Understanding the loss of electrochemical activity of nanosized LiMn2O4 particles: a combined experimental and ab initio DFT study

Author affiliations

Abstract

In the field of Li-ion batteries (LIBs), one prevalent expectation is that smaller sized electrode materials lead to better battery performances. Here, we show that this reasoning fails for nanoparticles of LiMn2O4 (LMO) below a certain critical average size. For this, using a microwave-assisted hydrothermal methodology and heat treatment, we obtained spinel LMO nanoparticles with genuinely small average sizes (4, 9, and 14 nm). When the performance of these LMOs for the Li-ion extraction/insertion processes was assessed by voltammetry and impedance spectroscopy, contrary to expectations, the decrease of the nanoparticle size caused a progressive hindrance of these processes. Using an ab initio DFT methodology, this phenomenon could be accounted for with a theoretical explanation for the significantly decreased electrochemical activity of the smallest LMO nanoparticles. We found that the redox voltage associated with the Li-ion insertion process becomes significantly higher as the average size of the nanoparticles decreases from 14 to 1.3 nm, changing from 3.93 to 4.64 V, thus hindering the process. We could also show that the redox voltage increase is due to a consequent significant increase of the energy barrier for Li-ion diffusion within the smaller LMO nanocrystallite, from 0.33 to at least 0.59 eV, caused by atomic relaxations (mainly of oxygen atoms) occurring on the surface of such a nanosystem. Clearly, when very small LMO nanocrystallites are intended for use as cathode materials in LIBs, the average nanoparticle size should not be smaller than the critical value of ∼15 nm; otherwise Li-ion extraction–insertion becomes significantly hindered or unfeasible.

Graphical abstract: Understanding the loss of electrochemical activity of nanosized LiMn2O4 particles: a combined experimental and ab initio DFT study

Back to tab navigation

Publication details

The article was received on 23 Mar 2018, accepted on 09 Jul 2018 and first published on 10 Jul 2018


Article type: Paper
DOI: 10.1039/C8TA02703J
Citation: J. Mater. Chem. A, 2018, Advance Article
  •   Request permissions

    Understanding the loss of electrochemical activity of nanosized LiMn2O4 particles: a combined experimental and ab initio DFT study

    E. A. Velásquez, D. P. B. Silva, J. B. Falqueto, J. Mejía-López, N. Bocchi, R. del Rio, J. Mazo-Zuluaga, R. C. Rocha-Filho and S. R. Biaggio, J. Mater. Chem. A, 2018, Advance Article , DOI: 10.1039/C8TA02703J

Search articles by author

Spotlight

Advertisements