Accelerated Li–S Chemistry at A Cooperative Interface Built In Situ

Abstract

The performances of lithium–sulfur (Li–S) batteries have been markedly handicapped by the intricate multi-electron sulfur chemistry involving reversible conversion of polysulfides (LiPSs) to Li2S upon discharge and back to S8 upon charge. Herein, graphene in-situ coated TiO2 nanotube is realized via direct chemical vapor deposition (CVD) techinique, leading to the design of graphene-TiO2 (G-TiO2) promotor for Li–S chemistry. With the aid of detailed experimental and theoretical characterizations, we reveal that the direct CVD-derived G-TiO2 realizes not only the coupling of Li+-ion diffusion and electron transfer but also efficient regulation of LiPSs, thereby producing synergistic catalyzing effect on both LiPS conversion and Li2S decomposition. As a result, S/graphene-TiO2 (S/G-TiO2) presents a remarkable rate capability and an ultralow capacity decay rate of 0.052% over 1000 cycles at 2.0 C. Even at a high sulfur loading of 9.4 mg cm–2, such cathode still delivers superior areal capacity of 8.7 mAh cm–2. This work would motivate the deep-seated revisiting of sulfur reaction mechanism and offer a rational strategy to construct high-energy and long-life Li–S batteries.

Back to tab navigation

Supplementary files

Publication details

The article was received on 08 Jul 2019, accepted on 12 Aug 2019 and first published on 12 Aug 2019


Article type: Paper
DOI: 10.1039/C9TA07342F
J. Mater. Chem. A, 2019, Accepted Manuscript

  •   Request permissions

    Accelerated Li–S Chemistry at A Cooperative Interface Built In Situ

    Y. Song, Z. Sun, J. Cai, N. Wei, M. Wang, Y. Shao, Z. Liu and J. Sun, J. Mater. Chem. A, 2019, Accepted Manuscript , DOI: 10.1039/C9TA07342F

Search articles by author

Spotlight

Advertisements