Compatibility driven self-strengthening during radical-responsive remolding process of poly-isoprene vitrimers

Abstract

Vitrimers usually show decreased mechanical properties after welding, recycling or remolding processes due to the hysteresis of topology network rearrangement. Herein, we propose a strategy for developing self-strengthening vitrimers whose mechanical properties increase upon network rearrangement. Such vitrimers are constructed based on the exchangeable β-hydroxyl ester network formed by two immiscible polymers, epoxidized polyisoprene (EPIP) and poly-(thioctic acid) (PTA). A radical capture agent, 1,3-diisopropenylbenzene (DIB), is introduced into the vitrimers. DIB is miscible with EPIP while immisible with PTA, yet it can react with PTA by capturing the free radicals released by the dynamic disulfide bonds of PTA at high temperature, thereby improving the compatibility between EPIP and PTA during network rearrangement. As a result, more β-hydroxyl ester linkages are formed between EPIP and PTA, and the density of crosslinking network in the vitrimers increases after repeated remolding process, which result in the improved mechanical properties after network rearrangement. This strategy of compatibility driven self-strengthening can be easily extended to other vitrimers composed of immscible components.

Back to tab navigation

Supplementary files

Publication details

The article was received on 23 Aug 2019, accepted on 11 Oct 2019 and first published on 12 Oct 2019


Article type: Paper
DOI: 10.1039/C9TA09292G
J. Mater. Chem. A, 2019, Accepted Manuscript

  •   Request permissions

    Compatibility driven self-strengthening during radical-responsive remolding process of poly-isoprene vitrimers

    F. Ling, Z. Liu, M. Chen, H. Wang, Y. Zhu, C. Ma, J. Wu and G. Huang, J. Mater. Chem. A, 2019, Accepted Manuscript , DOI: 10.1039/C9TA09292G

Search articles by author

Spotlight

Advertisements