Understanding the charge storage mechanism of conductive polymers as hybrid battery-capacitor materials in ionic liquids by in situ atomic force microscopy and electrochemical quartz crystal microbalance studies

Faculty of Engineering and the Environmen Southampton SO17 1BJ, UK. E-mail: T.Scho 51; Tel: +44 (0)2380 5989 31 Electrochemistry and Electroplating Group, Kirchhoff-Straße 6, 98693 Ilmenau, German Department of Chemistry, University of Leic Faculty of Engineering, Hokkaido University 8628 Hokkaido, Japan † Electronic supplementary informa 10.1039/c8ta06757k Cite this: J. Mater. Chem. A, 2018, 6, 17787


Broader context
High-performance energy storage devices such as lithium-ion batteries are characterised by having the highest practical specic energies (80 to 175 W h kg À1 ) and powers (200 to 300 W kg À1 ) among state-of-the-art rechargeable batteries. 1However, there are some major concerns about the safety and sustainability of lithium.These include ammability, difficult recycling and the limited availability of raw materials, which raise issues regarding the future viability of electric cars.
Therefore, there is a strong tendency in the battery community to investigate alternative batteries beyond lithium-ion to enhance the safety and sustainability of batteries while decreasing their costs.Increasing the acceptance of and access to electromobility may result in a course correction towards a more sustainable and cleaner future. 2,3reat efforts are being made to implement batteries based on more sustainable materials, such as aluminium, magnesium or sodium.However, pure metal batteries cannot achieve high performance, such as high specic energy or power, and thus cannot compete with state-of-the art batteries. 4In order to increase their performance, these negative metal electrodes must be combined with a positive electrode; these are characterised as charge-storage-materials.Charge-storage electrodes can accommodate additional ions by intercalation or doping.These types of electrodes demonstrate battery-like (faradaic) behaviour due to the oxidation and reduction of the active electrode species while simultaneously showing capacitive (non-faradaic) behaviour by inserting anion species in a threedimensional electrode structure. 5arbon materials, especially graphene, have important roles as electrode materials due to their relatively inert electrochemistry, wide potential stability windows and low cost as well as their environmentally friendly properties. 5However, carbon-based materials can reach only limited charge storage capacities.Another type of charge-storage material is conductive polymers; 6,7 they stand out for their low weights, low cost, relatively high conductivities and capacities and straightforward electrochemical synthesis.
Compared to batteries, capacitors have less energy per unit weight and store energy only for short periods.However, capacitors have higher specic powers and faster response times than batteries.In order to improve the specic energy and power of an energy storage system, the characteristics of batteries and capacitors must be combined in a hybrid system. 80][11] Pseudo-capacitive charge storage refers to a surface-bound process that contributes to the total capacitance of the system. 10,11onductive polymers such as poly(3,4ethylenedioxythiophene) (PEDOT) are typical examples of hybrid battery-(pseudo)-capacitor materials. 8They have the unique characteristic of undergoing a redox reaction, like a battery (eqn (1)), generating positively charged sites in the polymer structure during the oxidation (charge reaction).When the polymer is reduced (discharge reaction), the charged sites return to their neutral state.][14] The amount of doped charges per monomer unit is determined by the generated and accessible charged sites in the polymer; it increases with the doping potential.[17]

Monomer unit1
Furthermore, the formation of the doping/de-doping sites also depends on the polymer morphology, which is predetermined by the electro-polymerisation method, the applied potential and the doping anion. 17][19] This study aims to investigate the anion doping/de-doping process of the conductive polymer PEDOT while performing charge/discharge cycles and evaluating its capacitive and faradaic behaviour by cyclic voltammetry (CV) coupled with electrochemical quartz crystal microbalance (EQCM) experiments.In situ atomic force microscopy (AFM) measurements were found to show the morphological changes of the polymer surface during charging and discharging.Combining these results helps establish a model of how the polymer morphology determines the battery and capacitor characteristics of the conductive polymer.

Electrochemical quartz crystal microbalance measurements
The EQCM setup (Fig. 1) comprised a three-electrode arrangement in a PTFE-cell controlled by a potentiostat (Princeton Applied Research 263A).A quartz crystal with AT-cut and sputtered gold (KVG, 10 MHz, 0.22 cm 2 ) was used as the working electrode and substrate for the polymer.The polymer lm was electro-polymerised on the gold quartz crystal as described in paragraph 2.1.A vitreous carbon rod (micro to nano, diameter 0.3 cm) placed opposite to the quartz acted as the counter electrode, while an aluminium ring was used as the reference electrode (Alfa Aesar, 99.999% metal basis, diameter 0.5 mm).
When combining electrochemical and EQCM measurements, two electrical signals overlap at the working electrode: a DC voltage, applied by the potentiostat, and a high frequency AC voltage from the network analyser (Agilent E5100A).This causes the oscillation of the quartz.
The changes in the quartz resonance frequency caused by mass changes of the polymer lm due to anion doping/dedoping were determined by the admittance (reciprocal of the impedance) using the network analyser.The spectrum of the admittance has the form of a Lorentz curve; thus, the resonance frequency f and the quartz damping w, which is dened as the width at half the height of the admittance peak, can be determined by curve tting.
The resonance frequency and the damping provide information about the properties of the quartz crystal and the polymer lm because they are mechanically coupled.Therefore, the mechanical properties of the polymer can be combined with the quartz to obtain a single mechanic system, which can be read as one electrical signal.The most accurate electrical description of a quartz crystal is currently given by the Electric Line Model (Transmission Line Model), based on a Mason 3-port model. 20,21hanges in the electric impedance of the quartz can be translated into lm impedance of the polymer.The oscillation of the quartz causes a shear wave on the surface of the quartz, which is reproduced on the polymer lm.Depending on the polymer properties, such as lm density r f , the shear wave is dampened.Therefore, the lm impedance Z f is related to the shear modulus G of the system (eqn (2)). 20 The shear modulus describes the linear elastic deformation of the polymer lm and provides information about changes in the stiffness or soness of the polymer.
2.2.1.Determination of the shear modulus.Ideal planar and rigid lms move in phase with the quartz surface with area A. In this case, the change in the resonance frequency Df is proportional to the negative mass change Dm of the polymer lm, and the Sauerbrey equation (eqn (3)) 20,22 can be applied.The parameter f 0 indicates the resonance frequency of the unloaded quartz, which has a shear modulus m Q of 2957 Â 10 11 g cm s À2 and a density r Q of 2648 g cm À3 .
Because conductive polymers are not ideal planar rigid lms, their viscoelastic properties cause a shi and damping of the shear wave propagation.Furthermore, contact of the polymer lm with the electrolyte causes an additional lm impedance Z l .If the electrolyte is inside the polymer pores and on the rough polymer surface, its impedance must be considered because it contributes to the overall impedance, which depends on the lm thickness h f .
A complex shear modulus G* for viscoelastic materials can be dened (eqn ( 4)).G* comprises a real part G 0 , representing the deformation energy, which can be recovered (elastic behaviour), and an imaginary part G 00 , describing the amount of energy which is lost due to frictional heat.
The lm impedance Z f includes the unknown parameter shear modulus G* and the lm density r f , whereas the motional lm impedance, which is estimated by the Sauerbrey equation, Z m fSB , includes the lm thickness h f and the density (eqn ( 7)).
The reactance of the electrolyte is represented by X l (eqn ( 8)).
In order to determine the shear modulus, assumptions must be made for the thickness and the density of the polymer lm.For the polymer density, the monomer density is assumed.The lm thickness must be estimated.As a rst step, it is assumed that the polymer consists of a rigid planar lm, and the lm thickness h fSB is estimated by the Sauerbrey equation.In a second step, the polymer lm thickness is corrected by multiplying with the correction factor b (eqn ( 9)); this accounts for all deviations of a viscoelastic lm from an ideal lm, such as lm roughness and density differences (eqn (3)).
A correction factor b ¼ 1 indicates a rigid and planar surface.The upper limit should be slightly greater than one.In order to determine the correction factor and the complex shear modulus G*, the b value was varied.The correction factor b was determined by nding the maximum of G 0 because G 0 is a function of b. 20 In this study, an interval of b from 0.5 to 5.5 was selected.This is the main task of the developed algorithm script (ESI †).Because b is a parameter for the calculation of G*, a list "databb" is generated which contains all b-values.First, the Mathematica FindRoot[]-function determines Z f and then G* for each b in databb.Then, the maximum and the associated b G max are determined for G 0 .If both components of the shear modulus for b G max are greater than zero, they are added to the result list.

In situ atomic force microscopy
The experimental setup (Fig. 2) consists of a self-designed PTFE three-electrode cell with a vitreous carbon disc (micro to nano, 6.3 cm 2 ) as the substrate/working electrode, a vitreous carbon ring (micro to nano, diameter 3 cm) as the counter electrode and an aluminium wire (Alfa Aesar, 99.999% metal basis, diameter 0.5 mm) as the reference electrode.The electrochemical experiments were controlled by a Biologic SP-240 potentiostat.
The AFM (Dimension ICON, Bruker Co., Billerica, MA, USA) was located in a glove box (MBraun, Inertgas-Systeme GmbH, Garching, Germany) under argon atmosphere (water and oxygen levels below 10 ppm).The AFM measurements were carried out with a silicon probe coated with diamond-like carbon and a reective aluminium layer at the back (Windsor Scientic, Multi75DLC, spring constant 3 N m À1 , resonance frequency 75 kHz, tip radius < 10 nm).The probe was completely covered by the electrolyte during the duration of the electrochemical experiment.
Before the polymer lm was charged/discharged, an initial AFM image of the PEDOT surface in the uncharged state was captured.The polymer surface was scanned horizontally over an area of 5 mm Â 5 mm at 0.5 Hz, 512 samples per line and a 0.05 V force set point.The feedback gain was adapted automatically as the images were taken in ScanAsyst mode (peak force tapping mode).
The initial position of the polymer surface was set as a xed scanning position and charged/discharged by linear sweep voltammetry (LSV) with 100 mV s À1 from 0 V to 2.5 V vs. Al|Al(III) and reversed to the uncharged state at 0 V.The LSV was stopped aer every 500 mV and the potential was held at the OCP to capture the AFM image with the same set of parameters as the initial image.The OCP remained stable for the time spent to capture the image.
All AFM images were post-edited by a third-order polynomial attening procedure using Nanoscope Analysis soware (Bruker Co., Billerica, MA, USA) to remove tilt and curvature.A movie combining the AFM images obtained at every step of the charge/discharge cycles is available in the ESI † material.electro-polymerisation in Lewis neutral EMImCl-AlCl 3 with 0.1 mol dm À3 EDOT between À0.5 V and 2.5 V vs. Al|Al(III) (Fig. 3A).The damping change is signicantly larger than the frequency change, which indicates viscoelastic behavior of the polymer lm in ionic liquid.Therefore, a quantitative value of the polymerised mass as well as the doped/de-doped anion mass is rather vague because the mass change cannot be considered to be directly proportional to the frequency change (eqn (3)).However, a qualitative evaluation of the mass change depending on the polymerisation time/cycle can be performed.

Results and discussion
The temporal course of the resonance frequency shows an overall decrease and stabilisation around 740 s ($cycle 12), indicating continuous growth of the polymer lm on the quartz crystal (Fig. 3A).Each polymerisation cycle is characterised by a decrease of the resonance frequency followed by an increase, which are associated with the anion doping and de-doping, respectively.The anion doping during the monomer oxidation causes a decrease of the resonance frequency due to an increase of the polymer mass with inserted doping anions.The increase of the resonance frequency relates to the decrease of the polymer mass by removing the doping anions from the lm during the reduction.
The calculated real G 0 and imaginary G 00 parts of the shear modulus (Fig. 3B) show a similar trend to the frequency change.The overall increase of the shear modulus indicates a stiffening of the polymer lm, whereas with every polymerisation cycle, a decrease followed by an increase occurs.The anion doping causes an increase of the polymer soness (decrease of G 0 ), while the polymer lm regains stiffness during anion de-doping (increase of G 0 ).
The calculated lm thickness of the whole polymer lm (Fig. 3C) increases up to 360 nm during polymerisation.During doping/de-doping at every polymerisation cycle, the lm thickness uctuates by about 100 nm.
The mass of the polymer lm (Fig. 3C) is increased constantly by adding a PEDOT layer with every polymerisation cycle.
The correction factor b (Fig. 3D) is 2.3 in the oxidised/doped state and 1.8 in the reduced/de-doped state aer 12 cycles.A correction factor > 1 indicates that the lm is very porous.
3.1.2.Cycling in ionic liquid.The PEDOT lms electropolymerised in Lewis neutral ionic liquid were cycled in monomer-free Lewis neutral EMImCl-AlCl 3 .The overall frequency and damping change (Fig. 4A) remained approximately constant over time during all measured cycles.The decrease of the resonance frequency indicates anion doping during polymer oxidation/charging, whereas the increase indicates anion de-doping during reduction/discharging.The damping change is signicantly larger than the frequency change; thus, quantitative determination of the exchanged mass is difficult because the Sauerbrey equation (eqn (3)) cannot be applied.
The real part of the shear modulus (Fig. 4B) shows an overall decrease, pointing to a slight increase of the polymer soness with time.Every charging cycle shows a clear decrease of the shear modulus, while every discharging cycle is characterised by an increase.Thus, the anion doping (charging reaction) causes a soening of the polymer lm, which regains its stiffness when the anions are de-doped (discharge reaction).
The thickness of the PEDOT lm (Fig. 4C) uctuates about AE45 nm from its average value of 340 nm during charging and discharging cycles, indicating polymer swelling (increased lm thickness) during doping of AlCl 4 À anions and contraction (decreased lm thickness) during de-doping of AlCl 4 À anions.
There is nearly no net mass change in the polymer lm during cycling time (Fig. 4C).The mass of the polymer increases when the lm is doped with anions and decreases when it is dedoped.The PEDOT lm reaches >95% reversibility in terms of the anion doping/de-doping.Therefore, the doping anion AlCl 4 À is not trapped in the polymer backbone during charging and discharging.The electro-polymerised PEDOT lm has a calculated correction factor b (Fig. 4D) between 2.0 and 2.6, indicating a very rough surface area. 32Assuming that meaningful values were used for the physical properties of the system, these values are two to three times larger than those reported for aqueous systems (b $ 0.8) 20 due to the stronger interaction of PEDOT with the doping anion AlCl 4

À
, where the doping is not hindered by hydrate shielding.
Each charging and discharging cycle can be divided into four potential areas with different behaviours, as shown by cyclic voltammetry (Fig. 5A), the change in the resonance frequency (Fig. 5B) and the calculated shear modulus (Fig. 5C) for cycle 10.
Oxidation potential window I (0 V to 0.5 V).In the beginning of the polymer charging (oxidation) from 0 V to 0.5 V vs. Al|Al(III), the current density increases slightly.The frequency change also shows only a slight increase, which implies no signicant anion doping or de-doping.The shear modulus shows a clear decrease, indicating soening of the polymer.
Oxidation potential window II (0.5 V to 1.5 V).The following potential window from 0.5 V to 1.5 V vs. Al|Al(III) shows a wide oxidation peak of PEDOT, indicating the generation of positive charges in the polymer backbone.The frequency change reaches a maximum aer a slight increase but does not yet show anion doping.The shear modulus decreases further to its minimum.Thus, the polymer is soest in this potential window.
Oxidation potential window III (1.5 V to 2.1 V).The further oxidation from 1.5 V to 2.1 V vs. Al|Al(III) shows another oxidation peak of PEDOT.At this potential window, the resonance frequency decreases signicantly, which is a clear indication of anion doping.The shear modulus increases slightly, indicating a stiffening of the polymer backbone due to the large number of doping anions entering the polymer structure.
Oxidation potential window IV (2.1 V to 2.5 V).The last potential window from 2.1 V to 2.5 V vs. Al|Al(III) is characterised by a phase-out of the oxidation peak and a further signicant decrease of the resonance frequency, clearly showing anion  doping.The polymer soens again as the shear modulus decreases.
Reduction potential window IV (2.5 V to 2.1 V).The discharge reaction (towards reduction) shows that the current density decreases and the resonance frequency increases strongly, indicating reverse anion de-doping.The shear modulus decreases further, which may be related to the enhanced anion movement in the polymer backbone, opening paths between the polymer chains due to de-doping.
Reduction potential window III (2.1-1.5 V).The current density decreases almost linearly from 2.1 V to 1.5 V vs. Al|Al(III).Furthermore, there is almost no change in resonance frequency, indicating that there is no signicant anion de-doping.However, the polymer stiffens as the shear modulus increases.
Reduction potential window II (1.5 V to 0.5 V).The potential window from 1.5 V to 0.5 V vs. Al|Al(III) shows a reduction peak of PEDOT, indicating the removal of repulsive forces between the polymer chains.This leads to contraction of the polymer paths accompanied with anion de-doping, as shown by the increasing resonance frequency and further stiffening of the polymer as the shear modulus increases to a maximum.
Reduction potential window I (0.5 V to 0 V).The current density increases from 0.5 V to 0 V vs. Al|Al(III) and the frequency change is almost constant, showing that the anion de-doping is complete.The shear modulus increases again to its initial value, showing that it regains the original stiffness of the polymer.
In order to better understand the dependence of the capacitive and faradaic behaviour of PEDOT on the state of charge/ discharge, the scan rate of the CV of the polymer lm was varied between 10 mV s À1 and 200 mV s À1 in monomer-free Lewis neutral EMImCl-AlCl 3 (Fig. 6).
The anodic and cathodic current density increases with the scan rate from 10 mV s À1 to 200 mV s À1 .The cathodic peak at 0.6 V vs. Al|Al(III) for 200 mV s À1 shis towards higher potentials with decreasing scan rate.This indicates that the anion dedoping occurs at high electrode potentials and low scan rates, which demonstrates capacitive behaviour at higher potentials.
The slope of the linear function, obtained from the powerlaw relation (eqn (10)) by plotting the logarithm of the anodic current vs. the logarithm of the scan rate at 1.1 V and 2.1 V vs. Al|Al(III), provides information about the transport dynamics of the underlying charge-storage mechanism 11,37 (Fig. 6 inset diagram).
The calculated slopes x at 1.1 V and 2.1 V vs. Al|Al(III) are 0.6 and 0.7, respectively.A slope of 0.5 corresponds to a process limited by semi-innite diffusion (faradaic behaviour) and a slope of 1 shows a surface-limited process, such as the adsorption of ions at a surface (pseudo-capacitive behaviour).The calculated values show that the oxidation of PEDOT (faradaic reaction) is accompanied by anion doping (pseudocapacitive reaction) and that at higher anodic potentials (higher state of charge), (pseudo)-capacitive behaviour is predominant.This indicates that PEDOT as an electrode material can provide high specic energy at a low state of charge and high specic power at a high state of charge.

In situ atomic force microscopy
The in situ AFM measurements of PEDOT lms in monomerfree Lewis neutral chloroaluminate ionic liquid provided information about the morphological changes of the polymer surface during charging/discharging (anion doping/de-doping) cycles.The morphology of PEDOT polymerised in Lewis neutral chloroaluminate ionic liquid appears to be very porous and granular (Fig. 7) when PEDOT is in its uncharged or un-doped state.The agglomerated grains have an average size of 100 nm, and the maximum height difference between the agglomerated areas reaches 1 mm (Fig. 7) (brighter areas have greater heights).The average surface roughness R a is between 180 and 190 nm.
The polymer surface shows also local differences in terms of deformability (Fig. 8) in the uncharged state.It has been shown that PEDOT grows as vertically aligned granular pillars, which are directly connected to the substrate.These pillars, which appear as grains on the surface (Fig. 8A), are partially connected horizontally by a granular polymer layer.This layer has no direct contact with the substrate and is visible as stretched areas (Fig. 8A). 14The stretched areas are caused by the strong force applied between the tip and the polymer surface which is required to measure the deformability.It is assumed that the polymer pillars have lower deformability due to the direct contact with the substrate and appear as darker areas (Fig. 8B); the brighter areas with higher deformability can be attributed to the horizontally connecting polymer layers (Fig. 8B).
During the charging of un-doped PEDOT (Fig. 9A-E), the polymer oxidation and anion doping reaction causes the merging of the polymer granules.Conversely, during discharging (Fig. 9F-J), the polymer reduces and anion de-doping reaction occurs.This is characterised by a renewed separation of the granules, where the grain shape and position are not identical to the previous grain morphology before the charging reaction.The four areas indicated as squares a, b, c, and d (Fig. 9) clearly demonstrate the morphological changes and the merging of the granules and the reversible separation.The newly emerged grains have approximately the same sizes ($100 nm) as the initial grains.Most areas show recovery of the initial morphology.However, area d appears to not regain its initial surface morphology aer discharging.The overall surface roughness R q decreases from 180 to 190 nm up to $160 nm during charging and increases again during discharging up to $180 nm, which indicates high morphological reversibility during cycling.

Suggested model
The previously discussed EQCM and AFM results suggest that the changes in the polymer stiffness/soness and morphology as well as the faradaic and (pseudo)-capacitive behaviour depending on the state of charge are associated with each other.
The overall charging behaviour of PEDOT is characterised by swelling and soening of the grainy morphology accompanied by anion doping.Similarly, the discharging reaction shows contraction of the polymer grains, which regain stiffness.At the same time, the anions are fully de-doped.A closer look at each charging and discharging cycle reveals that the charge storage mechanisms depend on the state of charge.
Polymer charging (oxidation).It is known that the oxidation of PEDOT (Fig. 10A) generates positively charged centres on the monomer units in the polymer backbone, 20,38 which appear as peaks in the CV (Fig. 5A).During polymer charging, the number of positive charge carriers increases in the polymer backbone, leading to repulsive forces between the charged centres and the polymer chains (Fig. 10C).This implies a gradual opening of transport paths between the polymer chains; this provides access of the doping anions to the positive charges, which are consequently neutralised in the polymer backbone.Anion doping into the polymer has been demonstrated by the decrease of the resonance frequency (Fig. 5B) with EQCM, whereas the polymer oxidation (faradaic behaviour) occurs rst and is followed by the anion doping (pseudo-capacitive behaviour) at a lower state of charge.The calculated shear modulus decreases gradually to a minimum during the charging reaction, demonstrating a soening effect of the polymer (Fig. 5C) due to the gradual opening of the transport paths.The opening of the transport paths and the soening correlate with the observed polymer swelling and grain merging shown by the AFM measurements (Fig. 9A-E).A slight increase of the shear modulus and stiffening of the polymer at a high state of charge accompanies the polymer oxidation with simultaneous strong anion doping (pseudocapacitive behaviour), which stretches and expands the polymer backbone to its boundaries.The strong anion doping at a high state of charge (>2.1 V vs. Al|Al(III)) suggests predominant pseudo-capacitive behaviour of the polymer.
Polymer discharging (reduction).Vice versa, the polymer reduction (Fig. 10B) is accompanied by the removal of positive charges and, therefore, repulsive forces from the polymer backbone.This causes reversible anion de-doping (Fig. 5B) and contraction of the polymer morphology to its original grainy morphology, as shown by the AFM images (Fig. 9F-J).Simultaneously, the shear modulus increases to its initial value, indicating the regained polymer stiffness (Fig. 5C).
Furthermore, it is assumed that the polymer swelling causes stronger interchain charge transport due to the merged polymer grains.For example, the anion doping/de-doping at a higher state of discharge (2.1 V to 2.5 V vs. Al|Al(III)) appears to be more pronounced as the resonance frequency signicantly decreases/ increases (Fig. 5B).This may be related to the swollen polymer morphology with opened transport paths for anions between the polymer chains.The anions have the ability to move in and out of the polymer backbone more readily.Furthermore, PEDOT shows more (pseudo)-capacitive behaviour due to the enhanced anion doping/de-doping at this higher electrode potential (>2.1 V vs. Al|Al(III)).This has been proven by the steeper slope calculated by the power-law relation (Fig. 6).
It can be concluded that an increasing state of charge is accompanied with an increase of (pseudo)-capacitive behaviour of PEDOT and a lower state of charge is characterised by faradaic or battery-like behaviour.

Conclusions and foresight
In this work, the morphological and viscoelastic changes of the conductive polymer PEDOT in Lewis neutral EMImCl-AlCl 3 ionic liquid have been studied by in situ atomic force microscopy and electrochemical quartz crystal microbalance measurements in order to create a model for fundamental understanding of the hybrid battery-(pseudo)-capacitor characteristics of conductive polymers.
It has been shown that: (a) PEDOT undergoes a reversible morphological modication during charging (polymer oxidation) and discharging (polymer reduction) with simultaneous changes in its viscoelastic properties.
(b) The changes in the polymer characteristics are caused by polymer swelling and contraction phenomena, which can be explained by the generation and removal of repulsive forces between the monomer units accompanied by anion doping and de-doping of the polymer backbone.
(c) The charging reaction causes swelling and merging of the polymer grains as well as soening of the lm.This enables fast charge transfer of doping anions at a high state of charge, which results in non-faradaic capacitor-like behaviour.(d) The discharging reaction is characterised by contraction and separation of the previously merged polymer grains, whereas the grains relocate from their initial positions with decreasing state of charge.At the same time, the polymer regains its stiffness and shows pronounced faradaic battery-like behavior.
These fundamental insights suggest that electropolymerised conductive polymers that contain no extra weight due to additives or binders can be used as safe and sustainable energy storage materials in non-aqueous systems.Furthermore, understanding the properties of a polymer in accordance with the state of charge has an important inuence on polymer synthesis and design because the polymer morphology determines the performance and predominant electrode behaviour.Systematic structuring of the polymer can emphasise battery or capacitor characteristics depending on the wide range of applications.

Conflicts of interest
There are no conicts to declare.

Fig. 1 Fig. 2
Fig. 1 Illustration of the experimental setup of the quartz crystal microbalance.

Fig. 3
Fig. 3 (A) Frequency (black line) and damping (red line) changes in a gold-coated quartz crystal; (B) calculated shear moduli (real part, black line and imaginary part, red line), (C) polymer film thicknesses (black line) and masses (red line) and (D) correction factors during the polymerisation of EDOT in Lewis neutral EMImCl-AlCl 3 with 0.1 mol dm À3 EDOT from À0.5 V to 2.5 V vs. Al|Al(III), 100 mV s À1 , 25 C.

3. 1 .
Fig. 4 (A) Frequency (black line) and damping (red line) changes in a gold-coated quartz crystal; (B) calculated shear modulus (real part), (C) polymer film thickness (black line) and mass (red line) and (D) correction factor during the cycling of PEDOT in monomer-free Lewis neutral EMImCl-AlCl 3 from 0 V to 2.5 V vs. Al|Al(III), 100 mV s À1 , 25 C.

Fig. 5 (
Fig. 5 (A) Cyclic voltammogram, (B) frequency changes of a goldcoated quartz crystal; (C) calculated shear modulus (real part) and film thickness of the polymer film during charging (black lines) and discharging (red lines) of PEDOT in monomer-free Lewis neutral EMImCl-AlCl 3 from 0 V to 2.5 V vs. Al|Al(III) at cycle 10, 100 mV s À1 at 25 C.

Fig. 6
Fig. 6 Cyclic voltammograms of PEDOT in monomer-free Lewis neutral EMImCl-AlCl 3 at different scan rates, cycle 3 at 25 C.The inset diagram shows the relationship between log(anodic current) À log(scan rate) at 1.1 V and 2.1 V vs. Al|Al(III).

Fig. 8
Fig. 8 AFM images showing the differences in (A) height and (B) deformability of uncharged PEDOT in monomer-free Lewis neutral EMImCl-AlCl 3 .

Fig. 9
Fig. 9 AFM images at different states of charge (A-E) and discharge (F-J).The square areas (a-d) show the morphological surface changes of PEDOT in detail.

Fig. 10
Fig. 10 AFM images of PEDOT in monomer-free Lewis neutral EMImCl-AlCl 3 in the fully (A) charged and (B) discharged states and (C) schematic model of the morphological changes of a conductive polymer in an ionic liquid during charging (oxidation, anion doping) and discharging (reduction, anion-de-doping).
s À1 ] Z m fSB Mechanical impedance of the lm, calculated by Sauerbrey [g cm À2 s À1 ] Z l Impedance of lms in electrolyte [g cm À2 s À1 ] Z Q , Z q Characteristic impedance of the quartz [g cm À2 s À1 ] Z tr Impedance of lms with trapped electrolyte [g cm À2 s À1 ] a Degree of doping Df (Resonant)-frequency change [Hz] Dw Damping change [Hz] h l Kinematic viscosity of the electrolyte [g cm À1 s À1 ] m Q , m q Shear modulus of the quartz [g cm À1 s À2 ] r Density [g cm À3 ] r f Density of the polymer lm [g cm À3 ] r l Density of the electrolyte [g cm À3 ] r Q , r q Density of the quartz [g cm À3 ] r rl Density for a rigid layer [g cm À3 ] c Molar ratio [mol%] u Radial frequency [s À1 ] EDOT Molar mass of EDOT [g mol À1 ] M IL Molar mass of ionic liquid [g mol À1 ] N Amount of AlCl 3 n Amount of substance [mol] P spec Specic energy [W kg À1 ] Q Transferred amount of charges [mA s] Q spec Specic capacity [mA s kg À1 ] Damping of the quartz in uid [Hz] X l Reactance of the electrolyte [g cm À2 s À1 ] z Number of charge carriers Z f , Z s Film impedance [g cm À2