Enhanced desalination of electrospun activated carbon fibers with controlled pore structures in electrosorption process

Abstract

Capacitive deionization (CDI) is a promising ion-separation technology with energy-efficient features for low-salinity desalination. However, the electrosorption capacity limitation is a central challenge due to irregular pore structures and the use of polymer binder in porous carbon electrodes. The aim of this study is to prepare electrospun activated carbon fiber (ACF) webs with well-controlled hierarchical porous structures as a high-performance, binder-free electrode for electrosorption of ions. For characterization of electrospun ACF, nitrogen adsorption-desorption measurements, Raman spectroscopy, scanning electron microscopy, and cyclic voltammetry tests were carried out. As demonstrated, the electrospun ACFs, prepared from polyacrylonitrile by electrospinning and subsequent oxidation, carbonization, and activation processes with N2/CO2 at 900 °C for 90 min, had a high specific surface area of 1300 m2/g and a 39% increase in mesopores relative to total pore volume. In addition, electrospun ACFs with a high degree of graphitization have good capacitive behaviors for ion storage. As a result of batch-mode CDI experiments at 1.6 V, the electrospun ACFs had a promising electrosorption capacity of 10.53 mg/g and good cycling performance. Note that the electrosorption capacity of membrane CDI was three times higher than that of CDI. The significant improvement could be ascribed to additional interfiber porosity, which serves as ion-buffering reservoirs in the electrosorption process. Consequently, by controlling the electrospinning and activation processes without additives, high-performance CDI can be achieved using electrospun ACF electrodes, which have good conductivity and favorable pore structures (e.g., high specific surface area, large pore volume, and enhanced mesoporosity) for electrosorption of ions.

Back to tab navigation

Publication details

The article was received on 30 Aug 2019, accepted on 07 Nov 2019 and first published on 08 Nov 2019


Article type: Paper
DOI: 10.1039/C9EW00751B
Environ. Sci.: Water Res. Technol., 2019, Accepted Manuscript

  •   Request permissions

    Enhanced desalination of electrospun activated carbon fibers with controlled pore structures in electrosorption process

    N. Liu , L. Chen, S. Tsai and C. Hou, Environ. Sci.: Water Res. Technol., 2019, Accepted Manuscript , DOI: 10.1039/C9EW00751B

Search articles by author

Spotlight

Advertisements