRTEM). Analysis of surface morphology of the synthesized particles was carried out using a Zeiss Ultra Plus FEG Scanning Electron Microscope (SEM) equipped with an Oxford detector EDX at 20 kV which uses Aztec soware for elemental analysis. Kratos Axis Ultra DLD spectroscopy was used to record the X-ray photoelectron spectroscopy (XPS) and the equipment setup and specication were as previously reported. 32 Curve tting and quantitative analysis were conducted using Vision soware. NIST XPS database was used for peak assignment for the high-resolution spectra and all binding energies were calibrated against carbon at 284.9 eV.

Synthesis of bis(O-ethylcarbonodithioato)nickel(II)
; complex (1). In a typical reaction, nickel acetate tetrahydrate (1.2443 g, 5.0 mmol) was dissolved in distilled water (25.0 mL) followed by its drop-wise addition into the aqueous solution of potassium ethyl xanthogenate (1.603 g, 10.0 mmol). The reaction mixture was stirred for 1 hour, aer which the formed precipitates were washed with distilled water, dried under vacuum and recrystallized from chloroform.
Elemental analysis for C 6 (2). The synthetic procedure used to prepare complex (1) was followed using copper(II) chloride dihydrate (0.8524 g, 5 mmol) as the source of copper.
Elemental analysis for C 6

The solventless synthesis of NiCo 2 S 4 and CuCo 2 S 4 nanoparticles
Stoichiometric quantities of the required complexes (complexes (1) and (3) for NiCo 2 S 4 ; and complexes (2) and (3) for CuCo 2 S 4 ) were ground together to obtain a homogenized mixture. The mixture was then spread in a ceramic boat and placed at the center of a quartz tube. The sample was heated in the furnace at a specied temperature (200 C or 300 C) for one hour under N 2 ow and then allowed to cool down to room temperature.

Electrochemical studies
Electrochemical characterization of the synthesized materials was performed using Gamry Potentiostat using a three-electrode system. A paste consisting of the synthesized sample (80 wt%), acetylene black (10 wt%), and polyvinylidene diuoride (PVDF, 10 wt%) was prepared using N-methyl pyrrolidinone (NMP) as a solvent. This paste was then applied to pre-cleaned and weighted nickel foam. The paste was then dried under a vacuum at 60 C for 10 hours and used as a working electrode. A graphite rod/platinum wire and saturated calomel electrode (SCE) were used as counter and reference electrodes, respectively. All the experiments for energy storage and electrocatalysis were performed using 3 M and 1 M KOH electrolyte, respectively. Charge storage capacity was measured using cyclic voltammetry (CV) and galvanostatic charge-discharge (CD) at various scan rates and current densities. Electrocatalytic properties of the synthesized electrodes were studied using linear sweep voltammetry (LSV), cyclic voltammetry and chronoamperometry (CA). LSV was performed at a scan rate of 2 mV s À1 for both OER and HER measurements.

Characterization of the precursors and the nanoparticles
The preparation of complexes (1), (2), and (3) involved a wellknown synthetic procedure. 33 The thermal stability behavior of the complexes was analyzed by TGA and the results are shown in Fig. S1, ESI. † The analysis indicates that all three complexes decompose in a single step to give respective metal sulde. Specically, complex (1) shows initial decomposition at 132 C and complete decomposition occurs at 228 C. A weight loss of 72% is observed, and the remaining residual weight (28%) agrees well with that of NiS (29%). Complex (2) decomposes at 210 C with an onset temperature of 77 C. This yields a 30% residue, which corresponds to the theoretical value calculated for CuS (31%). On the other hand, complex (3) starts decomposing at 96 C and complete decomposition occurs at 203 C. A 27% residual weight which correlates with that of CoS (29%), is produced. Generally, all three complexes show complete decomposition at moderate temperatures, which is a characteristic feature of xanthate complexes. Compared to several other precursors, the low decomposition temperature and formation of volatile by-products (COS and an alkene) make xanthates complexes favourable precursors for the solventless synthesis of metal suldes. 34 The two ternary systems were synthesized via thermolysis of stoichiometric mixtures of the required complexes at 200 and 300 C. The solventless pyrolysis of a mixture of complexes (1) and (3) at both 200 and 300 C produced black residues, which upon p-XRD analysis, were identied as phase-pure cubic NiCo 2 S 4 (ICDD #: 00-020-0782) (Fig. 1a). The corresponding diffraction peaks are sharp, which denotes the crystallinity of the materials. The relative broad diffraction peaks observed for NiCo 2 S 4 synthesized at 200 C are indicative of small-sized particles. The average crystallite sizes were calculated from the Scherrer equation and were found to be 5.3 and 12.8 nm at 200 and 300 C, respectively. On the other hand, the solventless pyrolysis of a mixture of complexes (2) and (3) at the two temperatures yielded phase-pure cubic CuCo 2 S 4 (ICDD #: 00-042-1450) (Fig. 1b). The diffraction peaks are also sharp in this case, signifying the synthesis of crystalline CuCo 2 S 4 . The average crystallite sizes of CuCo 2 S 4 synthesized at 200 and 300 C were found to be 20.1 and 22.9 nm from the Scherrer equation, respectively.
The lattice parameters of the synthesized materials were calculated from the XRD data using the relation 1/d 2 ¼ (h 2 + k 2 + l 2 )/a 2 . The values were found to be approximately 9.350Å and 9.348Å for NiCo 2 S 4 nanoparticles synthesized at 200 and 300 C, respectively, and 9.443Å for CuCo 2 S 4 nanoparticles synthesized at 200 and 300 C, respectively. These values compare well with the theoretical lattice parameters (9.387Å for NiCo 2 S 4 and 9.474Å for CuCo 2 S 4 ).
Morphological properties of the synthesized materials were examined using TEM/HRTEM and SEM analyses. TEM analysis of NiCo 2 S 4 prepared at 200 C reveals the synthesis of highly agglomerated particles with undened morphology (Fig. 2a). Carrying out the synthesis at a higher reaction temperature of 300 C produced particles with a more dened morphology and reduced degree of particle-particle agglomeration. Elongated nanoparticles with approximately uniform sizes were obtained (Fig. 2b). The observed average particle size correlates with that calculated from the Debye-Scherrer equation. Due to the high degree of agglomeration, the average size of the particles synthesized at 200 C could not be estimated from their TEM image. The agglomeration observed at both 200 and 300 C is mainly due to the absence of a surface passivating agent. In the absence of surfactants, control over size and shape is challenging. The initially formed nano-sized particles have high surface energy and tend to agglomerate to lower their surface energy. Although melt reactions are sometimes characterized as 'self-capping', it has been shown that the control over the size and shape of the nanoparticles is mainly achieved with long alkyl chain precursors. For instance, Zhang et al. 33c reported the solventless synthesis of Ag 2 S nanoparticles via thermal decomposition of silver xanthate precursors of varying alkyl chain lengths. The size of the particles was observed to decrease with increasing the alkyl chain length of the precursor. O'Brien et al. 35 employed a similar approach to synthesize PbS nanocrystals from various xanthate precursors in which control over the size and shape of the nanocrystals was achieved by increasing precursor chain length. Therefore, the use of shortchain xanthates is thought to be another reason for the observed agglomeration behavior.
The HRTEM image of NiCo 2 S 4 nanoparticles synthesized at 300 C shows unidirectional lattice fringes with a d-spacing of 0.28 nm, which matches that of the (311) plane of the cubic phase NiCo 2 S 4 (Fig. 2c). The corresponding selected area electron diffraction (SAED) image shows bright spots, further detailing the crystalline nature of the material. The diffraction rings can be indexed to the (400), (311), (511) and (440) planes of cubic NiCo 2 S 4 (ICDD #: 00-020-0782) (Fig. 2d).
TEM images of CuCo 2 S 4 nanoparticles synthesized at both 200 C and 300 C are shown to exhibit a sheet-like morphology ( Fig. 3a and b). As was the case with NiCo 2 S 4 nanoparticles, the tendency of particle-particle agglomeration is also observed in this case. The HRTEM images of the particles synthesized at 300 C show two types of lattice fringes with a d-spacing of 0.33 and 0.28 nm which matches that of the (022) and (113) planes of cubic CuCo 2 S 4 , respectively ( Fig. 3c and d). The areas shown by red arrows indicate the presence of slightly distorted lattice planes (Fig. 3c). This can be a result of rapid growth, which is a characteristic feature of the melt method. 36 Rapid growth can cause atoms to be displaced from their original positions, inducing various crystal defects.
The composition of the synthesized materials was examined by Energy Dispersive X-ray Spectroscopy (EDX). The EDX spectra of NiCo 2 S 4 and CuCo 2 S 4 nanoparticles synthesized at both 200   (Fig. 4).
XPS analysis was carried out to study the surface composition and chemical states of the two ternary systems. NiCo 2 S 4 and CuCo 2 S 4 synthesized at 300 C were used as representative samples. The survey spectra of the two systems are shown in Fig. 5. The presence of Cu 2p peaks at 943 eV for CuCo 2 S 4 and Ni 2p peaks at 870 eV for NiCo 2 S 4 together with Co 2p at 790 eV and S 2p at 164 eV conrms that CuCo 2 S 4 and NiCo 2 S 4 were successfully synthesized. The O 1s (530 eV) and C 1s (285 eV)  peaks resulted from the method used in the preparation of the sample and from the metal ethyl xanthate precursors. A slight stoichiometric variation is evident as the elements nickel, cobalt, and sulfur have the tendency to exist in two mineralogical forms, i.e., NiCo 2 S 4 or CoNi 2 S 4 . Therefore, with different oxidation states, cobalt can interchangeably occupy tetrahedral or octahedral positions, which may affect the peak intensity and composition. Fig. 6 shows high-resolution spectra of Co 2p for (a) CuCo 2 S 4 and (b) NiCo 2 S 4 ; S 2p for (c) CuCo 2 S 4 and (d) NiCo 2 S 4 ; Cu 2p for CuCo 2 S 4 (e), and Ni 2p for NiCo 2 S 4 (f). The Co 2p for both samples showed three oxidation states Co 3+ , Co 2+ and Co + , and the NiCo 2 S 4 sample showed the presence of strong satellite peaks at high binding energy. The CuCo 2 S 4 sample exhibited a high concentration of Co 3+ species (70.1%) compared with 45.3% of NiCo 2 S 4 sample. Mixed oxidation states of Co were related to the presence of various sulfur oxidation states (S 2À , S 2 2À , C-S) as observed in Fig. 6c for CuCo 2 S 4 and (d) for NiCo 2 S 4 . The NiCo 2 S 4 sample in Fig. 6d Fig. 6f also showed mixed oxidation states at different binding energies with 26.4% metallic (Ni 0 ) at 853.2 eV and Ni 2+ at 855.9 (51.2%) and 858.5 eV (21.4%).

Electrochemical studies
Henceforth, the NiCo 2 S 4 nanoparticles synthesized at 200 C and 300 C will be referred to as NCS-200 and NCS-300, respectively, whereas CuCo 2 S 4 nanoparticles synthesized at 200 C and 300 C will be referred to as CCS-200 and CCS-300 respectively. 3.2.1. Energy storage application. The electrochemical charge storage mechanism of the synthesized NiCo 2 S 4 and CuCo 2 S 4 at different annealing temperatures was rst analyzed using CV tests. As observed from the CV curves at 5 mV s À1 , all the samples showed a distinct set of oxidation and reduction peaks (Fig. 7a). More specically, a higher intensity of redox peak indicates improved intercalation of electrolyte ions within the interstitial sites of the thiospinels structure. 37 As predicted by this study, the 300 C annealed samples showed a well-dened structure with minimal nanoparticle agglomeration, allowing a higher exposed surface area for the improved pseudocapacitive performance compared to the 200 C annealed samples. The CV curves for NCS-300 and CCS-300 electrodes at varying scan rates can be summarized from Fig. 7b and c. As the scan rates were decreased from 300 mV s À1 to 1 mV s À1 , pseudocapacitive characteristics of the synthesized electrodes were observed. This could be due to the improved accessibility of the electrolyte ions to facilitate near-surface redox reactions provided by our annealing process. The real-time charge storage performance of NCS-300 and CCS-300 was further analyzed using galvanostatic charge-discharge (CD) test in which a longer charge-discharge time was displayed by NCS-300, indicating higher charge storage activity (Fig. 7d-f).   À1 (a, b). Variation of specific capacitance vs. current density from 0.5 to 15 A g À1 (c, d).
The specic capacitance of NCS-300 and CCS-300 as a function of scan rates are shown in Fig. 8a and b. NCS-300 displayed the highest specic capacitance of ca. 2650 F g À1 at 1 mV s À1 , whereas CCS-300 achieved a specic capacitance of ca. 1700 F g À1 at the same scan rate. The variation of specic capacitance of the two electrodes as a function of current density is shown in Fig. 8c and d. It can be seen that NCS-300 exhibits the highest specic capacitance of 1201 F g À1 at the applied current density of 0.5 A g À1 . This value is much higher compared to several other reported NiCo 2 S 4 electrodes prepared by other methods. For instance, Pu et al. employed a sacricial template approach based on the Kirkendall effect to synthesize hollow hexagonal NiCo 2 S 4 nanoplates, which delivered a specic capacitance of 437 F g À1 at a current density of 1 A g À1 . 38 Xu et al. synthesized NiCo 2 S 4 nanoparticles via a one-step solvothermal approach, which displayed a specic capacitance of 519.51 F g À1 at a current density of 2 A g À1 . 39 Similarly, mesoporous NiCo 2 S 4 nanosheets prepared by Wu et al. via a one-pot hydrothermal method displayed a specic capacitance of 744 F g À1 at a current density of 1 A g À1 . 40 A further comparison with composites or heterostructures of NiCo 2 S 4 indicates that the specic capacitance observed for NCS-300 is also higher than, 41 or comparable to 39 several other values reported for NiCo 2 S 4 -based electrodes. As it is well-known, the synthetic methodology employed in the preparation of nanomaterials has a high inuence on the properties and applications of the materials. It can therefore be speculated that the  solventless approach employed herein plays an important on the observed performance. This is due to the fact that the method allows the synthesis of nanomaterials free of long-chained capping ligands, 42 which have been shown to be detrimental to the electrochemical performance of the materials. [25][26][27] Contrary to the performance observed for NCS-300, CCS-300 showcased a specic capacitance of 475 F g À1 at the same current density of 0.5 A g À1 . Although this performance is much lower than that of NCS-300, it is still higher than 43 or comparable to 38,44 some of the previously reported CuCo 2 S 4 /NiCo 2 S 4 -based electrodes. Generally, NCS-300 displayed better energy storage characteristics than CCS-300, which can be attributed to its high conductivity. 45 A detailed comparison of the observed specic capacitance values with previously reported values for unary and binary metal oxide/ sulde systems is given in Table S1. † 3.2.2. Energy generation application. Considering the higher oxidation and reduction activity of the 300 C annealed samples, we tried to further analyze their electrocatalytic performance on the overall water splitting reaction for the fuel cell applications.
The OER and HER activity of the synthesized NCS-300 and CCS-300 electrodes can be summarized in Fig. 9. Unlike supercapacitors, the catalytic activity observed from the polarization curves for NCS-300 and CCS-300 shows a distinct behavior. This is due to two different sets of reaction mechanisms involved in HER and OER reactions. The overall water splitting mechanism includes adsorption and desorption of hydrogen and oxygen atoms by breaking the water molecule over the catalyst surface. 46 The thiospinel structure facilitates tetrahedral and octahedral coordination to allow bi-functional oxygen and hydrogen evolution reactions. 46b Both the thiospinel catalysts showed high OER and HER activity. The CCS-300 showed higher OER catalysis with a low overpotential of 269 mV than NCS-300 (318 mV) at 10 mA cm À2 (Fig. 9a). On the other hand, NCS-300 showed higher HER catalysis with a low overpotential of 209 mV as compared to CCS-300 (224 mV) at 10 mA cm À2 (Fig. 9b). The high OER/HER activity could be due to coordination between high spin Co 3+ and Cu 2+ / Ni 2+ oxidation states with sulfur facilitating higher electronic conductivity for bifunctional catalysis. 47 The NiCo 2 S 4 nanowires/Ni foam electrode prepared by Sivanantham et al. achieved low overpotentials of 210 mV for HER and 260 mV for OER at 10 mA cm À2 , which is comparable to CCS-300. 48 The catalytic activity observed for CCS-300 is also comparable to that of CuCo 2 S 4 / NiCo 2 S 4 electrocatalyst synthesized via a hydrothermal approach. 49 Furthermore, the OER activity displayed by CCS-300 is superior to that of CuCo 2 S 4 nanoparticles (395 mV at 10 mA cm À2 ), 50 NiCo 2 -S 4 @N/S-rGO composite (470 mV at 10 mA cm À2 ), 51 and CuCo 2 S 4 nanosheets (310 mV at 10 mA cm À2 ), 52 prepared by other methods. A more detailed comparison for the HER/OER activity of CCS-300 and NCS-300 with previously reported catalysts is summarized in Table S2. † The Tafel plots for HER/OER activity for the two catalysts are summarized in Fig. 9c and d. The kinetics of the catalytic reaction observed from the Tafel plots directly correlate to the HER/OER performance observed during the polarization test in Fig. 9a and b. The Tafel slopes for the OER activity were calculated to be 89 and 103 mV dec À1 for NCS-300 and CCS-300, respectively, whereas the Tafel slopes for the HER activity were found to be 150 and 185 mV dec À1 for NCS-300 and CCS-300, respectively. For comparison purposes, the electrochemical performance of commercial Pt catalyst was also measured. As seen in Fig. S3, † Pt is a good catalyst for the HER process (overpotential of 33 mV); however, the catalyst displays an overpotential of 545 mV for the OER process, which is higher than that displayed by CCS-300 (269 mV).
The electrocatalytic stability test for both the catalyst electrodes was further examined for 2000 cycles. As shown in Fig. 10a, both the catalysts showed a negligible change in their OER/HER catalytic performance and maintained their low overpotential values for 2000 cycles. The OER chronoamperometry curves in Fig. 10b shows that both the catalysts retained their high current value corresponding to stable catalytic activity aer continuous polarization for more than 15 h.
The electrochemical surface area of NCS-300 and CCS-300 was calculated by performing CV at various scan rates in nonfaradic regions. The plotting relation of current density with scan rate is found to be linear. The slope was observed to be 38 mC cm À2 for NCS-300 and 39.4 mC cm À2 for CCS-300. The higher slope (electrochemical surface area) of CCS-300 suggests better electrochemical properties for the water-splitting application (Fig. 11).

Conclusion
In summary, we have employed a facile, solventless approach to synthesize uncapped NiCo 2 S 4 and CuCo 2 S 4 nanoparticles for supercapacitance and water splitting applications. The synthesis was achieved via thermolysis of respective metal ethyl xanthate precursors at 200 and 300 C. p-XRD and TEM analyses reveal the synthesis of highly crystalline phase pure Fig. 11 CV curves at various scan rates for NCS-300 and CCS-300. nanomaterials with some degree of particle-particle agglomeration. Electrochemical characterizations indicate that the particles synthesized at a high temperature of 300 C exhibits better energy storage characteristics. The highest specic capacitance of 1201 F g À1 at a current density of 0.5 A g À1 was observed for NiCo 2 S 4 nanoparticles, whereas CuCo 2 S 4 nanoparticles displayed a specic capacitance of 475 F g À1 at the same current density. Conversely, the best electrocatalytic activity was observed for CuCo 2 S 4 nanoparticles, which require overpotentials of 269 mV for OER, and 224 mV for HER, to deliver a current density of 10 mA cm À2 . The stability of the catalysts was examined for 2000 cycles in which a minor change in both OER and HER activities was observed.

Conflicts of interest
There are no conicts to declare.