Magneto-optical investigations of molecular nanomagnet monolayers †

Lanthanide single-molecule magnets possess much higher effective energy barriers towards relaxation of the magnetization than transition metal based ones. In addition, the blocking temperature of the magnetization has strongly increased during the last decade and has now reached 20 K. Here the blocking temperature of the magnetization is defined as the highest temperature at which coercivity in the magnetic hysteresis curve can be observed at conventional field sweep rates of ca. 1 T min. As a result of these recent successes, application in magnetic data storage devices, the main original aim of research in molecular nanomagnetism, has now come again into focus. It has become clear that successful improvement of lanthanide single-molecule magnets hinges on careful engineering of the crystal field (CF) splitting of the ground Russell– Saunders multiplet of the lanthanide ion. This can only be achieved through improved understanding of the factors influencing the CF splitting. Such understanding is now rapidly improving due to the synergetic combination of ab initio theory and advanced spectroscopy and magnetometry. It is clear that no device will be based on powder or single-crystal materials, but rather thin films or even monolayers. This was already realized in the molecular nanomagnetism community over a decade ago and this realization led to many investigations of molecular nanomagnets on surfaces. The majority of the earlier studies were largely topological, looking at the structure rather than the function of the thin layers. Later, synchrotron-based X-ray techniques such as X-ray absorption spectroscopy and X-ray magnetic circular dichroism started to be adopted. The early usage of the methods was to investigate the chemical stability of molecular nanomagnets on different surfaces. Later on, the physical properties of these were studied, culminating in the observation of quantum tunnelling of the magnetization in a monolayer of single-molecule magnets. In a different line of research, individual single-molecule magnets were investigated, by means of their insertion in break junctions and their attachment to carbon nanotubes. These studies are all necessarily performed at large scale facilities and/or extremely low temperatures. Such methods are eminently suitable for fundamental physical investigations, but less convenient for rapid material screening. Consequently, more easily accessible methods that have monolayer sensitivity would be of great benefit. A magnetometric method that may possess monolayer sensitivity is cantilever torque magnetometry. However, in magnetometric techniques the sum of signals due to all species in the sample is measured in contrast to the case of spectroscopic methods. Here we present the results of our investigations of monolayers of the lanthanide double-decker [Dy(Pc)2] (1) on quartz. The monolayers are prepared by Langmuir–Blodgett (LB) techniques and characterized by atomic force microscopy (AFM) and X-ray reflectivity (XRR) techniques. Magnetic circular dichroism (MCD) spectroscopy is used to investigate the electronic structure and magnetic properties of the adsorbed species.‡ MCD spectroscopy measures the absorption difference of leftand right-hand circularly polarized light in the presence of a magnetic field. It allows study of the electronic spectrum of complexes based on transition metals, or lanthanides, with greater precision than absorption spectroscopy because the MCD signal is a signed quantity. In addition, the MCD †Electronic supplementary information (ESI) available: UV/Vis and X-ray photoelectron spectra. See DOI: 10.1039/c6dt00839a CEITEC MU, Masaryk University, Kamenice 5, 62500 Brno, Czech Republic Department of Condensed Matter Physics, Faculty of Science, Masaryk University, Kotlářská 2, 61137 Brno, Czech Republic. E-mail: novak@physics.muni.cz Institut für Physikalische Chemie, Universität Stuttgart, Pfaffenwaldring 55, 70569 Stuttgart, Germany. E-mail: slageren@ipc.uni-stuttgart.de CEITEC BUT, Brno University of Technology, Purkyňova 123, 61200 Brno, Czech Republic Institute of Physical Engineering, Brno University of Technology, Technická 2896/2, 61669 Brno, Czech Republic

Lanthanide single-molecule magnets possess much higher effective energy barriers towards relaxation of the magnetization than transition metal based ones. 1 In addition, the blocking temperature of the magnetization has strongly increased during the last decade and has now reached 20 K. 2 Here the blocking temperature of the magnetization is defined as the highest temperature at which coercivity in the magnetic hysteresis curve can be observed at conventional field sweep rates of ca. 1 T min −1 .As a result of these recent successes, application in magnetic data storage devices, the main original aim of research in molecular nanomagnetism, has now come again into focus.It has become clear that successful improvement of lanthanide single-molecule magnets hinges on careful engineering of the crystal field (CF) splitting of the ground Russell-Saunders multiplet of the lanthanide ion.This can only be achieved through improved understanding of the factors influencing the CF splitting.4][5] It is clear that no device will be based on powder or single-crystal materials, but rather thin films or even monolayers.This was already realized in the molecular nanomagnetism community over a decade ago and this realization led to many investigations of molecular nanomagnets on surfaces. 6The majority of the earlier studies were largely topological, looking at the structure rather than the function of the thin layers.Later, synchrotron-based X-ray techniques such as X-ray absorption spectroscopy and X-ray magnetic circular dichroism started to be adopted.The early usage of the methods was to investigate the chemical stability of molecular nanomagnets on different surfaces.Later on, the physical properties of these were studied, culminating in the observation of quantum tunnelling of the magnetization in a monolayer of single-molecule magnets. 7In a different line of research, individual single-molecule magnets were investigated, by means of their insertion in break junctions and their attachment to carbon nanotubes. 8hese studies are all necessarily performed at large scale facilities and/or extremely low temperatures.Such methods are eminently suitable for fundamental physical investigations, but less convenient for rapid material screening.Consequently, more easily accessible methods that have monolayer sensitivity would be of great benefit.A magnetometric method that may possess monolayer sensitivity is cantilever torque magnetometry.However, in magnetometric techniques the sum of signals due to all species in the sample is measured in contrast to the case of spectroscopic methods.
Here we present the results of our investigations of monolayers of the lanthanide double-decker [Dy(Pc) 2 ] (1) on quartz.The monolayers are prepared by Langmuir-Blodgett (LB) techniques and characterized by atomic force microscopy (AFM) and X-ray reflectivity (XRR) techniques.Magnetic circular dichroism (MCD) spectroscopy is used to investigate the electronic structure and magnetic properties of the adsorbed species.‡ MCD spectroscopy measures the absorption difference of left-and right-hand circularly polarized light in the presence of a magnetic field.It allows study of the electronic spectrum of complexes based on transition metals, 9 or lanthanides, 5 with greater precision than absorption spectroscopy because the MCD signal is a signed quantity.1][12][13][14][15][16][17][18][19][20] In order to assess the sensitivity of MCD for thin layer samples, we prepared a thin film on quartz substrate by means of the spin coating technique from a 1 mM solution of (NBu 4 )[Dy(Pc) 2 ] (2) in chloroform solvent.The film morphology was characterized using profilometry.The average film thickness is (150 ± 30) nm.Interestingly, the MCD spectrum of the spin-coated layer reflects the features of the electronic spectrum of the neutral species 1 (Fig. 1 and S1 †), rather than those of the anionic species 2, indicating that the starting compound has oxidized during the deposition process.Oxidation of the anions of the lanthanide doubledeckers in chlorinated solvents is not uncommon (Fig. S1 †). 21e cannot exclude that ( part of ) the oxidation occurs after deposition.In any case, the oxidized species 1 is a better single-molecule magnet than 2. 22 The electronic transitions that are excited in the 600-700 nm range have ππ* character and are localized on the phthalocyanine ligands. 23The favourable signal-to-noise ratio of these measurements prompted us to prepare and study monolayers of 1.
We have chosen the LB technique to deposit monolayers, because this technique is generally applicable.In contrast, UHV techniques such as organic molecular beam deposition require volatility and thermal stability of the compounds. 11he LB technique has been used previously to prepare monolayers of single-molecule magnets. 24We have started from a 1 mM solution of 2 in chloroform, which was spread on the surface of a de-ionized water sub-phase in the Langmuir trough at a density of 30 µL per 100 cm 2 .The molecular monolayer formed on top of the sub-phase was then compressed to the target surface pressure of 15 mN m −1 .Finally, the ultrathin film of 1 on quartz was obtained by pulling out the substrate from the sub-phase at a speed of 0.5 mm min −1 while keeping the surface pressure constant.X-ray photoelectron measurements on the film show the clear presence of all the elements in 1 (Fig. S2 †).Furthermore, the binding energies for the N 1s peaks have typical values for phthalocyanines. 25The resulting film was studied by means of AFM in the semicontact mode (Fig. 2a).The AFM measurements show predominantly a molecular monolayer with some cracks and sparsely distributed thicker islands, due to locally deposited bilayers.Fig. 2b displays the height histogram of the film, with data-points collected over the morphology of the entire AFM image displayed in Fig. 2a.The bimodal distribution is interpreted as follows: the first peak corresponds to the bare surface, while the second corresponds to the top of the monolayer.The distance difference between the two peaks (1.7 nm) corresponds very well to the edge-on configuration of the phthalocyanine molecules (molecular diameter 1.49 nm), which is common for weakly interacting substrates. 26The finite width of the peaks corresponds to surface roughness of the substrate and the molecular layer, respectively.
In order to obtain mesoscopically averaged characteristics of the film relevant for the MCD, we measured X-ray reflectivity (Fig. 3).The data show a well pronounced interference fringe.The data are very well simulated considering a one box model that includes a single layer of (2.12 ± 0.05) nm thickness.This thickness is slightly more than the usual height of the molecular steps and accounts for the regions with molecular bilayer observed by AFM.The average molecular surface density obtained from the data fit amounts to (0.89 ± 0.07) nm −2 .
Fig. 1 Magnetic circular dichroism spectrum recorded on a spincoated layer of 1 (grey, 1.5 K, 2 T, intensity divided by factor 5) and a Langmuir-Blodgett layer of 1 (blue, same conditions), as well as the room temperature UV/Vis absorption spectrum of 1 in dichloromethane.We then investigated the LB film by MCD.The spectrum (Fig. 1) shows several peaks that correspond well to those found for the spin-coated layer.The peak position (656 nm) of the lowest-energy band corresponds very well to that found in the spin-coated layer (660 nm), proving intactness of the compound.Finally, we were able to measure a magnetization curve by monitoring the MCD intensity at 656 nm as a function of magnetic field (Fig. 4).We observe a clear magnetization signal, which changes on increasing the temperature, thus indicating its magnetic origin.We observe no coercivity which suggests that the magnetic field is not applied along the easy axis of the molecule.Unfortunately, 1 crystallizes in a monoclinic space group with two differently oriented molecules in the unit cell, 27 which precludes clarifying the orientation of the easy axis by single crystal magnetometry.Recently, it was reported that 200 nm thick films of the terbium derivative of 1 on quartz displayed both hysteresis and orientation-dependence. 11 We found no orientation dependence of the magnetization curve.
Our results demonstrate monolayer sensitivity of MCD for the investigation of the magnetic properties of monolayers of molecular nanomagnets on surfaces.This establishes MCD as a viable alternative to XMCD for the investigation of monolayers. 28,29In contrast to the latter, the former is relatively inexpensive and can be performed in a normal laboratory.XMCD is restricted to synchrotron sources and hence to large scale facilities.
In conclusion, we have measured the spectroscopic and magnetic properties of ultra-thin films of [Dy(Pc) 2 ] at a molecular surface density of 0.89 nm −2 by means of magnetic circular dichroism (MCD) spectroscopy, demonstrating monolayer sensitivity of the MCD technique.

Fig. 2
Fig. 2 (a) Atomic force microscopy image showing a Langmuir-Blodgett monolayer of 1 on quartz with a crack going diagonally across the image; (b) height density distribution extracted from the image (a), where the first peak is attributed to the bare surface, and the second to the top of the monolayer.

Fig. 3 X
Fig. 3 X-ray reflectivity curve recorded on a Langmuir-Blodgett monolayer of 1 on quartz.The solid line is the fit using a model consisting of substrate and one layer.

Fig. 4
Fig. 4 Magnetization curve recorded by MCD on the sample at λ = 658 nm and different temperatures and sweep directions as indicated.