Cationic xylan–METAC copolymer as a flocculant for clay suspensions

Abstract

The work presented herein focused on the flocculation of kaolin and bentonite clay suspensions using cationic copolymerized xylan under controlled conditions. Cationic xylan-2-(methacryloyloxy)ethyl]trimethyl ammonium chloride (METAC) copolymers were produced under the conditions of pH 7, 3 h reaction time, 80 °C and 2 or 3 mol mol−1 METAC/xylan ratio. The charge densities of the produced cationic xylan copolymers, CMX1, and CMX2 were +1.8 and +2.4 meq. g−1 while their molecular weights were 88 986 and 102 545 g mol−1, respectively. The attachment of METAC to xylan was confirmed by elemental and gel permeation chromatography analyses. CMX2 was a more efficient flocculant than CMX1 as it adsorbed and removed more clay particles from the clay suspensions. CMX2 also changed the zeta potential and turbidity of the clay suspensions more remarkably than CMX1, which was attributed to its higher charge density and molecular weight. CMX2 was more efficient in flocculating bentonite than kaolin suspensions. The presence of CMX on the clay particles was confirmed by Fourier Transform Infrared Spectroscopy (FTIR) analysis. The size of kaolin particles increased from 3.2 to 9.8 and 11.7 μm, and that of bentonite particles from 5.8 to 13.8 and 15.5 μm by having 16 mg L−1 of CMX1 and CMX2 copolymers in the clay suspensions, respectively. The reversibility of the flocculation process was assessed with a photometric dispersion analyzer. Furthermore, unmodified xylan was ineffective in flocculating clay particles.

Graphical abstract: Cationic xylan–METAC copolymer as a flocculant for clay suspensions

Article information

Article type
Paper
Submitted
27 Feb 2016
Accepted
11 Apr 2016
First published
14 Apr 2016

RSC Adv., 2016,6, 40258-40269

Cationic xylan–METAC copolymer as a flocculant for clay suspensions

S. Wang, M. K. R. Konduri, Q. Hou and P. Fatehi, RSC Adv., 2016, 6, 40258 DOI: 10.1039/C6RA05223A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements