An as-cast high-entropy alloy with remarkable mechanical properties strengthened by nanometer precipitates

Abstract

High-entropy alloys (HEAs) with good ductility and high strength are usually prepared by a combination of the forging and heat-treatment processes. In comparison, as-cast HEAs typically don’t reach strengths similar to those of HEAs produced by the forging and heat-treatment processes. Here we report a novel equiatomic-ratio CoCrCuMnNi HEA prepared by vacuum arc melting. We observe that this HEA has excellent mechanical properties, i.e., a yield strength of 458 MPa, and an ultimate tensile strength of 742 MPa with an elongation of 40%. Many nanometer precipitates (5 – 50 nm in size) and domains (5 – 10 nm in size) are found in the inter-dendrite and dendrite zones of the produced HEA, which is the key factor for its excellent mechanical properties. The enthalpy of mixing between Cu and Mn, Cr, Co, or Ni is higher than those of between any two of Cr, Co, Ni and Mn, which leads to the separation of Cu from the CoCrCuMnNi HEA. Furthermore, we reveal the nanoscale-precipitates-phase-forming mechanism in the proposed HEA.

Back to tab navigation

Article information


Submitted
27 Sep 2019
Accepted
02 Jan 2020
First published
06 Jan 2020

Nanoscale, 2020, Accepted Manuscript
Article type
Paper

An as-cast high-entropy alloy with remarkable mechanical properties strengthened by nanometer precipitates

G. Qin, R. Chen, P. K. Liaw, Y. Gao, L. Wang, Y. Su, H. Ding, J. Guo and X. Li, Nanoscale, 2020, Accepted Manuscript , DOI: 10.1039/C9NR08338C

Social activity

Search articles by author

Spotlight

Advertisements