NiFe2O4@ nitrogen-doped carbon hollow spheres with highly efficient and recyclable adsorption of tetracycline

Antibiotics can affect ecosystems and threaten human health; therefore, methods for removing antibiotics have become a popular subject in environmental management and for the protection of human health. Adsorption is considered an effective approach for the removal of antibiotics from water. In this study, NiFe2O4@nitrogen-doped carbon hollow spheres (NiFe2O4/NCHS) were synthesized via a facile hydrothermal method followed by calcination using NCHS as a hard template. The nanocomposite exhibited high adsorption activity and good recyclability. The nanocomposite was characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, and nitrogen adsorption–desorption to study its micromorphology, structure, and chemical composition/states. In addition, the factors affecting the adsorption process were systematically investigated, including tetracycline (TC) concentration, solution pH, ionic strength, and temperature. The maximum adsorption capacity for TC was calculated to be 271.739 mg g−1 based on the Langmuir adsorption model, which was higher than various other materials. This study provides an effective method for constructing the NiFe2O4/NHCS core–shell structure, which can be applied for the removal of TC from water.


Introduction
][3] However, the widespread use of antibiotics and the large amounts excreted by humans and animals have resulted in increasingly more pharmaceuticals being discharged into wastewaters and manures, which have led to adverse effects on ecosystem health. 4,5Therefore, the development of efficient methods to effectively eliminate antibiotics from wastewater is an important research topic for human health and environmental system management.
To date, many researchers have developed effective methods to remove traditional pollutants from the aquatic environment, such as adsorption, 5,6 coagulation/occulation, 7 photocatalysis, 8-10 chemical oxidation, 11 ion-exchange, 12 biodegradation, 13 and advanced oxidation. 14Of these, adsorption is the most pragmatic and convenient method for the removal of antibiotics from water sources, owing to its easy operation, convenience, low energy requirements, high efficiency, cost effectiveness, and facile recovery or reuse of the adsorbent.In addition, this process does not produce secondary pollutants.Hence, the selection of an appropriate adsorbent is an important and imminent task for the management of the aquatic environment.Until now, activated carbon, 15 metal oxides, 16 clay minerals, 17 and silicon nanomaterials 18,19 have been applied as conventional adsorbents for the removal of antibiotics from wastewater.However, the low adsorption capacity, high cost, and poor recyclability have restricted their practical application.1][22] For example, multifunctional magnetic microspheres (Mag@ZnO-Co 3 O 4 ) with bimetal oxide shells have been synthesized and showed excellent adsorption properties for oxytetracycline, with the maximum adsorption capacity of oxytetracycline found to be 128 mg g À1 , 23 and core-shell Fe 3 O 4 @ZIF-8 has been prepared and showed excellent adsorptive capacity for tetracycline (TC) antibiotics. 24However, there is still a challenge in producing a new generation of separation media magnetic nanocomposites.
In recent years, transition-metal oxides such as ZnFe 2 O 4 , MnFe 2 O 4 , and NiFe 2 O 4 have attracted extensive attention as anode materials, [25][26][27] photocatalyst materials, 28,29 electronics materials, 30 and solar cell materials 31 because of their low cost, excellent visible light response, and good photochemical stability.However, seldomly have these transition-metal oxides been used as adsorption materials.
To the best of our knowledge, this is the rst study to fabricate and grow magnetic porous NiFe 2 O 4 nanosheets on Ndoped carbon hollow spheres (NCHS), where NCHS also served as a hard template, which utilized a facile, mild, and ecofriendly method.A range of techniques including X-ray diffraction (XRD), scanning electron microscopy/transmission electron microscopy (SEM/TEM), X-ray photoelectron spectroscopy (XPS), nitrogen sorption, and magnetic hysteresis loop were employed to fully characterize the obtained materials.It was found that NiFe 2 O 4 /NCHS had a higher adsorption capacity for TC (271.739mg g À1 ) than that of pure NiFe 2 O 4 , as well as good recyclability and stability.The results from the present study provide a practical method for the removal of TCs from water.Furthermore, this magnetic material may have potential practical uses in sensors and for energy storage.

Preparation of NCHS carbon hollow spheres
All reagents used in the present study were purchased without any further purication.The NCHS was fabricated based on a previously reported method. 32Briey, 12 mL of anhydrous ethanol and 0.5 mL of ammonia (25%) were added to 40 mL of distilled water and vigorously stirred for 20 min, and then 1 mL of TEOS was added dropwise to the above solution.Then, 8 mL of dopamine hydrochloride (DA) aqueous solution (50 mg mL À1 ) was added into the above mixture and the mixture was stirred continuously for 32 h.The material (PDA/SiO 2 ) was collected aer centrifugation, washed four times with puried water, and then collected and dried via vacuum freeze drying.The precipitates were heated at 800 C for 3 h at a heating rate of 5 C min À1 under a N 2 atmosphere, and the NCHS was obtained.

Preparation of NiFe 2 O 4 /NCHS composite
The obtained NCHS (20 mg) was dispersed into 60 mL of deionized water under sonication for 30 min.Then, 0.2 mmol Ni(NO 3 ) 2 $6H 2 O, 0.4 mmol Fe(NO 3 ) 3 $9H 2 O, 0.38 mmol sodium citrate, 1 mmol NH 4 F, and 5 mmol urea were slowly added into the above suspension solution while being stirred for 60 min.Subsequently, the uniform mixture was transferred to an 80 mL Teon-lined stainless-steel autoclave and heated at 150 C for 36 h.The product was then collected aer centrifugation and washing several times with distilled water and ethanol.Finally, the obtained product was annealed at 300 C for 2 h in a N 2 atmosphere with a heating rate of 2 C min À1 .For comparison, NiFe 2 O 4 was obtained under the same conditions except for the exclusion of NCHS.

Results and discussion
The synthetic procedure of NiFe 2 O 4 /NCHS is rationally demonstrated in Scheme 1. First, PDA/SiO 2 with uniform spheres were prepared via the hydrolysis of TEOS and the polymerization of dopamine in a mixture of water and ethanol, combined in a one-pot process.Second, Ni 2+ and Fe 3+ ions were randomly adsorbed onto the surface of the PDA/SiO 2 and formed a Ni/Fe-based precursor with a hollow interior under facile hydrothermal treatment in an alkaline solution.Lastly, the NiFe 2 O 4 /NCHS with a hollow structure was obtained aer calcination treatment at 350 C for 2 h in a N 2 atmosphere.
The crystalline structures of the synthesized samples were investigated with XRD, as shown in Fig. 1.The XRD pattern of NiFe 2 O 4 /NCHS displayed broader diffraction peaks of (002) corresponding to graphitized carbon. 33In addition, the other characteristic peaks showed the reection planes of ( 220), (311), and (400) that were in agreement with the cubic spinel phase of NiFe 2 O 4 (JCPDS 54-0964). 34The peaks were broader than that of pure NiFe 2 O 4 because of an overlap with the corresponding peak of the NHCS substrate.Clearly, the sample displays uniformly dispersed spherical structures with an average diameter of approximately 200-300 nm.Moreover, the high-magnication FE-SEM image revealed the sample was composed of nanosheets.The microstructures of the NiFe 2 O 4 /NCHS sample were further characterized using TEM.The NiFe 2 O 4 /NCHS sample exhibited a hollow structure that was composed of interconnected nanosheets, which was similar to the results obtained from the FE-SEM image (Fig. 2c).The resolved interplanar distances of the lattice fringes were 0.25 nm apart, which corresponded to the (311) plane of the face-centered cubic lattice of NiFe 2 O 4 (JCPDS 54-0964). 35,36Importantly, it was found that the pattern and the surface morphology of the adsorbent did not change signicantly and remained relatively stable aer adsorption (Fig. S2 †).The surface chemical composition and structure of the NiFe 2 O 4 /NCHS were further studied with the XPS spectra.The XPS results displayed the existence of Ni, Fe, N, and O elements in the sample (Fig. 3a).For the Ni 2p spectrum shown in Fig. 3b, two main peaks were located at 854.2 and 871.9 eV, corresponding to the two spin-orbits Ni 2p3/2 and Ni 2p1/2, respectively, whereas the binding energy at 718.2 and 724.1 eV were in agreement with Fe 2p3/2 and Fe 2p1/2, respectively.In addition, the two spin-orbits Ni 2p and Fe 2p spectra of NiFe 2 O 4 /NCHS corresponded to two shake-up satellites (denoted as Sat.). 37Meanwhile, the spin-orbit peaks in Ni 2p and Fe 2p could be tted to two distinct peaks, which were attributed to the coexistence of Ni 2+ /Ni 3+ and Fe 2+ /Fe 3+ cations, respectively.The O 1s XPS spectrum showed two peaks at binding energies of 529.5 and 531.1 eV, which were consistent with the Ni-Fe-O bonds and oxygenic functional groups. 38 NCHS composite exhibited a type IV isotherm with a type H3 hysteresis loop, which were characteristic of a mesoporous structure. 39The hysteresis loop of the NiFe 2 O 4 /NCHS in the broad P/P 0 range of 0.45-1 indicated the presence of large mesopores and macrospores, which further conrmed the hierarchically porous structure of this carbon material.The Brunauer-Emmett-Teller specic surface area and the pore volume of NiFe 2 O 4 /NCHS were 268.8 m 2 g À1 and 0.22 cm 3 g À1 , respectively, which were much larger than that of pure NiFe 2 O 4 (21.85 m 2 g À1 and 0.04 cm 3 g À1 , respectively), as shown in Table S1.† 40,41 The increased surface area and hierarchical pore could be attributed to the adsorption of TC.In addition, the pore diameter of NiFe 2 O 4 /NCHS aer adsorption of tetracycline was smaller than that of before adsorption, indicating that the pollutants with large molecules may cause blockage of the external channel of adsorbent pores with small diameters (Fig. S4 †).Zeta potential measurements were carried out at pH 7 to investigate the surface charge of the samples in aqueous solution.As displayed in Fig. S5, † the TC dispersions are positive charged with a zeta potential of about 36.31 mV.Upon The magnetic properties of NiFe 2 O 4 /NCHS were further analyzed at room temperature (25-30 C), as shown in Fig. 5.The eld-dependent magnetization curves were completely reversible, which further indicated that the as-synthesis materials were superparamagnetic without coercivity and remanence.The saturation magnetization value of 85 emu g À1 demonstrated its excellent magnetic properties, allowing it to be easily separated from the treated samples by an external magnet. 42n order to examine the surface groups of NiFe 2 O 4 /NCHS before and aer adsorbent, the FTIR spectra were performed (Fig. 6).The absorption peaks in the range from 1700-1200 cm À1 is attributed to the skeleton vibration absorption peaks of the benzene ring in the tetracycline molecule. 434][45][46] The adsorption of TC was increased with increasing pH from 3.0 to 5.0, and the maximum adsorption capacity for TC was reached at 43.95 mg g À1 when the solution pH was 5.This was attributed to electrostatic and complexation attractions; thus, increasingly more TC was easily attracted to the surface of NiFe 2 O 4 /NCHS.However, the adsorption capacity of TC showed a similar rapidly decreasing uptake trend when pH values ranged from 5 to 7. Subsequently, when pH values exceeded 9, no signicant effect was found except for a slight decrease.Therefore, the optimum pH is a highly signicant factor for controlling the adsorption capacity of TC.
To investigate the effect of temperature on the adsorption process, a batch experiment was undertaken at four different temperatures (Fig. 7b) with an initial concentration of 10 mg L À1 at a pH of 5.The adsorption performance of the NiFe 2 O 4 /NCHS sample was signicantly improved with an increase in temperature from 288 K to 318 K, causing the adsorption amount to quickly increase aer 50 min from 32.5 mg g À1 to 41.3 mg g À1 .Hence, the adsorption process of TC on the NiFe 2 O 4 /NCHS sample was an endothermic process based on the calculated values of Gibb's free energy.
The removal of pollutants is oen inuenced by salt (especially inorganic salt) or ions (e.g., Na + , Ca 2+ , K + , Mg 2+ , Al 3+ , and so on) in water and further affects the adsorption capacity of TC.Three commonly encountered inorganic salts, NaCl, CaCl 2 , and KNO 3, in tap water and natural water were selected to investigate the effect of coexisting ionic species on the adsorption of TC (Fig. 7c).The different concentrations of NaCl and KNO 3 had little effect on the adsorption of TC.By contrast, aer the addition of CaCl 2 the adsorption capacity of TC was obviously decreased, which implies that it competes with TC for the active site on the surface of the adsorbent, causing a rapid decrease in the adsorption process of TC. 47,48 The kinetic curves for TC adsorption of NiFe   S2. † The results showed that all experimental data were distributed on the tted straight lines, which indicated that it did not match well with the pseudo-rst-order model (Fig. 8a). 49,50However, the experimental data displayed good agreement with the pseudo-secondorder model owing to the calculated q e values being matched with the experimental adsorption amount and values of R 2 were higher than 0.995 for NiFe 2 O 4 /NCHS (Fig. 8b).Hence, the pseudo-second-order kinetic model was more appropriate than the pseudo-rst-order kinetic model for the adsorption process, which displayed the adsorption process of tetracycline on Fig. 8 The kinetic models for TC adsorbed on the samples: (a) pseudo-first-order, (b) pseudo-second-order.
NiFe 2 O 4 /NCHS was more in accordance with chemical adsorption.In summary, the adsorption process of tetracycline NiFe 2 O 4 /NCHS was based on chemical adsorption, which was supplemented by physical adsorption.This is because tetracycline could be bound to metal ions (Ni 2+ , Fe 3+ ) to form an antibiotic-metal complex owing to its electron donor groups which could form strong coordination.
2][53][54] The respective tted parameters of the Langmuir isotherm equation and Freundlich model are listed in Table S3.† Compared with the different correlation coefficient (R 2 ) values, the Langmuir model simulation (R 2 $ 0.994) was larger than the Freundlich isotherm model (R 2 $ 0.960); therefore, the Langmuir adsorption model was more suitable to describe the TC adsorption equilibrium process.The maximum TC adsorption capacity of NiFe 2 O 4 /NCHS based on the Langmuir equation was 271.739 mg g À1 , which was consistent with the experimental data. 55In addition, the maximal TC adsorption capacity of NiFe 2 O 4 /NCHS was superior to that of previously reported materials (Table S4 †).
To evaluate the performance of NiFe 2 O 4 /NCHS for the removal of TC, the reusability and stability of the sample were studied (Fig. 10).NiFe 2 O 4 /NCHS was collected from the aqueous suspension by magnetic separation.The experiment results showed that there was a slight adsorbed activity loss of TC at the 4 cycle and 5 cycle, and there was over 85.6% TC removal ratio achieved aer 5 cycle tests.In addition, the adsorptiondesorption cycle studies were implemented to access the regeneration of NiFe  [56][57][58][59][60][61][62] Therefore, the as-prepared sample possessed an efficient and stable adsorbed TC activity, making it useful for the removal of TC from water.

Conclusions
In summary, NiFe 2 O 4 /NCHS was prepared via a simple hydrothermal method followed by calcination using NCHS as a hard template.The nanocomposite was characterized by a range of techniques to study its micromorphology, structure, and chemical composition/states.The NiFe 2 O 4 /NCHS had a large specic surface area and good adsorption capacity for TC.Based on the experimental results, we found that the adsorption kinetics followed the pseudo-second-order model and the adsorption isotherms obeyed the Langmuir adsorption model.Importantly, NiFe 2 O 4 /NCHS can be effectively separated for reuse by applying an external magnetic eld and it has an efficient and stable adsorbed TC activity, thus making it useful for the practical removal of TC from water.In addition, this magnetic material may have potential practical uses in sensors and for energy storage.The present study provides an effective approach to construct other hierarchical carbon-bimetal oxide composite materials.
Fig. 2a and b show representative eld emission SEM (FE-SEM) images of NiFe 2 O 4 /NCHS with hollow nanospheres.

Scheme 1
Scheme 1 Schematic of the synthesis and application of the NiFe 2 O 4 / NCHS composite.
XPS measurement further revealed the valence state of NiFe 2 O 4 /NCHS aer adsorption (Fig. S3 †).For comparison, the survey XPS curves of NiFe 2 O 4 /NCHS showed that existence of C, N, and O elements in the sample were remarkable enhancement.Importantly, the Ni 2p spectra of NiFe 2 O 4 /NCHS shied from 854.2 and 871.9 eV to 856.1 and 873.9 eV, while the Fe 2p spectrum of NiFe 2 O 4 /NCHS shied from 718.2 and 724.1 eV to 711.4 and 724.7 eV, respectively.This is due to the fact that the hydroxyl, carbonyl and amino groups of the tetracycline molecule provided a large number of electrons to Ni and Fe to form a metal complex.Furthermore, due to forming active oxygen-containing functional groups lead to the positions of O 1s offset occurs.As a result, the tetracycline molecule was successfully adsorbed NiFe 2 O 4 /NCHS.N 2 adsorption-desorption and pore size distribution were used to analyze the textural properties of the NiFe 2 O 4 and NiFe 2 O 4 /NCHS composite.As shown in Fig. 4, the N 2 adsorption-desorption isotherms of the pure NiFe 2 O 4 and NiFe 2 O 4 /
2 O 4 /NCHS and NiFe 2 O 4 are shown in Fig. 7d.The two curves revealed that the initial TC uptake rate was quite fast during the rst 20 min and reached adsorption equilibria within 40 min.Besides, because the NiFe 2 O 4 /NCHS sample had a much larger specic surface area and more positive surface charge, it showed faster adsorption rates and enhanced adsorption capacity than that of NiFe 2 O 4 under the same experimental conditions.The maximum TC adsorption quantities for the NiFe 2 O 4 /NCHS and NiFe 2 O 4 samples were 41.30 and 28.70 mg g À1 , respectively, aer 40 min of adsorption, with NiFe 2 O 4 /NCHS having more adsorption sites and faster adsorption rates than that of NiFe 2 O 4 .In addition, a series of NiFe 2 O 4 /NCHS with different dosages of Ni and Fe, pure NiFe 2 O 4, and NCHS were tested as adsorbents for TC adsorption (Fig. S1 †).Comparing the different samples, NiFe 2 O 4 /NCHS exhibited much higher adsorption capacity than that of NiFe 2 O 4 and NCHS.In
2 O 4 /NCHS.Adsorption desorption and regeneration deeply studies.The adsorbed NiFe 2 O 4 /NCHS was desorbed by NaOH and NH 3 $H 2 O to achieve the regeneration of NiFe 2 O 4 /NCHS aer equilibrium adsorption.The regeneration efficiency of NiFe 2 O 4 /NCHS and removal ratio of TC was illustrated in Fig. S6.† It was clearly observed that although the adsorption capacity of NiFe 2 O 4 /NCHS decreased with the increment in the times of adsorption-desorption of the adsorbent, the removal ratio of tetracycline was maintained at 80% or more aer ve times of adsorption-desorption cycles of the adsorbent with NaOH(0.001M)/NH 3 $H 2 O(0.01 M), which indicated that NiFe 2 O 4 /NCHS had a relatively good reusability and were a promising candidate for tetracycline adsorption in the practical condition.

Fig. 9
Fig. 9 (a) Langmuir and (b) Freundlich modeling of the isotherms for TC on the sample NiFe 2 O 4 /NCHS composite at 30 C.