The effect of size and delignification on the mechanical properties of polylactic acid (PLA) biocomposites reinforced with wood fibres via extrusion

Abstract

Natural fibres are promising candidates for polymer reinforcement due to their specific properties and renewability. To investigate the influence of wood fibre (WF) alkaline treatment on the mechanical properties of wood-plastic composites (WPCs), alkalised and raw WF-reinforced polylactic acid composites (40/60 wt%) were compounded using two different lengths of WF (100 and 400 μm) in the presence of maleic anhydride as the coupling agent. The structural analysis confirmed the removal of lignin and hemicellulose components from the fibres. The reinforcement increased the tensile and flexural moduli up to 140% and 137%, respectively, in the presence of a coupling agent. For raw fibre-reinforced composites, the tensile and flexural strengths increased by 12% and 12%, respectively. In contrast, alkalised fibres showed inferior performance, suggesting that the removal of hemicellulose and lignin added to the shear forces during extrusion led to their mechanical loss. Although all composites showed a decreased impact strength, the short fibre composites increased their properties by adding maleic anhydride. It can be clearly shown that short fibre-reinforced PLA performed mechanically better than the long counterparts and that the alkaline treatment did not produce better outcomes than the pristine raw fibres.

Graphical abstract: The effect of size and delignification on the mechanical properties of polylactic acid (PLA) biocomposites reinforced with wood fibres via extrusion

Article information

Article type
Paper
Submitted
26 Jan 2023
Accepted
16 Apr 2023
First published
21 Apr 2023
This article is Open Access
Creative Commons BY-NC license

RSC Sustain., 2023,1, 876-885

The effect of size and delignification on the mechanical properties of polylactic acid (PLA) biocomposites reinforced with wood fibres via extrusion

R. L. Cosse, V. S. D. Voet, R. Folkersma and K. Loos, RSC Sustain., 2023, 1, 876 DOI: 10.1039/D3SU00039G

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements