Porous NiCoP in situ grown on Ni foam using molten-salt electrodeposition for asymmetric supercapacitors

Author affiliations

Abstract

The construction of in situ grown porous structures can enlarge the contact area between electrodes and electrolyte and shorten the distance for ion diffusion, boosting the electrochemical properties of electrode materials. Herein, we combine molten-salt electrodeposition and AlP-assisted solvothermal phosphorization to design porous NiCoP in situ grown on Ni foam (p-NiCoP/NF). Even with a high mass loading of 10.1 mg cm−2, the as-prepared p-NiCoP/NF exhibits a remarkable mass specific capacity (Qm) of 1279.2 C g−1 (0.99 A g−1) and good rate capability. Furthermore, the p-NiCoP/NF//AC device, assembled using p-NiCoP/NF and active carbon (AC), presents a high energy density of 45.5 W h kg−1 at a power density of 124.2 W kg−1 and superior cycling stability (92.86% retention after 10 000 cycles). Finally, we introduce a four-electrode system to study the effect of the potential window of the positive and negative electrodes in an asymmetric supercapacitor (ASC) on its energy density, where it boosts the energy density and rate capability at the optimal working state.

Graphical abstract: Porous NiCoP in situ grown on Ni foam using molten-salt electrodeposition for asymmetric supercapacitors

Back to tab navigation

Supplementary files

Publication details

The article was received on 13 Sep 2018, accepted on 31 Oct 2018 and first published on 01 Nov 2018


Article type: Paper
DOI: 10.1039/C8TA08897G
Citation: J. Mater. Chem. A, 2018,6, 23746-23756

  •   Request permissions

    Porous NiCoP in situ grown on Ni foam using molten-salt electrodeposition for asymmetric supercapacitors

    Z. Huang, X. Li, X. Xiang, T. Gao, Y. Zhang and D. Xiao, J. Mater. Chem. A, 2018, 6, 23746
    DOI: 10.1039/C8TA08897G

Search articles by author

Spotlight

Advertisements