A non-typical sequence of phase transitions in (NH 4 ) 3 GeF 7 : optical and structural characterization †

Single crystals of germanium double salt (NH 4 ) 3 GeF 7 = (NH 4 ) 2 GeF 6 ·NH 4 F = (NH 4 ) 3 [GeF 6 ]F were grown and studied by the methods of polarization optics and X-ray di ﬀ raction. The birefringence Δ n = ( n o − n e ), the rotation angle of the optical indicatrix ϕ ( T ) and unit cell parameters were measured in the temperature range 100 – 400 K. Three structural phase transitions were found at the temperatures: T 1 ↓ = 279.2 K ( T 1 ↑ = 279.4 K), T 2 ↑ = 270 K ( T 2 ↓ = 268.9 K), T 3 ↓ = 218 K ( T 3 ↑ = 227 K). An unusual sequence of symmetry transformations with temperature change was established: P 4/ mbm ( Z = 2) (G 1 ) ↔ Pbam ( Z = 4) (G 2 ) ↔ P 2 1 / c ( Z = 4) (G 3 ) ↔ Pa 3¯ ( Z = 8) (G 4 ). The crystal structures of di ﬀ erent phases were determined. The experimental data were additionally interpreted by a group-theoretical analysis of the complete condensate of order parameters taking into account the critical and noncritical atomic displacements. Strengthening of the N – H ⋯ F hydrogen bonds can be a driving force of the observed phase transitions.

P4/mbm, and (NH 4 ) 3 TiF 7 (P4/mnc), 4 or cubic for (NH 4 ) 3 SnF 7 , 5 (NH 4 ) 3 PbF 7 , 6 and (NH 4 ) 3 WO 2 F 5 7 with sp.gr.Pm3 ˉm.][10] Fluorination reactions proceed exothermally (even at room temperature) with the entropy reserve.Moreover, elemental homologues silicon, germanium, and tin interact with NH 4 HF 2 with the formation of (NH 4 ) 3 MF 7 also. 11These fluorination reactions were used to obtain possible metal nitrides (M 3 N 4 ) or metal nitride fluorides (MNF).The semiconductor surfaces of Si and Ge can also be etched and cleaned with NH 4 HF 2 . 12 continue to investigate (NH 4 ) 3 [MX 6 ]F with respect to their phase transitions, the sequence of which depends on the nature of the central metal atom.Comparative analysis of the phase states of these compounds and their changes as a result of phase transitions (PTs) is an important task of our present and future research.
Recently, both powder and single crystal X-ray diffraction experiments 13 revealed that the real symmetry of (NH 4 ) 3 SnF 7 at room temperature was Pa3 ˉ(Z = 8) instead of (Pm3 ˉm) (Z = 1) suggested earlier. 5Moreover, a reversible structural PT in this compound of the first order between two cubic modifications Pa3 ˉ↔ Pm3 ˉm was found at about T 0 = 360 K. 13 Two reversible structural phase transitions of the first order at T 1↓ = 358.5K (T 1↑ = 360 K) and T 2↓ = 287.55][16] When the temperature rises, the phase symmetry lowers.Both transitions have striking features of the first order: an abrupt change of birefringence, a large temperature hysteresis and a significant change of entropy.The symmetry of the low-temperature G 3 phase was found as Pa3 ˉin ref. 15.Complicated twinning of tetragonal phases appearing after cycling through a first-order transition and the ability of easy reorientation of the fourth order axis direction due to weak uniaxial stress enabled the authors 14 to suggest and then to show the existence of a hightemperature "parent phase" G 0 with the Pm3 ˉm symmetry for (NH 4 ) 3 TiF 7 . 16The following sequence of symmetry transformations with temperature or pressure changes was established: [14][15][16] Only † Electronic supplementary information (ESI) available.See DOI: 10.1039/ c5dt04907e a point group symmetry was suggested for the G 1 phase.The temperature-pressure phase diagram showed the disappearance of two intermediate tetragonal phases under pressure. 16he ability of easy switching of the direction of the optical axis at 90°by a weak uniaxial compression is very interesting and a useful property of the (NH 4 ) 3 TiF 7 crystal. 14he investigation of the (NH 4 ) 3 GeF 7 crystal was limited by the structural study. 3At room temperature, its symmetry was determined as P4/mbm with unit cell parameters a = 8.210, c = 5.984 Å, and Z = 2.The related (NH 4 ) 3 TiF 7 has another space group: P4/mnc, a = 11.9492,c = 11.666Å, Z = 4. 4 The structures of these crystals differ in the degree of ordering of the octahedral MF 6 2− groups.The present work describes an unusual sequence of PTs of germanium double salt (NH 4 ) 3 GeF 7 in accordance with crystal optical and X-ray investigations.

Optical observations
Optical studies were performed using the polarizing microscope "Axioskop-40" and the temperature chamber "Linkam LTS 350" in the range of 90-400 K.The birefringence was measured by using a Berek compensator ("Leica") with accuracy ≈0.00001.It should be noted that all optical studies were performed using the oil under cover glasses because above 300 K crystals began to decompose with isolation of (NH 4 F = NH 3 + HF).

X-ray investigations
The powder diffraction data of (NH 4 ) 3 GeF 7 for Rietveld analysis were collected with a Bruker D8 ADVANCE powder diffractometer (Cu-Kα radiation) and a linear VANTEC detector.The beam was controlled by the 0.6 mm fixed divergence slit, 6 mm receiving VANTEC slit and Soller slits.An Anton Paar TTK450 attachment was used for low-and high-temperature measurements.
The variable counting time (VCT) scheme was used to collect the diffraction data at T = 303 K, T = 273 K, T = 243 K, and T = 143 K (Fig. 1S †).The measurement time was systemati-cally increased towards higher 2θ angles, leading to improved data quality. 17Two ranges were generated on diffraction patterns: (1) 2θ 5-72°, step 0.016°, step time 1 s; (2) 2θ 72-140°, step 0.032°, step time 4 s.These X-ray patterns were used to solve and refine crystal structures.15 additional X-ray patterns were collected from 163 K to 383 K with the standard scan time scheme to identify the space group transformation at phase transition.

Results and discussion
The grown single crystals of (NH 4 ) 3 GeF 7 , like (NH 4 ) 3 TiF 7 , 13 have a habitus of elongated rectangular prisms with extinctions along the growth faces.The small single-domain samples were optically uniaxial, which was in agreement with a tetragonal symmetry of the compound. 3However, the study revealed some differences between these two tetragonal crystals in spite of their similarities.The growing faces of (NH 4 ) 3 TiF 7 are the planes (100) t with the lattice parameters a = 11.95Å. 14 In (NH 4 ) 3 GeF 7 , growing faces are planes (110) t with interplanar spacing a ffiffiffi 2 p = 11.61Å.In (NH 4 ) 3 TiF 7 , the direction of the 4-fold axis can be easily reoriented to 90°under the small uniaxial pressure, such as pressing a needle. 14In the (NH 4 ) 3 GeF 7 crystal, the pressure application (up to crystal destruction) does not change the orientation of this axis.
Fig. 1 shows the photographs of the crystal plate (NH 4 ) 3 GeF 7 , which were taken in polarized light under cooling and heating.The selected sample consists of two blocks with different orientations of the 4-fold axis.This allows simultaneous observation of changes taking place in two crystallographic directions.The upper part of the sample with the (001) t orientation is optically isotropic (Δn c = 0) at room temperature and has a dark color (Fig. 1a).The lower part of the sample has the (110) t orientation, and the 4-fold axis lies horizontally.There are direct extinctions along the growth faces.
The observed pattern changes in the process of cooling below T 1↓ = 279.2K (T 1↑ = 279.4K).The upper part of the sample illuminates and the twin boundaries are formed at an angle of 45°to the faces of growth, i.e. along [100] t (Fig. 1b).This area has extinctions along the lateral edges (110) t .Further cooling of the sample leads to increasing of the anisotropy in the upper block.This is evident by the change of the interference color (Fig. 1c).In addition, the extinction position changes.Below T 2 = 270 K direct extinction remained only in the upper part of the sample.In the lower block thin lamellar twins with the "floating" position of extinction appear.
Further cooling reveals an abrupt transition to the optically isotropic (cubic) phase at T 3↓ = 218 K (Fig. 1d).The sample rapidly becomes uniformly dark.This transition temperature can be varied for the same sample within T 3↓ = 218-224 K.During heating the crystal also returns quickly to the anisotropic state at T 3↑ = 227 K.
Observations of the growth plate (110) t in polarized light showed that the fine twinning structure appeared during the cooling in the temperature range T 1↓ ≤ T ≤ T 3↓ , which does not allow measurement of the optical characteristics.However, after cooling to the isotropic state (below T 3↓ ) and returning to the anisotropic phases, the formed twin structure consists of large domains of type (I) or (II) (Fig. 2a and b).Region (I) has a stable position of extinction along the edges of growth, whereas it varies with temperature in (II).The temperature dependence of birefringence Δn (T ) and rotation of the optical indicatrix ϕ(T ) around the [110] t direction with respect to the [001] t direction were measured in these large areas.
At room temperature, the birefringence of the (NH 4 ) 3 GeF 7 crystal (Δn = n o − n e = 0.0034) is higher than that of (NH 4 ) 3 TiF 7 (Δn = 0.0023). 13The temperature dependence of optical characteristics Δn (T ) of (NH 4 ) 3 GeF 7 is shown in Fig. 3.It can be seen that the birefringence of a high-temperature phase varies smoothly with temperature.Below T 1 , the dependence Δn (T ) is divided into two curves measured in different twins.Curve 1 was obtained for the twin type (I) with the extinctions along the facet.The birefringence in this area gradually decreases approaching zero.Therefore, the interference color of the twin (I) is gray (Fig. 2b).In the area (II), the changing of color intensity indicates an increase of the optical anisotropy (Fig. 2a).Indeed, according to Fig. 3    Comprehensive polarization-optical and structural studies, as well as measuring the birefringence and the rotation angle of the indicatrix in the (NH 4 ) 3 GeF 7 crystal allowed establishment of the existence of three structural phase transitions between the G 1 , G 2 , G 3 , and G 4 phases of different symmetries.According to the temperature dependence of optical characteristics (Fig. 3 and 4), transitions G 1 ↔ G 2 ↔ G 3 occur smoothly, close to the second-order.Therefore, we assume that a successive lowering of crystal symmetry takes place upon cooling from the room temperature.The presence of the optical anisotropy Δn c and twin structure with boundaries along the [100] t direction enables one to distinguish the G 2 phase from the G 1 phase.These facts demonstrate the loss of the second order axes along the [100] t direction and (100) t plane.The position of extinction of the sample along the [110] t direction reveals the geometry of a new cell.Most likely, the group symmetry of the G 2 phase is orthorhombic, and two axes of the unit cell should be perpendicular to the 4-fold axis and directed along the unit cell diagonals of the tetragonal G 1 phase.
As the crystal structure of (NH 4 ) 3 GeF 7 at room temperature was solved earlier, 3 we used this model (P4/mbm) to make Rietveld refinement by using TOPAS 4.2. 18The refinement was stable and gave low R-factors (Table 1 and Fig. 1S(a) †).Atomic coordinates are given in Table 1S, † and the crystal structure is presented in Fig. 2S(a).† The compound (NH 4 ) 3 GeF 7 was very pure and all the lines were indexed by the P4/mbm phase (Fig. 1S(a) †).Cell parameters after refinement were close to those from ref. 3.
One can see (Fig. 5 and 6a) that the first wave of superstructure peaks appears at T = 279 K.It was concluded that at this PT (G 1 → G 2 ) the cell parameters increased.All these additional peaks can be described by the emergence of instability at the (1/2, 1/2, 0) k 18 -point (M) of the Brillouin zone of the G 1 -P4/mbm unit cell (hereinafter the designation of irreducible representations (irrep) and points of Brillouin zone are given in accordance with reference books). 19,20Additional useful information is that this PT G 1 ↔ G 2 is of the second order type (Fig. 3 and 4).Therefore, only a special space group should be considered.
It is well-known that group-theoretical analysis allows identification of critical OP and critical distortions of the crystal structure, which determines the symmetry of the distorted phase. 22Critical OP together with noncritical OP, which does not lead to a symmetry change, form a complete condensate of OP. 23 Group-theoretical analysis shows only the presence of critical and noncritical OP, but the numerical values of critical/noncritical OP and distortions are obtained from the experimental data, and the structural data are better in this case.
So, it was found that at PT P4/mbm ↔ Pbam, the Ge, F2, F3 and N2 atomic sites were splitting: Ge → Ge1 + Ge2; F2 → F2 + F3; F3 → F4 + F5; N2 → N2 + N3.Other sites remain unsplit.Only fluorine and ammonium ions are shifted at PT, and the largest shifts of 0.67 Å and 0.36 Å are observed for F2 and F5, respectively.The critical irrep M 1 − ⊕ M 4 − induces the greatest contribution to these distortions and leads to a critical shift of F2 on 0.66 Å along the a axis and that of F5 on 0.35 Å along the b axis of the orthorhombic phase.These movements can be represented as the rotation of the Ge1F 6 octahedron on a large angle ∼23°around the 4-fold axis in a tetragonal phase (Fig. 7a and b).The Ge2F 6 octahedron does not virtually change its orientation.The ammonium shifts are smaller: N1 (∼0.27 Å), N2 (∼0.2 Å) and N3 (∼0.1 Å).However, the largest contribution to distortion is due to the critical irrep M 1 − ⊕ M 4 − , leading to N1 and N3 shifts in the ab plane of the orthorhombic phase, preferably along the b axis, whereas N2 is preferably shifted along the a axis.Since F1 is only slightly displaced (∼0.08 Å), but NH 4 undergoes great shifts, then F1 is shifted from the F1N 6 octahedron center, staying exactly in the center of the tetragonal unit cell (Fig. 7b).The F1-N bond lengths vary in the range of 2.931(5)-2.970(1)Å for the tetragonal phase and they become 2.75(2)-3.13(2)Å for the orthorhombic phase.The decreasing of these bond distances may be due to the formation of stronger N-H⋯F hydrogen bonds.
The geometry of twinning, rotation of the optical indicatrix in the twin (II) and the absence of rotation in the twin (I) indicate the G 3 phase to be of monoclinic symmetry with a twofold axis along one of the two [110] t = [010] or directions.Therefore, the crystal symmetry group in this phase can be selected as monoclinic P12 1 /c1.The screw twofold axis is perpendicular to the former fourth-order axis and directed along [010] or of an orthorhombic unit cell of the G 2 phase.Such a crystallographic set requires an explanation of the data given in Fig. 3 (curves 1 and 2).The curve 1 is the Δn a (T ) dependence obtained from measurements in the twin (I) without rotation  of the indicatrix.Accordingly, the curve 2 is Δn b (T ) obtained in (II).The X-ray experiment of the G 3 phase (Fig. 1S(c) †) reveals that the main peak broadening occurs, but there are no additional superstructure peaks, therefore it can be concluded that this PT is associated with the emergence of instability at the same (1/2, 1/2, 0) k 18 -point (M) of the Brillouin zone of P4/mbm.Optical investigations showed a monoclinic symmetry of this phase, a unique axis b should be perpendicular to the 4-fold axis and directed along the unit cell diagonals of the tetragonal G 1 phase.Similarly to G 1 ↔ G 2 , this G 2 ↔ G 3 PT is of the second order type.Only one space group fulfills all these conditions, namely P2 1 /c (0,0,1),(1,1,0),(−1,1,0).The M 5 − irrep drives this PT and the transformation can be written as: , where (ξ, ξ) is another critical order parameter, which is transformed according to the M 5 − irrep of the sp.gr.P4/mbm.The crystal structure for Rietveld refinement in TOPAS 4.2 was prepared by the program ISODISTORT using M 5 − irrep distortion.
Refinement was stable and gave low R-factors (Table 1 and Fig. 1S(c) †).Atomic coordinates are presented in Table 1S, † the crystal structure is shown in Fig. 2S(c).† This PT can be considered as transition from the initial phase to the monoclinic phase P4/mbm ↔ P2 1 /c.Fluorine sites split further as F3 → F4 + F5 + F6 + F7, while the other sites remain unsplit like those in the orthorhombic phase Pbam.Below the transition at T 2 accompanied by the symmetry change Pbam ↔ P2 1 /c, a shear deformation with component x 5 (within the orthorhombic cell) appears causing rotation of the optical indicatrix at an unusually large angle ϕ ∼ 25°.Such great rotation angles of the indicatrix ϕ(T ) are characteristic of the "proper" ferroelastic transitions when a parameter of transition ξ is linearly related to the shear component of the spontaneous deformation ξ ∼ x 5 . 24For example, CsLiSO 4 and CsLiCrO 4 also belong to the class of "proper" ferroelastics with the observed value of rotation angles of the indicatrix of 30-40°. 25,26t should be noted that the above mentioned shear component x 5 within the orthorhombic cell transforms to x 5 and x 6 within the initial tetragonal phase.The components of shear strain x 5 and x 6 are converted by a two dimensional irrep Γ 5 + k 17 -point (Γ) (0, 0, 0) of the Brillouin zone of the P4/mbm cell.Thus, the transformation properties of the phenomenological parameter components of transition (ξ,ξ) are the same as those of shear strain x 5 and x 6 .In this case the components of OP (ξ,ξ) are linearly related to the components of shear strain, i.e. (ξ,ξ) ∼ (x 5 ,x 6 ).
Below T 3↓ = 218 K, the optically isotropic cubic phase was observed, where an additional wave of superstructure peaks appeared (Fig. 5 and 6a).However, main peaks collapsed in one peak after PT (Fig. 6b).It is a very strange situation because an ordinary situation is the splitting of peaks during cooling.The indexing shows that a cell in the G 4 phase becomes a cubic (Pa3 ˉ).A similar situation was observed in (NH 4 ) 3 TiF 7 , which underwent a reconstructive PT P4/mnc ↔ Pa3 ˉwith increasing symmetry under cooling. 14It should be noted that (NH 4 ) 3 SnF 7 has PT Pm3 ˉm ↔ Pa3 ˉwith the same low temperature phase Pa3 ˉ,13 as well as (NH 4 ) 3 WO 2 F 5 . 7All these phases have the same high temperature parent phase Pm3 ˉm and, as it turns out, have the same lowest temperature fully ordered phase Pa3 ˉ.Therefore, the crystal structure of (NH 4 ) 3 TiF 7 was taken as a starting model for refinement of the G 4 phase.The NH 4 group was refined as a rigid body similarly to that prepared in ref.
14.The refinement was stable and gave low R-factors (Table 1 and Fig. 1S(d) †).The atomic coordinates are given in Table 1S, † the crystal structure is shown in Fig. 1S(d).† Phase transition P4/mbm ↔ Pa3 ˉcannot be described by group-theoretical methods since this PT is reconstructive and large rotations of octahedra up to 45°appear.Similar reconstructive PTs were found earlier and studied. 13,15It should be noted that all hydrogen atoms of NH 4 + were localized and refined for the Pa3 ˉphase.However, the powder diffraction method is not very reliable, and it is still questionable whether NH 4 + ions remain ordered or not. 15Rather small values of F1-N distances of 2.663(7)-3.184(7) Å indicate the formation of N-H⋯F hydrogen bonds.All patterns from 163 K to 383 K were treated in a similar way and the temperature dependence of the cell parameters (Fig. 3S(a) †) and cell volume (Fig. 3S(b) †) was plotted.It should be noted that the peaks of the impurity phase (NH 4 ) 2 GeF 6 appeared at T = 323 K (Fig. 5), therefore, the decomposition process (NH 4 ) 3 GeF 7 → (NH 4 ) 2 GeF 6 + NH 3 + HF started at this temperature under heating.
Further details of the crystal structures of G 1 , G 2 , G 3 and G 4 phases may be obtained from Fachinformationszentrum Karlsruhe, 76344 Eggenstein-Leopoldshafen, Germany (fax: (+49) 7247-808-666; E-mail: crystdata@fiz-karlsruhe.de; http://www.fiz-karlsruhe.de/request_for_deposited_data.html on quoting the deposition numbers: CSD 430463, CSD 430464, CSD 430465 and CSD 430466, respectively.).The tetragonal symmetry of the G 1 phase is stable: in the temperature range of 280-380 K the changes of optical anisotropy are weak; the 4-fold axis does not change its direction during uniaxial compression up to crystal destruction.This probably means that in contrast to (NH 4 ) 3 TiF 7 , wherein the high-pressure parent phase G 0 with Pm3 ˉm symmetry was found, 15 such a phase is unattainable for (NH 4 ) 3 GeF 7 .
The driving force of all phase transitions in (NH 4 ) 3 GeF 7 can be associated with the emergence of hydrogen bonds N-H⋯F, because the value of N⋯F contacts decreases at PT under cooling.Such bond length shortening is connected with the F shift from the center of the FN 6 octahedron and its distortion.The largest ionic displacements at all PTs are associated with the GeF 6 octahedron.Their movements can be represented as rotation of the Ge1F 6 octahedron at PT P4/mbm ↔ Pbam, rotation of Ge1F 6 and Ge2F 6 octahedra around two directions at P4/mbm ↔ P2 1 /c, and huge rotations of all GeF 6 octahedra due to reconstructive PT P4/mbm ↔ Pa3 ˉ.
A final scheme of phase transitions including irreducible representations and the corresponding order parameters can be written as: The components of OP (ξ,ξ) at PT P4/mbm ↔ P2 1 /c are linearly related to the components of shear strain x 5 and, therefore, this compound belongs to the class of "proper" ferroelastics with a large value of rotation angles of the indicatrix.

For
obtaining single crystals of (NH 4 ) 3 GeF 7 Plitzko & Meyer 3 used ammonium hydrogen difluoride (NH 4 HF 2 ) as the fluorinating and oxidizing reagents in the reaction with Ge powder.The process was carried out at 573 K in a sealed Monel (Cu 32 Ni 68 ) ampoule at the Ge : NH 4 HF 2 molar ratio 1 : 4. We also used NH 4 HF 2 but for fluorination of GeO 2 of a reagent grade at 150-200 °C.It should be noted that the reaction began even at room temperature under grinding the initial components together.At least, a double excess of NH 4 HF 2 was taken relative to stoichiometric reactions: GeO 2 + 3.5NH 4 HF 2 = (NH 4 ) 3 GeF 7 + 0.5NH 3 + 2H 2 O.The cake obtained in this way was then water-leached, and colorless prismatic single crystals of (NH 4 ) 3 GeF 7 were formed under slow evaporation in the final solution under ambient conditions.

Fig. 1
Fig. 1 Single crystals (NH 4 ) 3 GeF 7 under polarized light during cooling: a -G 1 , b -G 2 , c -G 3 , d -G 4 phases, respectively.The sample in the G 1 phase consists of two blocks with different orientations of the 4-fold axis.The arrows indicate the position of extinction.
(curve 2), this twin has an increasing birefringence.Measurements in the twin (II) were made, taking into account the rotation of the indicatrix at each temperature.Below T 3↓ = 218 K, the birefringence of the crystal abruptly drops to zero.The anisotropic phase appears suddenly at T 3↑ = 227 K during the process of heating.The splitting of Δn (T ) into two curves below T 1 is associated with a reduction of crystal symmetry and the appearance of the optical anisotropy along the [001] t direction.The measurement results of Δn c (T ) are shown in Fig.4(curve 1).Birefringence appears at T 1 and smoothly changes near T 2 without large spikes, while the anisotropy disappears at T 3 .The temperature dependence of the angle rotation of the optical indicatrix ϕ(T ) in the twin (II) around one of the [110] t directions is shown in Fig.4(curve 2).It can be seen that the indicatrix rotates only in the temperature region T 3 ≤ T ≤ T 2 , where T 2↑ = 270 K, T 2↓ = 268.9K, δT 2 = 1.1 K.It should be noted that the rotation of the indicatrix occurs up to a very high angle ϕ ≈ 24°.

Fig. 2
Fig. 2 The formation of large twins in the (110) t plate after cooling till the G 4 phase and returning into the G 3 phase: (a) -(I) and (b) -(II) twins near the position of extinction.

Fig. 5 X
Fig. 5 X-ray powder diffraction patterns of (NH 4 ) 3 GeF 7 at different temperatures from 163 K to 383 K.The peaks of the impurity phase of (NH 4 ) 2 GeF 6 appeared at T = 323 K are marked by stars.

Fig. 7
Fig. 7 The main distortions of the (NH 4 ) 3 GeF 7 crystal structure at PTs, leading to rotation of Ge1F 6 octahedra during the G 1 ↔ G 2 transformation (a, b), and to rotation of Ge1F 6 and Ge2F 6 octahedra in the monoclinic phase G 3 (c) in two projections.Dashed red square surrounds the formula unit of different phases.
Fluorine and ammonium ions experience shifts at PT to the P2 1 /c phase like those in the Pbam phase.F3 and F4 have the largest shifts to 0.73 Å and 0.61 Å, respectively.The other fluorine shifts are in the range of 0.25-0.37Å.The critical irrep M 1 − ⊕ M 4 − induces a majority of distortions, leading to rotation not only in Ge1F 6 , but also to that of Ge2F 6 in the cb plane of the monoclinic phase.These octahedra are simultaneously rotated in the ca plane (Fig. 7c) that is induced by the critical M 5 − irrep.The shifts of N1 (∼0.39 Å), N2 (0.16 Å) and N3 (0.21 Å) atoms are also basically induced by M 1 − ⊕ M 4 − and M 5 − irreps.Herewith the greatest displacement of N1 on ∼0.27 Å, which occurs along the a axis of the monoclinic unit cell, is induced by M 5 − irrep.Such ammonium displacements lead not only to a shift of F1 from the F1N 6 octahedron center in the cb plane, but also to a noticeable shift along a axis of the monoclinic cell (the former 4-fold axis) (Fig. 7c).A rather short F1-N bond of 2.56(1) Å is formed, which indicates the N1-H⋯F1 hydrogen bond.In general, the range of F1-N distances expands to 2.56(1)-3.24(2)Å.

Table 1
Main parameters of processing and refinement of the (NH 4 ) 3 GeF 7 sample in four phases