Symbiotic, low-temperature, and scalable synthesis of bi-magnetic complex oxide nanocomposites

Functional oxide nanocomposites, where the individual components belong to the family of strongly correlated electron oxides, are an important class of materials, with potential applications in several areas such as spintronics and energy devices. For these materials to be technologically relevant, it is essential to design low-cost and scalable synthesis techniques. In this work, we report a low-temperature and scalable synthesis of prototypical bi-magnetic LaFeO3–CoFe2O4 nanocomposites using a unique sol-based synthesis route, where both the phases of the nanocomposite are formed during the same time. In this bottom-up approach, the heat of formation of one phase (CoFe2O4) allows the crystallization of the second phase (LaFeO3), and completely eliminates the need for conventional high-temperature annealing. A symbiotic effect is observed, as the second phase reduces grain growth of the first phase, thus yielding samples with lower particle sizes. Through thermogravimetric, structural, and morphological studies, we have confirmed the reaction mechanism. The magnetic properties of the bi-magnetic nanocomposites are studied, and reveal a distinct effect of the synthesis conditions on the coercivity of the particles. Our work presents a basic concept of significantly reducing the synthesis temperature of bi-phasic nanocomposites (and thus also the synthesis cost) by using one phase as nucleation sites for the second one, as well as using the heat of formation of one phase to crystallize the other.


Introduction
Strongly correlated electron oxides form a very important class of materials where interactions between the electronic spins, charges, orbitals, and lattice co-exist simultaneously. 1 This correlation typically produces a rich variety of states and leads to the occurrence of very many competing states in these materials. 2 As a result, this family of oxides shows a plethora of properties such as colossal magnetoresistance, 3 multiferroicity, 4 high-T c superconductivity, 5 and spin-liquid states, 6 to name a few. The existence of competing states with nearly equal energy scales of the dominant interactions also means that the ground state is extremely sensitive to doping and/or external perturbations such as electric and/magnetic eld, pressure, temperature, and strain. The ground states of these oxides can be changed not only using external perturbations, but also by reducing the particle size to the nano regime. Nanoparticles, with larger surface to volume ratios and quantum connement effects, possess distinct size-dependent optical, electronic, and magnetic properties. The effects of size reduction on the properties of strongly correlated electron oxides have been studied extensively over the last two decades, and are relatively well-established. [7][8][9][10][11][12][13] More importantly, this family of oxides is interesting not only from the point of fundamental studies, but also due to potential applications in different areas of technology. 14,15 In the quest for new systems with tunable properties, an alternative route that is being increasingly explored in recent years is to make nanocomposites of functional oxides, 16 where the properties of the individual components can be modied by an appropriate choice of the two phases. Nanocomposites are essentially different from single-phase materials, and offer greater exibility for obtaining custom-made properties by combining the properties of the two parent phases. Unlike single-phase materials where undesired secondary phases need to be eliminated, the focus while preparing nanocomposites is on obtaining pure bi-phasic compounds. Bi-phasic nanocomposites, where the individual components themselves are complex systems belonging to the family of strongly correlated electron oxide systems, are both interesting as well difficult systems to study. The difficulty lies as much in the synthesis of pure phase nanocomposites as in the understanding of the cross-correlated electronic and magnetic properties. Several synthesis approaches have been tried to create composite oxide nanostructures, oen involving techniques that are quite elaborate and costly 17 as well as requiring high-temperature processing. 18 With regard to particulate nanocomposites, a relatively easy synthesis route is to physically mix the two phases. However, a simple physical mixing of the two phases leads to clustering and aggregation of the individual phases on the micron scale that is oen detrimental to the physical properties of the nanocomposites. 19 To overcome such issues, different kinds of solution-based chemical approaches have been used yielding nanocomposites with different morphologies such as core-shell nanoparticles and matrix-dispersed composite materials. Samples prepared using chemical approaches oen exhibit better homogeneity 20 than physically mixed samples, as well as better coupling between the constituent phases. 21 At this stage, developing innovative, scalable, yet low-cost synthesis methods that can yield nanocomposites with the desired physical properties has become crucial.
Sol-gel chemistry is an established method to prepare complex oxide materials, and conventionally, sintering at high temperature is required to obtain phase pure materials. In this work, we report for the rst time a unique lowtemperature synthesis approach based on sol-gel chemistry for preparing nanocomposites, where we have eliminated the need for further sintering. In this synthesis technique, both the phases of the nanocomposite are formed during the same time. We demonstrate this bottom-up synthesis technique using LaFeO 3 (LFO) and CoFe 2 O 4 (CFO) as prototypical magnetic systems. While LFO is a canted G-type antiferromagnet with a high ordering temperature of $750 K, 22 CFO, is a typical ferrimagnet (ordering temperature $800 K) exhibiting high saturation magnetization, high coercivity, and large magnetic anisotropy. 23 The synthesis of LFO, like that of many other complex oxides, requires high-temperature annealing (>500 C) for phase formation, [24][25][26][27][28][29] including the synthesis of nanocomposites where LFO is one of the components. 30,31 The synthesis technique that we report here is based on the glycine-nitrate combustion synthesis method. 32,33 For the rst time, we use this method that has largely been used to prepare single-phase materials before, to synthesize bi-phasic nanocomposites at a signicantly reduced temperature. Remarkably, we observe that each of the two phases (LFO and CFO), instead of hindering the crystallization of the other, facilitate the synthesis process so that phase pure nanocomposites are obtained at temperatures much lower than that required for the crystallization of individual LFO. In the following sections, we will rst present the detailed synthesis followed by the structural, morphological, and magnetic characterization of the nanocomposites.

Synthesis
In a typical synthesis process of the LFO-CFO nanocomposites, two separate sols were rst prepared by dissolving stoichiometric amounts of the precursors of LFO i.e., La(NO 3 ) 3 $6H 2 O and Fe(NO 3 ) 3 $9H 2 O (Sigma-Aldrich), and the precursors of CFO i.e., Co(NO 3 ) 2 $6H 2 O and Fe(NO 3 ) 3 $9H 2 O (Sigma-Aldrich), respectively, in distilled water at room temperature. To these solutions, glycine was added to act as the chelating agent (number of moles of glycine ¼ total number of moles of cations). The two clear solutions were then mixed at room temperature and stirred for 20 min. The volume of each solution used to prepare the composite sol was dictated by the desired phase fraction of the composite. For example, to prepare an LFO(50)/CFO(50) nanocomposite, equal volumes of the LFO and CFO sols were mixed in a beaker to form the composite sol. The composite sol was then heated on a hot plate to 80 C and stirred for 20 min. Next, the temperature of the hot plate was increased and maintained at $150 C till the formation of a gel. Finally, the temperature of the hot plate was increased up to $250 C when a self-combustion reaction with ame occurred, yielding a uffy powder. No further annealing at higher temperature was performed. Three nanocomposites with phase fractions, LFO : CFO ¼ 95 : 05, 75 : 25, and 50 : 50, were prepared. We refer to these in the rest of the article as LFO(95)/CFO(05), LFO(75)/CFO (25), and LFO(50)/ CFO(50), respectively. For comparison, the end members, LFO and CFO, were also prepared using only the LFO and CFO sols, respectively.

Characterization techniques
Differential thermal analysis (DTA) and thermogravimetric analysis (TGA) were performed using a LabsysEvo 1600 DTA/ TGA (Setaram). Approximately 1.5 mg and 5 mg of the dried gel (before self-combustion) and sample (aer selfcombustion), respectively, were placed in an alumina crucible and heated from 30 to 800 C, at 10 C min À1 under an O 2 atmosphere (20 ml min À1 ). The DTA and TGA curves were elaborated using the dedicated soware Calisto (Setaram).
The samples obtained aer self-combustion were characterized by X-ray powder diffraction (XRPD) using a D-5000 diffractometer with CuK a radiation operating at 40 kV and 30 mA. The data were collected in the range 2q ¼ 20-70 , with a step size of 0.02 . Rietveld analysis was performed on the nanocomposites using MAUD. 34 Transmission electron microscopy (TEM) analysis was performed on the samples obtained aer self-combustion using a Philips CM200 microscope operating at 200 kV and equipped with a LaB 6 lament. For TEM observations, the samples, in the form of powder, were prepared using the following procedure. A small quantity of powder was dispersed in ethanol and subjected to ultrasonic agitation for approximately one minute. A drop of suspension was deposited on a commercial TEM grid covered with a thin carbon lm. Finally, the grid was kept in air until complete evaporation of the ethanol.
Fourier-transform infrared spectroscopy (FTIR) spectra were acquired with a Shimadzu IRPrestige-21, equipped with a Specac Golden Gate Single Reection Diamond Attenuated total reection (ATR). All samples were analyzed in the region between 4000 cm À1 and 450 cm À1 .
Physisorption with N 2 at 77 K was performed using an ASAP2020 MP Plus (Micromeritics, USA) equipped with the MicroActive Soware for data acquisition and elaboration. The samples were evacuated at 180 C for 4 h. The specic surface area was evaluated by the well-known Brunauer-Emmett-Teller (BET) method and the pore size distribution (PSD) was calculated using the Barrett-Joyner-Halenda (BJH) method.
Magnetic eld-dependent magnetization of the samples was collected using a superconducting quantum interference device (SQUID) magnetometer from Quantum Design Inc. Magnetic hysteresis loops were recorded at T ¼ 5 K and 300 K in the AE5 T eld range.

Investigation of the synthesis process
The TG and DTA curves of the dried gels (before self-combustion) are shown in Fig. 1. The TG curves reveal that for all the gels, irrespective of the fraction of the LFO and CFO phases, the selfcombustion process ends at 200 C, as indicated by a sharp weight loss at $200 C (Fig. 1a). At higher temperature, further variation in the TG curves was observed for the gels of LFO(95)/ CFO(05) and LFO(75)/CFO(25) (black and red curves), while for the gel of LFO(50)/CFO(50), no further weight loss was observed (blue curve). The corresponding DTA curves showed a strong exothermic peak centered at 180 C for all the samples (Fig. 1b). This is the rst indication that the reaction occurs below 200 C, thus offering the possibility of maintaining a low synthesis temperature. The TG curves obtained on the samples aer selfcombustion are shown in the ESI (Fig. S1 †). The TG curves reveal a progressive decrease of the weight loss with an increase in the CFO amount. For the gel of LFO(95)/CFO(05), the weight loss is $25% of the initial weight (black curve in Fig. S1 †), indicating the presence of a certain amount of intermediary products and amorphous phases that react to form the desired crystalline phases only at higher temperature. The weight loss is signicantly reduced for the gel of LFO(75)/CFO(25) (red curve in Fig. S1 †), and no variation in the TG curve is observed for the gel of LFO(50)/ CFO(50) (blue curve in Fig. S1 †).
FTIR spectra recorded on the nanocomposite samples ( Fig. S2 in the ESI †) conrm the observations made from thermogravimetric analysis. A ne analysis of the spectra is not easy in these kinds of systems. Nevertheless, the signal in the regions 1200-1600 cm À1 and 3100-3600 cm À1 can be clearly attributed to the presence of glycine residuals in the samples. 35 As expected, the intensity of the peaks increases considerably on decreasing the percentage of CFO, thereby conrming that the presence of CFO promotes the formation of the LFO phase. It should be underlined that the presence of a strong signal at $2400 cm À1 is due to atmospheric CO 2 due to the AT experimental conditions. The exact composition of the amorphous phases can be probed using detailed elemental analysis. This is, however, out of the scope of the present paper.

Structural and morphological characterization
The XRPD patterns of the as-synthesized samples are shown in Fig. 2. Fig. 2a shows the XRPD pattern of the as-synthesized LFO i.e., the sample obtained aer self-combustion. The reections corresponding to the orthorhombic structure of LFO (s.g. Pnma) can be observed and have been indexed in Fig. 2a. However, we also observe a broad shoulder from $25-30 that indicates the presence of amorphous material in the sample. This is not unexpected since earlier studies have shown that it is necessary to anneal the as-synthesized sample at $500 C or higher for complete crystallization of LFO [24][25][26][27][28][29] and for the complete combustion of organic precursors. In the absence of hightemperature annealing, the XRPD pattern of the LFO sample shows the expected presence of amorphous content. The XRPD pattern of the as-synthesized CFO is shown in Fig. 2e. All reections could be indexed to the cubic space group (s.g. Fd 3m), without the presence of any amorphous content. This is consistent with our earlier studies that have shown that the synthesis of pure phase crystalline CFO does not require hightemperature annealing. 36 In Fig. 2b, we can see the XRPD pattern of LFO(95)/CFO(05). The pattern looks very similar to that of the end-member LFO. The presence of CFO is not detected because of the small % of CFO in the sample. However, interestingly, the broad shoulder between 25-30 corresponding to the amorphous content in the sample seems to have Fig. 1 (a) TG and (b) DTA curves of the LFO/CFO gels (before self-combustion).

Paper
Nanoscale Advances decreased in the as-synthesized LFO(95)/CFO(05) sample in comparison with that of the end-member LFO. With an increase in the CFO content to 25%, the most intense reection (311) of the CFO phase is visible in the XRPD pattern (Fig. 2c), and is indexed in red. However, the more interesting point to note is that the broad shoulder between 25-30 corresponding to the amorphous content in the sample shows a clear decrease compared to that in the samples with lower CFO fraction ( Fig. 2a and b). We note that characteristic reections corresponding to CFO do not appear in the XRPD patterns even for LFO(95)/CFO(05) and LFO(75)/CFO(25) samples annealed at higher temperatures, except for the most intense CFO peak in the LFO(75)/CFO(25) samples (Fig. S3 in the ESI †), conrming that their absence is due to the low content of CFO in the samples, and not due to its incomplete crystallization. Fig. 2d shows the XRPD pattern of the LFO/CFO nanocomposite with a further increase in the CFO content (50%). Reections corresponding to both LFO and CFO are visible (s.g. Pnma and Fd 3m, respectively) and are indexed in black and red, respectively. Most notably, the broad shoulder between 25-30 corresponding to amorphous content in the sample has disappeared completely. The XRPD data is in agreement with our conclusions from the thermogravimetric analysis, i.e., in general, the amorphous content is seen to decrease with an increase in the CFO fractions, and in particular, for LFO(50)/CFO(50), the nanocomposite obtained aer self-combustion is wellcrystallized without any amorphous content.
The Rietveld analysis of XRPD data of the nanocomposites is shown in Fig. S4 in the ESI. † Using these ts, we attempted to quantify the relative LFO and CFO content in the LFO(50)/ CFO(50) and LFO(75)/CFO(25) samples i.e., the two nanocomposites where reections corresponding to both phases can be detected. The weight fractions obtained from the Rietveld renement in the two samples are 49 : 51(1) and 77 : 23(1), respectively, that are in very good agreement with the nominal weight fraction for the two samples. Notably, for the LFO(75)/ CFO(25) sample, it was necessary to include an amorphous hump in the background during the Rietveld renement, while for the LFO(50)/CFO(50) sample, no such amorphous hump was necessary for the renement. This conrms that for the LFO(50)/CFO(50) sample, all the precursors have crystallized to form the two desired phases (LFO and CFO), while for the LFO(75)/CFO(25) sample, some amorphous material is present. Since reections corresponding to CFO are not detected in the diffraction pattern of the LFO(95)/CFO(05) sample, it was not possible to quantify the relative LFO and CFO content of this sample using Rietveld renement.
Transmission electron microscopy observations were performed to investigate the structure of the nanocomposites in detail. Fig. 3 shows bright eld TEM images of the LFO(95)/ CFO(05) and LFO(50)/CFO(50) samples and the corresponding diffraction patterns. The LFO(95)/CFO(05) powder has a spongelike structure with a large number of pores and two kinds of visible regions: one having a large number of nanocrystals ( Fig. 3a and b), and the other showing a reduced degree of crystallinity ( Fig. 3d and e). In particular, in Fig. 3a, nanocrystals in Bragg condition give rise to a dark contrast (dark spots), while areas corresponding to pores appear brighter. Nanocrystals and Nanoscale Advances Paper pores are better identied in the magnied high-resolution image of Fig. 3b. The regions with a reduced degree of crystallinity are generally more extensive than the former ones and show a very different contrast. Dark spots, corresponding to nanocrystals in Bragg condition, are not visible in Fig. 3d and even at larger magnications, high-resolution images rarely show the presence of small nanocrystals, Fig. 3e. The different degree of crystallinity is further evidenced by the corresponding selected area electron diffraction (SAED) patterns taken under the same microscope operational conditions. Indeed, Fig. 3c shows well-dened diffraction spots arranged on rings typical of a polycrystalline material, while in Fig. 3f, only few diffraction spots are visible together with some diffraction rings having a diffused intensity typical of an amorphous material. The LFO(50)/CFO(50) powder still has a porous structure, but only areas with a high number of nanocrystals are visible ( Fig. 3g and  h). The average dimension of these crystals is approximately ve times larger than the ones in the previous sample, as can be seen by comparing Fig. 3a, b, g and h. The difference in crystal dimension in the two samples is also reected in the corresponding SAED patterns. Indeed, Fig. 3i still shows many well-dened diffraction spots as in Fig. 3c, but the selected area being the same for the two samples, a lower number of crystals contributes to the diffraction pattern in Fig. 3i and hence, the diffraction rings are not well dened. Analyzing the interplanar distances associated with the diffraction reections, it is possible to verify the presence of the LFO and CFO phases in both the samples. In particular, the most intense diffraction contributions of the two phases are shown in Fig. 3c and i. In contrast, in the regions of the sample LFO(95)/CFO(05) showing a lower degree of crystallization, it is possible to observe few diffraction spots attributable to the CFO phase while diffuse rings can be assigned to a poor crystallized LFO phase (Fig. 3f). All these results conrm the conclusions obtained from the XRPD experiments. We have conrmed the presence of pores as seen in the TEM images using nitrogen isotherm analysis at 77 K for all the nanocomposite samples (details in ESI and Fig. S5, S6 †). The presence of such pores is a typical characteristic of samples prepared using the self-combustion synthesis technique.
In order to identify the CFO and LFO nanoparticles, highresolution TEM (HR-TEM) observations were performed on both samples and the images were analyzed by a Fast Fourier Transform (FFT) approach. In particular, Fig. 4a shows some nanoparticles of the two phases and the Miller indexes associated with the visible atomic planes in the LFO(95)/CFO(05) This journal is © The Royal Society of Chemistry 2020 Nanoscale Adv., 2020, 2, 851-859 | 855 Paper Nanoscale Advances sample. Fig. 4b has been obtained by imaging the LFO(50)/ CFO(50) sample, and the crystallographic orientations of the two nanoparticles were identied by the FFT of the image. Generally, it was observed that the CFO nanoparticles have a particle size of approximately 10 nm, much smaller than the particle size of CFO in the absence of an LFO phase ($70 nm), while the LFO nanoparticles have a size of $10 nm and $50 nm in the LFO(95)/CFO(05) and LFO(50)/CFO(50) samples, respectively. It is important to note, that the CFO and LFO nanoparticles tend to share some atomic planes, suggesting an oriented growth of one phase over the other. In more detail, the inset of Fig. 4b shows some atomic planes of the LFO phase that deform in order to match the atomic planes of the CFO phase. This inset was obtained by removing the noise from the image indicated by the dotted square using the Gatan Microscopy Suite GMS3 soware. 37 The typical approach consists of obtaining the FFT of the image, the application of a mask to remove the noise, and an inverse FFT to reobtain the image. The atomic periodicity in the two phases is clearly evidenced in this way, and it is possible to observe the nature of the interface.

Magnetization measurements
Fig . 5 shows the isothermal magnetization loops of the nanocomposites recorded at T ¼ 5 K (Fig. 4a-c) and T ¼ 300 K (Fig. 4d-f). The corresponding magnetization loops of the pure phases (LFO and CFO) are shown in the ESI (Fig. S7 †). The single-phase like hysteresis loops indicate that the nanocomposites are strongly exchange-coupled, the shape of the loops signicantly changing when the percentage of CFO in the nanocomposites is increased. This change in shape is reected in a modication of the normalized remanent magnetization   Nanoscale Advances Paper that of pure LFO. Interestingly, LFO has been reported to be multiferroic with ferroelectric hysteresis loops 38 and ferroelastic effect 39,40 observed at room temperature. By combining antiferromagnetic LFO with a ferrimagnetic spinel system, CFO in this case, which has a reasonably high saturation magnetization, high coercivity, and large magnetic anisotropy, 23 one can improve the magnetic properties of LFO (as seen here), and thus, expect a promising candidate for applications such as in data storage media, spintronic devices, multiple stage memories, and sensors. 41 The coercivity values of the nanocomposites exhibit an anomalous trend, with H C reaching a maximum for the sample with CFO ¼ 25%, and decreasing for all other samples. Such a maximum in the coercivity of LFO/CFO nanocomposites for a particular composition has been reported before. 30 This nonmonotonic variation of coercivity can be ascribed to the coupling between the antiferromagnetic and ferrimagnetic phases, the strength of which can depend on the relative amounts of the antiferromagnetic and ferrimagnetic phases in the nanocomposites. 42,43 In addition, the coercivity can also be affected by a change in the magnetic anisotropy due to differences in particle size as well as orientational relationships between the two phases in the nanocomposites.

Mechanism of phase formation and symbiotic effect
The thermogravimetric, structural, and morphological investigations elaborated in the previous sections allow us to develop an insight into the mechanism of phase formation at low temperature in the nanocomposites. We have seen that the assynthesized LFO(50)/CFO(50) nanocomposite is wellcrystallized without any amorphous content despite 50% of the sample consisting of LFO, which normally requires a much higher annealing temperature for crystallization (>500 C). [24][25][26][27][28][29] This is made possible because the formation of CFO proceeds with an exothermic reaction, and the heat produced is sufficient to crystallize the LFO phase at temperatures as low as 200 C, without the need for further annealing at higher temperatures. HR-TEM observations indicate that the CFO phase acts as a nucleation site for the LFO phase, thereby reducing the energy of formation of the LFO phase. In turn, the LFO phase, growing on the formed CFO nanoparticles, prevents further growth of the CFO nanoparticles in the nanocomposite, as evidenced by the fact that pure CFO (in the absence of an LFO matrix) formed using the same synthesis technique yields particles with a larger size ($70 nm) as compared to the particle size of CFO in the LFO-CFO nanocomposites ($10 nm). The effect of the LFO matrix in restricting the growth of CFO particles is further conrmed by estimating the average size of coherent crystalline domains of CFO in the nanocomposites from the Rietveld renement of the XRPD patterns. Our renements yield an average crystallite size of 24.8(5) nm and 11.6(9) nm for CFO in the LFO(50)/CFO(50) and LFO(75)/CFO(25) samples, respectively. For the LFO(95)/CFO(05) sample, we were unable to estimate the size of CFO crystals, since we do not see any reections corresponding to CFO in the XRPD pattern. Notably, the average dimensions of the CFO crystals in the LFO(50)/ CFO(50) sample are approximately twice compared to the ones in the LFO(75)/CFO (25) sample. In other words, with an increase in the LFO matrix content, the average dimension of the CFO crystals decreases since the LFO matrix restricts the growth of the CFO particles. To the best of our knowledge, this is the rst observation of such a symbiotic phenomenon, where one phase of the nanocomposite helps in the crystallization of the second phase both by providing the heat required for crystallization as well as by reducing the energy of formation of the second phase by acting as nucleation sites, and, in turn, the second phase prevents grain growth of the rst phase.

Conclusions
In summary, we have developed a new composite sol-based synthesis technique for complex oxide nanocomposites, and demonstrated it by synthesizing LFO/CFO bi-magnetic nanocomposites at a signicantly reduced synthesis temperature ($200 C). The thermogravimetric analysis performed on the dried gels (before self-combustion) conrms that the reaction occurs at 180 C in all the nanocomposites, irrespective of the relative ratio of the two phases. The XRPD data reveals a wellcrystallized as-synthesized LFO(50)/CFO(50) nanocomposite, despite 50% of the sample consisting of LFO, which normally requires a very high annealing temperature for crystallization (>500 C). This is enabled by our unique synthesis strategy, where we allow both phases of the nanocomposite to form at the same time, thereby utilizing the heat of formation of one phase (CFO) to crystallize the other phase (LFO). Thus, our new synthesis strategy allows us to signicantly reduce the temperature (and thereby, the cost) of synthesis by eliminating the need for high-temperature annealing. This is indeed remarkable because most oxides belonging to the family of strongly correlated electron oxides (including pure LFO) require annealing at higher temperatures (>500 C) for complete crystallization. We also observe a symbiotic effect, where the LFO phase, in turn, restricts grain growth of the CFO phase. Although we have demonstrated our results using prototypical LFO-CFO nanocomposites, it is possible to extend this concept to the synthesis of other bi-phasic nanocomposites as long as the heat of reaction of one phase is sufficient to crystallize the second phase. For example, our studies reveal that replacing CFO with NiFe 2 O 4 (NFO) leads to very similar results (the XRPD patterns of the as-synthesized LFO-NFO nanocomposites are shown in Fig. S9 in the ESI †). This proves that the synthesis technique reported in this work is not specic to CFO, but rather to the concept of using the heat of reaction generated during the synthesis itself for crystallization and phase formation rather than any external heat source. We believe that this study will provide a new route for scalable, low-temperature synthesis of nanocomposites of different functional complex oxides.

Conflicts of interest
There are no conicts of interest to declare.