Direct synthesis of hierarchical ZSM-5 zeolite using cetyltrimethylammonium as structure directing agent for methanol-to-hydrocarbons conversion

• A submitted manuscript is the author's version of the article upon submission and before peer-review. There can be important differences between the submitted version and the official published version of record. People interested in the research are advised to contact the author for the final version of the publication, or visit the DOI to the publisher's website. • The final author version and the galley proof are versions of the publication after peer review. • The final published version features the final layout of the paper including the volume, issue and page numbers.


Introduction
Zeolites are crystalline microporous aluminosilicates commonly used as catalysts, adsorbents and membranes in the chemical industry.][3][4][5][6][7][8][9][10] The void-filling organic templates are called structure-directing agents (SDAs).ZSM-5 is one of the most widely used zeolites and belongs to the pentasil family of zeolites.It contains a three-dimensional 10-membered ring pore system composed of channels and intersections. 11Notwithstanding the advantages of the microporous nature of zeolites in terms of shape selectivity, the small pore size for ZSM-5 (∼5.5 Å) as compared with typical crystal size (0.1-10 μm) usually limits the catalytic performance due to severe mass transport limitations, as not the entire internal micropore space is effectively used and secondary reactions such as coking can prematurely deactivate the zeolite catalyst by pore blocking. 6,12Optimizing catalytic performance through tailoring the pore texture of zeolites is currently a very important research topic in academia and industry. 8,13ncreased mass transport from active sites in the zeolite micropore space to the external surface can for instance be achieved by decreasing the diffusion length, e.g., by shaping zeolite crystals into rods, sheets or nanocrystals.5][16] An alternative approach is to use surfactants that form a liquid crystals at early synthesis times.8][19][20][21][22] Surfactants usually have a hydrophilic head group which can serve as a structure-directing moiety in zeolite synthesis, while the hydrophobic tail can be involved in stabilizing textures at the mesoscale.So, cetyltrimethyl-ammonium (CTA, usually charge-stabilized by Br − or OH − ) is up for consideration, as it is an inexpensive, long-tail surfactant, and an analogue of tetramethyl ammonium (TMA), a known SDA in zeolite synthesis. 23hen CTA's surfactant-like properties were successfully exploited in silica condensation, hexagonal arrays, similar to those in beeswax, of silicate were formed: MCM-41. 24Yet, the structure does not contain long-range atomic order and the walls are made up of amorphous silica: structure-direction at the meso-scale comes at the cost of microcrystallinity and hydrothermal stability.][27][28][29][30] There have been many attempts at synthesizing hierarchical zeolites with CTA.A notable strategy relied on combining a conventional SDA such as tetrapropylammonium for ZSM-5 synthesis with CTA.But the resulting materials are invariably physical mixtures of MCM-41 and zeolite, which shows that two types of SDA do not generally work in concert to generate a hierarchical structure. 25,26][33][34][35] Yet, it remains unclear what obstructs obtaining mesoporous ZSM-5 with CTA directly. 36Following the breakthrough finding that using the diquaternary ammonium surfactant (DQAS) SDAs developed by Ryoo's group can lead to the formation of ZSM-5 zeolite nanosheet. 17Zhu et al. recently showed that the difference between Ryoo's DQAS SDA and CTA resides in fact that the CTA's quaternary ammonium head group fails to enter the inorganic matrix from the very onset of silica condensation, while the diquaternary ammonium head group in DAQS SDA shows enforced interaction with the silica matrix already during room temperature mixing of the zeolite synthesis ingredients. 37Recently, we have demonstrated that replacement of NaOH by KOH facilitates dissolution of silicate from the initially amorphous condensed silica precursor, allowing to obtain highly crystalline hierarchical ZSM-5 zeolites in a singlestep synthesis procedure with CTA as the only organic SDA. 38his approach emphasizes that CTA can act both as an SDA and as a mesoporogen towards hierarchical ZSM-5 formation.The faster crystallization is due to the higher dissolution rate of the mesoporous silica precursor in the presence of KOH.The increased concentration of silicate anions at elevated temperatures induces zeolite nucleation.Thus, hierarchical ZSM-5 zeolite is obtained according to a dissolution-crystallization mechanism rather than a solid-solid transformation.The obtained zeolite showed much higher catalytic performance in the methanol-to-hydrocarbon (MTH) reaction compared with a bulk ZSM-5 sample.
Herein, we investigated the crystallization of gels containing CTA as a SDA and mesoporogen in more detail in order to establish under which conditions direct synthesis of mesoporous ZSM-5 zeolite is possible.We varied the type of base (LiOH, NaOH, KOH, RbOH and CsOH), the CTA concen-tration, the counter ion of CTA and the Al content.The obtained materials were characterized by elemental analysis, powder X-ray diffraction (XRD), Ar porosimetry, highresolution scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FTIR).The catalytic performance of the hierarchical ZSM-5 zeolites was compared with a bulk ZSM-5 zeolite in the MTH reaction.

Sample preparation
Cetyltrimethyl-ammonium hydroxide (CTAOH, TCI, 10 wt%) and cetyltrimethyl-ammonium bromide (CTABr, Aldrich, 95%) were used as received.Ludox AS-40 (Aldrich, 40 wt%) was the silica source in all syntheses.Aluminum hydroxide and all the mineralizing agents (e.g.NaOH, KOH) in the work were purchased from Aldrich.Hydrothermal synthesis was performed using the gel compositions given in Table 1.In a standard synthesis, 0.299 g KOH and 3.350 g CTAOH solution were added to 11.085 g demi-water at room temperature.Afterwards, 0.033 g aluminium hydroxide and 3.167 g Ludox AS-40 were added to the mixture under vigorous stirring.The final gel had a molar composition of 5CTA : 12K 2 O : 0.95Al 2 O 3 : 95SiO 2 : 4000H 2 O.After stirring at room temperature for 2 h, the resulting gel was transferred into a 45 mL Teflon-lined steel autoclave and heated under rotating (50 rpm) at 413 K for 6 days.After crystallization, the white product was filtered, washed with demi-water followed by drying overnight at 383 K.The zeolite was calcined at 823 K for 10 h under flowing air to remove the surfactant.The calcined zeolite was ion-exchanged three times with 1.0 M NH 4 NO 3 solutions followed by calcination at 823 K for 4 h in flowing air to obtain the final proton form.For comparison, bulk-ZSM-5 zeolite was synthesized using tetrapropylammonium hydroxide (TPAOH, Merck, 40 wt%) as template.

Characterization
Elemental analysis.The elemental composition of the zeolites was determined by ICP-OES (Spectro CirosCCD ICP optical emission spectrometer).For analysis, an equivolumetric mixture of HF (40 wt% in water), HNO 3 (65 wt% in water) and water was used to completely dissolve the zeolites.
XRD patterns.XRD patterns were recorded on a Bruker D4 Endeavor using Cu Kα radiation with a scanning speed of 0.02°s −1 in the 2θ range of 5-40°and 0.004°s −1 in the 2θ range of 0.7-5°.
Ar physisorption.Surface area and porosity of zeolites (H form) were determined by Ar physisorption in static mode at 87 K on a Micromeritics ASAP 2020 instrument.The zeolites were outgassed at 723 K for 6 h prior to the sorption measurements.The BET surface area of ZSM-5 zeolite was determined in the relative pressure range 0.05-0.25.The total pore volume was calculated at p/p 0 = 0.97.The micropore, mesopore volume and pore size distribution (PSD) of zeolites were determined by the NLDFT method (Ar at 87 K assuming slit pores without regularization).
This journal is © The Royal Society of Chemistry 2017 Electron microscopy.Scanning electron microscopy (SEM) images were taken on a FEI Quanta 200F scanning electron microscope at an accelerating voltage of 5 kV.Transmission electron microscopy (TEM) pictures were taken on a FEI Tecnai 20 at 200 kV.The samples were suspended in ethanol and dispersed over a holey Cu grid coated with carbon film prior to measurements.
FTIR spectroscopy.FTIR spectra were recorded in the range of 4000-800 cm −1 by a Bruker Vertex V70v instrument.The spectra were acquired at a 2 cm −1 resolution and averaged over 64 scans.Typically, an amount of about 10 mg of zeolite was pressed into thin wafers with a diameter of 13 mm and placed inside a controlled-environment infrared transmission cell.Before measurement, the zeolite wafer was firstly heated to 823 K at a rate of 2 K min −1 in artificial air.Then, the cell was outgassed at the final temperature until the residual pressure was below 5 × 10 −5 mbar.A background IR spectrum was recorded.For CO adsorption, the sample was cooled to 77 K and CO was introduced into the cell via a sample loop connected to a Valco six-port valve.After each dosage, a spectrum was recorded at 77 K.
NMR spectroscopy. 27Al Nuclear Magnetic Resonance (NMR) spectra were measured using a 11.7 Tesla Bruker DMX500 NMR spectrometer operating at 132 MHz.The NMR experiments were performed using a Bruker Triple Channel 2.5 mm MAS probe head spinning at 25 kHz.Saturated AlĲNO 3 ) 3 solution were used for 27 Al NMR shift calibration.

Catalytic activity measurements
The catalytic activity of ZSM-5 zeolites in the MTH reaction was determined in a quartz tubular fixed-bed reactor with an inner diameter of 4 mm.Typically, the proton form of ZSM-5 zeolite was pressed and sieved into 250-425 μm particles.Prior to the reaction, the sample was calcined in the reactor at 823 K in 20 vol% O 2 in He (30 mL min −1 ) for 4 h.The methanol-to-hydrocarbons reaction was performed at 673 K. Methanol (Merck, 99%) was introduced to the reactor by passing a He flow of 30 mL min −1 through a thermostated saturator.The weight-hourly space velocity (WHSV) of methanol was kept at 6 h −1 .The product effluent was analyzed online by gas chromatography (an Interscience Compact GC equipped with TCD and FID detectors with RT-Q-Bond and Al 2 O 3 /KCl columns).Catalytic lifetime is defined as the time to reach 50% of methanol conversion.Dimethyl ether (DME) was considered as a reactant. 10

Influence of CTA concentration
We first optimized the synthesis of mesoporous ZSM-5 zeolite in the KOH/SiO 2 /CTA system and varied the H 2 O/CTAOH ratio.Fig. 1 shows that crystalline ZSM-5 zeolite can be obtained after 6 days autoclaving at 413 K with a molar H 2 O/ CTAOH ratio in the 800-3200 range.Without CTA, only amorphous silica and a small fraction of α-quartz was obtained.The broad feature in the small-angle region of the XRD patterns, observed for all zeolites, is too diffuse to be correlated to any sort of symmetry although it hints at partial order at the mesoscale.The order increases with rising CTA concentration.At the highest CTA concentration, crystallization did not occur and only amorphous silica was formed.
The SEM images in Fig. 2A show substantial differences in the morphology among the materials.Without CTA in the gel, the obtained material exhibits two morphologies, namely that of nanolayers and nanoparticles, which are assumed to be This journal is © The Royal Society of Chemistry 2017 related to α-quartz 39 and amorphous silica, respectively.The three zeolites have the morphology of agglomerated nanocrystals.Increasing the surfactant CTAOH concentration in the synthesis gel led to a decreased crystal size.This emphasizes the role of CTA as mesoporogen during crystallization.In Ar physisorption (Fig. 2B), the ZSM-5 zeolites MFI(2.5CTA,K, 0.95Al) and MFI(5CTA, K, 0.95Al) display a clear hysteresis loop and a climbing slope at the intermediate pressure range.The loop does not close until the relative pressure is quite close to the saturation pressure.The hysteresis is more pronounced with increasing CTA concentration in the gel.According to IUPAC classifications, the two isotherms are of the IV shape with a H4 hysteresis loop, 40,41 which is generally attributed to a hierarchical porous material containing both micropores and mesopores.The strong uptake at low relative pressure certifies the presence of micropores. 40Differently, the zeolite MFI(1.25CTA,K, 0.95Al) has a type I isotherm.The limited Ar uptake after the initial uptake in the micropores indicates the low external/mesopore surface area.As common estimations for the pore size distribution (PSD) such as the BJH method are considered unreliable for isotherms containing H4-type hysteresis loops, 40 we employed the NLDFT method assuming slitshaped pores without regulation.A distinct peak at ~0.53 nm in the PSDs of all the zeolites (Fig. 2C) corresponds to the pore size of ZSM-5 zeolites.There is also a wide distribution of larger pores, stretching into the mesopore range up to 40 nm.The corresponding textural properties are listed in Table 2.The total pore volume and the mesopore volume of the zeolites follow the sequence: MFI(1.25CTA,K, 0.95Al) < MFI(2.5CTA,K, 0.95Al) < MFI(5CTA, K, 0.95Al), indicating the importance of CTA for generating mesopores in zeolites.Consistent with the high crystallinity of these three samples, their micropore volume is similar.Both the isotherms and shape of the PSDs fit our SEM analysis, emphasizing that the secondary set of pores in the zeolites originates from voids between intergrown nanocrystals.The three HZSM-5 zeolites were evaluated as catalysts for the MTH reactions (Fig. 2D).Details including the product distribution after 1 h time on stream are listed in Table 3.The catalytic performance of bulk-ZSM-5 with similar Al content (Table 2) was included for comparison.Methanol conversion was complete for all the zeolites at the beginning of the reaction.The lifetime of the zeolites in MTH reaction follows the sequence: bulk-ZSM-5 < MFI(1.25CTA,K, 0.95Al) < MFI(2.5CTA,K, 0.95Al) < MFI(5CTA, K, 0.95Al), indicating that the additional porosity strongly enhances the catalyst lifetime.3][44] Although the exact nature of the "hydrocarbon pool" species in the MTH reaction remains unclear, [45][46][47][48] it is widely accepted that ethylene selectivity can be used for assessing the importance of the propagation via polymethylated benzenes, while C 4+ selectivity is considered as an indicator for the degree of propagation via the olefins-based cycle. 10,49A salient detail noted from the data in Table 3 is that the C 4+ /ethylene ratio of the ZSM-5 zeolites increased in the order: MFI(1.25CTA,K, 0.95Al) < MFI(2.5CTA,K, 0.95Al) < MFI(5CTA, K, 0.95Al).Thus, the olefins-based cycle appears to become more important with increasing mesoporosity.We tentatively attribute this to a shorter intracrystalline residence time of aromatics with decreasing crystalline domain size.The increasing mesoporosity is due to a smaller crystalline domain size.

Influence of base
Fig. 3A and B respectively show the small-and wide-angle XRD patterns of the as-synthesized materials using different bases.Similar with the standard synthesis procedure, the XRD pattern of the sample synthesized in the presence of RbOH instead of KOH is characteristic for MFI zeolite.The electron microscopy images (Fig. 3C and D) show that the MFI(5CTA, Rb, 0.95Al) sample is made up from aggregates of MFI nanocrystals.The Ar physisorption isotherm in Fig. 4A is of type IV with a H1 hysteresis loop.According to literature, such hysteresis loop is often associated with porous materials exhibiting a narrow distribution of relatively uniform cylindrical-like pores. 40,41In accordance with this, the PSD of this material (Fig. 4B) shows a sharp peak centered at about 3.75 nm in the mesopore range.The textural properties collected in Table 2 show that the hierarchical ZSM-5 possesses higher total pore volume and mesopore volume in comparison with the bulk-ZSM-5 zeolite.On the other hand, the micropore volumes of these two zeolites are comparable, justifying the conclusion that the crystallinity of MFI(5CTA, Rb, 0.95Al) is high.Important for our later comparison of the catalytic performance of these samples in the MTH reaction, Table 2 shows that the MFI(5CTA, Rb, 0.95Al) possesses similar framework Al content as the bulk-ZSM-5 sample.illustrates that the MFI(5CTA, Rb, 0.95Al) has a longer lifetime in MTH reaction than the bulk-ZSM-5 zeolite, which is mainly due to the hierarchical structure of the zeolite in line with earlier findings for mesoporous ZSM-5 synthesized by V meso e (cm 3 g −1 ) V micro, NLDFT f (cm standard procedure. 10Importantly, compared with bulk-ZSM-5, the higher C 4+ /ethylene ratio of MFI(5CTA, Rb, 0.95Al) in the product selectivities (Table 3) indicates the higher contribution of the olefins-based cycle in methanol conversion.Interestingly, although with substantial mesoporosity, the MFI(5CTA, Rb, 0.95Al) displays much shorter lifetime than MFI(5CTA, K, 0.95Al) synthesized in the presence of KOH.When the same syntheses were carried out with NaOH or CsOH in the gel, the XRD patterns of the obtained materials were that of amorphous silica. 50The use of LiOH as base resulted in the mixture of amorphous silica and lithium  metasilicate. 51The lithium metasilicate part consists of nanorods with a thickness around 50 nm.
A tentative mechanism for the growth of these hierarchical zeolites in the presence of different bases is shown in Fig. 5.
Upon ageing the gel at room temperature, an amorphous silica-alumina precursor is formed in which the negatively charged silicate surface is compensated by alkali and CTA cations. 52It has been demonstrated before that, compared  with Cs + and Li + , K + and Rb + favor dissolution of silicate species from amorphous silica to form monomeric silicate species. 53,54We argue that (super)saturation of soluble (monomeric and oligomeric) silicate species will therefore occur easier and so does nucleation. 54As discussed earlier, nucleation likely involves the interaction of silicate species with the quaternary ammonium head group of CTA.The hydrophobic tails then have the effect of interrupting zeolite growth, resulting in final hierarchical ZSM-5 zeolite.Another aspect of the work of Van Santen and co-workers is that TMA also slows silica dissolution.This explains the recalcitrance to crystallization at high CTA concentration in our study.
To further support the hypothesis that nucleation is indirectly inhibited by the stabilization of the silica-alumina precursor by Li + , Na + and Cs + ions, a small amount of HZSM-5 seeds was added to the synthesis gel (Fig. 5). 55From the XRD patterns in Fig. 6, we can see that in all the three cases ZSM-5 zeolite was obtained after 6 days of hydrothermal synthesis.Interestingly, the morphologies of these three materials are quite different.MFI(5CTA, Li, 0.96Al, seed) contains ZSM-5 particles and certain impurities of rod-like lithium metasilicate.MFI(5CTA, Na, 0.96Al, seed) is composed of aggregated nanoparticles (<50 nm), while the MFI(5CTA, Cs, 0.96Al, seed) zeolite is not uniform in morphology, containing nanolayers and nanoparticles.Correspondingly, the catalytic performance of these three materials (H form) in MTH reaction differs significantly.MFI(5CTA, Na, 0.96Al, seed) had a lifetime as high as 89 h.Although initial methanol conversion reached 97%, the MFI(5CTA, Cs, 0.96Al, seed) zeolite started to deactivate already after 5 min time on stream.MFI(5CTA, Li, 0.96Al, seed) only converted 42% of methanol in the initial time on stream, and its catalytic activity decreased dramatically in 24 h reaction.

Influence of Al content
We also varied the Al content in the synthesis gel.XRD shows that without Al in the gel phase-pure ZSM-48 zeolite is obtained.This zeolite has the *MRE topology comprised of a tubular pore system with pore diameter of 0.56 nm × 0.56 nm. 56,57The corresponding SEM (Fig. 8A and B) and TEM (Fig. 8C) images show that the obtained ZSM-48 zeolite is composed of aggregated nanowires with a thickness of about 20 nm.According to the database of the Structure Commission of the International Zeolite Association (IZA-SC), both MFI and *MRE frameworks contain the composition building unit of mel.Besides, the MFI structure contains mor (t-tes), cas and mfi (t-pen) units, while the *MRE topology contains imf (t-imf-7) and afi (t-afi) units.These units are shown in Fig. 9.We hypothesize that under our synthesis conditions, in the initial nucleation stage of zeolite formation, the presence of Al is necessary for forming part of/all mor (t-tes)/cas/ mfi (t-pen) units, which results in further MFI zeolite growth.Instead, in the absence of Al the units of imf (t-imf-7) and afi (t-afi) are formed for further *MRE zeolite growth.Fig. 10 displays the Ar physisorption isotherm and corresponding PSD of calcined ZSM-48.A type IV isotherm can be seen with a distinct H1 hysteresis loop at very narrow relative pressure range between p/p 0 = 0.35 and 0.65, which indicates a narrow distribution of mesopores. 40A weak uptake at low relative pressure is indicative of the low micropore volume.In line with this, there is no clear feature related to micropores in the PSD.A distinct peak centered around 3.4 nm can be ascribed to the uniform voids between nanorods, which is inconsistent with the display of a hysteresis loop in a narrow relative pressure range.The corresponding textural properties are listed in Table 2.The nano-rod ZSM-48 zeolite has a total pore volume and a mesopore volume of 0.40 cm 3 g −1 and 0.35 cm 3 g −1 , respectively.The BET surface area is about 234 m 2 g −1 .The micropore volume is only 0.02 cm 3 g −1 .
Interestingly, the XRD pattern confirms that the addition of a small amount of Al in the gel (Si/Al = 200) already changed the outcome of the synthesis towards formation of ZSM-5 zeolite instead of ZSM-48.The MFI(5CTA, K, 0.24Al) sample only contains 0.31 wt% of Al according to elemental analysis, with about half of it ending up in framework positions after calcination (Table 2).SEM (Fig. 8D) shows that MFI(5CTA, K, 0.24Al) is not uniform in particle size.Ar physisorption presents a clear H4 hysteresis loop in the type-IV isotherm with a narrow PSD in the mesopore range centered at about 3.4 nm (Fig. 10A and B).The distinct peak at 0.53 nm is in line with the pore size of MFI topology.A salient detail noted from the data in Table 2 is that MFI(5CTA, K, 0.24Al) zeolite possesses a high mesopore volume of 0.14 cm 3 g −1 .The micropore volume is 0.13 cm 3 g −1 , similar with that of bulk-ZSM-5.Due to the low Al content, the methanol conversion was not complete for this hierarchical ZSM-5 at the start of the MTH reaction, although it presented a good stability (Fig. 10C).This may be due to the lower acid site density which implies a lower rate of secondary reactions leading to coke. 43Secondly, the hierarchical pore system leads to the enhanced utilization of Brønsted acid sites in the inner crystal particles. 50,58Similar with the bulk-ZSM-5, the main products were ethylene, propylene and C 4+ products after 1 h time on stream.The product distribution was shifted to propylene and aromatics instead of ethylene and higher olefins.
Setting the Si/Al ratio to 20 in the synthesis gel, the obtained MFI(5CTA, K, 2.38Al) material shows a broad peak between 15-35°in XRD pattern (Fig. 7), which is typical for amorphous silica. 50The corresponding SEM image confirms that MFI(5CTA, K, 2.38Al) consists of nanoparticles.A tentative explanation is that the high Al content of the solid precursor binds the cations strongly so that dissolution is slowed down and therefore no supersaturation as well as nucleation is reached.To confirm this hypothesis, a small amount of ZSM-5 seeds was added into the gel.As expected, the obtained material shows the characteristic XRD pattern of MFI zeolite (Fig. 11A).Importantly, the broadening of the reflections between 22-25°are indicative of the small crystal domain size. 9In agreement with this, the SEM images (Fig. 11B) show that the zeolites are aggregated nano-needles with a uniform thickness about 20 nm.The proton-form of this zeolite shows a distinct H1 type hysteresis loop in the Ar physisorption isotherm (Fig. 11D), indicating the presence of uniform mesopores.The PSD displays two peaks centered at 0.53 nm and 4.0 nm, which can be related to MFI micropores and uniform voids between the nano-needles, respectively.The corresponding textural properties are listed in Table 2.
Consistent with its high crystallinity, the micropore volume of MFI(5CTA, K, 2.38Al, seed) is similar with that of bulk-ZSM-5.In contrast, the hierarchical zeolite contains  significantly higher mesopore volume (0.24 cm 3 g −1 ) and total pore volume (0.37 cm 3 g −1 ) than its bulk counterpart.According to 27 Al NMR spectroscopy, most of the Al ends up in the zeolite framework position for such high Al content.
Compared with bulk-ZSM-5, MFI(5CTA, K, 2.38Al, seed) shows pronounced stability in the MTH reaction.The deactivation only occurs after 40 h time on stream.Especially, the aromatics selectivity is much higher than for bulk-ZSM-5.This is ascribed to the higher reaction rates of oligomerization, cyclization and dehydrogenation of olefins in zeolite channels that contain more Brønsted acid sites. 44

Influence of CTA counter-ion
We also verified the outcome of the synthesis when CTAOH was replaced by CTABr.The wide-angle XRD patterns (Fig. 12B) confirm that pure MFI zeolite was obtained after 8 days hydrothermal synthesis using CTABr as SDA.Compared with the standard recipe in which highly crystallized MFI zeolite was obtained after 6 days hydrothermal synthesis using CTAOH as the SDA, the application of CTABr as SDA slows the crystallization slightly and about 8 days are required to obtain highly crystalline zeolite.The broad peak in the small-angle XRD patterns (Fig. 12A) evidence the partially ordered mesoporosity of MFI(CTABr, K, 0.96Al).SEM (Fig. 12C) and TEM (Fig. 12D) images show that the zeolite consists of agglomerated nano-particles with dimensions in the range of 20-50 nm.These images also show mesoporous voids between the primary particles.We mention that in establishing solid certainty on the validity of this result, we have reproduced the synthesis on 5 occasions, using different and sterile autoclaves for each experiment.It turns out that only 2 out of these 5 occasions succeeded, while the other 3 cases resulted in the formation of amorphous silica.Differently, in the case of using CTAOH as SDA, we always obtained the desired crystalline zeolite material.As seen in Fig. 13, when CTABr is used as SDA, variation of the parameters results in similar materials as obtained   Fig. 14 shows the hydroxyl and CO stretch regions in the FTIR spectra of bulk-ZSM-5 and MFI(5CTABr, K, 0.96Al) recorded at 77 K.The two zeolites show an OH stretching band around 3300 cm −1 , characteristic for strongly acidic bridging hydroxyl groups that are perturbed by CO. 59,60 They involve, for both cases, a red shift of ∼316 cm −1 with respect to unperturbed bridging OH groups. 10The equal red shift for these two materials implies that the Brønsted acid sites are similar in strength.In the carbonyl stretching region, two bands at 2175 cm −1 and 2137 cm −1 can be observed, which belong to CO adsorption on Brønsted acidic sites and physisorbed CO, respectively. 10The frequency of CO coordinating to the Brønsted acid sites does not depend on the morphology of these two ZSM-5 zeolite.
Ar physisorption isotherm and PSD for MFI(5CTABr, K, 0.96Al) zeolite are shown in Fig. 15.The additional presence of mesoporosity in the zeolite is evident from the H4 type hysteresis loop in the Ar physisorption isotherm.The strong uptake at low relative pressure confirms the presence of micropores.The PSD indicates the presence of mesopores, next to the micropore system of ZSM-5.Table 2 further shows that this hierarchical zeolite has very favorable textural properties and, most notably, a high mesopore volume (0.11 cm 3 g −1 ).The potential of this mesoporous ZSM-5 zeolite in acid catalysis was evaluated by determining its catalytic performance in the MTH reaction.Fig. 15C shows methanol con-version as function of time on stream for MFI(5CTABr, K, 0.96Al) and bulk-ZSM-5.The hierarchical ZSM-5 zeolite showed much longer lifetime (46 h) than bulk-ZSM-5 (19 h).As the elemental analysis and 27 Al NMR data confirm that these samples contain a similar amount of framework Al (Table 2), the greatly improved performance can be attributed to the smaller crystal domains in the hierarchical zeolite, effectively reducing mass transport limitations.The product distribution for MFI(5CTABr, K, 0.96Al) is similar with the one observed for bulk-ZSM-5 after 1 h time on stream, in which the main products are ethylene, propylene and C 4+ hydrocarbons.

Conclusions
In this work, we explored the conditions under which hierarchical ZSM-5 zeolite can be obtained in a one-pot synthesis procedure using CTA as the only template.A key aspect in these syntheses is that a mesoporous silica-alumina precursor is obtained initially which can transform to mesoporous zeolite through dissolution of silicate species at temperatures conducive to zeolite nucleation in the presence of CTA via a dissolution-recrystallization mechanism.We varied the base (LiOH, NaOH, KOH, RbOH and CsOH), the H 2 O/CTA ratio, the Al content and the counter ion of CTA (Br − or OH − ).
Mesoporous ZSM-5 zeolite can be obtained in this way in the KOH/CTAOH/SiO 2 system at H 2 O/CTA ratios in the 800-3200 range.Without CTAOH, a mixture of amorphous silica and α-quartz was obtained, while a too high H 2 O/CTA did not allow fast enough dissolution of silicate species, consistent with the known role of quaternary ammonium cations in stabilizing silica.While KOH and RbOH allowed obtaining hierarchical ZSM-5 zeolite in this way, the use of NaOH and CsOH as base mainly led to amorphous silica.That is a too small or too large alkali cation impedes silica dissolution.
For LiOH, this was also the case with an additional lithium silicate being obtained in that particular case.The conclusion that solubilisation of silica is too slow with LiOH, NaOH and CsOH is corroborated by the finding that seeding the synthesis with ZSM-5 resulted in formation of mesoporous ZSM-5 zeolites in all cases.Our results also point out the necessity of Al in the synthesis gel for crystallizing ZSM-5 zeolite.Without Al, only ZSM-48 was obtained.Setting the Si/Al ratio in the 50-200 range in the gel resulted in hierarchical ZSM-5.Higher Al content in the gel (Si/Al = 20) did not allow obtaining zeolite, although again the use of seeds facilitated ZSM-5 crystallization in the form of nano-needles with uniform thickness.This result indicates an important role of Al concentration in zeolite nucleation.Finally, replacing CTAOH with CTABr led to similar results although the reproducibility of such syntheses was found to be lower.A highly crystalline, free from extraframework Al and hierarchical ZSM-5 synthesized from a gel with KOH as base, H 2 O/CTAOH 800, Si/Al = 50 and CTAOH as the template displays the highest catalytic performance in the MTH reaction, clearly outperforming bulk ZSM-5.An important implication of this work is that care has to be taken when exploring the use of organic templates in the synthesis of hierarchical zeolites using NaOH as mineralizing base.Stabilizing an amorphous silica precursor by Na + at temperatures at which zeolite nucleation can in principle proceed may obscure the potential of organic surfactants to direct silicate structures at the micro-and mesoscale.
Fig.3Aand B respectively show the small-and wide-angle XRD patterns of the as-synthesized materials using different bases.Similar with the standard synthesis procedure, the XRD pattern of the sample synthesized in the presence of RbOH instead of KOH is characteristic for MFI zeolite.The electron microscopy images (Fig.3C and D) show that the MFI(5CTA, Rb, 0.95Al) sample is made up from aggregates of MFI nanocrystals.The Ar physisorption isotherm in Fig.4Ais of type IV with a H1 hysteresis loop.According to literature, such hysteresis loop is often associated with porous materials exhibiting a narrow distribution of relatively uniform cylindrical-like pores.40,41In accordance with this, the PSD of this material (Fig.4B) shows a sharp peak centered at about 3.75 nm in the mesopore range.The textural properties collected in Table2show that the hierarchical ZSM-5 possesses higher total pore volume and mesopore volume in comparison with the bulk-ZSM-5 zeolite.On the other hand, the micropore volumes of these two zeolites are comparable, justifying the conclusion that the crystallinity of MFI(5CTA, Rb, 0.95Al) is high.Important for our later comparison of the catalytic performance of these samples in the MTH reaction, Table2shows that the MFI(5CTA, Rb, 0.95Al) possesses similar framework Al content as the bulk-ZSM-5 sample.Fig.4C

Fig. 9
Fig. 9 Composite building units of *MRE and MFI zeolites according to database of the Structure Commission of the International Zeolite Association.

Fig. 13
Fig. 13 Phase diagrams obtained using CTABr as SDA by varying parameters of (A) Al content, (B) type of base, and (C) CTA concentration.*Success rate: 2 out of 5 synthesis.

Fig. 14 (
Fig. 14 (Left) Hydroxyl and (right) CO stretch regions in the FTIR spectra of bulk-ZSM-5 (a and b) and MFI(5CTABr, K, 0.96Al) (c and d, H form) recorded at 77 K.The spectra were normalized by the weight of the catalysts.

Table 2
Textural properties of the zeolites SampleAl content a (%) Al framework b

Table 3
Lifetime and product selectivities of ZSM-5 zeolite catalysts for the MTH reaction after 1 h time on stream a Time to reach methanol conversion of 50%, DME was considered as reactant.WHSV = 6 h −1 ; T = 673 K.