The large piezoelectricity and high power density of a 3D-printed multilayer copolymer in a rugby ball-structured mechanical energy harvester

Author affiliations

Abstract

Piezoelectric polymers are characterized by their flexibility and ease of processing into shapes, however, their piezoelectric coefficients, such as d33, are quite low (∼24 pC N−1). Here we report a 3D-printed multilayer β-phase PVDF-TrFE copolymer which does not require high temperature annealing or complicated transfer processes and exhibits a much higher effective piezoelectric coefficient (d33 ∼ 130 pC N−1 for six 10 μm layers). In order to confirm its high power density, a rugby ball-shaped energy harvester, which operates via a flextensional mechanism, was prepared using the multilayer copolymer. The experimental results show that it can produce a peak voltage of ∼88.62 Vpp and a current of 353 μA, which are 2.2 and 10 times those of a single-layer PVDF-TrFE harvester, respectively, under a pressure of 0.046 MPa. Notably, its peak output power density was as high as 16.4 mW cm−2 (according to Ppeak = (VpeakIshort)/2); while at a load of 568 kΩ, it was still 5.81 mW cm−2. The proposed copolymer processing method and flextensional mechanism in a rugby ball configuration show great potential for future micro-energy development in flexible, wearable electronic devices and wireless sensor networks.

Graphical abstract: The large piezoelectricity and high power density of a 3D-printed multilayer copolymer in a rugby ball-structured mechanical energy harvester

Back to tab navigation

Supplementary files

Article information


Submitted
04 Jun 2019
Accepted
14 Oct 2019
First published
15 Oct 2019

Energy Environ. Sci., 2020,13, 152-161
Article type
Paper

The large piezoelectricity and high power density of a 3D-printed multilayer copolymer in a rugby ball-structured mechanical energy harvester

X. Yuan, X. Gao, J. Yang, X. Shen, Z. Li, S. You, Z. Wang and S. Dong, Energy Environ. Sci., 2020, 13, 152
DOI: 10.1039/C9EE01785B

Social activity

Search articles by author

Spotlight

Advertisements