Preparation of hydrophobic epoxy–polydimethylsiloxane–graphene oxide nanocomposite coatings for antifouling application

Author affiliations

Abstract

Epoxy–polydimethylsiloxane–graphene oxide (EPG) nanocomposite coatings were successfully developed by loading different wt% of graphene oxide nanosheets (GNs) into an epoxy–hydroxy-terminated-polydimethylsiloxane (EP–hPD) matrix via a facile in situ preparation technique. The inclusion of GNs into EPN led to an increase in modulus of elasticity and tensile strength up to 1570.46 MPa and 31.54 MPa, respectively, in the case of 1 wt% loading of GNs in the EP–hPD matrix. Also, an increase in the water contact angle from 90.1° to 115.2°, 104.5° and 101.7° was discerned at 1, 3 and 5 wt% loadings of GNs respectively. Taber abrasion results demonstrated a decrease in abrasion loss by 33.3% at 1 wt% loading of GNs in comparison to the unreinforced coating. An improvement in the glass transition temperature (Tg) was observed from 63.5 °C for the neat sample to 77.6 °C, 76.3 °C and 71.6 °C for the 1, 3 and 5 wt% EPG nanocomposites, respectively. An inevitable enhancement in the properties of the nanocomposites was affirmed due to the synergistic effect of GNs dispersed within the EP–hPD blend matrix. The prominent findings of this work include a minimum corrosion rate of 0.73 × 10−2 mm per year and upgradation in the antifouling performance of the nanocomposite coatings in comparison to the neat coating.

Graphical abstract: Preparation of hydrophobic epoxy–polydimethylsiloxane–graphene oxide nanocomposite coatings for antifouling application

Back to tab navigation

Supplementary files

Article information


Submitted
29 Sep 2019
Accepted
08 Dec 2019
First published
09 Dec 2019

Soft Matter, 2020, Advance Article
Article type
Paper

Preparation of hydrophobic epoxy–polydimethylsiloxane–graphene oxide nanocomposite coatings for antifouling application

S. Verma, S. Mohanty and S. K. Nayak, Soft Matter, 2020, Advance Article , DOI: 10.1039/C9SM01952A

Social activity

Search articles by author

Spotlight

Advertisements