A ﬂ uorescence switching sensor based on graphene quantum dots decorated with Hg 2+ and hydrolyzed thioacetamide for highly Ag + -sensitive and selective detection

* a A selective ﬂ uorescent sensor based on graphene quantum dots (GQDs) was developed for the determination of silver ions (Ag + ). The GQDs were prepared by the citric acid pyrolysis method. In the presence of mercury ions (Hg 2+ ), the ﬂ uorescence intensity of the GQDs decreased linearly and it was fully recovered by the hydrolysis of thioacetamide (TAA), giving hydrogen sul ﬁ de in the reaction system. This research study was aimed at using the ﬂ uorescence turn-o ﬀ sensor for the selective determination of Ag + . Upon the addition of Ag + , the ﬂ uorescence intensity of the generated sul ﬁ de-(Hg 2+ quenched GQDs) decreased as a linear function of the Ag + concentration. Then, the acquired GQDs showed steady, selective, and highly sensitive detection of Ag + . The experimental parameters a ﬀ ecting the ﬂ uorescence turn-on/o ﬀ sensor were investigated and optimized. The optimum conditions included 4 m M Hg 2+ concentration, 70 m M TAA concentration, solution pH of 7 and a 5 min reaction time. Under the optimized conditions, the working linear concentration range, limit of detection and limit of quanti ﬁ cation for Ag + were 0.5 – 10.0, 0.18 and 0.60 m M, respectively. The proposed method was successfully applied for the selective determination of trace amounts of Ag + in ﬁ ve real water samples with satisfying levels of recovery (89.31 – 114.08%).


Introduction
Silver ions (Ag + ) are included in the list of heavy metal ions, and their potential toxicity for the environment and human body has drawn people's attention.Owing to their broad employment in many industries, such as electronics, photography, mirrors, and pharmacy, a large amount of silver is released into the environment annually from industrial waste and emissions, especially into sludge waste and even surface waters. 1,2It has also been found that silver is toxic to humans at concentrations as high as 0.9 mM in drinking water. 3Considering these facts, applying a simple, rapid and accurate method to monitor silver ions at trace levels in various samples is of great importance.Various techniques have been used for the determination of silver in real samples, such as the spectrophotometric method, 4 graphite furnace atomic absorption spectroscopy (GFAAS), 5 high-resolution continuum source ame atomic absorption spectrometry (HR-CS FAAS), 6 inductively coupled plasma optical emission spectrometry (ICP-OES), 7 differential pulse anodic stripping voltammetry (DPASV), 8 and spectrouorimetry. 9,10lthough these techniques are highly sensitive and selective, they require tedious sample preparation and preconcentration procedures, expensive instruments, and professional personnel.
Recently, nanomaterials have been used to build sensitive analytical sensors for the analysis of various inorganic and organic substances including trace amounts of hazardous substances in the environment.Such sensors possess certain advantages, e.g.high sensitivity, short analysis time, low cost, and simple preparation and treatment. 11Graphene quantum dots (GQDs) have generated enormous excitement because of their superiority in a variety of advantageous properties.They were discovered very recently as a class of zero-dimensional graphitic nanomaterials with lateral dimensions less than 100 nm, and they have either a single layer, double layers, or a few layers (3 to <10). 12,13Compared with organic dyes and semiconductive quantum dots (QDs), GQDs are superior in terms of their excellent properties, such as their high photostability against photobleaching and blinking, biocompatibility and low toxicity. 15Moreover, similar to graphene, GQDs have excellent characteristics such as large surface areas, large diameters, ne surface graing via the p-p conjugated network or surface groups, and other special physical properties. 16,17urthermore, the carboxyl and hydroxyl groups at their edge enable them to display excellent water solubility and suitability for successive functionalization with various organic, inorganic, polymeric or biological species.For these reasons, GQDs have attracted signicant attention worldwide.9][20][21] Furthermore, most of the uorescent sensors for Ag + showed limitations in their practical application due to their low water solubility, serious toxicity even at relatively low concentrations, and other drawbacks.Hence, it remains essential to develop much simpler, more efficient and robust methods for silver ion probing that can be used for the selective detection of Ag + in real samples.
In this research, a selective uorescent sensor for the determination of silver ions (Ag + ) was developed based on GQDs.The GQDs were prepared by the citric acid pyrolysis method.In the presence of mercury ions (Hg 2+ ), the uorescence intensity of the GQDs decreased linearly and it was fully recovered by the hydrolysis of thioacetamide (TAA).This study is aimed at using a uorescent sensor for the determination of Ag + .Upon the addition of Ag + , the uorescence intensity of the TAA-(Hg 2+ quenched GQDs) decreased as a linear function of the Ag + concentration.In addition, the optimum conditions including the Hg 2+ and TAA concentrations, pH of the solution and reaction time were investigated in detail.

Chemicals and reagents
All of the chemicals used were of analytical grade.The citric acid, sodium hydroxide, silver chloride, potassium chloride, and barium chloride were purchased from Ajax Fine Chem Pty. Ltd. (Australia).The mercury nitrate, cobalt nitrate hexahydrate, lead nitrate, zinc nitrate hexahydrate, cadmium nitrate tetrahydrate, copper nitrate trihydrate, potassium cyanide, potassium iodide, thioacetamide (99.0%), and sodium sulde were purchased from Sigma-Aldrich (Germany).

Apparatus
UV-Vis absorption spectra were obtained using an Agilent 8453 spectrophotometer (Agilent, Germany).Emission spectra were recorded using an RF-5301PC spectrouorophotometer (Shimadzu, Japan) with excitation and emission slit widths of 5 nm.A quartz cuvette (1 cm path length) was used for both the UVvisible absorption and uorescence measurements.Transmission electron microscopy (TEM) images were obtained using a JEOL1200 (JEOL Ltd., Japan).The functional groups of the GQDs were characterized by an attenuated total reectance-Fourier transform infrared (ATR-FTIR) spectrometer (TENSOR 27, Bruker, Germany).A pH meter (UB-10 Ultra Basic, Denver, USA) and analytical balance (AC121S, Sartorius, USA) were also used in this study.

Synthesis and characterization of the GQDs
The GQDs were prepared from citric acid by a pyrolysis method with a modied procedure. 12-14Briey, 2.0 g of citric acid was added into a 250 mL beaker.The beaker was heated to 200 C using a paraffin oil bath for about 5 min.The solid citric acid was slowly liquated and had a yellow color.100 mL of 0.25 M NaOH was added into the beaker with continuous stirring for 30 min at room temperature.The obtained sample solution was neutralized to pH 7 with HCl, and the GQD stock solution was stored at 4 C before use.
The quenching effect of the GQDs using Hg 2+ 20 mL of a 2.0 mg mL À1 GQD solution and 1 mL of 1 M phosphate buffer with a pH of 7.4 were mixed in a 10 mL volumetric ask.Then, various concentrations of Hg 2+ were added to an aliquot of the GQD solution (10 mL nal volume) at room temperature.The Hg 2+ quenched uorescence spectra of each of the GQD solutions were recorded immediately at l ex /l em 370/ 460 nm.Then, such spectral measurements were used to plot the quenching calibration curve for Hg 2+ .
To conrm the selectivity of the Hg 2+ quenched GQDs, the following procedure was carried out.An individual stock solution of various metal ions (0.01 mM) was prepared by the dissolution of metal salts in ultrapure water.10 mL of the GQD solution was mixed with 100 mL of 0.01 mM solutions of each of the metal ions (10 mM nal concentration) and adjusted to a nal volume of 10 mL in a volumetric ask with DI water.
The selectivity of the Hg 2+ -GQDs uorescence turn-on by the hydrolysis of TAA The uorescence measurement of the GQDs was performed using a 10 mL volumetric ask containing 20 mL of GQDs (2.0 mg mL À1 ) mixed with 4 mM Hg 2+ in a 0.1 M phosphate buffer solution with a pH of 7. Various concentrations of TAA and Na 2 S as a reference were added to the solution mixture and adjusted to 10 mL with DI water.The emission spectra of the test solution were recorded with an excitation wavelength of 370 nm.In addition, the effect of the concentration of ammonium acetate solution was investigated in order to nd out any common ion effects, i.e. acetate and ammonium ions, except hydrogen sulde, generated by the hydrolysis of TAA.
The selectivity of the Hg 2+ -GQDs-TAA uorescence turn-off sensor for Ag + detection The uorescence measurement of the GQDs was performed using 20 mL of GQDs (2.0 mg mL À1 ) mixed with 4 mM Hg 2+ and 70 mM TAA in a 0.1 M phosphate buffer solution with a pH of 7. Various concentrations of Ag + were added to the mixture solution and adjusted to various pH values with a 10 mL nal volume with DI water.The emission spectra of the test solution were also recorded with an excitation wavelength of 370 nm.Spectral measurements were used to plot the quenching calibration curve for Ag + .
The optimization of the conditions for the uorescence turnoff sensor for Ag + The uorescence measurement of the GQDs was performed in a phosphate buffer solution at a pH of 7 in a 10 mL volumetric ask.Briey, 1 mL of the GQDs (200 mg L À1 ) was mixed with 4 mM Hg 2+ and 70 mM TAA in a 0.1 M phosphate buffer solution at a pH of 7.Then, various concentrations of Ag + were added to the sample solution.Finally, the volume of the solution was adjusted to 10 mL with DI water.The emission spectra of the sample mixtures were recorded with a spectrouorometer.
To obtain the optimum conditions of the proposed sensor, the following parameters were studied using the same procedure as mentioned above.The effect of the pH of the solution was studied by varying the pH of the solution from 3-12 using an acetate buffer (pH 3-5) and phosphate buffer (pH 6-12).The incubation times were studied from 0-1 h.The effect of the concentration of Hg 2+ was investigated by varying the concentration from 0 to 10 mM.

The selectivity of the uorescent sensor
To evaluate the selectivity of the proposed uorescent sensor, the following procedure was carried out.An individual stock solution of each of the various metal ions (0.01 mM), including Li + , Na + , K + , Ba 2+ , Ca 2+ , Cd 2+ , Co 2+ , Cu 2+ , Fe 2+ , Fe 3+ , Mg 2+ , Mn 2+ , Ni 2+ , Pb 2+ , Zn 2+ , Cr 3+ and Al 3+ ions, was prepared by the dissolution of their metal salts in DI water.Then 100 mL of their stock solutions were added to 10 mL volumetric asks each containing 1 mL of the GQDs (200 mg L À1 ), 4 mM Hg 2+ , and 70 mM TAA in a 0.1 M phosphate buffer solution with a pH of 7. Finally, the volume of the reaction mixture was adjusted to 10 mL with DI water.

Results and discussion
The characterization of the synthesized GQDs Fig. 1(a) shows the UV-Vis absorption spectrum of the synthesized GQDs, which exhibits two absorption bands at around 230 nm.The broadened absorption band centered at 230 nm, resulting in nearly no uorescence signal, is attributed to the pp* electronic transition of the aromatic sp 2 domains. 22The other typical absorption peak centered at 365 nm is assigned to the n-p* transition of the graphitic sp 2 domains. 23The photoluminescence (PL) spectra of the synthesized GQDs show strong peaks at 460 nm when excited at 370 nm and the full width at half maximum (FWHM) is about 100 nm, which is approximately the same as those of most reported GQDs. 24o further characterize the optical properties of the synthesized GQDs, a detailed PL investigation was carried out with different excitation wavelengths (Fig. 1(b)).When the excited wavelengths change from 320 to 370 nm, the PL intensities increase markedly, but the uorescence emission peak remains unshied.This excitation-independent PL behavior is also attributed to a similar trend to the behaviour of previously reported GQDs. 25 Fig. 2(a) shows the FT-IR spectrum of the GQDs.The strong bands at around 1556 cm À1 are due to the C]C stretching mode of polycyclic aromatic hydrocarbons, 26 indicating that the GQDs retain their graphene structure.Moreover, the bands at around 1718 cm À1 correspond to the carboxyl groups, and the bands at around 3440 cm À1 are attributed to the stretching vibrations of the hydroxyl groups.The peaks at 1364-1068 cm À1 are attributed to the C-O bond in the COH/COC (epoxy) groups. 27o determine the particle size of the obtained GQDs, the sample was characterized by transmission electron microscopy (TEM).Fig. 2(b) shows the image of the GQDs.Using image J soware, the GQD particles, which had a diameter in the range of 3.33 nm to 8.33 nm, are shown to be distributed uniformly.The small particle size of the GQDs provides evidence for the uorescence intensity.
From Fig. 3, it was clearly found that Hg 2+ could quench the uorescence intensity of the GQDs very strongly, while both the Fe 2+ and Fe 3+ ions had a slight quenching effect.The other ions scarcely quenched the uorescence intensity of the GQDs.The high selectivity may be attributed to the fact that the Hg 2+ ions have a stronger affinity towards the carboxylic groups on the GQD surface than other reported metal ions. 28The quenching mechanism presumably occurs via either electron or energy transfer from the GQDs to the Hg 2+ ions. 29e optimum conditions for the quenching effect of the GQDs by mercury ions The optimum concentration of Hg 2+ was studied as shown in Fig. 4(a) and (b).When the Hg 2+ concentration increased, the emission intensity of the GQDs gradually decreased.A linear  relationship was obtained when the maximum intensity of the GQDs at 460 nm was plotted against the Hg 2+ concentration in the range of 1-4 mM.When the concentration of Hg 2+ was 4 mM, the uorescence intensity of the GQDs was efficiently quenched.Therefore, 4 mM Hg 2+ was used for the further studies.
To improve the quenching effect of Hg 2+ , several experimental parameters were optimized including the reaction time and solution pH value.Aer the addition of 4 mM Hg 2+ , the uorescence (FL) spectrum of the GQDs (pH 7.0 and 20 mg L À1 GQDs), was recorded at every 5 min interval.Thus, the FL intensity of the GQDs at 460 nm decreased as much as 82% within a minute aer the addition of Hg 2+ (Fig. 5(a)), then the FL intensity gradually decreased until 5 min, and then nally it remained constant over the next 60 min.From the results, it is suggested that the quenching process is almost completed within 5 min.
For the effect of the pH, a series of acetate and phosphate buffers at different pH values were prepared, and then the GQD solutions (20 mg L À1 nal concentration) together with 4 mM Hg 2+ were added into each different buffer solution (pH: 3.0, 4.0, 5.0, 6.0, 7.0, 8.0, 9.0, 10.0, 11.0 and 12.0 in 0.1 M).The FL intensity was measured at 460 nm from each of the two buffered solutions of GQD only and GQDs with Hg 2+ (Fig. 5(b)).The FL intensity of the GQDs increased gradually with pH values from 3.0-7.0and stabilized under alkaline conditions.It was implied that a suitable quenching effect occurred with pH > 7.0.Thus, the working pH for a sufficiently sensitive and stable quenching of Hg 2+ was 7.0.
The optimum conditions for the uorescence turn-on of the Hg 2+ quenched GQDs using the hydrolysis of thioacetamide TAA is an active organosulfur, which undergoes hydrolysis giving hydrogen sulde in the solution.As shown in reaction (1), the homogeneously generated hydrogen sulde and sulde ions (HS À and S 2À ) can act in similar roles to the thiol group, then they can bind to Hg 2+ through Hg-S interactions.This causes the Hg 2+ -GQD complex to dissociate, resulting in the restoration of the uorescence intensity of the GQDs. 30 To make sure that H 2 S can have a uorescence enhancing effect on the Hg 2+ -GQDs, a common sulde salt was used.In this regard, a solution of Na 2 S was added to the Hg 2+ -GQDs reaction mixture and then the uorescence intensity of the GQD system was measured compared with that of the Hg 2+ -GQDs mixture using TAA.From the results (Fig. 6), it was found that both kinds of the two sulde solutions provided a similar trend, suggesting that the H 2 S generated from TAA could enhance the uorescence intensity of the Hg 2+ -GQDs.However, the optimum concentration of TAA was also studied as shown in Fig. 7(a) and (b).When the concentration of TAA increased, the FL intensity of the Hg 2+ -GQDs was gradually restored.A linear relationship was obtained when plotting the maximum intensity of the Hg 2+ -GQDs at 460 nm against the TAA concentration in the range of 0-70 mM (Fig. 7(b)).At 70 mM TAA, the uorescence intensity of the Hg 2+ -GQDs was efficiently restored.Therefore, 70 mM TAA was selected for further studies.
Also, to improve the uorescence restoration efficiency of the Hg 2+ -GQD complex, the reaction time and pH value were optimized (Fig. 8(a)).Aer the addition of 70 mM TAA, the FL intensity of the GQD system (pH 7.0) was recorded every 5 min and it increased rapidly.The results suggested that the restoration process is completed within a minute.
To study the effect of the pH, 70 mM TAA was added to the Hg 2+ -GQD complex in the buffer solution at different pH values.As the results show in Fig. 8(b), the FL intensity of the GQDs increased gradually with the pH increasing from 3.0-7.0and stabilized under alkaline conditions.It is implied that a suitable FL enhancing effect occurred with pH > 7.0.Thus, the working pH of the hydrolysis of TAA for a sufficiently sensitive and stable FL enhancing effect was 7.0.

The optimum conditions for the uorescence turn-off sensor for silver ions
The overall assay strategy for the sensing of Ag + is shown in Fig. 9.The GQDs showed strong blue uorescence in an  aqueous buffer solution.Upon the addition of Hg 2+ , it bound to the GQDs resulting in uorescence quenching of the GQDs.But when TAA was added, the TAA could react with the Hg 2+ ion through Hg-S interaction.When the Hg 2+ -GQD complex dissociated, the uorescence of the GQDs was restored.Lastly, when Ag + ions were added to the reaction mixture, the uorescence intensity of the GQDs decreased.The FL turn-off mechanism possibly occurs, and this means that the Ag + ion has more affinity to bind with a sulfur atom on the thiol group compared with the mercury ion.Thus, when Ag + was added to the mixture, it would bind with the sulfur atom of H 2 S and break the Hg-S bond.Therefore, the free Hg 2+ ion would bind to the GQDs again, leading to the uorescence turn-off sensing of the GQD system.
As shown in Fig. 10(a), the uorescence intensity of the GQDs gradually decreased when the concentration of Ag + increased.A linear relationship was obtained when the maximum intensity of the GQDs at 460 nm was plotted against the Ag + concentration in the range of 0.5-10 mM (Fig. 10(b)) with the Stern-Volmer plot shown in Fig. 10(c).
To improve the performance of the quenching of Ag + , several experimental conditions, i.e. the reaction time and solution pH value, were optimized.Aer the addition of 10 mM Ag + , the FL spectrum of the GQDs was recorded at ve min intervals.The FL intensity of the quenched GQDs at 460 nm rapidly decreased and remained constant within 5 min (Fig. 11(a)), and the FL intensity remained constant over the next 60 min.The results suggest that the quenching process is completed within 5 min.
The effect of the pH on the FL sensing system was studied from pH 3-12 in two selected buffer solutions.10 mM Ag + solution was added to the GQD solution at different pH values, as shown in Fig. 11(b).The FL intensity of the GQDs increased gradually from pH 3.0-7.0and stabilized under the alkaline conditions.It is implied that the most suitable quenching effect occurred with pH > 7.0.Thus, the working solution pH for the Ag + quenching effect was also found to be 7.0.

The selective determination of the silver ion
To study the selectivity of the developed GQD uorescent sensor for Ag + detection, the values of (F À F 0 )/F 0 for the GQD system in the presence of 18 different cations, Ag + , Li + , Na + , K + , Ba 2+ , Ca 2+ , Cd 2+ , Co 2+ , Cu 2+ , Fe 2+ , Fe 3+ , Mg 2+ , Mn 2+ , Ni 2+ , Pb 2+ , Zn 2+ , Cr 3+ , and Al 3+ , were plotted using a 10 mM concentration of each metal.Fig. 12 shows that the addition of Ag + to the reaction mixture of the GQD system resulted in uorescence quenching, whereas the other remaining cations had no signicant effects under the same experimental conditions.

Method validation
The analytical characteristics of the developed method were validated under the optimized conditions in terms of the linearity, limit of detection (LOD), limit of quantication (LOQ), precision and reproducibility (expressed as the relative standard deviation (RSD) of the calibration curve slope obtained from both intra-day and inter-day analysis) to estimate the efficiency and feasibility of the method for use with tap and drinking water samples.The linearity values are from 0.5-10.0mM (R 2 ¼ 0.9918).The linear calibration graph is as follows: y ¼ 32.14x + 63.66 (where y is the uorescence intensity and x is the concentration of Ag + ).The LOD, dened as 3SD/m (where SD is the standard deviation of the low concentration of Ag + and m is the slope of the calibration graph), was 0.18 mM.While the LOQ, dened as 10SD/m, was 0.60 mM.The precision, which was

The analysis of real samples
To demonstrate the applicability and reliability of the developed method, it was successfully applied to ve water samples including tap water, three brands of drinking water (Brand 1, Brand 2, and Brand 3), and one brand of natural drinking water (Brand 4).The amounts of Ag + in each sample tested were obtained as shown in Table 1.The results showed that Ag + was not detected in all of these samples.In addition, to evaluate the matrix effect, the accuracy of the method was veried by calculating the recovery study in the real samples.Each sample was spiked with three concentrations (2.0, 4.0, and 6.0 mM) of the standard solution of Ag + .Then, the relative percentage recoveries were calculated as follows: 31,32 % recovery ¼ [(C found À C real )/C added ] Â 100 where, C found , C real , and C added are the concentration of the analyte found aer the addition of a known amount of the standard in the real sample, the concentration of an analyte in the real sample, and the concentration of the known amount of standard that was spiked in the real sample, respectively.From the results (Table 1), it is evident that the recoveries of the developed method expressed as the mean percentage (n ¼ 3) were in the range of 89.31-114.08%.This demonstrates that the method provides acceptable recovery for the determination of Ag + in these real samples, and its LOD is rather low as a trace level compared with other reported literature (Table 2).In addition, it can be concluded that the matrix has a negligible effect on the efficiency of the developed method.

Conclusion
A highly sensitive and selective uorescent sensor for the detection of Ag + based on Hg 2+ quenched GQDs in the presence of TAA was obtained.This novel approach based on GQDs for Ag + determination was carried out at a trace level.The GQDs were simply prepared from citric acid pyrolysis and characterized by molecular absorption and emission spectrophotometry, FT-IR spectroscopy and TEM.The optimum conditions for the uorescence turn-on/off sensing probe, including the effects of the solution pH, the concentration of the GQDs, Hg 2+ , Ag + , and TAA, and the reaction time, were investigated.The Stern-Volmer plot for the Ag + quencher in the presence of homogeneously generated sulde from TAA showed higher sensitivity compared with that of the common sulde salt used.The selectivity of the uorescence quenching for Ag + compared to various interfering metal ions was demonstrated.The analytical features of merit, including accuracy, precision, linearity, and limits of detection (LOD) and quantication (LOQ), were validated.The application of the developed method for the trace determination of Ag + in tap water and drinking samples was demonstrated.

Fig. 1
Fig. 1 (a) The absorption (black line), fluorescence excitation (red line) and fluorescence emission (blue line) spectra of the GQDs and (b) the fluorescence spectra of the GQDs at different excitation wavelengths.

Fig. 3
Fig.3The quenching of the fluorescence intensity of the GQDs by different metal ions.All the cation concentrations were 100 mM.F and F 0 are the emission intensities of the GQDs at 460 nm in the presence and absence of the metal ions.

Fig. 4
Fig.4(a) The changes in the emission spectra of the GQDs at different Hg 2+ concentrations (0-10 mM) and (b) changes in the emission intensity at 460 nm versus the Hg 2+ concentration (inset, the plot of (F 0 À F)/F 0 versus the concentration of Hg 2+ ).

Fig. 5 Fig. 6
Fig. 5 (a) The changes in the fluorescence intensity of the GQDs at different reaction times.Conditions: 4 mM Hg 2+ in 0.1 M phosphate buffer at a pH of 7.0 and (b) the changes in the fluorescence intensity of the GQDs at different values of pH.Conditions: 4 mM Hg 2+ and 5 min reaction time.

Fig. 7
Fig. 7 (a) The changes in the FL spectra of the Hg 2+ -GQDs at different TAA concentrations (0-100 mM).Conditions: 4 mM Hg 2+ in a 0.1 M phosphate buffer with a pH of 7.0 and (b) the changes in the FL intensity at 460 nm versus the TAA concentration.Conditions: 4 mM Hg 2+ in 0.1 M phosphate buffer with a pH of 7.0 (inset, plot of (F 0 À F)/F 0 versus the concentration of TAA).

Fig. 8
Fig. 8 (a) The changes in the FL intensity of the Hg 2+ -GQDs at different reaction times.Conditions: 0.1 M phosphate buffer pH 7.0, 4 mM Hg 2+ and 70 mM TAA and (b) the changes in the FL intensity of the Hg 2+ -GQDs at different pH values.Conditions: 4 mM Hg 2+ , 70 mM TAA and 5 min reaction time.

Fig. 9 A
Fig. 9 A schematic illustration of the FL turn-off/on/off mechanism of the GQD-based Ag + sensing.

Fig. 10 (
Fig.10 (a)The changes in the FL intensity of the Hg 2+ -GQDs at different Ag + concentrations (0-50 mM), (b) the changes in the FL intensity at 460 nm versus the Ag + concentration (inset, the plot of (F 0 À F)/F 0 versus the concentration of Ag + ) and (c) the Stern-Volmer plots of the Ag + quenching effect for both Hg 2+ -GQDs in the presence of either TAA or Na 2 S solution.

Fig. 11 (
Fig. 11 (a) The changes in the FL intensity of the Hg 2+ -GQDs at different reaction times.Conditions: 0.1 M phosphate buffer with a pH of 7.0, 4 mM Hg 2+ , 70 mM TAA and 10 mM Ag + and (b) the changes in the FL intensity of the Hg 2+ -GQDs at different pH values.Conditions: 4 mM Hg 2+ , 70 mM TAA, 10 mM Ag + and a 5 min reaction time.

Fig. 12
Fig.12The selectivity of the GQD FL sensor for different cations (10 mM) under the optimum conditions.

Table 1
The Ag + content and recoveries of the water samples using the GQD system (n ¼ 3) a a n.d.¼ not detected.This journal is © The Royal Society of Chemistry 2017 RSC Adv., 2017, 7, 48058-48067 | 48065

Table 2
The fluorescence turn-on/off sensor for Ag + detection using carbon based probes