Hydrothermal synthesis of cobalt telluride nanorods for a high performance hybrid asymmetric supercapacitor

Cobalt telluride nanostructured materials have demonstrated various applications, particularly in energy generation and storage. A high temperature and reducing atmosphere are required for the preparation of cobalt telluride-based materials, which makes this a difficult and expensive process. The development of a facile route for producing the desirable nanostructure of cobalt telluride remains a great challenge. We demonstrated a simple hydrothermal method for preparing cobalt telluride nanorods (CoTe NRs) and telluride nanorods (Te NRs) for supercapacitor applications. The morphology of CoTe NRs and Te NRs was analyzed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The prepared CoTe NR electrode material exhibited a high specific capacity of 170 C g−1 at a current density of 0.5 A g−1 with an exceptional cyclic stability. The asymmetric supercapacitor was assembled using CoTe NRs and orange peel-derived activated carbon (OPAA-700) as a positive and negative electrode, respectively. The fabricated device delivered a high energy density of 40.7 W h kg−1 with a power density of 800 W kg−1 at 1 A g−1 current density. When the current density was increased to 30 A g−1, the fabricated device delivered a high power density of 22.5 kW kg−1 with an energy density of 16.3 W h kg−1. The fabricated asymmetric supercapacitor displayed a good cyclic stability performance for 10 000 cycles at a high current density of 30 A g−1 and retained 85% of its initial capacity for after 10 000 cycles. The prepared materials indicate their applicability for high performance energy storage devices.


Introduction
In 21 st century, the global demand in the energy sectors and limited availability of fossil fuels require society to move towards substantial developments in the energy conversion and storage devices. 1,2 For energy storage, batteries and conventional capacitors are the main devices that can deliver a high energy and high power, respectively. Currently, batteries possess a high energy density and low power density, while the conventional capacitor delivers a high power but limits its energy storage. 3,4 Supercapacitors, also known as ultracapacitors, have drawn a great interest in recent years because of their high power performance, fast charge/discharge ability, long cycle life and low cost. [5][6][7][8][9][10][11] Commercial-based symmetric supercapacitors in non-aqueous electrolytes have delivered high-power densities in the range of 12-14 kW kg À1 with energy densities of 4-6 W h kg À1 . So, the progress of supercapacitors continues mostly towards the development of high energy and low-cost nanostructured electrode materials. The energy density of the supercapacitor depends on the capacity of the material and cell voltage. However, the low cell potential of the aqueousbased symmetric supercapacitor limits its potential application due to water decomposition. Recently, hybrid asymmetric supercapacitors in an aqueous electrolytes have been developed in which the faradaic metal oxide/hydroxide/sulde/telluride and an EDLC-based carbon electrode materials are used as the positive and negative electrodes, respectively.
Hybrid supercapacitors can efficiently utilize the potential gap between the two types of electrodes to increase the cell voltage. The energy density of the supercapacitor materials depends on the capacity of the electrode material and cell voltage, while increasing the cell voltage the energy density get enhanced. Ni-, Co-and Fe-based battery-type electrode materials are promising materials for high energy storage applications due to the low cost, environmental sustainability, intrinsic electronic conductivity, high capacity, good rate performance, long life span and high redox behavior. [12][13][14][15][16] For example, Wang et al. fabricated a Ni 3 S 4 battery-type electrode supercapacitor with a specic capacitance of 898.5 C g À1 at 0.5 A g À1 current density. 17 Ni 3 S 2 /CdS exhibit a capacity of 545.6 C g À1 at the current density of 1 A g À1 with the capacitance retention of 103% aer 5000 cycles. 18 Liu et al. reported on Ni-Co@Ni-Co layered double hydroxide for solid state battery-type supercapacitor. It gives an energy density of 100 W h kg À1 and cyclic stability of 98.6%. 19 Ce-doped a-Co(OH) 2 shows a specic capacity of 415 C g À1 with a cyclic stability of 73%, even aer 2000 cycles. 20 To obtain a new device with a large energy density, power density and potential window of the asymmetric supercapacitor (ASC) has received a great attention by the combination of two different types of electrodes to make asymmetric congurations resulting in the storage of more energy and a wider cell potential due to the utilization of faradaic and non-faradaic process in a single device. In ASC, the faradaic electrode as the positive electrode (energy source) generally uses transition metals such as Ni(OH) 2 and CoO because of their high specic capacity and electrochemical performance. The EDLC as a negative electrode (power source) uses materials like activated carbon, carbon nanotubes and graphene because of their high surface area, high stability and high electrical conductivity. 21,22 In this scenario, metal chalcogenides are a new type of electrode material for the electrochemical supercapacitor. In the metal chalcogenides, the metal ion undergoes fast surface redox reactions associated with different oxidations of the transition metal ion. Transition metal chalcogenides like NiS, CoS, CuS, MoS 2 , NiSe, CoSe, and MoSe 2 nanostructures are more interesting towards supercapacitor applications due to the high surface area, specic capacitance, excellent electrochemical properties, high electrical conductivity and stability. 23 Recently, metal tellurides like CoTe, NiTe, La 2 Te 3 , MoTe 2 and Sm 2 Te 3 have been used as an electrode materials for supercapacitor applications. Among these metal tellurides, CoTe is of immense interest due its high theoretical capacity of 1034 C g À1 . CoTe nanowires can extend their potential voltage to 1.6 V and give energy and power density values of 32.9 W h kg À1 and 800.27 W kg À1 , respectively, even aer 5000 cycles at the current density (5 A g À1 ) with an initial capacitance of 90.5%, as reported by Xiao et al. 21 Ye et al. synthesized a CoTekAC asymmetric supercapacitor electrode grown on carbon ber paper by hydrothermal method, which showed a specic capacitance of 120 C g À1 with an energy density of 67.0 W h kg À1 . 22 Cao et al. reported on Te NWs arrays with high conductivity grown on a exible carbon ber to fabricate hybrid Te/Au/MnO 2 core-shell nanostructures as a supercapacitor with 97% capacitance retention for 1000 cycles. 24 Zhou et al. prepared NiTe rods as a positive electrode material for an asymmetric supercapacitor (ASC) with a specic capacitance of 804 F g À1 (current density 5 A g À1 ) and 91% of capacitance retention for 1000 cycles. 25 Liu et al. recorded that few-layer 1T 0 MoTe 2 obtained a high specic capacitance of 835 C g À1 at a current density of 1 A g À1 . 26 Kumbhar et al. synthesized Sm 2 Te 3 thin lms through a one-step chemical route with a specic capacitance of 129 C g À1 with high energy and power density values of 25.60 W h kg À1 and 14.18 kW kg À1 , respectively. 27 Patil et al. successfully synthesized La 2 Te 3 thin lm via a successive ionic layer adsorption and reactive method for supercapacitor charge storage properties. It exhibited a specic capacitance of 161 C g À1 with a capacitance retention of 82% over 1000 cycles at a scan rate of 100 mV s À1 . 28 In our previous work, we demonstrated a nickel telluride nanorod (NiTe NR) by hydrothermal method using ascorbic acid and CTAB as the reducing agent and surfactant, respectively. High specic capacitances of 370 C g À1 were achieved at the current density of 1 A g À1 with good electrochemical cyclic stability. 29 Here, all capacitance values are recalculated as capacity values for consistency.
CoTe has attracted great interest because its thermal, electrical and magnetic properties have shown a variety of applications such as electrocatalysis, 30 water splitting, 31 solar cells, 32 batteries, 33 photocatalysis 34 and biosensors. 35 Cobalt telluride nanostructure materials have demonstrated various applications particularly in energy generation and storage. High temperatures and a reducing atmosphere are needed for the preparation of cobalt telluride-based 2-D nanostructure materials, which makes it difficult and expensive for the large-scale production and fabrication of supercapacitors. Thus, the development of a facile route for desirable CoTe nanostructures remains a great challenge. To the best of our knowledge, this is the rst report on hydrothermally prepared CoTe and Te NRs as electrode materials for supercapacitor applications. The asprepared CoTe NR electrode material delivered a high specic capacity of 170 C g À1 at a current density of 0.5 A g À1 , which is much higher than the Te NRs. Depending on the growth condition of the materials, it can exhibit various surface morphologies. The capacity of the materials differs from the different morphologies because of both faradaic and nonfaradaic processes. Here, the CoTe surface area is higher than Te. In the case of morphology, it is the opposite. Asymmetric supercapacitors (ASC) were fabricated using CoTe NRs and orange peel-derived activated carbon (OPAA) 36 as positive and negative electrodes, respectively. The fabricated device delivered a high energy density and power density of 40.7 W h kg À1 and 22.5 kW kg À1 , respectively. In addition, the fabricated device exhibited an excellent rate performance and good cycling stability, which make it a potential electrode material for energy storage applications.

Preparation of CoTe nanorods
Sodium telluride (Na 2 TeO 3 , Sigma Aldrich), cobalt acetate (Co(CH 3 COO) 2 $4H 2 O, Sigma Aldrich), ascorbic acid (C 6 H 8 O 6 ), cetyltrimethylammonium bromide (CTAB, Sigma Aldrich) and deionized water from a Milli-Q-ultra pure water system (18.2 MU cm À1 ) were used as the starting materials. In the hydrothermal method, 14.2 mmol of C 6 H 8 O 6 was dissolved in 40 ml of deionized water. Then, 0.82 mmol of CTAB was added gradually and stirred for 30 min. In the next step, 1.88 mmol of Na 2 TeO 3 and 1.88 mmol of Co(CH 3 COO) 2 $4H 2 O was dissolved in 30 ml of deionized water and slowly added to the above solution and a white TeO 2 precipitate was obtained immediately. Finally, the resultant solution was transferred into a 100 ml Teon-lined stainless-steel autoclave that was sealed and maintained at 180 C for 24 h in an oven, then allowed to cool to room temperature. The obtained black powder was collected and washed with deionized water and ethanol several times, and dried at room temperature. For comparison, pure Te was prepared in the absence of cobalt acetate by the same method. 37

Preparation of orange peel-derived activated carbon
For the full cell fabrication of ASC, OPAA was used as a negative electrode material. The detailed synthesis procedure and characterizations are described in our previous publications. 36 In detail, the dry orange peel powder was subjected to carbonization at 600 C for 3 h in an argon (Ar) atmosphere and followed by chemical activation. The carbonized sample was mixed with KOH in a weight ratio of 1 : 3, and the obtained slurry was again heat-treated at 700 C for 1 h in an Ar atmosphere to obtain the chemically activated carbon. The resulting activated carbon was washed thoroughly with 1 M HCl solution, followed by DI water until the pH of the sample became neutral. The resulting activated carbon was dried at 80 C for 5 h.

Characterizations
The phase formation and crystalline nature of the synthesized materials were analyzed by powder X-ray diffraction (XRD) analysis using PANalytical XRD X'pert pro with Cu Ka radiation (a ¼ 1.5418 A). The elemental composition and oxidation states of the metal ions were examined by X-ray photoelectron spectroscopy (XPS; MULTILAB 2000, Thermo Scientic) using Mg Ka (1253.6 eV) as the X-ray source. The surface morphology and particle size of the synthesized materials have been studied by scanning electron microscope (SEM), Hitachi S-3000 H and transmission electron microscope (TEM), Jeol Jem-2100, respectively. An N 2 adsorption-desorption experiment was carried out using a Micromeritics ASAP 2020 analyzer, and the surface areas were determined using BET (Brunauer-Emmett-Teller). The electrochemical performance of the electrode materials for supercapacitor application was evaluated by cyclic voltammetry (CV), galvanostatic charge discharge (GCD) and electrochemical impedance spectroscopy (EIS) analysis using electrochemical workstation (Biologic-SP300).

Preparation of electrode for supercapacitor
The working electrode was fabricated by mixing the active materials, acetylene black and polyvinylidene uoride (PVDF) with a weight ratio of 75 : 20 : 5, respectively. This mixture was continuously ground in a mortar and 0.5 ml N-methyl-2pyrrolidone (NMP) was used as a solvent to make a homogenous slurry. This homogenous slurry was coated on a nickel foam (2 Â 2 cm 2 ) current collector, and then dried at 90 C for 12 h in a vacuum oven. The weight of the active material ($4 mg) was optimized based on the weight of the Ni foam before and aer coating. In a three-electrode conguration, active material-coated Ni foam, Pt foil and Hg/HgO (20% KOH) served as the working, counter and reference electrodes, respectively. The CV and GCD measurements were carried out using 3.5 M KOH as the electrolyte with different scan rates from 5 to 100 mV s À1 and different current densities from 1 to 10 A g À1 , respectively. The electrochemical impedance spectroscopic (EIS) study was also carried out by applying an alternate current (AC) with a bias voltage of 5 mV amplitude in the frequency range from 100 kHz to 10 mHz. The specic capacity of the electrode materials was calculated from the following formula: 4 where C is the specic capacity of the electrode materials (C g À1 ), I is the discharge current (A g À1 ), Dt is the discharge time (s), and m is the mass of the active material (g). The theoretical capacity of the electrode was calculated using the equation: where n is the number of electrons transferred in the redox reaction, F is the Faraday constant, M is the molar mass and V is the operating potential window. The hybrid asymmetric supercapacitor (ASC) was constructed using the faradaic type CoTe NRs as a positive electrode, EDLC-type activated carbon derived from orange peel biomass-derived activated carbon as a negative electrode with 3.5 M KOH as an electrolyte. The advantages of the ASC are a higher cell potential with a high specic capacity. To obtain better ASC performance, it is necessary to maintain the charge balance between the positive and negative electrodes using the following relationship: q + ¼ q À , where q + and q À are the stored charges in the positive and negative electrode surfaces, respectively. The amount of charge stored on the electrodes depends on the capacity (C) and mass of the electrode materials (m). Thus, the mass balance equation is expressed as follows: 3,38 where C + and C À are the capacity of the positive and negative electrodes, and m + and m À are the mass of the positive (4.66 mg) and negative electrodes (2 mg). The capacity of the OPAA material (specic capacity is 280 C g À1 at 2 A g À1 current density) was calculated based on our previous work. 14 The mass ratio for optimal electrochemical performance of ASC between the positive and negative electrodes was calculated to be 2.33. The energy and power density values were calculated by the following equations: 39 where the energy density (E), power density (P), C is the specic capacitance (c g À1 ), DV is the potential window (V), and Dt is the discharging time (s).

Results and discussion
Scheme 1 represents the synthesis of CoTe NRs. In the synthesis process, ascorbic acid covered the surface of the Te nanorods. Co 2+ ions spread over the carbon shells and react with Te to form CoTe. 40 CTAB is a cationic surfactant that controls the shape, size and aggregation of nanostructures due to the formation of micelles in the liquid medium. It forms the elongated stable micelles during the addition of CTAB into the water. This can absorb the CoTe nanoparticles and grows as nanorods, and also prevents the further aggregation of the CoTe nanoparticles. The bonding between the CTAB and CoTe nanoparticles enhances the lengthening of the crystals rather than the growth in the axial direction. 41  The SEM images of CoTe and Te show the formation of uniform nanorod bundles, consisting of nanorods with an average length of up to 1 mm (Fig. 2a and b). The average diameter of the CoTe NRs is less than that of the Te NRs. The samples were further analyzed by TEM analysis. Fig. 3(a and b) shows TEM images of the Te NRs at different magnications. A lattice-resolved higher magnication TEM image in Fig. 3(b) indicates the interplanar spacing of 0.32 nm, which corresponds to the (101) plane of hexagonal Te and conrms the formation of the Te NRs. Fig. 3(c-e) shows the TEM images of the CoTe NRs at different magnications. At higher magnication images ( Fig. 3f and g), the formation of nanorods are clearly indicated with an average diameter in the range of 11-15 nm, and the surface of each rod was found to be rough. A lattice-resolved higher magnication TEM image in Fig. 3(h) indicates the interplanar spacing of 0.28 nm, which corresponds to the (101) plane of hexagonal CoTe and conrms the formation of CoTe NRs. It was further conrmed that the average diameter of the CoTe NRs is less than that of the Te NRs. These results support the previous analysis (e.g., SEM and XRD analysis). Fig. 4a shows Co 2p 3/2 at 781.2, 786.4 eV and Co 2p 1/2 at 796.9, 801.4 eV. The energy difference is 15.7 eV for the Co 2p 3/2 and Co 2p 1/2 spin-orbit interaction, which reveals the presence of Co 2+ and Co 3+ ions. 43 The Te 3d spectrum in Fig. 4b is divided into four peaks. The satellites at 572 and 583 eV are assigned to Te 3d 5/2 and Te 3d 3/2 of the Te 2À ions, and the major peaks at 576 and 586 eV arise due to the formation of the Te 4+ ions. 44   12 nm for Te NRs and CoTe NRs (Fig. 5(a and b) (inset)), respectively. The unique meso-and microporous nature with the high specic surface area of the CoTe NRs could improve the mass transport and electron transfer as an electrode in the electrochemical process; this may be an advantage for the excellent electrochemical performance. Therefore, it is estimated that the CoTe NRs can offer higher electrochemical activity than the Te NRs.

Electrochemical performance
Initially, the electrochemical properties of the electrode materials were characterized by CV, GCD and EIS analysis. The CV prole of the Te NR and CoTe NR electrodes at a scan rate of 50 mV s À1 showed redox-type voltammograms, which demonstrate the faradaic charge storage mechanism (Fig. 6a). The CV prole of the CoTe NR electrode displayed a wider and high current density than the Te electrode. Fig. 6(b and c) shows the CV prole of the Te and CoTe NR electrode at different scan rates ranging from 5 to 50 mV s À1 . Both electrode materials have a strong pair of redox peaks during the CV analysis, which resulted from the following surface reversible redox reaction between Co 2+ and Te for CoTe NRs and Te NRs in the presence of OH À ions, respectively. The possible redox reactions in the Te and CoTe electrodes can be described as follows: 22,45 Te + OH À # TeOH + e À (8) CoTe + OH À # CoTeOH + e À (10) While the scan rate increased, the oxidation and reduction peaks shied to negative and positive potentials, respectively, because the ion diffusion rate had to be limited to satisfy electronic neutralization during the redox process. At a slow scan rate, the OH À ions have enough time to intercalate with the inner and outer surfaces of the electrode. But, in the case of a high scan rate, the OH À ions have less time to intercalate with the surfaces of the electrode.
The electrode materials were further investigated by GCD analysis at various current densities from 1 to 10 A g À1 at the potential range of 0.0 to 0.5 V vs. Hg/HgO (20% KOH).   Compared to the CV prole, the active potential window was slightly decreased for GCD analysis because of gas evolution at low current density. Fig. 6d shows the GCD prole of the Te and CoTe electrodes. CoTe had a higher discharge time compared to the Te electrode at the current density of 1 A g À1 . The GCD prole exhibits non-linear charge/discharge proles that conrm the faradaic nature of the electrode materials, which is in good agreement with the CV analysis. The calculated specic capacities of the Te NRs and CoTe NRs were 87 and 148 C g À1 , respectively, at 1 A g À1 current density. The GCD prole of the Te NR and CoTe NR electrode materials at different current densities are shown in Fig. 6(e and f). The specic capacity of all electrode materials as a function of different current densities is displayed in Fig. 7a. The calculated specic capacities of the Te NRs from the GCD prole are 87, 86, 80, 65, 60, 53, 48, 42, 37, and 34 C g À1 at current densities of 1, 2, 3, 4, 5, 6, 7, 8, 9 and 10 A g À1 , respectively. The calculated specic capacities of the CoTe NRs from the GCD prole are 170, 148, 120, 98, 86, 83, 75, 71, 66, 62, and 61 C g À1 at current densities of 0.5, 1, 2, 3, 4, 5, 6, 7, 8, 9 and 10 A g À1 , respectively. Even at the high current density of 10 A g À1 , the CoTe NRs and Te NRs delivered a good rate performance of 36 and 39%, respectively. The specic capacitance value decreased while increasing the current density; this may be attributed to the diffusion of ions at different current rates. At a lower current density, the electrolyte ions have a sufficient time to diffuse to the inner pores of the electrode surfaces to attain the maximum utilization of the active surface areas of the electrode materials. 46,47 At high current densities, the electrolyte ions can access only the surface of the electrode materials. They do not have enough time to intercalate the inner pores of the electrode surfaces to attain the minimum utilization of the active surface areas of the electrode materials. Here, we have compared the specic capacities of some metal chalcogenide-based electrode materials with our synthesized materials. Although the specic capacity of CoTe was slightly lower than that of the reported materials, its capacity retention was much higher even aer 5000 cycles. The interfacial resistance of the electrode materials at the electrode and electrolyte interfaces was evaluated using the EIS technique. Fig. 7b reveals the Nyquist plot of the CoTe NR and Te NR electrode materials tted with an appropriate equivalent circuit model. The equivalent circuit model contained solution resistance (R s ), charge-transfer resistance (R ct ), double layer capacitance (C dl ), Warburg impedance (W) or diffusion resistance and faradaic capacitance (C F ). From the tting analysis, the CoTe NR and Te NR electrodes showed R s values of 0.18 and 0.21 U, respectively. The R ct values were 2.3 and 2.7 U for the CoTe NR and Te NR electrodes, respectively. In addition, the CoTe electrode materials showed a vertical line along the y-axis in the low frequency region of more than 45 , which implied the ideal capacitive behavior of the electrode materials with less interfacial charge transfer resistance at the electrode/electrolyte interface.
The electrochemical stability is one of the vital properties for a supercapacitor. To assess the cyclic stability of the electrodes, a GCD test was carried out up to 5000 cycles at a high current density of 10 A g À1 as shown in Fig. 7c. Aer 5000 cycles, 98.5% (Te) and 99% (CoTe) of the initial specic capacitance was retained. For all 5000 cycles, the Coulombic efficiency of the electrode materials remained constant ($98%), which conrms the high reversibility of the charge storage process. This good stability reveals that the highly reversible surface redox reaction took place between the electrolyte and electrode surface. To this end, the CoTe NR electrode shows higher electrochemical activity than the Te NR electrode. For the full cell analysis, CoTe NRs was used as a positive electrode and OPAA was used as the negative electrode for further studies. Fig. 8a represents the CV prole of OPAA and CoTe electrodes occupying different potential windows of À1.0 to 0 V and 0 to 0.6 V at the scan rate of 50 mV s À1 , respectively. The CV proles of the hybrid ASC (CoTekOPAA) at different cell potentials from 1 to 1.6 V at the scan rate 50 mV s À1 are shown in Fig. 8b. The device remained stable with increasing cell potential up to 1.6 V. The set of redox peaks with a wider CV prole indicates the existence of faradaic and EDLC nature properties. At the cell voltage of 1.6 V, the CV curves of the CoTekOPAA hybrid ASC at different scan rates from 5 to 100 mV s À1 are given in Fig. 8c. While the scan rate increased, the oxidation and reduction peaks shied to negative and positive potentials because the ion diffusion rate had to be limited to satisfy electronic neutralization during the redox process. At a slow scan rate, the OH À ions have enough time to intercalate with the inner and outer surfaces of the electrode. However, in the case of a high scan rate, the OH À ions have less time to intercalate with the surfaces of the electrode. Fig. 8d reveals the GCD curves of the hybrid ASC device performed at a current density of 1 A g À1 in different cell potentials (1.2 to 1.6 V). From the discharge prole, the calculated specic capacity of the hybrid ASC cell was 144, 160, 169, 181 and 183 C g À1 at cell potentials of 1.2, 1.3, 1.4, 1.5 and 1.6 V, respectively. The specic capacity as a function of the cell potential is shown in Fig. 8e, where the capacity value increased with increasing cell potential. Even at 1.6 V cell potential, the CD prole shows a peak-like charge-discharge prole without any gas evolution. Fig. 8f demonstrates the GCD prole of the hybrid ASC cell with a cell potential of 1.6 V at different current densities. The calculated specic capacity of the hybrid ASC cell was 183, 160.4, 154, 146, 140.5, 120, 92 and 78 C g À1 at the current density values of 1, 2, 3, 4, 5, 10, 20 and 30 A g À1 , respectively. When the current density was increased to 30 A g À1 , the hybrid ASC cell retained 42.6% of the initial specic capacity (Fig. 9a). Fig. 9b Illustrates the Nyquist plot of the fabricated hybrid ASC cell, which exhibited R s and R ct values of $0.4 and $0.6 U, respectively. From the EIS studies, it was conrmed that the fabricated hybrid ASC cell had excellent electrical contact with minimum ionic resistance.

Hybrid asymmetric supercapacitor
For viable applications, a supercapacitor should have high electrochemical stability. In order to nd the electrochemical stability of the fabricated hybrid ASC cell, cycling studies were carried out for 10 000 cycles at the high current density of 30 A g À1 . Fig. 9c shows the capacity retention and coulombic efficiency of the hybrid ASC cell as a function of the cycle number. The fabricated hybrid ASC cell delivered an excellent electrochemical stability of 85% of the initial specic capacity aer 10 000 charge-discharge cycles with a coulombic efficiency of 99.9%. The fabricated hybrid ASC cell with CoTe NRs and OPAA electrode materials as the positive and negative electrodes shows good discharge reversibility and outstanding cycle stability, respectively. These electrochemical stability values are higher than the recently reported materials, such as CoTekAC (90% for 5000 cycles), 21 CoTekAC (80% for 3000 cycles), 22 NiTe (81% for 3000 cycles), 25 1T-MoTe 2 (87% for 5000 cycles). 26 The Ragone plot is a typical tool to evaluate the supercapacitor device with other types of energy storage devices in terms of their energy and power density values. Fig. 10 displays the Ragone plot of the fabricated CoTekOPAA hybrid ASC device. The fabricated hybrid ASC device exhibited high energy density values of 24, 28.9, 32.9, 37.7 and 40.7 W h kg À1 with cell potential values of 1.2, 1.3, 1.4, 1.5 and 1.6 V, respectively. Notably, the energy density of the device increased with increasing cell potential. Similarly, the power density also  This journal is © The Royal Society of Chemistry 2020 RSC Adv., 2020, 10, 13632-13641 | 13639 increased to 600, 650, 701, 750 and 800 W kg À1 with increasing cell potential at 1.2, 1.3, 1.4, 1.5 and 1.6 V, respectively (Fig. 10).
The high energy and power density values of the fabricated hybrid ASC at a current density of 1 A g À1 at the cell potential of 1.6 V were 40.7 W h kg À1 and 800 W kg À1 , respectively. When the current density increased to 30 A g À1 , the fabricated hybrid ASC device delivered a high-power density of 22.5 kW kg À1 and retained an energy density of 16.3 W h kg À1 . The above observed high energy and power densities were signicantly higher than the reported values for the metal oxide-based electrode materials in ASC using an aqueous electrolyte. For instance, Ye et al. synthesized CoTekAC ASC that delivered an energy density of 67 W h kg À1 for the pristine electrolyte. 22 Quan et al. fabricated a CuS-CNTs@NFkAC ASC showing the specic capacitance of 164 F g À1 at a current density of 0.5 A g À1 with an energy density of 22.14 W h kg À1 . 48 The assembled Ni 3 NkPRPC-1K ASC possessing a high energy and power density of 30.9 W h kg À1 and 412 W kg À1 , respectively, have been reported by Peng et al. 49 Wang et al. constructed a NiCo LDHkAC ASC displaying a specic capacitance of 58 F g À1 at the current density of 1 A g À1 with an energy and power density of 18 W h kg À1 and 750 W kg À1 , respectively. 50 The remarkable electrochemical performance of the fabricated hybrid ASC can be attributed to the good combination of the faradaic-based CoTe NRs and EDLC-based high surface area activated carbon (OPAA) CoS nanoparticles and activated carbon electrode. In addition, this methodology could be readily extended to the preparation of other metal tellurides.

Conclusions
In this work, a simple hydrothermal method has been used for the synthesis of Te NRs and CoTe NRs. The XRD pattern revealed the formation of hexagonal CoTe NRs, and the compositional analysis conrmed the presence of Co and Te. The prepared materials showed a signicant enhancement in the electrochemical performance when they were used as electrode materials in a supercapacitor. The CoTe NR electrode shows a high specic capacity of 170 C g À1 at a current density of 0.5 A g À1 and excellent life cycle (99%). The fabricated CoTekOPAA ASC achieved a specic capacity of 183 C g À1 with a high-energy density of 40.7 W h kg À1 and power density of 800 W kg À1 at the current density of 1 A g À1 . The device delivered a high power density of 22.5 kW kg À1 with an energy density of 16.3 W h kg À1 at a high current density of 30 A g À1 . The fabricated hybrid ASC cell delivered an excellent electrochemical stability of 85% of the initial specic capacity even aer 10 000 charge-discharge cycles with a coulombic efficiency of 99.9%. The prepared materials have shown a promising results as an electrode for supercapacitor applications. The proposed simple hydrothermal method could be scaled up for a large-scale preparation of CoTe and other Te-based materials for their viable applications in energy storage. Furthermore, these materials have a great potential in other applications such as lithium-ion batteries, catalysts and data storage devices.

Conflicts of interest
There are no conicts to declare.