Biomimetic Management of Orthodontic White Spot Lesion

Abstract

Objectives: White spot lesions (WSLs) may develop in patients with inadequate oral hygiene during orthodontic treatment. This study aimed to develop a natural remineralization agent by creating artificial WSLs in vitro. Materials/Methods: WSLs were created in teeth with orthodontic buttons in vitro. The teeth were divided into the following groups: P11-4 (Group 1), Nano-HA Solution Before Sintering (Group 2), Nano-HA Solution After Sintering (Group 3), P11-4 and Nano-HA Mixture Before Sintering (Group 4), P11-4 and Nano-HA Mixture After Sintering (Group 5), Boron-Containing Nano-HA Mixture Before Sintering (Group 6), Boron-Containing Nano-HA Mixture After Sintering (Group 7), CPP-ACP (Group 8), and Artificial Saliva (Group 9).Measurements were taken before and after demineralization, and at the 7th, 14th, 21st, and 28th days of remineralization. Images were recorded using DIAGNOcam and VistaCamIX, area measurements were made with Image J, and SEM was used for remineralization assessment. Results: All groups except Group 9 showed a reduction in the WSL area,with statistically significant results. SEM analysis revealed the lowest remineralization in Groups 8 and 9,while the other groups exhibited more intense remineralization. Conclusions: The most successful groups for WSL remineralization were those containing pure Nano-HA (Groups 2 and 3), with other groups showing varying levels of remineralization. Keywords: White spot lesion, biomimetic materials, boron, hydroxyapatite, orthodontics, peptide.