Magnetic and magnetocaloric effect study of a polycrystalline Gd0.5Sr0.5−xCaxMnO3 compound

Abstract

The magnetic and magnetocaloric properties of polycrystalline Gd_0.5Sr_0.5−xCa_xMnO₃ (x = 0.0, 0.2, 0.3, 0.4 and 0.5) compounds have been investigated. Depending upon the Ca and Sr proportions, fascinating magnetic ground states were observed in the Gd_0.5Sr_0.5−xCa_xMnO₃ compounds. Here, the dominating nature of the canted magnetic state (for the Gd_0.5Ca_0.5MnO₃ compound) and glassy (disordered ferromagnetic) magnetic state (for the Gd_0.5Sr_0.5MnO₃ compound) are observed. However, for the intermediate doped samples (x = 0.2, 0.3, 0.4), a competing nature is found in their magnetic and exchange bias properties. Additionally, in the low temperature region, a significantly large magnetocaloric effect is observed for all the samples. At a 70 kOe external magnetic field, the highest observed value of the magnetocaloric entropy change is 21.58 J kg⁻¹ K⁻¹ (for the Gd_0.5Ca_0.5MnO₃ sample) and the lowest is 10.15 J kg⁻¹ K⁻¹ (for the Gd_0.5Sr_0.5MnO₃ sample).