The crystallisation of copper(II) phenylphosphonates†

The crystal structures and syntheses of four different copper(II) phenylphosphonates, the monophenylphosphonates α-, β-, and γ-Cu(O3PC6H5)·H2O (α-CuPhPmH (1) β-CuPhPmH (2) and γ-CuPhPmH (3)), and the diphosphonate Cu(HO3PC6H5)2·H2O (CuPhP2mH (4)), are presented. The compounds were synthesized from solution at room temperature, at elevated temperature, under hydrothermal conditions, and mechanochemical conditions. The structures of α-CuPhPmH (1) and CuPhP2mH (4) were solved from powder X-ray diffraction data. The structure of β-CuPhPmH (2) was solved by single crystal X-ray analysis. The structures were validated by extended X-ray absorption fine structure (EXAFS) and DTA analyses. Disorder of the crystal structure was elucidated by electron diffraction. The relationship between the compounds and their reaction pathways were investigated by in situ synchrotron measurements.


Introduction
Metal phosphonates can form a wide range of structural architectures, ranging from isolated complexes to three-dimensional frameworks. The structural variability results in different properties and applications. [1][2][3][4] Molecular metal phosphonates are of interest due to their catalytic and magnetic properties. The higher dimensional structures are coordination polymers (CP 5 ) and are candidates for classical application in gas storage and catalysis. [6][7][8][9] The materials can be used as proton conductors and for the modification of surfaces because of their polar pores and different organic groups. [10][11][12][13][14][15][16] Zirconium(IV) phenylphosphonate was one of the first described metal phosphonates. 17 Cunningham et al. showed different syntheses of divalent metal phenylphosphonates with the general formula M(II)(O 3 PC 6 H 5 )·H 2 O. 18 The authors identified four polymorphs of copper(II) phenylphosphonate monohydrate (CuPhPmH), but they were not able to solve the structures from the obtained powder diffraction data. A layered structure and an octahedral coordination of the central metal were proposed. Mallouk et al. were able to solve the structure of the manganese phenylphosphonate monohydrate and could show that the divalent metal phenylphosphonates are isomorphic. 19 An exception is a CuPhPmH compound, characterized by Clearfield et al. 20 Here, the copper-ion is coordinated in a distorted tetragonal pyramid. Nowadays, metal phosphonate chemistry is intensively studied. Highthroughput syntheses were developed. 21 Structure solutions are performed increasingly from powder X-ray diffraction (PXRD) data. 12,13,22,23 Recently, mechanochemical syntheses of metal phosphonates were described. [23][24][25] Here, we present the syntheses, characterization, and crystal structures of three polymorphs of CuPhPmH (1-3) and a copper(II) phenylphosphonate containing two monodeprotonated phenylphosphonate ligands Cu(HO 3 PC 6 H 5 ) 2 ·H 2 O (CuPhP2mH (4)). The existence of the three polymorphs was described by Cunningham et al. 18 The compounds were named α-CuPhPmH (1), β-CuPhPmH (2), and γ-CuPhPmH (3). The polymorph γ-CuPhPmH (3) was described by Clearfield et al. 20 We present different synthesis routes including solventbased synthesis at ambient conditions, at elevated temperatures, hydrothermal, and mechanochemical synthesis. The crystal structures were solved from powder and single crystal XRD data. The structures were further characterized by extended X-ray absorption fine structure (EXAFS) and DTA analyses. Some of the polymorphs showed diffuse scattering in single-crystal electron diffraction data which is one of the reasons why the crystal structures were unresolved so far. Therefore, we put a particular focus on analysing the disorder in the structures. Finally, we also report on mechanistic studies conducted in situ using synchrotron XRD. † Electronic supplementary information (ESI) available. CCDC 1490687-1490689.
For ESI and crystallographic data in CIF or other electronic format see DOI: 10 (2). 400 mg (2 mmol) copper(II) acetate monohydrate and 316 mg (2 mmol) of phenylphosphonic acid were dissolved separately in 15 mL of a HCl solution (0.5 mol L −1 ). The clear solutions were mixed and 500 mg of urea was dissolved in this mixture. After ten minutes of stirring, the clear solution was filled in a teflon lined autoclave with a volume of 45 mL and heated in a furnace for three days at 150°C. Under these conditions the urea is hydrolysed and the generated NH 3 increases the pH of the solution. 20  . For the synthesis, a vibration ball mill (Pulverisette 23, Fritsch GmbH, Germany) was used. 296.3 mg (1.5 mmol) of copper(II) acetate monohydrate, 703.7 mg (4.5 mmol) of phenylphosphonic acid and two stainless steel balls (4 g, diameter 10 mm), were added in a 10 mL stainless steel vessel and ground together for 15 min at 50 Hz. The resulting light blue powder was washed with acetone and filtrated. After drying in air 529 mg (yield = 89%, with regard to Cu) of a white powder were obtained. CHN analysis (calculated values in brackets): C: 36.72% (36.42%), H: 3.62% (3.57%), N: 0.08% (0%).

Analytical techniques
PXRD patterns were collected with Cu K α radiation (λ = 1.54056 nm) on a D8 Discover diffractometer (Bruker AXS, Germany) equipped with a Lynxeye detector. Samples were measured in transmission geometry in a 2θ range from 4°to 60°with a step size of 0.009°. For structure solution the measurement time per step was 20 s.
Single crystal XRD measurements were performed on a D8 Venture diffractometer (Bruker AXS, Germany) using Mo K α radiation (λ = 0.71073 nm) monochromatized by a graphite crystal.
In situ and ex situ investigations of all reactions using synchrotron XRD were performed at the µSpot beamline (Bessy-II, Helmholtz Centre Berlin for Materials and Energy, Berlin, Germany). 26 The scattered intensities were collected with a two-dimensional MarMosaic CCD detector with 3072 × 3072 pixels ( pixel size 73 µm). In situ investigations of the mechanochemical reactions were performed as described elsewhere. 25 Further details are given in the ESI. † In situ investigations of precipitation reactions were conducted with the stopped-flow module SFM3000 (Bio-Logic SAS, France) equipped with a capillary head. A detailed description and a representation of the setup is given in the ESI. † Two modes of operation could be used. (i) Certain points in time of the reaction were investigated while the reaction mixture was flowing constantly through the capillary. (ii) Scan measurements over a longer time-period were taken with the reaction mixture stored in the horizontal capillary holder. All obtained scattering images were processed employing an algorithm of the computer program FIT2D. 27 For the graphical representations, scattering vector (q) values were transformed to the diffraction angle 2θ for Cu K α radiation to provide a direct comparison to results obtained in laboratory PXRD experiments.
The EXAFS measurements were performed at the BAMline (Bessy-II, Helmholtz Centre Berlin for Materials and Energy Berlin, Germany). 28 The experimental conditions and data processing are described in the ESI. † TEM work was done using a FEI TECNAI F30 TEM operated at 300 kV with a field emission gun. Electron diffraction tomography data was collected using the automated acquisition module described elsewhere. 29 The data was collected using a high-tilt Fischione tomography holder within the tilting range of ±60°, with a tilt step of 1°, at room temperature and at liquid nitrogen temperature. During the acquisition the electron dose rate was kept as low as 1 e Å −2 s −1 . The data was processed using the dedicated software ADT3D (Nanomegas, Brussels, Belgium). Electron diffraction patterns were simulated using the eMap software (Analitex, Stockholm, Sweden).

Structure solution and refinement
The structure solution of α-CuPhPmH (1) was conducted from PXRD data. The powder data were indexed using the indexing routine of the software TOPAS (version 5, Bruker AXS, 2014). The resulting lattice constants are similar to crystal data of a group of isomorphous compounds with the formula M(II) (O 3 PC 6 H 5 )·H 2 O. The structure of the new compound was solved starting from the structure of Fe(O 3 PC 6 H 5 )·H 2 O. 22 Simulated annealing was conducted in EXPO2014. 30 The Rietveld refinement was performed using TOPAS. The final Rietveld and difference plots are shown in Fig. 1a. Two possible positions of the phenyl rings were detected.
The structure solution of β-CuPhPmH (2) was conducted from single crystal XRD data. A blue plate like crystal of the product was measured at 180 K. The data reduction was performed using the Bruker AXS SAINT and SADABS packages. The structure was solved using direct methods and refined by full-matrix least squares calculation using SHELX. 31,32 Anisotropic thermal parameters were refined for non-hydrogen atoms. The hydrogen atoms were treated isotropically with U iso = 1.2 times the U eq value of the parent atom. A comparison of the measured PXRD pattern with the calculated PXRD pattern from the crystal data for that structure is shown in Fig. 1b.
The structure solution of CuPhP2mH (4) was conducted from PXRD data. The diffraction pattern was indexed using the N-TREOR program implemented in the EXPO software. The structure was solved using the simulated annealing routine implemented in DASH. 33 The position of the copper atom was fixed at (0, 0, 0). The Rietveld refinement was performed using TOPAS. The final Rietveld and difference plots are shown in Fig. 1c. Selected bond length and angles for all new structures are shown in Tables S1-S3. † Missing hydrogen atoms were inserted according to the directions of the hydrogen bonds.
The crystal structures were validated by EXAFS measurements. The EXAFS data for all compounds are shown in Fig. S3-S6, † and the fit parameters are shown in Tables S3-S6 † for compound (1)- (4).
For all compounds DTA-TG measurements were performed. In all cases a loss of the crystal water could be obtained. The data is given in Fig. S8-S11. †

Structure description
The structure of α-CuPhPmH (1) is shown in Fig. 2a along the c-axis. The structure is isomorphic to the group of divalent metal phenylphosphonate monohydrates M(II)(O 3 PC 6 H 5 )·H 2 O with M = Mn, 19 Fe, 22 Co, 34 Ni, 35 Zn, 36 and Cd. 37 The Cu 2+ -ion is coordinated by five oxygen atoms of four different phenylphosphonate ligands and one oxygen atom of a water molecule. The result is a strongly distorted octahedral coordination.  are included in the coordination. Two of them chelate one Cu 2+ion and bridge at the same time two other Cu 2+ -ions. The third oxygen atom (O1) coordinates to another Cu 2+ -ion. Perpendicular to the layer, the phenyl rings are arranged alternating above and below the layer. The phenyl rings connect the layers via van der Waals forces. The orientation of the phenyl rings is disordered. There are two half-occupied positions, perpendicular to each other and rotated around the C1-P1 axis. The structure of β-CuPhPmH (2) is shown in Fig. 2b along the b-axis. It is related to the structure of γ-CuPhPmH (3), described by Clearfield et al. (see Fig. 2c). 20 The inner layer structure of both compounds is similar. The Cu 2+ -ion is coordinated by five oxygen atoms forming a distorted tetragonal pyramid. Three oxygen atoms in the plane and the one at the top stem from four different phenylphosphonate ligands. The coordination is completed by a water molecule. For β-CuPhPmH (2) the lengths of the Cu-O-bonds in the plane differ from 1.925(2) Å to 1.992(2) Å and at the top the bond length amounts to 2.343(2) Å.
The distortion of the pyramid becomes apparent from the values of the respective angles. The angles between one oxygen atom of the plane, the Cu 2+ -ion and the oxygen atom in the top range from 81.41(6)°to 109.26(6)°. Two of such pyramids build pairs. They share two oxygen atoms from two phenylphosphonate ligands and are connected via one edge. These Cu 2 O 8 -pairs are only connected by the phosphonate group. The lengths of the three P-O-bonds differ only in a small range from 1.527(2)-1.536(2) Å. All values are very similar to the structure data of γ-CuPhPmH (3).
The difference between the two structures is the position of the phenyl rings between the layers and the resulting different layer stacking. In β-CuPhPmH (2) the phenyl rings adopt only one orientation. Seen along the b-axis, the phenyl rings are tilted compared to the layer build by the CuO 5 -pyramids. The angle between the C1, P1 and an adjacent P1 atom is 82.13(7)°. The phenyl rings bound to the same layer are perpendicular to each other. Since the β-angle (91.750(2)°) is almost orthogonal, the length of the a-axis is approximately the layer distance. Table 1 Crystal data of the copper(II)-phenylphosphonates α-CuPhPmH (1), β-CuPhPmH (2), γ-CuPhPmH (3) and CuPhP2mH (4) (1)  γ-CuPhPmH (3) contains two kinds of layers. One layer is the same as described for β-CuPhPmH (2). For the second layer the described tilting of the phenyl ring is in the opposite direction. The comparable angles are 81.3(2)°for one kind of layer and 99.3 (2) for the other one. The layers are arranged in an alternating manner. As a result, the unit cell has a doubled volume and its symmetry is orthorhombic. Following the structure described by Clearfield et al. the distance between the layers is half of the c-axis. Consequently, this c-axis is about twice the size of the a-axis of the unit cell of β-CuPhPmH (2). The other two axes are very similar.
The structure of CuPhPmH2 (4) is shown in Fig. 2d along the c-axis. The Cu 2+ -ion is coordinated by six oxygen atoms stemming from four phenylphosphonate ligands and two water molecules. The resulting octahedron is only slightly dis- The stacking disorder in copper phenylphosphonates The presence of disorder in metal phenylphosphonates was already reported by Cao et al. 19 The appearance of weak additional reflections doubling the unit cell was assigned to an ordering of the phenyl rings. Attempts to refine the structure using a larger unit cell did not improve the structure refinement. Diffuse scattering was observed for different metal phenylphosphonates, 22,34-36 but no attempt to clarify possible structure models was undertaken.
The partial ordering of the phenyl rings should appear as background diffuse scattering between the Bragg reflections. 38 In contrast, the diffuse scattering observed in the diffraction data of phenylphosphonates appears as smeared reflections lines in the reciprocal volume. These effects are usually associated with stacking faults in a layered structure. Electron diffraction data of α-CuPhPmH (1) is shown in Fig. 3. Fig. 3b shows  Fig. 3c and d. One can see an alternating sequence of diffuse and discrete lines, so that the diffuse scattering is "extinct" for the rows h′k′l′ with h′ + l′ = 2n. So, the rows −2k′0, −2k′2 (Fig. 3c) and −3k′1, −3k′3 (Fig. 3d) do not bear the diffuse scattering.
So far the doubling of the unit cell does not make much sense as the structure can easily be reduced back to the initial basis; one needs to split the average structure into the two different conformations present in the new cell.
Packing of the phenyl rings can to some extent be approximated by the packing of benzene molecules. The benzene molecules create a sandwich configuration (as a result of π-π stacking), orthogonal T-shaped conformation, and a paralleldisplaced conformation. 39 The energy minimum for the sandwich conformation is reached at the intermolecular distance of 3.7-3.9 Å, the typical value for interplanar distance between the planar conjugated moieties. The T-shaped benzene molecular dimer is the most stable at the distance of 4.9-5.0 Å; here one molecule is looking into the plane of the other. This situation is realized in the β-CuPhPmH (2) structure.
Transferring this information to our system of the phenyl rings attached to a relatively rigid inorganic layer, we can say that if the phenyl rings are placed at distances close to 4 Å, they will try to stack parallel, if they are separated by 5 Å, they will form a T-shaped orthogonal packing. This situation is realized in the β-CuPhPmH (2), the neighbouring phenyl rings have a distance of 4.944 Å and 5.778 Å and are arranged at an angle of 84°. The structure does not show any unambiguity in the position of the phenyl rings and no diffuse scattering in the data. Approximately the same distance between the phenyl rings is realized in the structure of α-CuPhPmH (1): 4.796 Å and 5.659 Å, which allows proposing the same configuration of the phenyl rings: the T-conformation. Thus the disorder cannot be caused by the phenyl-ring arrangement within one layerthey all will be placed orthogonally to each other. Noticeably, the two adjacent layers have a well-defined rule on how they click to each other defined by the phenyl ring orientation (see Fig. 4b).
The orthogonal orientation of the rings allows a chemically sensible splitting of the two phenyls within a newly defined doubled unit cell of the α-CuPhPmH (1) structure. A layer element of the structure with orthogonally arranged phenyl rings is shown in Fig. 4a. The rings are arranged as alternating tilted left or right in the orthogonal manner. For simplicity, the tilting positions of the rings are color-coded as blue and green disks.
The top and the bottom layers of the rings are not in a direct contact. In principle two layer types can be realizedlayer type A with the mirrored sequence of the rings and layer type B with a half of a c-vector shifted sequence. An example of an irregular sequence of the layers ABAABA is shown in Fig. 4b. Note, that the clicking rule between the adjacent phenyl rings is welldefined as in the β-CuPhPmH (2) structure.
A simulated electron diffraction pattern of the model shown in Fig. 4b is presented in the Fig. 4c. The simulated diffraction pattern reproduces the general diffuse scattering distribution in the experimental data well: each of h + l = 2n rods consist of discrete reflections, while all of h + l ≠ 2n rods are diffuse (Fig. 3).
The disorder in the α-CuPhPmH (1) is essentially reduced to the random stacking of layers with a shift vector of [0.5 0.5 0] translation of the structure. This produces a diffuse scattering pattern in the reciprocal space with alternating diffuse and discrete reflection rows as described earlier.
A careful inspection of the diffuse scattering in γ-CuPhPmH (3) (Fig. 5) shows that in contrast to the α-CuPhPmH (1) phase, the rows with discrete reflections are not strictly discrete but possess a diffuse component. The cuts through the reciprocal space representing the −4kl and −3kl planes are shown in Fig. 5c and d. The rows −41l, −43l, −30l, −32l are completely diffuse, while the other rows show a discrete sequence with the fine diffuse content, breaking the h + l ≠ 2n extinction condition for diffuse scattering. Thus, apart from the [0.5 0.5 0] layers shift, another type of disorder must be present in the structure.
The structure of γ-CuPhPmH (3) can be described as a regular packing of two types of layers -A and B related by  gliding mirroring. One can easily imagine stacking faults in the structure caused by an irregular sequence of the layers. The interface between A and B layers is given by the average crystal structure and is optimal from the point of phenyl rings packing. The interface between the layers of the same type (AA and BB) has to be optimized by a layer shift in order to achieve the optimal packing of the phenyl groups. The shift with a vector of [0 0.034 0] at the AA and BB interfaces allowed the maintaining of the proper geometry of the phenyl rings between the layers. The sequence with a shift vector which is not a rational fraction of the unit cell creates a model which does not have any defined periodicity in the (a, b) direction. As a result all reflection rows in the simulated diffraction pattern (Fig. 5d) contain diffuse intensities along the c* direction.

Mechanistic studies of precipitation reactions
The finally formed product in precipitation reactions depends on the pH value of the reaction solution, the temperature and the solvent.
The synthesis of α-CuPhPmH (1) can be easily performed by the addition of an aqueous phenylphosphonic acid solution to an aqueous copper(II) acetate solution at room temperature. The product precipitates immediately. No precipitate can be obtained using copper(II) sulfate pentahydrate. The reason is the pH value of the copper(II) salt solutions. The basic acetate ion leads to a higher pH value (5.8) than the sulfate ion (4.2). The addition of a sodium hydroxide solution (10%) to the reaction mixture with copper(II) sulfate results consistently in an immediate precipitation of α-CuPhPmH (1). The existence of β-CuPhPmH (2) as a side product depends on the sodium hydroxide addition. A fast addition of a larger amount of the sodium hydroxide solution results in a higher ratio of β-CuPhPmH (2).
The product formation can also be influenced by the solvent. The reaction of 599 mg (3 mmol) copper(II) acetate monohydrate with 632 mg (4 mmol) phenylphosphonic acid in 60 mL of a 1 : 1 mixture of water and methanol was investigated by in situ synchrotron PXRD. Using the stopped-flow module and a custom-made extension the reaction mixture was inserted into a capillary and left for 15 min. The resulting PXRD patterns of the time dependent scan measurement are shown in Fig. 6. The first pattern shows only reflections of α-CuPhPmH (1) (e.g. 6.1°, 12.3°, 16.8°, 19.5°). During the next minutes, these reflections vanish and reflections of β-CuPhPmH (2) or γ-CuPhPmH (3) appear. The reflection of the final product at 17.7°appears after 1.00 min and increases in the next minutes. The two reflections of α-CuPhPmH (1) at 16.8°and 19.5°start to vanish after 2.15 min. No reflections of α-CuPhPmH (1) could be detected after 7.00 min of reaction time. In agreement with the investigated reaction pathway, a colour change of the precipitate from white to blue could be obtained in the lab synthesis. A comparison of the PXRD pattern of the final product with the calculated PXRD patterns of β-CuPhPmH (2) and γ-CuPhPmH (3) shows that it is more probably β-CuPhPmH (2), but the crystallinity is weak and a mixture of both phases, β-CuPhPmH (2) and γ-CuPhPmH (3), cannot be ruled out (Fig. S12 †).
The results indicate that in solution the formation of α-CuPhPmH (1) is kinetically favoured. The thermodynamic favoured product is γ-CuPhPmH (3). The balance between these three polymorphs is susceptible and can be influenced by the pH-value, using one starting material in excess, using methanol as solvent and by heating.
The synthesis of α-CuPhPmH (1) was investigated in situ using synchrotron PXRD and the SFM setup, described in the Experimental section. The first seconds of the reaction were investigated as specific points in time. The resulting powder patterns are shown in Fig. 7a for 1-10 s. A reflection at 5.0°c ould be detected in all measurements, suggesting the existence of an unknown intermediate. With increasing reaction time, the intensity of the reflection decreases. The unknown compound is probably a layered metal phosphonate, evident from the strong reflection at very low 2θ. A second reflection at 5.6°, observable at all points in time, suggests the intermediate formation of CuPhP2mH (4). Its intensity increases with time. At 1 s, 3 s, and 6 s a reflection at 6.1°indicates the formation of α-CuPhPmH (1). Since this reflection occurs in an irregular manner, α-CuPhPmH (1) seems to be formed spontaneously without being stable at this time in the reaction. Fig. 7b shows the results of the scan measurement over 45 min represented Following Ostwald's rule of stages, CuPhP2mH (4) has to be less stable than α-CuPhPmH (1). With 26.30 min the reac-tion time was much longer than known from the lab synthesis.
Here, the precipitate was separated by filtration after five minutes. A phase change after the separation is not probable, because the pure CuPhP2mH (4) is completely stable in air. The decrease of reaction speed is more probable a result of the missing convection in the capillary setup. The diffusion rate of the reactants determines the reaction speed.
A schematic overview of all precipitation reaction pathways is shown in Fig. 8.

Mechanistic studies of mechanochemical reactions
CuPhP2mH (4) can be easily obtained from mechanochemical synthesis. The reaction was investigated in situ by synchrotron PXRD. The synthesis conditions were the same as described in the Experimental section except that a Perspex jar was used. The 2D plot of the in situ investigation at 50 Hz is shown in Fig. 9a. At the beginning only reflections of both starting materials could be detected (copper(II) acetate: 2θ = 12.8°, 14.3°, 15.1°etc., phenylphosphonic acid: 2θ = 13.7°, 14.7°, 20.1°etc.) After 1.15 min two reflections of an unknown phase (2θ = 7.4°and 8.8°) appeared. Reflections for the product appeared after 3.00 min of milling time. The strongest reflection is the (200) at 5.6°. The reflections of the unknown intermediate and copper(II) acetate monohydrate could be detected until 4.45 min. Until the end of the reaction only reflections of the product and phenylphosphonic acid could be detected. The results show that there is an unknown intermediate, characterized by only two reflections. This compound could be detected intermediately for different mechanochemical syntheses with phenylphosphonic acid and a divalent metal acetate. 23,25 It is most probable an isomorphic metal phenylphosphonate or a phenylphosphonic acid polymorph. Reflections of phenylphosphonic acid could be detected until the end because of its excess use.
Although the composition of copper and phenylphosphonic acid is 1 : 2 in this compound, it appears when the molar ratio of phenylphosphonic acid is three or four times higher than the one of copper(II) acetate monohydrate. The mechanochemical synthesis with the correct ratio of 1 : 2 results in a different product side by side with phenylphosphonic acid. This product is most probable β-CuPhPmH (2) as based on EXAFS and PXRD measurements, discussed in the ESI. † This product can be synthesized purely when the mechanochemical synthesis is done in a 1 : 1 ratio of copper(II) acetate and phenylphosphonic acid.
The milling synthesis of β-CuPhPmH (2) with a 1 : 1 ratio of the starting materials was investigated by synchrotron PXRD ex situ at 50 Hz and in situ at 30 Hz and 50 Hz.
The 2D plot of the reaction at 30 Hz is shown in Fig. 8b. At the beginning only reflections of the starting materials can be detected. After 1.15 min milling time two reflections at 7.4°a nd 8.8°indicate the formation of the unknown intermediate. Reflections of phenylphosphonic acid persist until 6.30 min. The product reflections can be detected for the first time after 9.45 min (2θ = 6.2°, 12.5°, 17.8°etc.). Additionally, the strong reflection of CuPhP2mH (4) at 5.6°can be detected. It persists The in situ monitoring of the milling synthesis at 50 Hz leads to comparable results but the reaction is accelerated. The pure product could be detected after 3.15 min. Furthermore,  there are no reflections of CuPhP2mH (4). A detailed description is given in the ESI (Fig. S15b †).
The resulting powder patterns of the ex situ monitoring of the synthesis of β-CuPhPmH (2) at 50 Hz are shown in Fig. S15a. † The reaction is finished after 7 min and the strong reflection at 5.6°of CuPhP2mH (4) appears intermediately.
It can be assumed, that CuPhP2mH (4) is an intermediate in the mechanochemical formation of β-CuPhPmH (2), based on the results of the ex situ investigation and the in situ investigation at 30 Hz. At 50 Hz it could not be detected. Probably, the reaction is just too fast for a crystallisation of CuPhP2mH (4) or the endurance of the intermediate is too short for the 30 s time resolution. The reaction time is different in all three investigations. The decrease of the frequency from 50 Hz to 30 Hz resulted in a pronounced decrease of the reaction speed. Instead of 3.15 min the reaction needed 26.15 min. These results support the diffusion mechanism, which could be observed earlier for this setup. 23,24,40,41 The reaction time in the ex situ investigation at 50 Hz is longer than in the in situ investigation at 50 Hz. The milling process is stopped every 30 s which interrupted the reaction process and can result in a slower process. It is also possible that the waiting time between the removal of the sample and the measurement give the intermediate phases enough time to form as a crystalline compound.
The investigation of the mechanochemical synthesis of CuPhP2mH (4) did not succeed ex situ at 50 Hz and in situ at 30 Hz.

Conclusions
We presented the synthesis of four copper(II) phenylphosphonates from solution at room temperature, elevated temperatures, under hydrothermal conditions, and from mechanochemical syntheses. The structures of three new phases were determined from PXRD and single X-ray analysis. Disorder of the crystal structures were clarified from single-crystal electron diffraction data.
The reaction pathways for precipitation reactions at room temperature and mechanochemical reactions were investigated in situ. These results allowed estimation of the stability order of the compounds for both investigated reaction types.