Carbon nano-fiber forest foundation for ruthenium oxide pseudo-electrochemical capacitors

s, 2017, vol. MA2017-01, p. 604. 44 D. Sridhar, J. L. Meunier and S. Omanovic, Mater. Chem. Phys., 2019, 223, 434–440. 45 Q. Li, S. Zheng, Y. Xu, H. Xue and H. Pang, Chem. Eng. J., 2018, 333, 505–518. 46 I.-H. Kim, J.-H. Kim, Y.-H. Lee and K.-B. Kim, J. Electrochem. Soc., 2005, 152, A2170–A2178. 47 X. Wang, Y. Yin, C. Hao and Z. You, Carbon N. Y., 2015, 82, 436–445. 48 K. S. Yang, C. H. Kim and B. H. Kim, Electrochim. Acta, 2015, 174, 290–296. 49 A. L. M. Reddy and S. Ramaprabhu, J. Phys. Chem. C, 2007, 111, 7727–7734. 50 S. Yan, H. Wang, P. Qu, Y. Zhang and Z. Xiao, Synth. Met., 2009, 159, 158–161. 51 Y. W. Ju, G. R. Choi, H. R. Jung, C. Kim, K. S. Yang and W. J. Lee, J. Electrochem. Soc., 2007, 154, 192–197. 52 H. K. Hassan, N. F. Atta, M. M. Hamed, A. Galal and T. Jacob, RSC Adv., 2017, 7, 11286–11296. 53 C. C. Hu, H. Y. Guo, K. H. Chang and C. C. Huang, Electrochem. Commun., 2009, 11, 1631–1634. 54 N. Kang, T. Yu, G. H. Lim, T. Koh and B. Lim, Chem. Phys. Lett., 2014, 592, 192–195. 55 V. D. Patake and C. D. Lokhande, Appl. Surf. Sci., 2008, 254, 2820–2824. 56 Y. Guo, W. Zhang, Y. Sun and M. Dai, MethodsX, 2018, 5, 795–796. 57 Y. R. Ahn, M. Y. Song, S. M. Jo, C. R. Park and D. Y. Kim, Nanotechnology, 2006, 17, 2865–2869. 58 K. Y. Kumar, S. Archana, R. Namitha, B. P. Prasanna, S. C. Sharma and M. S. Raghu, Mater. Res. Bull., 2018, 107, 347–354. 59 Y. Yin, X. Wang and Z. You, Int. J. Electrochem. Sci., 2017, 12, 3883–3906. 60 A. Ponrouch, S. Garbarino, E. Bertin and D. Guay, J. Power Sources, 2013, 221, 228–231. 61 X. Wang, Y. Yin, X. Li and Z. You, J. Power Sources, 2014, 252, 64–72. 62 J. Li, M. Zhu, Z. An, Z. Wang, M. Toda and T. Ono, J. Power Sources, 2018, 401, 204–212. 63 D. P. Dubal, G. S. Gund, R. Holze, H. S. Jadhav, C. D. Lokhande and C. J. Park, Electrochim. Acta, 2013, 103, 103–109. 64 R. Warren, F. Sammoura, F. Tounsi, M. Sanghadasa and L. Lin, J. Mater. Chem. A, 2015, 3, 15568–15575. 65 S. Ardizzone, G. Fregonara and S. Trasatti, Electrochim. Acta, 1990, 35, 263–267. 66 M. Ramani, B. S. Haran, R. E. White and B. N. Popov, J. Electrochem. Soc., 2002, 148, A374. 67 X. Hao, J. Zhao and Q. Zhang, Ceram. Int., 2016, 42, 9170–9177. 68 W. Sugimoto, in Encyclopedia of Applied Electrochemistry, ed. G. Kreysa, K. Ota and R. F. Savinell, Springer New York, New York, NY, 2014, pp. 1813–1821. 69 I.-H. Kim and K.-B. Kim, J. Electrochem. Soc., 2006, 153, A383. 70 W. Dmowski, T. Egami, K. E. Swider-Lyons, C. T. Love and D. R. Rolison, J. Phys. Chem. B, 2002, 106, 12677–12683. 71 C. C. Hu, W. C. Chen and K. H. Chang, J. Electrochem. Soc., 2004, 151(2), A281–A290. 72 V. K. A. Muniraj, C. K. Kamaja and M. V. Shelke, ACS Sustainable Chem. Eng., 2016, 4, 2528–2534. Paper Materials Advances O pe n A cc es s A rt ic le . P ub lis he d on 1 4 A pr il 20 20 . D ow nl oa de d on 9 /1 3/ 20 20 1 :2 2: 42 P M . T hi s ar tic le is li ce ns ed u nd er a C re at iv e C om m on s A ttr ib ut io n 3. 0 U np or te d L ic en ce . View Article Online


Introduction
Due to the rapid depletion of fossil fuels and the increasing severity of environmental pollution, innovation and research towards harnessing alternative energy resources have gained considerable attention. 1 One of the key challenges here is the storage and conversion of harnessed energy in an efficient manner. Among the energy storage devices currently available, batteries are favored by the market because of their high energy density. Supercapacitors, on the other hand, have a relatively lower energy density, but they offer a fast charge/discharge rate, good stability, very long life-cycles, and have a high power density. [2][3][4] These unique advantages of supercapacitors make them desirable as power sources either individually or combined with other energy storage devices to build a hybrid power supply system. Lower energy densities are the biggest downside of these devices when compared to batteries. Developing economically viable high energy density materials for supercapacitor electrodes would be the potential solution for this problem.
Currently, various carbon-based materials have been intensively studied and proved to be excellent electrode materials for supercapacitors, which include carbon nanotubes (CNT), carbon aerogels, activated carbon, fullerene, graphene and carbon nano-fibers (CNF). [5][6][7][8] The carbon materials have special advantages such as a high specific surface area, an excellent thermal and electrochemical stability, a wide operating temperature range, as well as good compatibility with metals oxides. 9 However, one common problem among most carbon-based materials is their inherent difficulty to be used directly as an electrode on the current collector as most carbon materials are in powder or flake forms. Therefore, binders are needed to produce a slurry mixture of the materials to manufacture mechanically intact electrodes. Inevitably, the binders are electrically non-conductive which will result in higher electric resistance and undesired coverage of the electrode material surface area, which will further reduce the overall performance of a supercapacitor. 10,11 Besides, the specific capacitance of carbon-based materials is still low because of their charge storage mechanism, which is based on the electrostatic charging/ discharging of the electrochemical double-layer.
Another category of supercapacitor is called pseudocapacitor, which are mostly based on pseudocapacitive metal oxide/hydroxide materials such as RuO 2 , MnO 2 , V 2 O 5 , ZnO, IrO 2 , etc. [12][13][14] Transition metal oxides/hydroxides can provide much higher capacitance than carbon-based materials because of the contribution of very fast reversible redox reactions during the charge storage process on the surface and within the thin sub-surface region. 15,16 Among the transition metal oxides mentioned above, RuO 2 is believed to be one of the best candidates for its recordhigh capacitance, excellent electrical conductivity, and superior electrochemical reversibility and stability. 17,18 However, the major drawbacks that prevent using ruthenium oxide for commercial production include its high costs and loss of power density when operating at high charge/discharge rates. A promising solution to solve the problems mentioned above is to fabricate composite materials that utilize the porous structure and larger surface area of carbon materials together with transition metal oxides. 19,20 The hybrid materials show strength in improving energy and power density, as well as enhancing the cyclic stability of the electrodes operating in various electrolytes.
In this work, we introduce for the first time, RuO 2 loaded on CNF directly grown on nickel foam (Ni-f) substrates via a thermal decomposition method. The highly active redox nature of RuO 2 was fully realized by enhanced surface area from the underlying CNF, which further provided exceptional specific energy and specific power. The novel and facile technique to produce binder-less electrodes are easy to scale up for commercial production due to minimal preparation steps and minimal use of RuO 2 . The effect of electrode preparation temperature on the capacitance was carefully investigated utilizing both surface characterization techniques and electrochemical measurements. This high-performance material with superior cycling stability makes it an outstanding candidate as pseudocapacitor electrodes for practical applications. Compared with ruthenium oxides produced by other methods, the capacitance of our electrodes is amongst the highest level of state of the art pseudocapacitors.

Electrode preparation
CNF were grown on Ni-f (80 mM thick, MTI corp.) using the method described in our previous article. 6 Briefly, Ni-f was cut into 1 cm Â 1 cm squares and cleaned in 0.1 M acetic acid and then sonicated in ethanol for 10 minutes. Further, these pieces were dried and weighed (ultramicro balance Sartorius S4). Then, these cleaned foam pieces were placed on a ceramic boat and positioned at the center of a horizontal split furnace (Lindberg-Blue HTF5500; 120V/30A). Argon at a flow rate of 500 sccm was flown throughout the process. The Ni-f structure was preheated at 410 1C for 30 min and then 50 sccm of acetylene was passed for 5 min (injection phase), followed by a 30 min growth phase, and later the furnace was cooled down to the room temperature. The Ni-f was weighed before and after the growth of CNF to determine the carbon mass accumulation. The carbon accumulation was found to be 3.88 AE 0.07 mg cm À2 .
The ruthenium oxide layer was coated on the CNF by the thermal decomposition method. The precursor solution of 0.15 M RuCl 3 ÁxH 2 O (Sigma Aldrich 206229) was carefully applied on the CNF substrate using a pipet. A total of 3 drops (22.5 mL in total) of the precursor solution were deposited on the surface of CNF substrate to ensure the surface was fully covered. After applying the first coat, the CNF substrate was placed into the furnace in air and was annealed for 15 min at different temperatures (200 1C, 250 1C, 300 1C, 350 1C, 400 1Cexperimental parameter). Then, the CNF substrate was removed from the furnace and placed at room temperature for cooling for 10 min before another layer was applied. Three layers of RuCl 3 ÁxH 2 O precursor solution was applied in total and the last layer was annealed in the furnace for 1 h in order to fully oxidize the precursor. This method was determined as being optimal, following several experiments using variations in coating layers (results not discussed in this article). A schematic of the electrode preparation is shown in Fig. 1. Error bars in the graphs or the measure of variability reported in this work represent standard deviation with n = 3, unless specified with a different n value.

Material characterization
Hitachi Cold FE SU-8000 SEM (scanning electron microscope) along with energy-dispersive X-ray spectroscopy (EDX) was used to evaluate the surface topography and elemental composition. Transmission electron microscope (TEM) images were captured using Talos-F200X from Thermo Fisher scientific. S160 carbon film-200 mesh copper grids from Agar Scientific were used to mount the sample. The RuO 2 -CNF electrode was simply scraped off the Ni-f, and then acetone (optima, Fischer chemical) was added onto the scraped power and pipetted onto the grid. This method was adopted to ensure the presence of RuO 2 on the grid. For imaging uncoated CNF, the whole CNF forest (including Ni-f) was sonicated in acetone for two minutes and drop cast on the grid. K-Alpha X-ray Photoelectron Spectrometer system (XPS) from Thermo Fisher Scientific was used with an aluminum X-ray source to find the elemental surface composition. An X-ray spot size of 400 mm and a pass energy of 20 eV were used for high-resolution HR-XPS curves and the dwell time was set at 50 ms with energy step size 0.10 eV. A dwell time of 10 ms and pass energy of 200 eV with an energy step size of 1.00 eV was used to acquire the survey spectrum. Avantage v5.932 software was used for curve fitting. The background of each spectrum was corrected using the Shirley-type background subtraction and the mixed Gaussian-Lorentzian line shape functions were used to fit all HR-XPS. Thermal gravimetric analysis (TGA, TA Instruments Q500) was performed at a ramp rate of 5 1C min À1 in air. The whole electrode, including the Ni-f current collector, was used for the analysis. A small piece of the electrode (including the Ni-f current collector) was loaded onto the platinum pan and loaded into the analysis chamber. Raman spectroscopy measurements were obtained using a DXR3 Raman (Thermo Fisher Scientific) with a laser wavelength of 532 nm, and a laser power of 5 mW.

Electrochemical characterization
The electrodes were assembled into a 2-electrode symmetric setup using a stainless-steel split cell, and the electrodes were separated using a filter paper (P8 Fisher scientific) soaked in 6 M KOH (electrolyte). Autolab PGSTAT30 (Metrohm, Netherlands) with NOVA software (v. 2.3; Metrohm, the Netherlands) was used to perform cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) and electrochemical impedance spectroscopy (EIS) analysis. Experiments were also repeated using a three-electrode setup for the best performing sample in 6 M KOH, using Hg/HgO (1 M KOH, À129 mV vs. saturated calomel electrode) reference electrode and a graphite rod as the counter electrode. The working electrode was housed in a PTFE holder (WonATech Co., Ltd, South Korea) with a working area of 1 cm 2 exposed to the electrolyte, and the graphite rod was placed in a glass frit to separate it from the working electrode (Ace glass, Inc., USA). HR-TEM of the CNF (uncoated) in Fig. 3a shows a mixture of graphitized and amorphous regions. We also see a narrow hollow core in this image, however not all CNF have shown such tubular structure (SFig. 3, ESI †). A small region in Fig. 3b indicated by the white square is digitally magnified and shown Fig. 3b. These graphitized pockets are disorganized in orientation amidst the amorphous region. The spacing between the graphitic lattice is about 0.34 nm. Graphitic layers here are wavy, discontinuous and the crystallite size appears to be small. The mean crystallite size (La) can be estimated from the Raman spectra (SFig. 4, ESI †) using a formula proposed by Mallet-Ladeira et al., 21 and was evaluated to be 2.21 AE 0.08 nm (n = 4). Raman spectra showed only faint peaks centered around 640 cm À1 and 520 cm À1 in the case of RuO 2 -CNF, in addition to the standard D (B1344 cm À1 ), G (B1586 cm À1 ), G 0 (B2681 cm À1 ) peaks, and a peak at B2390 cm À1 , which is a combination scattering peak of D and G 0 . 22,23 It is reported in the literature that Ru crystallites show peaks centered at B520 cm À1 and B640 cm À1 . 24 In this study these peaks are hard to decipher mostly due to the shadowing of the peaks intensity with the background from the bulk CNF forest underneath it. The defect ratio (I D /I G ) of the as-grown CNF is found to be 2.28 AE 0.08 (n = 4), indicating a relatively high disorder in the structure. 25 The curve fitting parameters of the D and G peaks are shown in STable 1 (ESI †). A TEM image of the prepared RuO 2 -CNF sample shows sheet-like RuO 2 formation (Fig. 3c). It is to be noted that samples prepared for the TEM imaging were scrapped off the electrode. Thus, it does not really represent the topography of the actual electrode structure. It can be observed that these RuO 2 sheets are randomly present on top of the CNF. A TEM at higher magnification showing the ruthenium oxide deposits, an HR-TEM and the associated EDX spectra confirming the presence of RuO 2 are shown in SFig. 5 (ESI †).

Surface and material composition analysis
An XPS-survey spectrum confirms the presence of ruthenium, carbon, oxygen, and chloride on the electrode surface (Fig. 4a). The elemental composition determined from the EDX (SFig. 1, ESI †) and the XPS is shown in Fig. 4b. Fig. 5a-c show the HR-XPS for Cl 2p, Ru 3p and O 1s, respectively. Ru 3p corelevel spectra are analyzed instead of Ru 3d to avoid peak overlapping with C 1s core level spectra, which could deter the identification of Ru species appropriately. NIST database was used to assign the majority of the fitted peaks 26 and the fitted peak values of all the elements are shown in STable 2 (ESI †).
In Fig. 5a, the peaks at 198.29 AE 0.02 and 199.99 AE 0.02 eV correspond to the Cl 2p 3/2 and Cl 2p 1/2 , respectively, due to the presence of chlorides remained from the hydrous RuCl 3 precursor after the thermal decomposition (0.95 AE 0.05 atom% of Cl in the coating, Fig. 4b). Fig. 5b shows Ru 3p spectra with a doublet fitted with curves assigned to the same chemical states as in Ru 3d spectra. In the Ru 3p 3/2 part of the spectra, the curves with peaks at 462.87 AE 0.22, and 466.02 AE 0.30 eV were assigned to RuO 2 , and RuCl 3 respectively. Spin-orbit splitting (SOS) between Ru 3p 3/2 and Ru 3p 1/2 is found to be B22 eV.

View Article Online
In the O 1s core spectra shown in Fig. 5c, RuO 2 is assigned to the curves with a peak centered at 530.35 AE 0.09 eV. Additionally, the peak at 532.43 AE 0.15 eV can be assigned to CQO. 27 TGA was performed in air to further investigate the electrode composition (electrode prepared 250 1C), and the change in the electrode weight percentage in the temperature range 30 1C to 650 1C is shown in SFig. 6a (ESI †). The bare CNF structure on the Ni-f shows a sharp decline in the mass percentage beyond 450 1C, which is mainly due to the decomposition of the CNF. This behavior is consistent with the literature where CNF were prepared using different techniques. [28][29][30] Thermal decomposition of hydrous RuCl 3 can be represented by eqn (1).
Interestingly the TGA curve for RuO 2 -CNF has an initial gradual slope due to the loss of physically adsorbed water at lower temperatures, followed by the loss of water in the crystal. 31 This is followed by the early onset of carbon combustion at ca. 300 1C. Even though it is observed that RuO 2 shows no weight loss until 1025 1C, 32 the weight loss for the RuO 2 -CNF exclusively due to the loss of water is difficult to estimate. This is because the carbon oxidation onset point for RuO 2 -CNF will be lowered in comparison to that of pure CNF due to the catalytic effect of the RuO 2 present on the CNF surface. 33 (Fig. 6a). In order to reach a stable response, the two-electrode cell was initially cycled for 20 cycles at 100 mV s À1 , followed by five cycles at a given scan rate and the 5th cycle was then recorded and displayed in Fig. 6a. This stabilization was done in order to open the pores in the electrode and remove the plausible effect of irreversible surface functionalities which would lead to irreversible redox peaks. Only the electrode prepared at 200 1C showed visible reversible broad peaks on the CV. SFig. 7 (ESI †) shows CV of the electrode prepared at 200 1C at different scan rates. The broad anodic peak centered at around 0.5 V and the corresponding cathodic peak centered at around 0.45 V (Fig. 6a), can be deconvoluted into multiple peaks, which could be associated with redox transitions of ruthenium, presented in a very simplified way as: 35 RuO x (OH) y + zH 2 O + ze À -RuO xÀz (OH) y+z + zOH À (2) All other electrodes exhibit a rectangular pattern, similar to the EDLC behavior. However, the underlying charging/discharging processes are both of the electrostatic (electrostatic double layer charging/discharging) and redox nature (eqn (2)). This explanation is well documented in the literature. 36,37 Variation of CV curves and the dependence of the peak currents with the scan rate for the electrodes prepared at 200 1C is shown in SFig. 7 (ESI †). As the peak currents are linearly proportional to the scan rates, it can be inferred that the reaction is surface area limited rather than being diffusion controlled. This hints additional pseudo capacitance which is mostly contributed by the fast-redox reaction in the voids and pores which can be expected in samples prepared at 200 1C where more hydrous content is preserved. Subsequently, the peaks also become subdued at higher scan rates further indicating the role of additional hydrous pores and voids which would be harder for the electrolyte ions to access at higher scan rates. Electrodes prepared at higher temperatures shows no appearance peaks, due to the manner in which the redox peaks overlap (Fig. 6a). As mentioned earlier, there are multiple redox reaction happening even though, the CV appears to be rectangle similar to EDLC behavior. The capacitance of the material was calculated from the CVs in Fig. 6a using eqn (3), where a factor of 2 is used to calculate the capacitance of only one electrode. 6,38 where Q avg (AsQC) is the average cathodic and anodic charge, and DV (V) is the voltage window. Samples of RuO 2 -CNF prepared at 200 1C showed the highest capacitance, 944 AE 17 mF cm À2 , and the capacitance is shown to decrease with the increase in the electrode preparation temperature (Fig. 6b). The presence of water in the lattice of the RuO 2 is the plausible reason for the increased capacitance at lower temperatures due to enhanced protonic and electronic conduction. 39 At higher temperatures (4300 1C), RuO 2 is known to become more crystalline and loses water content (SFig. 6a, ESI †), which leads to proton (or hydroxyl ion) diffusion limitation causing reduced capacitance. 17,[40][41][42] Additionally, the decreased capacitance could be associated with the reduced electrolyte accessible surface area due to the loss of water in the inter-particle (both carbon fibers and metal-oxide) voids, and increased particle aggregation at higher oxide forming temperatures. Fig. 7a shows CV recorded at different scan rates for the electrodes prepared at 250 1C. The shape of the CV remains semi-rectangular even at higher scan rates, signifying the easy access of ions into the porous structure of the electrode to rapidly form a double layer along with lower series resistance. The linear dependence of the anodic current recorded at 0.5 V with varying scan rates (Fig. 7b) suggests a surface-controlled behavior rather than a diffusion-controlled behavior. This is due to the easy accessibility of the ions into the pores followed by the occurrence of the pseudo capacitance due to redox reaction (eqn (2)), along with the electrostatic double-layer charging, as previously mentioned. The variation of capacitance with scan rate is shown in Fig. 7c. It can be observed that the capacitance at the scan rate of 5 mV s À1 is lower than the capacitance at 10 and 20 mV s À1 , and the same was recorded in GCD measurements (Fig. 9); this appears counter-intuitive when compared to literature data for most of electrodes. This anomality could have resulted due to the structural collapsing of the carbon fibers in the electrode at very low scan rates, which results in decreased access to the electrode surface area resulting in lower capacitance. Similar trend has been reported with uncoated carbon nano fibers in the past. 43,44 3.2.2. Galvanostatic charge/discharge. Although CV can be used to determine the capacitance of an electrode, a more suitable way of doing this is by employing the galvanostatic charge/discharge method, which more closely reflects the real use of a supercapacitor. The galvanostatic charge-discharge curves of RuO 2 -CNF electrodes produced at different temperatures were recorded at a current density of 20 mA cm À2 and are shown in Fig. 8a. These curves show symmetric triangular behavior, like most of EDLC/pseudo-capacitor materials 45 and affirm the extraordinary reversibility of the redox reaction. Contrary to CV measurement for 200 1C sample (Fig. 6a) which showed broad peaks, the GCD for the same samples does not show any obvious deviation from linearity. This example alone clearly suggests the best method for evaluating capacitance would be GCD for obtaining more realistic capacitance.
Capacitance was calculated from the discharge curve using the following equation: where C is the specific capacitance (F cm À2 ), j is the applied current density (A cm À2 ) and dV/dt is the slope of the discharge curve after the initial iR drop portion. A factor of 2 is used to estimate the capacitance for only one electrode. The capacitance values obtained at 20 mA cm À2 for various electrodes with an operating voltage window from 0 to 0.8 V are summarized in Fig. 8b. As control electrodes, CNF on Ni-f and RuO 2 deposited directly on the Ni-f, are shown. The CNF electrode gave a capacitance of 142 AE 07 mF cm À2 , which is in agreement with previous studies. 44 When RuO 2 was deposited on the Ni-f, the resulting capacitance decreased to 53 AE 08 mF cm À2 . This shows that, despite the fact that RuO 2 is an excellent pseudocapacitor material whose capacitance is based on the occurrence of fast reversible redox reactions in the solid phase (eqn (2)),   [53][54][55][56] Some of the recent results reported in the literature are shown in Table 1. Fig. 8b shows decreasing capacitance values with increasing electrode preparation temperature. This trend in capacitance behavior shows higher capacitance at lower oxide preparation temperatures when compared to previously studied RuO 2 electrodes. 39,46,[65][66][67][68] The method of preparation employed in this work along with the underlying evenly distributed CNF has enabled higher capacitance values. Studies have reported that the protonic and electronic conduction pathways in the RuO 2 ÁxH 2 O varies with the water content within the rutile structure. [69][70][71] In this study, the underlying CNF forest, which acts like a large surface area template, influences the availability of the electrochemically active surface area along with its influence on some physical properties due to nanostructured effects.
In order to investigate the influence of current density on the charging/discharging rate and the resulting capacitance, GCD curves for the electrode prepared at 250 1C were recorded (Fig. 9a), and the variation of capacitance with current density is shown in Fig. 9b. It is to be noted that, electrodes prepared at 250 1C were chosen for this analysis despite their lower capacitances compared to electrodes prepared at 200 1C, considering their much better cycling stability, which is discussed later in this article. As it can be seen from Fig. 9a, the shape of the GCD curves is not dependent on the current density; all the curves show symmetrical/triangular behavior. With an increase in current density, the charging/discharging rate increases, as evidenced by the increase in the corresponding slopes of the curves. To evaluate if this is at the expense of a decreased capacitance, the corresponding values were calculated; as it can be seen in Fig. 9b, the capacitance shows a general decrease with the increase in current density, which is to be expected. Capacitance values change from roughly 830 mF cm À2 at 3 mA cm À2 to 760 mF cm À2 at 100 mA cm À2 . It is noticed that the capacitance remained slightly lower at 3 mA cm À2 than at 5 mA cm À2 , which was already discussed previously in relation to CV data (Fig. 7).
Most ruthenium-based capacitors have the disadvantage of lower capacitance (and thus also lower energy density) at higher charge/discharge currents. 31,52,72,73 However, for the RuO 2 -CNF electrodes (Fig. 9b), only a 10% decrease in the capacitance is observed at a high current density of 100 mA cm À2 when compared to the capacitance at 5 mA cm À2 . This is because the high surface area and the well-connected CNF support provide a template for the distribution of the RuO 2 leading to faster proton diffusion, less series resistance and the larger double layer area formation at the electrode surface, leading to these enhanced supercapacitor qualities.
3.2.3. Electrochemical impedance spectroscopy measurements. To elucidate the electrochemical characteristics of various components within the electrochemical cell, EIS measurements were performed (Fig. 10a). Analyses are carried out at a dc cell voltage of 0 V, and with a sinusoidal ac voltage amplitude of AE10 mV in the frequency range 10 mHz to 100 MHz. A semicircle in the higher frequency region (inset to Fig. 10a) is attributed to the parallel combination of the charge transfer resistance (R ct ) and the corresponding pseudocapacitance. Only samples prepared at 200 1C show a clear semicircle in the higher frequency region, suggesting a larger charge transfer resistance.
Remaining electrodes formed at the higher temperatures show an inclined line instead of the semi-circle in the higher frequency region. The disappearance of semi-circle may be due to better conductivity of the coating and better accessibility of the porous region on the electrode. 6,74 All electrodes show a vertical trend in the lower frequency region, almost parallel to the imaginary impedance axis, indicating good capacitive behavior. Therefore, a series RCmodel was adapted to interpret the data and the capacitances at a low frequency (0.01 Hz) were calculated for various samples using eqn (5). 75,76 where f (Hz) is the frequency, and Z 00 (O cm 2 ) is the imaginary part of the impedance. The calculated capacitance values are shown in Fig. 10b, and they are comparable to the values obtained from CV (Fig. 7b) and GCD (Fig. 8b) measurements.    Fig. 11 shows the Ragone plots of the RuO 2 -CNF electrode prepared at 250 1C, together with CNF fibers only. 44 Specific energy and specific power of the cell were calculated using eqn (6) and (7) respectively. For the RuO 2 -CNF electrode, a specific energy value varied from 362 mW h m À2 to 336 mW h m À2 when the power density was increased from 12 W m À2 to 957 W m À2 . This translates roughly into a maximum energy density of 13.51 W h kg À1 and a max power density of 35.71 kW kg À1 (estimated based on mass loading of RuO 2 only, and the mass loading is shown in SFig. 8, ESI †). This performance is significantly higher than just that of CNF electrodes, and the ability to deliver higher specific power at higher specific energy is enhanced when compared to many carbon and metal oxide based electrodes. [77][78][79] The present specific energy results are comparable to other high specific capacitance yielding electrodes, such as RuO 2 -CNT/CNF-based electrodes, 50,63,64,72 RuO 2 -graphene oxide-based electrodes 54,73 and other RuO 2composite based electrodes. 49,74 P ¼ E t 3.2.5. Three and two electrode measurement comparison. As shown in Fig. 9b, capacitance decreases with an increase in current density. This could be related to the decrease in utilization of surface area of the electrode, i.e. to the accessibility of the electrode area to electrolyte ions. For pseudocapacitors, it can also be related to a decrease in the depth of intercalation of protons below the metal-oxide surface area or simply a fast charge transfer reaction at the surface. In order to examine this in more detail, CV measurements in a threeelectrode cells were recorded at various scan rates. A comparison with the two-electrode cell at a scan rate of 20 mV s À1 is presented in Fig. 12a and b. The three-electrode configuration was used here because the potential of the reference electrode is fixed, thus enabling monitoring the behavior of only one electrode in a well-defined potential region, as a function of scan rate.
The CV curves with varying scan rates are shown in Fig. 13a. These curves tend to slant at higher scan rates, suggesting higher series resistance. A comparison with EIS confirms higher series resistance in the three-electrode supporting this trend (SFig. 9, ESI †). This effect diminishes in the two-electrode cell, as the electrodes are pressed against each other tightly, which then compresses the CNF and form a conducive network for better conductivity. Capacitance values at scan rates varying from 5 to 500 mV s À1 were calculated from the CVs in Fig. 13a using the average cathodic and anodic charge, and are presented in Fig. 13b. It is to be noted that the capacitance values continuously increased as the scan rate decreased, unlike the trend found using the two-electrode system where the electrodes were pressed tightly against each other, where the first point shows a lower capacitance than the second point (Fig. 7c). This result reinforces the possibility of structural collapsing of the carbon fibers and the requirement of certain current density (scan rate) to provide more electrochemical active surface area. In three electrode measurements, the electrode was simply exposed to the bulk electrolyte solution with no separator and the other half-cell electrode pressing against the working electrode. Thus, surface area available for the redox reaction and double layer formation increased with the decrease in the scan rate.
To evaluate the contribution of the inner and outer layer of the electrode to the capacitance, Trisatti's method was used (Fig. 14) Fig. 10 (a) Nyquist plots for RuO 2 -CNF electrodes prepared at different temperatures (inset: the zoomed-in high-frequency region). The spectra were recorded at cell potential of 0 V (b) capacitance values obtained from EIS measurements for electrodes prepared at different temperatures. using the results from the three-electrode measurements. 65 At an infinitely high scan rate it is assumed that only the easilyaccessible outer surface area of the electrode participates in the formation of the capacitance (C outer ), while at an infinitely low scan rate, a maximum (total) possible capacitance (C T ) is achieved. The intercept of the linear portion of the trend in Fig. 14a with the ordinate yields a value of 60 mF cm À2 , which represents the contribution of an outer surface area of the electrode (C outer ) to the total capacitance. On the other hand, the intercept of the linear trend in Fig. 14b yields a value of 1062 mF cm À2 , which includes both inner and outer surface contribution to the maximum/total capacitance (C T ). The contribution of the inner surface capacitance (C inner ) to the total capacitance can then be calculated by subtracting C outer from C T , which yields a value of 1002 mF cm À2 . 3.2.6. Cycling stability. In order to evaluate the stability of the prepared RuO 2 -CNF electrodes, long-term cycling (5000 cycles) GCD experiments were performed at a current density of 200 mA cm À2 (Fig. 15) in a full cell (i.e. 2 cell electrode). Electrodes prepared at 200 1C, showed a steep linear decrease in capacitance until 3000 cycles and then remained relatively stable during the later cycles, yielding the overall capacitance retention of ca. 60% after 5000 cycles. These electrodes   were also observed to have poor physical stability when assembled into a cell with electrolyte. Electrodes prepared at 250 1C, 300 1C, 350 1C, 400 1C showed a capacitance retention of 94%, 95%, 93% and 81% respectively after 5000 cycles. This also suggests that oxide forming temperatures of 250 1C and above provide stable coatings. All these electrodes showed a minor gradual decrease in capacitance. Even though electrodes prepared at 400 1C seemed to be mechanically stable after the cycling test, the increased dropped in capacitance retention could be mostly attributed to the architecture of the electrode. As deduced from TGA curves (SFig. 6, ESI †), these electrodes barely have any hydrous protonic/hydroxyl ion conduction path, and the capacitance is solely depended on the electrochemically active surface area. The capacitance would have dropped due to the mechanical degradation of micro and meso porous area of the electrode with cycling. It was also found that the stability of the capacitance for the Ni-f/RuO 2 -CNF structure generated at 250 1C is much better than other high capacitance rutheniumbased electrodes reported in the literature. 46,[80][81][82][83][84]

Conclusion
In this article, RuO 2 was coated directly on CNF forests grown on Ni-f. The influence of different preparation conditions on the electrochemical performance for supercapacitor applications was studied. The deposition of RuO 2 shows to significantly increase the specific capacitance when compared to CNF only or RuO 2 only electrodes. This increase is due to the pseudo capacitance offered by RuO 2 along with the surface area of the CNF template, and the preparation conditions of the electrode. RuO 2 coated at 250 1C showed 94% capacitance retention after 5000 cycles, and maximum specific energy and maximum specific power of 362 mW h m À2 and 957 W m À2 . High specific capacitance, cycling stability and the facileness of the electrode preparation that easily enables scaled up, make this a promising material in applications where the charge per area is essential. This methodology can be used to prepare other metal oxide and conductive polymer coats for similar applications.

Conflicts of interest
There is no conflicts to declare.