A CTAB-mediated antisolvent vapor route to shale-like Cs4PbBr6 microplates showing an eminent photoluminescence

Compared with nanoscale quantum dots (QDs), the large-sized perovskite crystals not only possess better stability but also are convenient for application exploration. Herein, we develop a facile and efficient antisolvent vapor-assisted recrystallization approach for the synthesis of large-sized Cs4PbBr6 perovskite crystal microplates. In this method, for the first time, the shale-like Cs4PbBr6 microplates with lateral dimensions of hundreds of microns are fabricated by employing cetyltriethylammnonium bromide (CTAB) as a morphology-directing agent. FESEM, TEM, and AFM characterizations indicate that the as-obtained shale-like Cs4PbBr6 microplates are actually formed by 6–8 nm thick Cs4PbBr6 nanosheets with orientational stacking. Importantly, such highly crystalline Cs4PbBr6 microplates with shale-like morphology exhibit a narrow and intense green PL emission with a 59% PL quantum yield. Moreover, the planar structure of shale-like Cs4PbBr6 microplates makes it easy to form a preferred orientation on a substrate, which endow them with promising potential in optoelectronic devices such as lighting and displays.


Introduction
All-inorganic lead halide perovskites with superior photoluminescence (PL) performance are promising functional materials for next-generation optoelectronic devices such as low-cost visible LEDs. [1][2][3][4] Synthesis of perovskite-related materials with high PL quantum yield (PLQY), chromatogram purity, low-threshold lasing, and narrow emission line-width have aroused a wide range of interest in the past few years. [5][6][7][8][9] Up to now, CsPbX 3 (X ¼ Cl, Br, I) perovskite quantum dots (QDs), nanocrystals (NCs), nanowires, and nanoplates as well as Cs 4 PbBr 6 and CsPb 2 Br 5 perovskite-related materials (PRMs) have been routinely synthesized by various solution processing approaches. [10][11][12][13][14][15][16][17] Compared with nanoscale materials, the large-sized perovskites not only possess better stability but also are convenient for application exploration. [18][19][20][21][22][23][24][25][26][27][28] Furthermore, it is well known that the large-sized crystals are very important to identify the essential properties of a material. [18][19][20] As a result, more and more researchers have recently begun to focus on the synthesis of microscale or even centimeter-scale perovskite crystals. [18][19][20][21][22][23][24][25][26][27][28][29][30][31][32] Currently, pure-phase CsPbBr 3 perovskite crystals with dimensions of several millimeters were successfully prepared by an antisolvent crystallization method. 19 Unfortunately, such large sized CsPbBr 3 crystals are almost non-luminescent. 12 While, Tang et al. reported the perovskite-related CsPb 2 Br 5 microplates with superior crystallinity, enhanced stability, and tunable optical properties. 29 It has been revealed that such plate-like perovskites crystals exhibit excellent optical properties due to the absence of tunnel barrier or grain boundary in the planar dimensions. 30 More recently, as another number of Cs-Pb-Br family, Cs 4 PbBr 6 PRMs have also attracted enormous attention. [12][13][14][15] It has been revealed that Cs 4 PbBr 6 PRMs have a higher exciton binding energy (E g $ 180 meV) which benets for the recombination of photogenerated charge carriers, resulting in the high efficiency photon emission. 12,33,34 Interestingly, Cs 4 PbBr 6 PRMs endows a very high quantum connement even in the bulk form which make its prospect entirely depends on its crystal structure rather than shape and size. 12,15 These merits are critical for the high-performance photoelectric devices such as LEDs. Apart from their excellently emissive properties, Cs 4 PbBr 6 PRMs possess superior high-order nonlinear optical properties in a broad spectral region from 500 to 1500 nm due to the strong connement effects with a high dipole moment. 35 Such gures make them showing great potential for multi-photon based imaging as well as optoelectronic devices. Accordingly, the synthesis of Cs 4 -PbBr 6 PRMs received great interest in recent years.
Since the pure-phase Cs 4 PbBr 6 perovskite solids with green emission were reported by Bakr et al. via a low-temperature solution-processed synthesis, many efforts have been devoted to synthesizing luminescent Cs 4 PbBr 6 perovskite materials. [12][13][14][15] So far, in addition to some micron scale perovskite solid powders with irregular shape, 12-15 large-sized Cs 4 PbBr 6 single crystals were also successfully prepared by various solution methods. 18,19,31,32 For example, Bastiani et al. harvested 500 mm pure-phase Cs 4 PbBr 6 single crystals with smooth surfaces and well-dened rhomboid shape through an antisolvent crystallization process. 31 An HBrassisted slow cooling method was developed by Chen et al. for the growth of centimeter-sized Cs 4 PbBr 6 crystals with embedded highly luminescent CsPbBr 3 NCs. 18 As is known, unlike CsPbBr 3 possessing a higher symmetry simple cubic structure with connected corner-sharing PbBr 6 4À octahedra, the PbBr 6 4À octahedra in Cs 4 PbBr 6 are fully isolated from each other in the crystal lattice with interspersed Cs + cations. 12,13,15,33,34 Therefore, the large-sized Cs 4 PbBr 6 PRMs reported generally have an irregular or rhomboid shape but the plate-like Cs 4 PbBr 6 perovskite crystals are rarely reported until now. [12][13][14][15]18,19,31,32 Therefore, developing an effective route for the synthesis of large scale plate-like Cs 4 PbBr 6 perovskite materials with highly photoluminescence is of great signicance for practical applications. 17,[21][22][23][24][25]29,30 Herein, for the rst time, we report a facile and efficient route for the synthesis of highly luminescent shale-like Cs 4 PbBr 6 microplates with hundreds of microns in lateral dimension and tens of microns in thickness. The synthesis of shale-like Cs 4 PbBr 6 microplates was designed according to the supersaturated recrystallization method with the assistance of antisolvent vapor, in which, the heated toluene vapor is diffused into the DMF solution containing PbBr 2 , CsBr, and CTAB. Although the overall thickness of the as-synthesized shale-like Cs 4 PbBr 6 microplates is dozens of microns, they are actually formed by 6-8 nm thick Cs 4 PbBr 6 nanosheets with orientational stacking. Such shale-like Cs 4 PbBr 6 single crystalline microplates not only have superior optical properties, but easy to form a preferred orientation on a substrate, which endows them with promising potential in optoelectronic devices such as lighting and displays.

Synthesis of shale-like Cs 4 PbBr 6 perovskite microplates
The synthetic procedure for shale-like Cs 4 PbBr 6 perovskite microplates was as follow: the precursor solution was rstly prepared by dissolving a given amount of PbBr 2 , CsBr, and CTAB into DMF under the sonication. The nal concentrations of PbBr 2 , CsBr, and CTAB in the precursor were 10 mM, 10 mM, and 15 mM, respectively. Subsequently, 2 mL of the as-prepared precursor solution and 5 mL toluene as antisolvent were separately introduced to one of glass vessels in a connector as illustrated in Fig. S1. † Aer sealing both of vessels, the vessel containing toluene was heated at 80 C in an oil-bath, while the vessel with precursor was put into a 25 C water-bath. In this case, the toluene vapor was gradually evaporated into the precursor solution during the reaction process. Aer about 36 h, the shale-like microplates with yellow-green color were yielded at the bottom of the vessel in the water-bath. Finally, the yellowgreen microplates were harvested and washed repeatedly with toluene for characterization and performance evaluation. Further experiments were performed to reveal the roles of CTAB on the synthesis of shale-like Cs 4 PbBr 6 perovskite microplates.

Characterizations and measurements
To determine the crystal structure of the as-prepared perovskite crystals, X-ray diffraction (XRD) patterns were recorded on a Rigaku Ultima IV X-ray diffractometer with Cu Ka radiation (l ¼ 1.5418 A) by painting the as-prepared products on a silicon wafer. The morphologies of the products were characterized by transmission electron microscopy (TEM, JEOL JEM-1400) and high-resolution transmission electron microscopy (HRTEM, JEOL JEM-2100). The samples for TEM and HRTEM observations were prepared by putting the products on a thin carbon lm coated copper grids. Field-emission scanning electron microscope (FESEM) and energy-dispersive X-ray (EDX) elemental mapping were carried out on ZEISS Gemini-300. Atomic force microscope (AFM, Bruker Multimode-8) was carried out to obtain the thickness of the as-prepared shale-like Cs 4 PbBr 6 microplates. The absorption spectrum was recorded on Shimadzu UV-3101PC with an integrated sphere by using diffuse-reectance mode. The steady-state PL was measured using a Shimadzu RF-6000 spectrouorometer. The PLQY and PL lifetime of the as-prepared samples were characterized by using an Edinburgh FLS920 multifunction steady state and transient state uorescence spectrometer. The excitation wavelength used for all the PL measurements were set at 360 nm. Optical microscope and uorescent pictures of shale-like Cs 4 -PbBr 6 perovskite microplates were recorded on a Nikon ECLIPSE-E100 with an UV lamp. The photoelectric parameters including correlated color temperature (CCT) and CIE coordinates of the fabricated devices were evaluated on a spectroradiometer system (EVERFINE, SPIC-200).

Fabrication of white light-emitting diode (WLED) device
To fabricate WLED device, the silicone gel A and B were rstly blended with an A to B volumetric ratio of 1 : 4. The as-prepared shale-like Cs 4 PbBr 6 perovskite microplates and the commercial red phosphors were introduced into the above silicone mixture gel to form uniform colloids. A given amount of the as-prepared green-red emitting colloids were nally painted onto a blue GaN chip and then dried in a vacuum oven at 60 C.

Morphological characterization of shale-like Cs 4 PbBr 6 microplates
In this work, a CTAB-mediated antisolvent vapor approach was designed for the synthesis of shale-like Cs 4 PbBr 6 perovskite microplates by using toluene as antisolvent and DMF as precursor solvent. As presented in Fig. S1, † the precursor solution and toluene are separately added to one of glass vessels in a connector. To enable toluene diffusion into the precursor solution, the toluene was heated at 80 C and the precursor solution was kept at 25 C. As the reaction time increasing, the volume of liquid in toluene container decreased gradually while the volume of the liquid in the precursor solution container increased, which indicated that toluene was transferred into the precursor. Interestingly, the yellow-green crystals were precipitated from the precursor aer reaction about 36 h and the upper solution appears clear and colorless.
FESEM observation was rstly employed to get the morphology of the as-obtained crystals. As presented in Fig. 1a and b, FESEM images show that almost all the products are plate-like particles with hundreds of microns in dimension and tens of microns in thickness. The lateral FESEM image presented in Fig. 1b reveals that the as-obtained microplates have a multilayer structure. Specically, a single microplate composes of countless oriented stacking ultrathin nanosheets, which is similar to the natural shale demonstrated in Fig. 1c. The EDS elemental mapping images for a random microplate indicates that the Cs, Pb, and Br elements are homogeneously distributed in the whole plates ( Fig. 1d-g), reecting that the assynthesized microplates is a kind of cesium lead bromide compounds. The weight percentages of Cs, Pb, and Br elements in the product are 42.8%, 19.0%, 38.2%, respectively, corresponding to a Cs : Pb : Br atomic ratio of 4 : 1.1 : 5.9 (Fig. S2 †), which is close to the stoichiometric ratio of Cs, Pb, and Br elements in Cs 4 PbBr 6 .
The XRD measurement was carried out to reveal the crystallographic structure of the as-obtained cesium lead bromide compound. As shown in Fig. 2a, all the XRD diffraction peaks are well indexed to rhombohedral phase Cs 4 PbBr 6 (JCPDS no. 73-2478). Interestingly, the (006) diffraction peak of Cs 4 PbBr 6 is extremely higher than other peaks. The peak intense is obviously different from that in the JCPDS. Such variation is indeed frequently observed in the XRD diffraction patterns of plate-like materials such as Au and BiOCl nanosheets. 36,37 This is because that, unlike the quasi-spherical particles, the particles with  plate-like morphology prefer to form a preferential orientation when they are dispersed on a slide. This thus results in the lattice planes which parallel to the surface of the substrate have an intense XRD diffraction peak. On the basis of the above results and analyses, we infer that the obtained Cs 4 PbBr 6 microplates are abundant with {006} planes but they have a preferred orientation with h006i direction on the substrate due to their planar geometry shape. Furthermore, it can be rationally inferred that the top and bottom surfaces of Cs 4 PbBr 6 microplates paralleled to the substrate are {006} lattice planes.
The morphological features of Cs 4 PbBr 6 microplates were further characterized by TEM and AFM. The TEM and AFM images also illustrate the as-obtained Cs 4 PbBr 6 is a multilayer microplates constructed by ultrathin nanosheets (Fig. 2b-d).
The thickness of the ultrathin nanosheets is measured by AFM at the edge of a random microplate (Fig. 2b). The AFM images and line proles indicate that the thickness of the ultrathin nanosheets, the elementary units for Cs 4 PbBr 6 microplates, is about 6-8 nm. Moreover, HRTEM image shown in Fig. 2e veries that the interplanar distances was about 0.691 nm, which can be indexed as the {110} planes of the rhombohedral phase Cs 4 PbBr 6 . According to the above morphology characterizations, the product obtained by the CTAB-mediated antisolvent vapor approach presented here is thus denoted as shalelike Cs 4 PbBr 6 microplates.

The optical properties of shale-like Cs 4 PbBr 6 microplates
The inset in Fig. 3a presents the optical microscope picture of the shale-like Cs 4 PbBr 6 microplates under nature light and uorescent picture under 365 nm UV light. It is clearly observed that shale-like Cs 4 PbBr 6 microplates appears to be yellow-green under the natural light and exhibits a bright green emission under 365 nm UV light, indicating that the products possess an excellent photoluminescence. 15 The optical properties of shale-like Cs 4 PbBr 6 microplates were further studied by photoluminescence spectrum and UV-Vis absorption. The asprepared shale-like Cs 4 PbBr 6 microplates exhibit a single, intense, and stable emission at 520 nm when the excitation wavelengths is greater than 350 nm ( Fig. 3a and b). In addition, the absorption spectrum in Fig. 3c with an absorption edge onset at 540 nm is observed, which was consistent with the literature reports. 12 Furthermore, the PLQY of the shale-like Cs 4 PbBr 6 microplates is about 59% obtained by a spectrouorometer equipped with an integrated sphere under the excitation of 360 nm illumination (Fig. S3 †). Fig. 3d shows the timeresolved decay curve of the as-obtained shale-like Cs 4 PbBr 6 microplates, which is well tted by a biexponential function:

Roles of CTAB for the formation of shale-like Cs 4 PbBr 6 microplates
Further experiments revealed that CTAB play a key role for the synthesis of the shale-like Cs 4 PbBr 6 microplates. Fig. S4a and S4b † present the results of the product obtained by using a precursor solution containing PbBr 2 and CsBr but without using CTAB. In this case, the nal color of the product appeared brown and almost no luminescence was observed under UV light. The corresponding FESEM image and XRD pattern verify that the nal product yielded in the absence of CTAB is rectangular CsPbBr 3 microcrystals with edge lengths range from tens to hundreds of microns, as typically illustrated in Fig. 4a and f. Almost no luminescent signal for such big CsPbBr 3 crystals is detected in PL measurement (Fig. S4k †), agreeing well with the uorescent picture (Fig. S4a †) and literatures. 12,15,19 This result unambiguously reveals that CTAB is very crucial for the formation of shale-like Cs 4 PbBr 6 microplates with highly photoluminescence.
To further explore the role of CTAB in the formation of shalelike Cs 4 PbBr 6 microplates, a series of experiments were performed by varying its concentration in the initial precursor and keeping other parameters invariant. When CTAB concentration is 5 mM, besides a small amount of plate-like crystals with green emission, the product is still predominately made up of nonluminescent CsPbBr 3 microcrystals but its grain size becomes smaller (Fig. 4b, S4c, and S4d †). Interestingly, a weak PL emission at 520 nm is detected in the corresponding PL spectrum in the present case (Fig. S4k †). The PL emission of the harvested products is further enhanced as the increase of CTAB concentration and reaches the maximum if the CTAB concentration is above 15 mM. This is well consistent with the observation of the samples under nature and UV light. A distinct color evolution from orange to yellow-green under nature light (Fig. S4c, S4e, S4g, and S4i †) and the enhancement of green emission under UV light (Fig. S4d, S4f, S4h, and S4j †) are clearly observed as the CTAB concentration is increased from 5 mM to 20 mM. Correspondingly, XRD measurements indicate that the crystalline phases of the as-obtained products are changed from orthorhombic CsPbBr 3 to rhombohedral Cs 4 PbBr 6 compound (Fig. 4f). Moreover, the morphology of the products evolution from small cube (Fig. 4b) to small plate-like crystals (Fig. 4b), and nal obtained large-sized microplates (Fig. 4d and e). Furthermore, the nal products obtained by high concentration CTAB are dominated by single-crystalline Cs 4 PbBr 6 compound with {006} lattice planes as the basal surfaces. FESEM observations indicate that the population of the shale-like Cs 4 PbBr 6 microplates is increased as the increase of CTAB concentration (Fig. 4a-e). This further conrms that the generation of the shale-like Cs 4 PbBr 6 microplates does closely relate to CTAB.
As one of the most common shape-directing agents, the cationic surfactant CTAB has always been a widely utilized in the synthesis of functional materials. 40,41 Fig. S5a and S5b † show the results of the same amount of CTAB were respectively added in DMF and toluene. We nd that the CTAB in DMF solution is clear and colorless, whereas the CTAB in toluene appears turbid with white color. This suggests that CTAB can dissolve into DMF easily but do not dissolve into toluene. Similarly, the solubility of CsBr and PbBr 2 in DMF and toluene is also signicantly different: DMF is a good solvent for CsBr and PbBr 2 while toluene is a very poor solvent for them. 10,13 As aforementioned, in the present synthesis, toluene can be easily entered into the DMF precursor solution containing CsBr, PbBr 2 , and CTAB through an evaporation process. Interestingly, the result illustrated in Fig. S5c † indicates that CTAB can be recrystallized to form white micelles if toluene is introduced into DMF solution containing CTAB. Moreover, the recrystallization of Cs + , Pb 2+ , Br À ions from DMF solution by using toluene as an anti-solvent has also been well evidenced in recent researches. 10,13,15 Obviously, with the reaction time increasing, the precursor ions (e.g. Cs + , Pb 2+ , Br À ) and CTAB will be recrystallized together due to the increase of toluene content in the reaction solution. Furthermore, it is well known that (i) CTAB can be facilely self- assembled to form layered micelles when its concentration in a solution is higher than the critical concentration 40,41 and (ii) the Gibbs free energy of heterogeneous nucleation is generally lower than that of homogeneous nucleation. 42,43 On the basis of the above information and our experimental results, we infer that, under a slow crystallization process like our case, the layered structure CTAB micelles may act as the so templates and in turn direct the growth process of cesium lead bromide compound, thus leading to the formation of shale-like Cs 4 PbBr 6 microplates. Specially, shale-like Cs 4 PbBr 6 microplates are exclusively produced when the CTAB concentration in the initial precursor is greater than 15 mM (Fig. 4). According to our results and the above analysis, the morphologies of Cs 4 PbBr 6 PRMs formed with various CTAB concentrations are summarized and schematically illustrated in the ESI (Fig. S6 †).

Application in WLED devices
To illustrate their potential applications, a prototype white light-emitting diode (WLED) device were fabricated by using a 450 nm emissive GaN chip as blue light source. Fig. 5a presents the framework of WLED device. Fig. 5b and c present the photograph for the prototype of WLED device in non-working and working state. It is clearly observed that the shale-like Cs 4 PbBr 6 microplates-based WLED device exhibits a saturated white emission at an operation current of 2 mA (Fig. 5c). Fig. 5d shows the corresponding electroluminescence (EL) spectrum of the WLED device under working state. On the basis of the WLED device framework presented in Fig. 5a, we attribute the luminescent peaks at 450 nm, 520 nm, and 615 nm in the EL spectrum (Fig. 5d), respectively to the emission from GaN chip, Cs 4 PbBr 6 perovskite, and commercial red phosphors. Moreover, as demonstrated in Fig. 5e, the as-fabricated WLED device exhibits a cold white light with a color temperature of 5612 K, and the CIE 1931 color coordinate of (0.33, 0.34), which is close to the standard white color (0.33, 0.33). 15,18,44 Such results described above suggest that the great potential applications of shale-like Cs 4 PbBr 6 microplates in lighting and display devices.

Conclusions
In summary, in this work, we develop a facile and efficient antisolvent vapor-assisted crystallization approach for the synthesis of shale-like Cs 4 PbBr 6 microplates with large size. Interestingly, the shale-like Cs 4 PbBr 6 microplates with highly PL are rationally synthesized by using toluene as anti-solvent and DMF as precursor solvent. Structural characterizations by FESEM, TEM, and AFM indicate that the as-obtained shale-like Cs 4 PbBr 6 microplates are constructed by 6-8 nm thick Cs 4 PbBr 6 nanosheets with orientational stacking. The cationic surfactant CTAB as a morphology-directing agent is found to be crucial role for the formation of shale-like Cs 4 PbBr 6 microplates. Importantly, such shale-like Cs 4 PbBr 6 single crystalline microplates on a substrate are easy to form a preferred orientation lm with h006i direction due to their planar structure, which makes them easy to process for application exploration. Finally, a prototype WLED device is successfully fabricated by combining the shale-like Cs 4 PbBr 6 microplates as the green emitters, commercial red phosphors as the red emitters, and blue emitting GaN chips as the blue emitters, which shows their great potential application in optoelectronic devices such as lighting and displays.