Electrochemical analysis of Na–Ni bimetallic phosphate electrodes for supercapacitor applications

Bimetallic sodium–nickel phosphate/graphene foam composite (NaNi4(PO4)3/GF) was successfully synthesized using a direct and simple precipitation method. The hierarchically structured composite material was observed to have demonstrated a synergistic effect between the conductive metallic cations and the graphene foam that made up the composite. The graphene served as a base-material for the growth of NaNi4(PO4)3 particles, resulting in highly conductive composite material as compared to the pristine material. The NaNi4(PO4)3/GF composite electrode measured in a 3-electrode system achieved a maximum specific capacity of 63.3 mA h g−1 at a specific current of 1 A g−1 in a wide potential range of 0.0–1.0 V using 2 M NaNO3 aqueous electrolyte. A designed and fabricated hybrid NaNi4(PO4)3/GF//AC device based on NaNi4(PO4)3/GF as positive electrode and activated carbon (AC) selected as a negative electrode could operate well in an extended cell potential of 2.0 V. As an assessment, the hybrid NaNi4(PO4)3/GF//AC device showed the highest energy and power densities of 19.5 W h kg−1 and 570 W kg−1, respectively at a specific current of 0.5 A g−1. The fabricated device could retain an 89% of its initial capacity with a coulombic efficiency of about 94% over 5000 cycling test, which suggests the material's potential for energy storage devices applications.


Introduction
With the advent of electric vehicles and portable electronic devices human demand for energy has continued to increase. Due to the energy consumption rate of these components, energy is regarded as the major problem facing humanity. 1,2 Although there are different types of energy sources 3 that could be explored to power these devices, the renewable sources (such as wind and solar) have been mooted as the best option to use due to the low or zero green gas emission rate. However, as a result of the intermittent nature of the green energy sources, their successful exploitation requires reliable and efficient electrical energy storage systems. Following this development, the design of new energy storage devices remains an active and expanding eld of research. 4,5 Electrochemical energy storage systems, which include but are not limited to batteries and electrochemical capacitors (ECs), 6 have been embraced as efficient storage devices. The reason for this is that the storage technique takes advantage of the fact that both chemical and electrical energy have a common charge carrier (known as the electron), thus limiting losses due to energy conversion from one form to another. For many years, batteries have been used as the storage devices mainly because of their high energy density. However, they take time to charge and discharge, which reduces their tendency to deliver power. In applications requiring high and instant power, engineering the right battery for the task would typically lead to an increase in the size and cost requirements. Consequently, supercapacitors are very attractive candidates in the eld of energy-storage to replace conventional chemical batteries for use in hybrid vehicles, portable electronics and backup energy systems owing to the strength of their unique power densities, fast charge-discharge rate, and stable cycling performance. 7,8 Supercapacitors are generally classied into two categories based on the storage mechanism: the electrical double layer capacitors (EDLC) (by electrostatic storage) and the pseudocapacitors (by fast redox process), which can overcome the low energy density of EDLC. 9 However, the shortage that restricts the application of supercapacitors in portable electronic devices is the design and also the bulkiness of the device. So the requirements of such devices like mobile phones and wearable electronics are lightweight, safety, exibility, high-performance and reliable power sources. 10 As a sort of charge mechanism storage, the performance of supercapacitors conguration depends on the fundamental characteristics of the materials in the cell. Transition metal oxide as well as conducting polymer has been strongly considered as active materials for supercapacitors. Presently, due to excellent chemical stability, rich valences, and good electrochemical performance, various transition metal oxides have also been candidates in this eld. [11][12][13][14] Among these transition metal oxides (TMOs), such as RuO 2 and IrO 2 , RuO 2 is a conductive metal oxide, with three oxidation states accessible within 1.4 V, exhibiting an impressive reported specic capacitance up to 2000 F g À1 . 15 RuO 2 is known to be the most effective electrode material, but the extremely high cost and toxicity limit its applications. 16 Hence, cheaper transition metal oxides, such as nickel oxides, cobalt oxides, manganese oxides and iron oxides, are actively studied and found to exhibit good electrochemical performance. This has triggered strong research interest in the materials. Among these, nickel phosphates are regarded as good candidates owing to their low cost, lower toxicity, easy synthesis and high theoretical specic capacity, while sodium phosphate is a novel energy storage cathode material based on an affordable and globally available element. 17,18 Besides the oxides, transition metal phosphates, on the other hand, have reported performing in a promising manner when subjected to the test of safety, environmental inertness, structural stability and energy efficiency. 19 Li-based phosphates having a common formula LiMPO 4 (M ¼ Ni, Fe, Co or Mn) have been extensively used as a cathode material for a battery. These compounds contain tetrahedral anion structure units (XO 4 ) nÀ with strong covalent bonding, generating oxygen octahedral sites occupied by other metal ions. 20 Among the several metal atom substitutions, lithium-iron and lithium-manganese phosphates have been observed as promising cations in the olivine structure. This is mainly due to low cost, environmental inertness, cycling stability and a high degree of reversibility. 21 Na-based phosphate with chemical formula NaMPO 4 (M ¼ Mn, Co, Ni and Fe) is also considered as an interesting cathode candidate for the new generation of sodium-ion batteries. 22 This consideration is mainly owing to some unique advantages including thermal stability and higher voltage due to the inductive effect which made the phosphate-based materials to be the capable cathode materials in Na-ion batteries. 23 To the best of knowledge, there are insufficient studies reported considering metal phosphate as an electrode for supercapacitor application. Zhang et al. reported the synthesis of a series of mesoporous Ni x Co 3Àx (PO 4 ) 2 hollow shells where they have used boiling a mixture at 185 C. The Ni x Co 3Àx (PO 4 ) 2 hollow shells has used as a material for supercapacitor, sensor and catalyst applications. As a supercapacitor electrode, the material achieved a specic capacitance of 940 F g À1 at a specic current of 1 A g À1 and 85% of the initial capacitance was maintained aer 1000 cycles. 24 Senthilkumar et al. reported the synthesis of NaMPO 4 (M ¼ Mn, Co and Ni) maricite-type following a solution combustion method. The materials have tested in 1 M NaOH and achieved specic capacitance as follow: NaMnPO 4 (163 F g À1 ), NaCoPO 4 (249 F g À1 ) and NaNiPO 4 (368 F g À1 ). Moreover, the NaNiPO 4 maricite-type used as positive electrode in a device with AC as a negative electrode, where energy density of 20 W h kg À1 and power density of 138 W kg À1 were reported. 25 Ha-Kyung Roh et al. synthesized NaTi 2 (PO 4 ) 3 / rGO through direct precipitation of NaTi 2 (PO 4 ) 3 nano-sized on rGO. 1 M NaClO 4 dissolved in a mixture of ethylene carbonate (EC) & dimethyl carbonate (DMC), (1 : 1) was used as an electrolyte. The NaTi 2 (PO 4 ) 3 /rGO was used as a negative electrode in a device with AC as a positive electrode. The device could operate in a wider voltage of 2.7 V as result of organic electrolyte used. Consequently, an energy density of 53 W h kg À1 and a power density of 334 W kg À1 at specic current of 0.25 A g À1 was delivered. 26 On the other hand, in order to efficiently enhance the performance of monometallic active material (for example NiPO 4 ); one can take advantage of the synergistic effect of combining two metals in a bimetallic active material. A bimetallic phosphate e.g., NaNiPO 4 in contrarily to the monometallic phosphate is expected to provide a better redox process. Firstly, we are using the highly conductive Ni cation in sodium analogue in an aqueous electrolyte. 25 Secondly, an addition of graphene into the matrices of the material is another practical step of compositing. Graphene is considered to be motivating choice for composite-material. Graphene has an attractive advantage like high electronic conductivity (16 000 S m À1 ), high intrinsic carrier mobility (200 000 cm 2 V À1 s À1 ), high specic surface area (2630 m 2 g À1 , theoretical value), and high superior mechanical strength which makes it a favorable material in a wide diversity of applications. 27 Furthermore, exible graphene also serves as a buffer to alleviate possible volume changes during charge/discharge process, especially in cyclability test processes. 28,29 In the present work, we introduced a direct and easy precipitation method to synthesize a novel hierarchical nanosphere bimetallic sodium-nickel phosphate and demonstrated its capacitive capability in aqueous electrolyte. These distinctive nanospheres brought out the synergy of conductive Ni cation in sodium analogue composited with a conductive graphene. A comparison of pristine NaNi 4 (PO 4 ) 3 and composite NaNi 4 (-PO 4 ) 3 /GF as electrodes for supercapacitors in 3 electrode conguration aqueous electrolyte were carried out. The composites NaNi 4 (PO 4 ) 3 /GF has resulted in a superior capacitive properties than the pristine NaNi 4 (PO 4 ) 3 in a wide potential window up to 1.0 V using a 2 M NaNO 3 aqueous electrolyte. The composite NaNi 4 (PO 4 ) 3 /GF was then used as a positive electrode in a hybrid cell device with activated (AC) as a negative electrode. The hybrid NaNi 4 (PO 4 ) 3 /GF//AC was found to operate in a very wide cell potential of 2.0 V.

Materials
Nickel nitrate hexahydrate (Ni(NO 3 ) 2 $H 2 O), sodium nitrate (NaNO 3 ), ammonium phosphate (N 2 H 9 PO 4 ) and urea (CH 4 N 2 O) were purchased from Sigma Aldrich and used as received without further modication. Graphene foam used in this work was prepared by means of an atmospheric pressure chemical vapor deposition (APCVD) technique as reported in our previous work. 30

Synthesis of NaNi 4 (PO 4 ) 3 /GF
For the synthesis of pristine NaNi 4 (PO 4 ) 3 , nickel nitrate hexahydrate (5.82 g), sodium nitrate (1.70 g), ammonium phosphate (2.64 g) and urea (1.20 g as a reducing agent) were all dissolved in 20 ml deionized water and stirred for 30 min. The mixture was then placed on a hot plate at 200 C for dehydration. Aer complete dehydration the obtained yellowish solid was then transferred into an atmospheric electric furnace set at 300 C for 15 min for heat treatment as shown in Scheme 1. The same procedure was followed for the synthesis of the NaNi 4 (PO 4 ) 3 /GF composite but with addition of 60 mg graphene foam (GF).

Synthesis of activated carbon (AC)
The AC sample used in this work was prepared in two steps as follows: initially, the peanut shell (PS) was washed with deionized (DI) water and dried in ambient condition before being ground to ne powder. Aerward, 5 g of the powder (PS), 1 g of NaCl and 0.5 g urea were mixed together with DI water to form a mud cake, which was placed in an electric oven at 80 C overnight to dry. The prepared cake was then carbonized at 600 C under argon gas for 2 h at 5 C per min heating rate to obtain a hydrochar. The recovered hydrochar was washed several times with DI water and dried in an oven for 12 h at 80 C. Thereaer, the hydrochar was mixed with KOH in a ratio of 1 : 4 and then transferred into a horizontal tube furnace for activation at 850 C for 1 h at a ramping rate of 5 C per min under Ar gas. The nal product was soaked in 3 M HCl to remove residual KOH, and then washed with DI water until neutral pH was obtained and then dried at 80 C overnight.

Structural characterization
X-ray diffraction was used for structure analysis in the range 2 theta ¼ 15-80 . The specication of the instrument is as follow: XPERT-PRO diffractometer (Analytical BV, the Netherlands) with q/2q geometry and a counting time of 5.240 s per step. Qualitative phase examination of the samples was directed with the X'Pert Highscore search-match soware at room temperature using Co K1a (l ¼ 0.178897 nm). Surface area was obtained by the Brunauer-Emmett-Teller (BET) technique from the N 2 adsorption isotherm technique from a Micrometrics Tristar II 3020 (version 2.00) Analyser at 90 C. The pore size distribution plot was obtained from the desorption branch of the Barrett-Joyner-Halenda (BJH) plots. The SEM images were obtained on a Zeiss Ultra Plus 55 eld emission scanning electron microscope (FE-SEM) (Carl Zeiss, Oberkochen, Germany) operated at an accelerating voltage of 2.0 kV. The Raman spectra for the samples were obtained using a WITec alpha 300 RAS+ confocal micro-Raman microscope (Focus Innovations, Germany) at a 532 nm laser wavelength was adopted to characterize the samples with a spectral acquisition time of 150 s and laser power of 5 mW.

Electrochemical characterization
To make electrodes for 3-electrode conguration, 80% of the active material was mixed with 10% carbon black and 10% polyvinylidene diuoride (PVDF) as a binder. The role of the carbon black on the mixture was to increase the conductivity of the material. A 1-methyl-2-pyrrolidinone (NMP) was later added to make slurry. Aer perfect mixture of the material with the NMP, pasted on the nickel foam with a diameter of 1 cm 2 and allocated in an oven set in 70 overnight to evaporate the NMP. The electrochemical measurements were done in a 3-electrode system using Ag/AgCl (3 M KCl saturated) and glassy carbon as the reference electrode and counter electrode respectively. A neutral 2.0 M NaNo 3 aqueous electrolyte was used in this experiment. A coin cell type CR2025 was used to assemble the hybrid supercapacitor. Different anodic and cathodic materials were used and the microber glass lter paper used to separate the two electrodes. Cyclic voltammetry (CV) was applied to conrm the cell-type while galvanostatic charge-discharge (GCD) was applied for further conrmation of the cell-type and also to calculate the cell capacity. Both the CV and CD were carried out in a cell potential ranging between 0.0 and 2 V. The impedance of the hybrid was also investigated with electrochemical impedance spectroscopy (EIS) in range 100 kHz to 0.01 Hz with zero potential amplitude using a Bio-logic VMP-300 potentiostat (Knoxville, US) driven by the EC-lab soware.

Structure, texture and morphology
The crystal structure of the as-prepared NaNi 4 (PO 4 ) 3 nanospheres was characterized by X-ray diffraction (XRD) using Diamond soware. 31 In Fig. 1(a)  space group: pmnn (58) orthorhombic. From Fig. 1(a), all of the diffraction peaks are sharp and can be well indexed with NaNi 4 (PO 4 ) 3 (ICSD -50724). These diffraction peaks with narrow shapes indicate that the sample possesses good crystallinity. Usually, crystalline materials can electrochemically perform better since their stable crystal structure cannot be destroyed easily during charge-discharge processes. 32 Fig. 1(b) shows the possible schematic crystal structure of the sample. The information from the standard PDF card reects the presence of strong electron localization in NaNi 4 (PO 4 ) 3 . Moreover, altering the site of Na and Ni causes the triphylite form creating more space for Na ions to occupy and intercalate along onedimensional channel in its orthorhombic framework, which is an essential factor for energy storage host materials. Fig. 1(c) shows the XRD pattern of the NaNi 4 (PO 4 ) 3 and NaNi 4 (PO 4 ) 3 /GF composite. It can be observed that with an introduction of GF the XRD pattern of the NaNi 4 (PO 4 ) 3 /GF/GF remained unchanged however, a peak corresponding to GF was observed at about 30.9 degree and indexed as (002). This conrms the presence of GF in the NaNi 4 (PO 4 ) 3 /GF composite. Fig. 2(a) shows Raman analysis of the pure graphene foam (GF), NaNi 4 (PO 4 ) 3 , and NaNi 4 (PO 4 ) 3 /GF composite. G and 2D band were observed at about 1577 cm À1 and 2701 cm À1 respectively as Raman signature of graphene foam which are representative of C-C vibration mode and double resonance process. 33 The G and 2D bands were also seen in NaNi 4 (PO 4 ) 3 / GF but with slightly less intensity which conrms the existence of GF in this composite and also the incorporation of GF into the matrix of NaNi 4 (PO 4 ) 3 electrode material. The peak at about 1043 cm À1 on the NaNi 4 (PO 4 ) 3 as well as NaNi 4 (PO 4 ) 3 /GF is attributed to the symmetric stretching and vibrational mode of PO 4 3À . 34 Another Raman peaks were observed at about 737, 721, 636, 613, 566 and 473 cm À1 which could be referred to Na-Ni-O. 35,36 I 2D /I G peak ratio is calculated to be equal to $0.97 which is an indication that GF used to form the composite is a few layers. 34 The pore texture of the NaNi 4 (PO 4 ) 3 and NaNi 4 (PO 4 ) 3 / GF was analyzed by N 2 adsorption/desorption measurements. Fig. 2(b) shows that the materials exhibit a type-III behavior with type-H3 hysteresis loop suggesting material containing mainly mesopores and macropores. The specic surface area (SSA) of the NaNi 4 (PO 4 ) 3 and NaNi 4 (PO 4 ) 3 /GF are 4.3 m 2 g À1 and 10.1 cm 2 g À1 respectively. The increase in the specic surface area in the composite can be attributed to the presence of graphene foam. Consequently, the electrochemical performance of the composite is expected to be signicantly improved. The pore size distributions (Fig. 2(c)) was calculated using the Barrett-Joyner-Halenda (BJH) analysis from the desorption branch and the pore size in the materials is mainly distributed within 5-50 nm range. Scanning electron microscopy (SEM) was used to investigate the morphology of the pristine and composite materials. Fig. 3(a) and (b) shows a low and high magnication SEM micrographs of pristine NaNi 4 (PO 4 ) 3 sample. They exhibit a hierarchical nano-spheres morphology and it can be seen that the NaNi 4 (PO 4 ) 3 nano-spheres are inter-connected with each other but still keeping a sphere-like morphology. Fig. 3(c) and (d) shows a low and high magnication of NaNi 4 (PO 4 ) 3 /GF composite. It is worth mentioning that the graphene foam (GF) sheet could not be identied in the SEM morphology of the composites. This could be due to ultra-sonication of the graphene for hours aer been dispersed in deionized water and also aer the precursors were added to it. 37 Further microscopic analysis of both the pristine NaNi 4 (-PO 4 ) 3 and NaNi 4 (PO 4 ) 3 /GF composite materials was investigated Paper by using a transmission electron microscopy (TEM) technique, and is shown in Fig. 3(e and f). It can be clearly observed that the NaNi 4 (PO 4 ) 3 material composed of hierarchical spheres-like morphology in agreement with SEM images with a single sphere having an average diameter of about 49 nm, as shown in Fig. 3(e). A uniform dispersion of the NaNi 4 (PO 4 ) 3 nano-spheres wrapped with the graphene foam sheet was observed as shown in Fig. 3(f) which is needed for providing the necessary surface required for efficient charge transport and storage. Fig. 4(a) displays BET results of the activated carbon from the peanut shell (AC) used in this work. This gure shows type-IV and H4 hysteresis loop indicating the material possessing mainly mesopores and micropores as can be observed from the inset to the gure. The specic surface area obtained for this material was 2547 m 2 g À1 , suggesting the material contains a high surface area. The morphology of the activated carbon (AC) was determined by SEM. Fig. 4(b) represent SEM of the AC in 20 micrometer scale, and as can be seen, the material is full of cavities which are benecial for the energy storage application. 38

Electrochemistry (3-electrode measurements)
The performance of NaNi 4 (PO 4 ) 3 and NaNi 4 (PO 4 ) 3 /GF composite hierarchical nanospheres as electrode materials for supercapacitors was investigated by cyclic voltammetry (CV), galvanostatic charge-discharge techniques (GCD) and electrochemical impedance spectroscopy (EIS). The experiment was performed in a 2 M NaNO 3 electrolyte within a potential window range of 0.0-1.0 V. Fig. 5(a) represents CV curves of the NaNi 4 (PO 4 ) 3 /GF investigated at different working potential windows ranging from 0.8 to 1.0 V in a 2 M NaNO 3 neutral electrolyte. In these CVs an optimization to determine the stable potential window of the material was done. The CV curves exhibit redox reactions within these potential windows which is typical of faradaic supercapacitors signature. With increasing voltage range the CV still sustains the same shape with a slight increase in capacity value. The extended potential window of the material within 1.0 V could be due to the low concentration of hydrogen ions relative to those of acidic and basic electrolytes. 39 Fig. 5(b) and (c) show a possible comparison of CV and GCD curves for pristine NaNi 4 (PO 4 ) 3 and composite NaNi 4 (PO 4 ) 3 /GF at a scan rate of 50 mV s À1 and specic current of 2 A g À1 respectively. The shapes of the curves in these gures are different from those of ideal electrochemical double-layer capacitance, showing two well-dened redox peaks which are responsible for the faradaic behavior of the electrode materials. However, the current response and discharge time of CV and GCD curves respectively in NaNi 4 (PO 4 ) 3 /GF composite are much higher than that of NaNi 4 (PO 4 ) 3 which is an indication that the NaNi 4 (PO 4 ) 3 /GF electrode has a better capacitive performance than NaNi 4 (PO 4 ) 3 . This can be attributed to the effect graphene foam has in the composite which had improved specic surface area as compared to the pristine sample indicated by BET results (see Fig. 2(a)). Fig. 5(d) shows the CV curves of the NaNi 4 (PO 4 ) 3 /GF composite at different scan rates. It can be seen that the current response of the CV curves increases gradually with increasing scan rate conrming the fast charge movement mechanism of the electrodes. 40 The shape of the CV curves clearly implies that faradaic reactions occurred during the processes. The material exhibited a pair of redox peaks at around 0.3 V and 0.7 V which is due to the diffusion-controlled reversible redox reaction of Ni 2+ 4 Ni 3+ . 18 Fig. 5(e) shows the GCD curves of NaNi 4 (PO 4 ) 3 /GF at different current densities in range of 1-10 A g À1 . Visibly, the GCD curves are nonlinear which further conrms the faradaic property of the electrode material. Fig. 5(g) demonstrates cyclic stability of NaNi 4 (PO 4 ) 3 /GF composite which was conducted under a constant GCD at 10 A g À1 for 3000 cycles. A 99% coulombic efficiency and 96% of its initial capacity retained revealing good electrochemical stability of the electrode material.
where I d represents specic current (A g À1 ) and Dt represents discharge time (s).

Electrochemistry (2-electrode measurements)
The NaNi 4 (PO 4 ) 3 /GF was further used for the fabrication of hybrid device, a hybrid device was designed considering NaNi 4 (PO 4 ) 3 /GF composite as a positive electrode material and AC as a negative electrode material as shown in Fig. 6(a). To ll the gap of the different current response as well as the different potential window between NaNi 4 (PO 4 ) 3 /GF and AC, a charge balance was done using the formula (2) and (3). The hybrid device was assembled based on the charge stored in both positive and negative electrode ruled by the following formula:  Fig. 6(b). The specic capacity of the  device (see Fig. 6(d)) at different specic currents of 0.5, 1.0, 2.0, 3.0, 4.0 and 5.0 A g À1 were calculated using eqn (1) to be 15.1, 11.2, 9.4, 7.1, 5.7 and 5.5 mhA g À1 respectively. These low values of the specic capacities are ascribed to the fact that neutral electrolytes have less ionic conductivity and bigger ionic hydrated radius compared to alkaline and acidic electrolytes. 42 To study the conductivity and the ion diffusion control rate of the hybrid NaNi 4 (PO 4 ) 3 /GF//AC, electrochemical impedance spectroscopy (EIS) measurement was conducted, the results of which are shown in Fig. 6(e) with the inset showing an equivalent circuit tted with a ZFIT soware associated with the BioLogic EC-lab. 43 The equivalent circuit composed of the series Fig. 5 (a) CVs of NaNi 4 (PO 4 ) 3 /GF composite at a different potential window at a scan rate of 50 mV s À1 , (b and c) CV and GCD curves of pristine NaNi 4 (PO 4 ) 3 and NaNi 4 (PO 4 ) 3 /GF composites at scan rate of 50 mV s À1 and specific current of 2 A g À1 respectively, (d and e) CV and GCD curves of NaNi 4 (PO 4 ) 3 /GF composite at different scan rates and different specific currents respectively, (f) a specific capacity calculated for NaNi 4 (PO 4 ) 3 / GF at different specific currents and (g) double Y plot illustrating coulombic efficiency and specific capacity versus cycle number of NaNi 4 (PO 4 ) 3 / GF at a specific current of 10 A g À1 (the inset is some GCD cycles).
resistance (R s ), which represents the intrinsic resistance property of the electrode materials, electrolyte and the contact resistance between the electrode and the current collector interface. Charge transfer resistance R CT and the interface connection capacitance Q CT describe the rate of resistance and the electrochemical redox reactions that might come about at the electrode/electrolyte interface. The constant phase element Q L and leakage resistance R L are associated with electrical double layer capacitance. Warburg impedance W, associated to the transition from high frequency to low frequency is related to diffusion of the ions in the cell. 44 Stability test is one of the main factors used to determine the performance of a device. The capacity retention and coulombic efficiency of the device were measured as a function of cycle numbers at a specic current of 5 A g À1 over 5000 cycles as demonstrated in Fig. 6(f). From the gure, the device's capacity was noticed to be uctuating but became very stable at about 2000 cycles and beyond. This is due to the electrode material's lack of enough wettability at the initial cycles. The device could retain an 89% of its initial capacity as well as a coulombic efficiency of approximately 94% over 5000 cycles, suggesting the material's potential for electrochemical devices applications. Fig. 7 presents a Ragone plot which demonstrates the position of the device in this work in terms of energy density and power densities in comparison to some recently published bimetallic phosphate-based devices from the literature. The NaNi 4 (PO 4 ) 3 /GF//AC hybrid device delivered a highest energy and power density of 19.5 W h kg À1 and 570 W kg À1 , respectively, at a specic current of 0.5 A g À1 within extended cell potential of 0.0-2.0 V. These energy and power densities values were calculated according to eqn (4) and (5) below: where i represent applied current (mA), m represent the total mass of the active material (mg), Ð V dt is the area under the discharge curve of the device, and Dt is the discharge time (s).
The results presented in Table 1 show the signicance of our work in terms of improved energy and power densities as well as Fig. 6 (a) A hybrid device demonstrating CV of NaNi 4 (PO 4 ) 3 /GF as a positive electrode and AC as a negative electrode, (b) CV of the hybrid NaNi 4 (PO 4 ) 3 /GF//AC measured at different scan rates, (c) GCDs of the hybrid NaNi 4 (PO 4 ) 3 /GF//AC measured at different specific currents, (d) a specific capacity of hybrid NaNi 4 (PO 4 ) 3 /GF//AC calculated at different specific current, (e) EIS of NaNi 4 (PO 4 ) 3 /GF//AC (the inset is an equivalent circuit used to fit the EIS data) and (f) double Y plot showing coulombic efficiency and specific capacity versus cycle number for NaNi 4 (PO 4 ) 3 /GF// AC hybrid device at specific current of 5 A g À1 .

Conclusion
In conclusion, a hierarchical spherical morphology of sodium nickel phosphate graphene foam composite (NaNi 4 (PO 4 ) 3 /GF) was synthesized through direct and simple chemical precipitation method. The material has been tested in three electrode measurement using 2 M NaNO 3 electrolyte within working potential of 0.0-1.0 V. A specic capacity of 63.3 mA h g À1 was obtained at 1 A g À1 specic current. A hybrid device was a assembled with NaNi 4 (PO 4 ) 3 /GF composite as a positive electrode and AC as a negative electrode, and was found to exhibit specic capacity of 15.1 mA h g À1 , energy density of 19.5 W h kg À1 and a power density of 570 W kg À1 at specic current of 0.5 A g À1 .

Conflicts of interest
There are no conicts to declare.