Zirconium complexes of bipyrrolidine derived salan ligands for the isoselective polymerisation of rac -lactide †

Herein we report the synthesis and characterisation of a series of Zr( IV ) 2,2 0 -bipyrrolidine–salan derived complexes and their exploitation for the ring opening polymerisation of rac -lactide to afford highly isotactically enriched polymers.

Poly(lactic acid) is unequivocally a success story in modern sustainable chemistry. 1This is in no small part due to the desirable properties of the resultant polymer-namely biodegradability and the fact that the monomer is sourced from annually renewable raw materials. 2Poly(lactic acid) (PLA) is currently commercially produced using tin(II) octanoate as the initiator.However, there is a desire to prepare new initiators that are faster and able to control the microstructure of the resultant polymer. 3The stereochemistry of PLA dramatically affects the properties of the material-for example isotactic PLLA (or PDLA) has a melting point of ca.170 1C, moreover for stereoblock/gradient PLA with isotactic sequences of L-and D-lactide the T m increases to 180-220 1C. 4 There are many impressive examples in the literature reporting the stereoselective polymerisation of rac-lactide (rac-LA). 3,5Compared to the number of initiators that are active for the production of heterotactic PLA, isoselective initiators are rare.The metal centres that are typically used for the production of isotactic PLA from rac-LA are Zn(II), 6 Al(III) 5c,7 and Y(III). 3,8Du and co-workers have recently reported a series of Zn(II)-amido-oxazolinate complexes for the ring opening polymerisation (ROP) of rac-LA, which afforded high isoselectivity in toluene at 50 1C.Full conversion was achieved after 30 min with a P m (probability of isotactic enchainment) up to 0.8. 6When the temperature was lowered to 23 1C this could be increased to 0.91, but full conversion was only reached in 44 hrs at this temperature.Williams has recently shown that Yttrium phosphasalen complexes can produce PLA with a P m of up to 0.84, very rapidly. 3Examples of Al(III) include the early work of Spassky, Feijen and Nomura with salen derived complexes.7a-d Whilst there have been many elegant examples of the utility of group 4 complexes for the ROP of rac-LA, the vast majority produce atactic or heterotactic PLA. 9 However, Davidson and co-workers have shown that C 2 -symmetric Zr(IV) amine-bis(phenolates) are capable of producing moderate isotacticity (P m = 0.7). 10 More recently Kol and Okuda have prepared a series of Zr(IV) complexes with ONSO ligands, which depending upon the flexibility of the backbone, produce either heterotactically (P r up to 0.87) or isotactically inclined PLA (P m up to 0.67). 11Group 4 initiators have the added advantage of being easy to prepare, relatively moisture stable and can be trialled under the industrially preferred melt conditions.
In this paper we report the preparation of three Zr(IV) complexes based on a 2,2 0 -bispyrrolidine and their exploitation in the ROP of rac-LA.Examples based on such ligands are rare in the literature 12 and this is only the second example of the use of this meso-ligand in catalysis 13 (Scheme 1).
The ligands were prepared by modified Mannich reactions involving either enantiopure (R,R or S,S) or meso variants of 2,2 0 -bispyrrolidine.12c All ligands have been characterised by NMR spectroscopy, HR-MS and the solid-state structure has been This journal is © The Royal Society of Chemistry 2014 determined for the meso ligand (3H 2 ); see ESI † for full details.All Zr(IV) complexes were characterised by single crystal X-ray diffraction.The metric data for the complexes are similar and are in agreement with literature reported salan complexes. 10The R,R and S,S ligands coordinate to Zr(IV) in a fac-fac fashion with the R,R enantiomer forming the D-isomer and the S,S enantiomer the L-isomer exclusively in the solid-state (Fig. 1).Zr(1)(O i Pr) 2 crystallises in the chiral space group P4 1 whereas Zr(3)(O i Pr) 2 in P4 3 .This is in agreement with Kol and co-workers for related Ti(IV) complexes where the ligands lead to a predetermined chirality at the metal centre. 14The 1 H NMR spectra of complexes Zr(1/2)(O i Pr) 2 were indicative of the solid-state structure being maintained in solution, see ESI. † The ligands are locked in position as indicated by discrete doublets for the methylene CH 2 moieties, furthermore there are no exchange peaks observed in the NOESY/ EXSY spectrum at 298 K (CDCl 3 ).
In the solid state Zr(3)(O i Pr) 2 crystallises in the monoclinic P2 1 /c space group, with both enantiomers (the L and D forms) present, arbitrarily the D-isomer is shown in Fig. 1.Compared to the chiral ligands a different coordination mode of the salan (fac-mer) was observed, this is presumably due to the syn relationship of the hydrogen atoms pertaining to the C-C bond between the five membered rings (cf.antiperiplanar for the chiral complexes).When this complex was recrystallised from toluene, the room temperature solution state NMR spectrum (in either CDCl 3 or d 8 -THF) was complicated, with clearly more than one species present in solution.The ground state energies of various isomers have been studied via DFT methods.† Unsurprisingly the observed structure is the most thermodynamically stable, however the trans isomer is only 8.3 kcal mol À1 higher.Fortunately, when Zr(3)(O i Pr) 2 was recrystallised in hexane the product gave an NMR spectrum that was consistent with the fac-mer isomer, with discrete doublets for the methylene CH 2 moieties being observed along with two observed resonances for the methine isopropoxides and four resonances in the aryl region.Room temperature NOESY/EXSY measurements showed the presence of exchange peaks, indicating that in solution an equilibrium exists which potentially is D-isomer 3 L-isomer.† Presumably, these enantiomers are interconverting in solution at room temperature giving rise to the exchange peaks, which were absent in the chiral complexes Zr(1/2)(O i Pr) 2 .
The majority of examples of the polymerisation of rac-LA using group 4 initiators use sublimation methods to purify the monomer.In this study we have simply used recrystallised monomer to mimic more industrially relevant conditions (entries 4 and 11 use sublimed monomer as a comparison).The selectivity and dispersity appear to be relatively similar for the sublimed monomer compared to recrystallised, although similar conversions are achieved in a slightly shorter time frame for the sublimed monomer.The solution polymerisations of rac-LA are incredibly well controlled with low dispersities obtained.For Zr(3)(O i Pr) 2 in the melt (entries 3 and 4) the dispersity of the polymer is slightly higher indicating a degree of transesterification.
Interestingly, the Zr(3)(O i Pr) 2 yielded PLA with a high isotactic bias (P m = 0.86 in solution), which to the best of our knowledge is the highest reported isotactic initiator in the literature to date utilising a group 4 initiator.Analysis of this highly isotactic polymer prepared in solution via DSC showed there to be a major endothermic peak at 190 1C, indicative of stereoblock isotactic PLA.4b Moreover, in the case of Zr(3)(O i Pr) 2 the sis tetrad is significantly smaller than the sii, iis and isi tetrads indicating isotactic PLA of a blocky nature.5g,15 Furthermore, the MALDI-ToF analysis has a repeat unit of 144 g mol À1 , this coupled with the low M w /M n (1.05) indicates a controlled polymerisation with little transesterification occurring.The expected H-and -O i Pr end groups from the coordination insertion mechanism were also observed.The solution state kinetics of the polymerisation were investigated with Zr(3)(O i Pr) 2 at room temperature in CDCl 3 (100 : 1 LA : Init), for rac-LA k app = 4.3 Â 10 À3 min À1 was observed, Zr(3)(O i Pr) 2 polymerises L-LA significantly faster with a k app = 5.9 Â 10 À3 min À1 , Fig. 2. Both Zr(1-2)(O i Pr) 2 complexes were inactive for the solution state polymerisation of rac-LA in CDCl 3 at room temperature.However, the chiral complexes were active at 70 1C in toluene -with ca.50% conversion being achieved after 4 and 8 hours respectively, with a strong isotactic bias observed and T m = 178 1C, from DSC (Table 1, entry 5) and T m = 176 1C, from DSC (Table 1, entry 7).In the case of Zr(1-2)(O i Pr) 2 the mechanism of polymerisation is presumably enantiomorphic site control.There does appear to be a slight difference in selectivity with reaction time (entries 5 vs. 7 and 6 vs. 8), at low conversion (ca.10%) P m = 0.75 similar to the 4 h run (entries 5 and 6).Only ca.50% conversion of rac-LA could be achieved in solution with the chiral complexes compared to 85% with the meso complex in the same timeframe (N.B. the Zr(3)(O i Pr) 2 test was at 20 1C cf.70 1C for Zr(1/2)(O i Pr) 2 ).The polymerisation was investigated further with L-LA, where L-Zr(2)(O i Pr) 2 was active (k app = 4.1 Â 10 À4 min À1 after 37 h, conversion to PLLA = 58% M n = 6900, M w /M n = 1.07) and D-Zr(1)(O i Pr) 2 was slow (k app = 0.97 Â 10 À4 min À1 after 37 hrs, conversion to PLLA = 18%) Fig. 3. 16 However, we tentatively suggest that if the ''wrong'' insertion occurs the complex can convert to the other form and now the chirality of the metal and chain end complement each other again, Scheme 2, and propagation continues leading to stereoblock isotactic PLA.It is also interesting to note that the rate of ROP of L-lactide with Zr(3)(O i Pr) 2 is significantly faster than that of L-Zr(2)(O i Pr) 2 , this may well be due to the difference in coordination of the ligand around the Zr(IV) centre.
Work is currently on-going to investigate the mechanism in more detail, the applicability of the initiators with other cyclic esters and for co-polymer formation.Encouragingly, Zr(3)(O i Pr) 2 is active for the ROP of rac-butyrolactone ([M] : [Init] 300 : 1, T = 80 1C solvent free; conversion = 75%, M n = 19 500, M w /M n = 1.10 after 4 hours to produce atactic polymer).
Zirconium(IV) complexes have been prepared and screened for the polymerisation of rac-LA.Stereoblock isotactic PLA is prepared with the meso salan complex Zr(3)(O i Pr) 2 , which is significantly faster than either of the chiral complexes Zr(1/2)(O i Pr) 2 .It is hypothesised that this reflects the fluxionality of Zr(3)(O i Pr) 2 .We wish to thank the EPSRC (EP/G03768X/1), the EPSRC UK National Service for Computational Chemistry Software (CHEM752), Corbion for lactide and support of the CDT at Bath and the University of Bath for funding.

Fig. 1
Fig. 1 The solid state structures of D-Zr(1)(O i Pr) 2 (left) and L-Zr(2)(O i Pr) 2 (right) and Zr(3)(O i Pr) 2 (bottom) ellipsoids are shown at the 30% probability level and hydrogen atoms have been removed for clarity.