Mechanism of magnetic heating in Mn-doped magnetite nanoparticles and role of the intertwined structural and magnetic properties


We study the mechanism of heat generation, induced by an alternating magnetic field, in magnetite nanoparticles doped with manganese, produced by thermal decomposition from organometallic precursors. We investigate a set of four samples obtained by varying the duration of the reflux treatment carried out at the temperature of 300 °C during the synthetic procedure. On increasing this parameter from 60 to 180 minutes, the mean size of the nanoparticles increases, though remaining below 10 nm, as well as the saturation magnetization, which in all the samples, thanks to the Mn doping, is higher than in magnetite nanoparticles taken as a reference. The combination of these two events has two main consequences. First, it determines the intensity of the dipolar interactions between the nanoparticles, thus influencing their magnetic relaxing behavior, which, in turn, is closely related to the heating efficiency. Secondly, in a heating test, it is possible to operate in the regime of non-linear magnetic response of the nanoparticles at values of amplitude and frequency of the alternating field usually employed for biomedical applications. We show that, in this regime, the Specific Absorption Rate (SAR) in each sample depends linearly on the fraction of nanoparticles that are not superparamagnetic. This opens to the possibility of modulating the heating capacity of the produced nanoparticles, so as to match specific needs, changing only a single synthesis parameter and opportunely exploiting the strict connection between structural features, magnetic properties and measurement conditions.

Back to tab navigation

Supplementary files

Publication details

The article was accepted on 02 May 2019 and first published on 03 May 2019

Article type: Paper
DOI: 10.1039/C9NR03131F
Nanoscale, 2019, Accepted Manuscript

  •   Request permissions

    Mechanism of magnetic heating in Mn-doped magnetite nanoparticles and role of the intertwined structural and magnetic properties

    L. Del Bianco, F. Spizzo, G. Barucca, M. R. Ruggiero, S. Geninatti Crich, M. Forzan, E. Sieni and P. Sgarbossa, Nanoscale, 2019, Accepted Manuscript , DOI: 10.1039/C9NR03131F