Synthesis of a hollow-structured flower-like Fe3O4@MoS2 composite and its microwave-absorption properties

In order to realize the characteristics of new types of wave-absorbing materials, such as strong absorption, broad bandwidth, low weight and small thickness, a hollow-structured flower-like Fe3O4@MoS2 composite was successfully prepared by simple solvothermal and hydrothermal methods in this paper. The structural properties were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Besides, the microwave properties and magnetic properties were measured using a vector network analyzer and via a hysteresis loop. SEM and TEM images revealed that MoS2 nanosheets grew on the surface of hollow nanospheres. The results showed that the composite exhibited excellent absorbing property. When the molar ratio of Fe3O4 and MoS2 was 1 : 18, the minimum reflection loss value reached −49.6 dB at 13.2 GHz with a thickness of 2.0 mm and the effective absorption bandwidth was 4.24 GHz (11.68–15.92 GHz). Meanwhile, the effective absorption in the entire X-band (8–12 GHz) and part of the C-band (4–8 GHz) and Ku-band (12–18 GHz) could be achieved by designing the sample thickness. In addition, the hollow structure effectively reduced the density of the material, which was in line with the current development trend of absorption materials. It could be predicted that the hollow core–shell structure composite has a potential application prospect in the field of microwave absorption.


Introduction
With the advent of 5G, the relationship between wireless communication installations and human livelihoods is increasingly inseparable. Microwave radiation is becoming one of the most serious factors threatening human wellbeing, 1,2 so it is urgent to settle the issue of electromagnetic contamination. Consequently, the exploration of electromagnetic absorbers is imbued with distinct real-world signicance owing to the characteristics of strong absorption, 3 low density, 4 broad bandwidth and small thickness. 5 Compared to the conventional electromagnetic shielding materials, use of microwave absorbers is regarded as a more efficacious method to dominate electromagnetic contamination. 6 A good electromagnetic absorber must have impedance matching and attenuation characteristics to eliminate the problem of secondary reection contamination and allow the electromagnetic energy to be converted into heat energy in the material. 7 According to the fundamental formula, when the dielectric constant 3 (3 ¼ 3 0 À j3 00 ) is equal to the permeability m (m ¼ m 0 À jm 00 ), the incident wave can totally enter the material without reection. 8 And the attenuation characteristics depend on the loss mechanism itself, which consists of magnetic loss, dielectric loss and conductivity loss. In addition, it has been reported that the morphology and construction have non-negligible effects on the absorbing properties. 9 Traditional ferrite materials possess exclusive features of strong saturation magnetization, high complex permeability as well as being of low cost, which have been extensively applied in the eld of microwave absorption. 10,11 Ferrosoferric oxide (Fe 3 O 4 ) as the simplest ferromagnetic substance has been widely used in dye degradation, 12 biomedical applications, 13 hydrogen storage, 14 energy storage devices, 15 electromagnetic absorbers, 16 etc. Especially in the domain of microwave absorption, natural resonance and eddy-current effect reveal unexceptionable magnetic loss in the high-frequency range. Nevertheless, the high permeability and low permittivity of the material mean it is difficult for it to satisfy the requirements of new wave-absorbing materials. In recent years, some combinations of ferromagnetic and graphene materials have been shown to exhibit excellent microwave absorption performance. The advantages are as follows. First, satisfactory impedance matching can be achieved by adjusting the electromagnetic parameters. Second, the completely different loss mechanisms produce benecial synergistic effect. For example, Wang et al. 17 investigated novel ower-like CoFe 2 O 4 @graphene complexes, in which hundreds of CoFe 2 O 4 microspheres are combined using graphene as a medium to form a whole ower-like structure. The characteristic appearance utilized multipolarization, hierarchical and synergistic effect to reveal an excellent miraculous absorbing capacity. The minimum reection loss (RL) value reached À42 dB at 12.9 GHz with a thickness of 2.0 mm and the effective absorption (less than À10 dB) reached 4.59 GHz (11.2-15.79 GHz). Bateer et al. 18 prepared NiFe 2 O 4 @RGO composite; the minimum RL value reached À27.7 dB at 9.2 GHz with a thickness of 3.0 mm and the effective absorbing bandwidth was 3.1 GHz. This material disperses well in nonpolar solvents, which has broad application prospects. However, the costly graphene and the high density of ferrite present new challenges. Therefore, it is necessary to nd an alternative to graphene and to reduce the density of ferrite. This is because light and economical absorbing material has practical signicance in industrial production.
The two-dimensional (2D) material molybdenum disulde (MoS 2 ) with graphene-like layered structure plays a signicant role as a semiconductor, 19 solid lubricant, 20 catalyst, 21 etc. In the past few years, scientic researchers have discovered that MoS 2 has superb dielectric loss property and is of low weight, which have made it a popular material in the preparation of lightweight electromagnetic absorbers. High-purity MoS 2 can be prepared by means of hydrothermal treatment. Generally speaking, its morphology can be described as like a blooming ower which is made of aky structures stacked on top of each other. This peculiar appearance will contribute to the amplication of specic surface area and consolidation of microwave absorbing capacity. 22 Furthermore, the raw material is cheap and available and the yield is high, making it promising for replacement of graphene.
In this paper, hollow pellets of Fe 3 O 4 were prepared by a facile solvothermal method in order to reduce the density. Then, MoS 2 nanosheets were gradually grown on the hollow Fe 3 O 4 microspheres by hydrothermal treatment and the obtained Fe 3 O 4 @MoS 2 composite showed a hollow ower-like structure. The morphology and structure of Fe 3 O 4 MPs, MoS 2 MPs and Fe 3 O 4 @MoS 2 MPs were investigated and their electromagnetic parameters and microwave absorption properties were explored. The results indicated that the composite possessed properties of good microwave absorption, wide bandwidth and low mass.

Synthesis of hollow Fe 3 O 4
The synthesis of hollow Fe 3 O 4 was achieved by a facile hightemperature reaction. Firstly, 2.0 g FeCl 3 $6H 2 O, 2 g CH 4 N 2 O, 2 g PEG-400 and 70 ml EG were mixed in a glass beaker, and stirred for a while by a magnetic stirrer until the solid substance was completely dissolved and the solution became transparent orange. Then all the liquid was transferred into a 100 ml Teon liner equipped with a stainless steel reactor and the temperature was maintained at 200 C for 16 h. Aer the product was cooled to normal temperature, it was collected by a magnet and washed with deionized water and anhydrous ethanol three times. Finally it was dried at 60 C and ground ready for further use. The synthesis process of the Fe 3 O 4 @MoS 2 composite was as follows: a certain amount of Fe 3 O 4 powder, (NH 4 ) 6 Mo 7 O 24 $4H 2 O and thiourea were dissolved in 60 ml deionized water, and then the mixture was transferred into a 100 ml Teon liner and kept at 180 C for 12 h. The product was collected by centrifugation and washed with deionized water and anhydrous ethanol three times. At last, it was dried at 60 C and ground ready for further use. Here, we obtained multiple sets of target products by adjusting the molar ratio of the two materials, and denoted them as T3, T4, T5. Meanwhile, T1 and T2 represented pure Fe 3 O 4 and MoS 2 , respectively. Table 1 presents the detailed data.

Characterization
Here, X-ray diffraction (XRD; Rigaku Ultimate IV, scanning angle from 10 to 80 ) and X-ray photoelectron spectroscopy (XPS; Thermo Scientic K-Alpha) were utilized to characterize the compositions of materials. The surface morphology was investigated by scanning electron microscopy (SEM; Hitachi High-Technologies-4800) and transmission electron microscopy (TEM; JEOL JEM 2100) imaging. Simultaneously, the magnetic property was measured by hysteresis loop (VSM, Lake Shore 7404).
The electromagnetic parameters were obtained with a vector network analyzer (VNA; N5224A), which measured bands in the 2-18 GHz range. A diagram of the VNA is shown in Fig. 1. Firstly, powders of samples were mixed with paraffin at 1 : 1 mass ratio. Then each was compressed into a concentric ring with a speci-ed size (F out ¼ 7 mm, F in ¼ 3.04 mm) by a standard mold. Finally, the data of the samples were calculated by the analysis soware and simulated the electromagnetic parameters of the samples under different thicknesses.

Mechanism of structure formation
The formation process of the hollow Fe 3 O 4 /MoS 2 ower-like structure composite is shown in Fig. 2 with hollow structure were prepared by a solvothermal method.

. Firstly, Fe 3 O 4 pellets
The synthesis route is revealed as follows: The hollow structure can be explained by the Ostwald ripening mechanism. During the reaction, the growth of the nanospheres is due to the combination of the grains. It is well known that the chemical potential of a particle decreases with an increase of particle size, which results in the energy of the internal grains being greater than nanospheres. 23,24 Finally, under the action of high temperature, grains gradually dissolve and diffuse to the surface of the sphere to form again. At this time, the energy of nanospheres reaches the lowest value, and the hollow structure is formed. Then the MoS 2 nanosheets were formed on the surface of the spheres. The reaction equations are as follows: 25  The process of the hydrothermal method is similar to that of crystallization in nature. Herein, the cations on the surface of Fe 3 O 4 and the anions in molybdate solution attract each other due to the Coulomb force, and the MoS 2 crystal nucleus is formed at the growth site. With the diffusion of ions to the surface of crystal nucleus and deposition, the crystal will grow directionally along the specic direction and form a unique morphology.

Structural properties
The characterization of crystal structure is conducive to analyze phase components and purity. Fig. 3a shows the XRD patterns of the samples (T1-T5). By referring to Fe 3 O 4 (JCPDS no. 75-0033) and MoS 2 (JCPDS no. 75-1539) standard cards, we can see that the strong diffraction peaks of pure Fe 3 O 4 (T1) correspond to the face-centered cubic structure planes of (1 1 1), (2 2 0), (3 1 1), (2 2 2), (4 0 0), (4 2 2), (5 1 1), (4 0 0) and (5 3 3). And the principal diffraction peaks of pure MoS 2 (T2) correspond to the planes of (0 0 2), (1 0 0) and (1 0 2). As for the composite samples (T3-T5), the correlative characteristic peaks of the two component materials are displayed, and the diffraction angle values are at the identical positions. All the patterns have distinct characteristic peaks without impurity peaks, indicating favorable purity and high crystallinity of the products. XPS was used to analyze the surface elements of the samples (Fig. 3b-f) and the full wide-scan spectrum (Fig. 3b) displays the coexistence of Fe, O, Mo and S in the composite. Fig. 3c depicts the O 1s spectrum of composite T4 and it shows four peaks at 529.83 eV, 530.9 eV, 531.6 eV, and 533.06 eV, which correspond to the lattice oxygen, H-O bond, oxygen vacancies and adsorbed water on the surface respectively. 26 The S 2p spectrum shows two peaks at 161.23 eV and 162.38 eV, which correspond to S 2p 3/2 and S 2p 1/2 orbitals respectively. What is more, the peak at 168.58 eV proves the existence of the S-O bond (Fig. 3d). As is shown in Fig. 3e, the two peaks at 710.88 eV and 724.73 eV represent Fe 2p 3/2 and Fe 2p 1/2 orbitals while the small peak at 715.13 eV indicates the existence of the Fe-Mo bond. This heterogeneous structure is due to the existence of a large number of atomic vacancies in MoS 2 . In the hydrothermal process, Fe ions diffuse into MoS 2 at the interface. 27 Fig. 3f shows the Mo 3d spectrum and the two peaks at 228.33 eV and 231.48 eV represent Mo 3d 5/2 and Mo 3d 3/2 orbitals. Obviously, the Mo element comes from 1T MoS 2 (228.38 eV and 231.53 eV), 2H MoS 2 (229.98 eV and 232.98 eV), and MoO 3 (235.58 eV and 232.38 eV). 28 Therefore, the results of XRD and XPS are favorable evidence for the existence of composite.
The morphology of a material has a great inuence on the microwave-absorbing property. Therefore, SEM and TEM observations are indispensable. Fig. 4a-f show the microscopic morphology of each sample. As for pure Fe 3 O 4 (T1), the diameter of each nanosphere is about 550 nm, and the size is uniform and the dispersion is good because the solvothermal method provides a stable and mild environment for growth (Fig. 4a). It can be seen from the TEM image that pure Fe 3 O 4 consists of hollow spheres with outer diameter of 550 nm and inner diameter of 300 nm (Fig. 4b). This unique structure follows the Ostwald ripening mechanism, which not only reduces the system density effectively, but also contributes to the internal multiple reection loss of EMW. 9 The pure MoS 2 (T2) looks like some owers made of nano-akes stacked together and it is not very dispersive and has an obvious agglomeration phenomenon (Fig. 4c). It can be predicted that the sheet structure extends in all directions greatly increasing the specic surface area of the material. Then the petal structure grows on the microspheres. As is shown in Fig. 4d, when the molar ratio of Fe 3 O 4 to Mo precursor is 1 : 10, the nanosheets only grow locally on the microspheres and most of the microspheres are exposed, which indicates the amount of Mo precursor does not reach the ideal proportion. Aer further increasing the Mo precursor ratio, it can be seen that the surface of the microspheres is completely covered with nanoakes (Fig. 4e). The composite looks like a ower in full bloom and each microsphere is about 850 nm in size. MoS 2 nanosheets construct a conductive network around the composite. The dipole polarization generated by the defects and the rapid movement of the polarized electrons provide efficient conduction loss. Meanwhile, the heterogeneous structure of Fe 3 O 4 -MoS 2 produces interfacial polarization and the interior of the composite provides magnetic loss. Compared to T1 and T2, we can predict that the synergies between the component materials will lead to better microwave absorption. 29 Fig. 4f shows the microstructure of T5; with the increase of Mo precursor, it is difficult for the microspheres to provide enough growth sites on the surface, and the remaining nanosheets can only grow between the petals. In brief, combined with the above structural properties, we successfully prepared hollow-structured owerlike Fe 3 O 4 @MoS 2 .

Microwave properties
It is well known that impedance matching and attenuation characteristics determine the absorbing properties of materials. Ideal impedance matching requires the minimum reectivity of the EMW on a material's surface. The reectivity is determined by the reection coefficient (R), 30 the formula being expressed as follows: 31,32 where Z 0 and Z in represent the air impedance and the interfacial impedance of the material and E and H are the electric and magnetic eld strengths. They are all related to complex permittivity (3) and complex permeability (m). As mentioned above, when 3 is equal to m, Z in and Z 0 are matched and R reaches zero. According to Z in and Z 0 , we can obtain the following formulas for calculating the reection loss: 33 Here, j is the imaginary part of a complex number, f is the frequency of incident wave, d is the thickness of absorbing layer and c is the speed of light in a vacuum. The effective EMW absorption band refers to the frequency range when the reection loss is lower than À10 dB. In this case, we consider that 90% of EMW will be absorbed. The reection loss diagrams of samples T1-T5 are shown in Fig. 5.
We have selected the obvious absorption curves for each sample and marked the corresponding thicknesses. As for T1 ( Fig. 5a and f), the magnetic loss generated by natural resonance means the minimum reection loss value reaches À12.78 dB at 5.12 GHz with a thickness of 5.5 mm and the effective absorbing bandwidth is 1.52 GHz. Obviously, pure Fe 3 O 4 has no palpable absorption in other bands except the C band, and the weak absorption capacity, narrow bandwidth and large thickness are not satisfactory. The EMW absorption of pure MoS 2 (T2) is shown in Fig. 5b and g. Unlike T1, it has distinct absorption peaks in the X and Ku bands. When the thickness is 2.0 mm, the minimum reection coefficient is À15.65 dB with effective absorption of 5.2 GHz (11.84-17.04 GHz). It exhibits wide bandwidth and small thickness, and can achieve effective absorption within 5.28-18 GHz by designing the thicknesses. Fig. 5c-e show the absorption of composites T3, T4, and T5. For T3, the absorption performance is signicantly improved and the minimum reection loss value reaches À29.50 dB at 5.44 GHz, which indicates that MoS 2 plays a positive role. Effective absorption can be achieved in the range of 4. 16-14.24 GHz when the thickness is changed in the range of 2.5-5.5 mm. However, the improvements of effective absorbing bandwidth and thickness are limited. With an increase of Mo precursor, the maximum absorption peak moves towards high frequency. As displayed in Fig. 5d, the reection loss of T4 is À49.6 dB at 13.2 GHz and the effective absorbing bandwidth is 4.24 GHz (11.68-15.92 GHz) when the thickness is only 2.0 mm. With an increase of thickness, the sample still maintains outstanding reection loss. At a thickness of 2.5 mm, 3.0 mm and 3.5 mm, the effective absorption bandwidth is 3.2 GHz (9.28-12.48 GHz), 3.12 GHz (7.52-10.64 GHz) and 2.32 GHz (6.48-8.8 GHz), respectively. The EMW absorption capacity could not continue to increase with the addition of Mo precursor. The minimum reection loss value of T5 is À35.25 dB at 14.8 GHz. This is because the growth of excessive MoS 2 among adjacent petals alters the ower-like structure and affects multiple reection loss. Moreover, the increase of dielectric constant destroys the electromagnetic balance. Surprisingly, the effective absorbing bandwidth is 5.52 GHz . In the process of adjusting the sample thickness from 2.0 mm to 4.0 mm, it was found that the product could achieve effective absorption in the frequency band 5.2-18 GHz, which contains the X band, the Ku band and most of the C band. The reection loss curve of each sample with a thickness of 2.0 mm is depicted in Fig. 5k, which shows that the microwave absorption intensity and effective absorption bandwidth of composites T4 and T5 were much better than those of single-material T1 and T2 under the condition of relatively small thickness. Although sample T4 has the highest microwave absorption intensity, the effective absorption bandwidth is slightly smaller than that of sample T5, which is attributed to the addition of excessive Mo precursor. In addition, the absorption curves could shi to the low-frequency direction during the process of increasing the sample thickness. This variation can be explained by the quarter-wavelength matching theoretical equation: 34 4f m ffiffiffiffiffiffiffi ffi j3mj p ðn ¼ 1; 3; 5; .Þ (12) where t m is the sample thickness and f m is the corresponding frequency. When the value of n is 1 and c is the constant speed of light, t m is inversely proportional to f m . Therefore, we can acquire strong absorption in corresponding frequency band by designing an appropriate thickness. However, it is difficult to achieve both strong absorption and small thickness in the lowfrequency region. The microwave attenuation mechanism is closely related to electromagnetic parameters, which can be expressed by the following formula: 35 ðm 00 3 00 À m 0 3 0 Þ þ ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi ðm 00 3 00 À m 0 3 0 Þ 2 þ ðm 00 3 00 þ m 00 3 0 Þ 2 q r (13) where a is the attenuation constant, f is the frequency, c is the speed of light in vacuum, m 0 and 3 0 represent the real part of the dielectric constant and permeability, and m 00 and 3 00 represent the imaginary part of dielectric constant and permeability. It is widely known that the real part of electromagnetic parameters indicates the EMW storage capacity, and the imaginary part of electromagnetic parameters represents the EMW loss capacity. In order to explore the mechanism of loss, we calculate the dielectric constant, permeability and the tangent of loss. The relevant data are shown in Fig. 6.
As a high dielectric loss material, MoS 2 has the highest values of 3 0 and 3 00 among the ve sets of samples, and the curve has an obvious downward trend with an increase of frequency. However, Fe 3 O 4 is completely opposite to MoS 2 : it has the lowest values of 3 0 and 3 00 and the variation of curves is not signicant at 2-18 GHz. As shown in Fig. 6a-c, when increasing the ratio of Mo precursor from T3 to T4, the dielectric coefficient and dielectric loss of the composites are increased. This is due to the leading role of MoS 2 nanosheets in the construction of an electron transport network. We know that the rapid transfer of electrons contributes to conduction loss and the nanosheets provide channels for electron conduction. As shown in Fig. 6b and c, 3 00 and tan d 3 have similar curve distributions, which indicates that 3 00 can reect the dielectric loss indirectly. Fig. 6df show the complex permeability and magnetic loss. We can see that pure Fe 3 O 4 (T1) and pure MoS 2 (T2) have the highest and lowest values of m 0 and m 00 , respectively. With an increase of Mo precursor ratio, the magnetic loss of the samples decreases gradually. Comparing with the variation of complex permittivity, we nd that Fe 3 O 4 has the characteristics of high magnetic loss and low dielectric loss, while MoS 2 has those of low magnetic loss and high dielectric loss. Therefore, by controlling the ratio, a composite with double loss mechanism can be obtained and the electromagnetic parameters can be balanced. Besides, there are some resonance peaks located at 2-8 GHz for all samples (Fig. 6e and f). Magnetic loss is divided into hysteresis loss, eddy-current loss and residual loss. Since natural resonance exists at relatively low frequency, we consider that these characteristic peaks are caused by natural resonance.
In order to better understand the magnetic property of samples T1, T3, T4, and T5, hysteresis loop tests were carried Fig. 6 Plots of the real part of the permittivity (a) and permeability (d), the imaginary part of the permittivity (b) and permeability (e) and the tangent of dielectric loss (c) and magnetic loss (f) for samples T1-T5. out and the results are shown in Fig. 7. The data of saturation magnetization and coercivity are exhibited in Table 2.
We know that high saturation magnetization is usually accompanied by high initial permeability and the high initial permeability leads to high magnetic loss. As is shown in Table 2, pure Fe 3 O 4 (T1) exhibits the highest saturation magnetization of 75.95 emu g À1 with the highest coercivity of 37.5 Oe, while saturation magnetization of 29.36, 13.52, and 5.46 emu g À1 and coercivity of 32.5, 28.6, and 30.9 Oe are found for T3, T4 and T5. It follows that the magnetic loss of samples can be arranged in the following order: T1 > T3 > T4 > T5; the result is consistent with the curves in Fig. 6f. In addition, the dielectric loss of samples shown in Fig. 6c can be ranked in the following order: T2 > T5 > T4 > T3 > T1; and according to Fig. 5a-j, the order of absorption intensity is T4 > T5 > T3 > T2 > T1. The three different sets of results suggest that remarkable absorbing capacity is not determined by a single loss mechanism, but by the synergistic effect of multiple loss mechanisms.
The magnetic loss of ferrite is caused by resonance and eddy current loss. The C 0 (C 0 ¼ m 00 (m 0 ) À2 f À1 ) values of the samples are calculated from the magnetic permeability and the curves are drawn. In Fig. 8a, each sample has some obvious vibration peaks in the frequency range of 2-10 GHz. Considering that natural resonance generally occurs in the lower frequency band, it can be considered that it is caused by natural resonance. In addition, when the C 0 value of the sample remains constant, the magnetic loss at this time is considered to be eddy current loss. Fig. 8a shows that in the frequency range of 10-18 GHz, C 0 values of all curves tend to atten out or even stop changing, so there is eddy current loss in the sample.
In order to further illustrate the microwave attenuation capacity of the samples, the attenuation constant (a) of each sample was calculated and the results are shown in Fig. 8b. According to the formula of the attenuation constant, an increase of m 00 , 3 00 and frequency is benecial to increase its value. In samples T1-T5, the attenuation constant of sample T1 is the smallest, which is consistent with the reection loss result. And the curve increases rst and then decreases, because T1 has the highest m 00 at low frequencies. Surprisingly, the highest attenuation constant was found for sample T2, which reached a maximum of 277 at a frequency of 18 GHz. The attenuation constant curves of samples T2-T5 showed an upward trend on the whole, but uctuated slightly due to the inuence of m 00 . In general, a good attenuation constant value should be accompanied by an excellent microwave loss capacity. However, compared with samples T4 and T5, the reection loss value of sample T2 is obviously lower. This indicates that the attenuation constant is not the only factor affecting the loss capacity of microwaves.
As mentioned earlier, attenuation and impedance matching are important factors in determining microwave loss ability. Fig. 9 shows the impedance modulus corresponding to the maximum absorption curves of each sample (T1-T5). We know that when Z ¼ 1, a material reaches impedance matching. The corresponding impedance moduli of T4 and T5 at frequencies of 13.2 GHz and 14.8 GHz are 0.975 and 0.961, which are almost a perfect match. As for T1, T2 and T3, their corresponding impedance moduli at frequencies of 5.12 GHz, 14.4 GHz and 5.44 GHz are 1.576, 0.7058 and 0.7686, respectively. Obviously, the combination of MoS 2 and Fe 3 O 4 effectively adjusts the electromagnetic parameters, which leads to the Fe 3 O 4 @MoS 2 composite having better impedance matching than single materials. Although T2 has the largest attenuation constant, poor impedance matching has a negative effect on its microwave absorption ability.
In summary, the three composite samples exhibit better absorption ability, effective bandwidth and thickness than each single component. The reason is attributed to the unique construction, the suitable impedance matching and double loss  mechanism. The loss model of EMW is shown in Fig. 10. First, the ower-like surface which is stacked by MoS 2 sheets greatly increases the specic surface area of the material and enables it to receive EMW from all directions. The multiple reection of incident waves is one of the most signicant factors to remove EMW, which occurs not only between the adjacent nanosheets, but also between each ower-like nanosphere. 24 Second, under a high-frequency electromagnetic eld, there are a large number of atomic vacancies on MoS 2 nanosheets to generate dipole polarization, and the polarized electrons that gain energy move toward the inner core. Third, the heterostructure of Fe 3 -O 4 @MoS 2 is conducive to the accumulation of free charge, which makes each Fe 3 O 4 sphere negatively charged outside and positively charged inside, resulting in the phenomenon of interfacial polarization and a great loss of electromagnetic energy. 36 Finally, the residual EMW enter the sphere and disappear as heat under the action of resonance and eddy current loss. Meanwhile, the internal hollow structure causes multiple reections of EMW, which accelerates the loss of electromagnetic energy. The excellent loss property and good impedance matching mean that the Fe 3 O 4 @MoS 2 composite has remarkable absorption strength (À49.6 dB) and satisfactory effective absorption bandwidth (4.24 GHz) at an extremely small thickness. In recent years, a lot of research has been done on Fe 3 O 4based materials, and Table 3 lists results for some other absorbers. Through comparison, it is found that the Fe 3 O 4 @-MoS 2 composite is expected to be an outstanding microwaveabsorbing material.

Conclusion
In short, a hollow-structured ower-like Fe 3 O 4 @MoS 2 composite was successfully prepared by simple solvothermal and hydrothermal methods. Compared with Fe 3 O 4 and MoS 2 , excellent impedance matching and synergies between materials play a positive role, with the composite exhibiting strong absorption, broad bandwidth and small thickness. In Fig. 8 The magnetic eddy current (a) and attenuation constant (b) for samples T1-T5. Fig. 9 The impedance modulus corresponding to the minimum reflection loss curve of each sample. particular, sample T4 has the highest absorption intensity of microwaves, its reection loss is À49.57 dB at 13.2 GHz and the effective absorbing bandwidth is 4.24 GHz (11.68-15.92 GHz) when the thickness is only 2 mm. Effective absorption in the entire X-band (8-12 GHz) and part of the C-band (4-8 GHz) and Ku-band (12)(13)(14)(15)(16)(17)(18) can be achieved by designing the sample thickness. Sample T5 has the largest effective absorption bandwidth. When the thickness is 2 mm, the effective absorption bandwidth is 5.52 GHz , and the minimum reection loss value is À35.25 dB. By adjusting the sample thickness, effective absorption in the 5.2-18 GHz frequency band can be realized. In addition, the hollow structure not only effectively reduces the density of material, but also has a positive effect on microwave absorption. It can be predicted that the hollow-structured ower-like composite has a potential application prospect in the eld of microwave absorption.