Domain engineering and full matrix material constants of the [111]c-poled 0.63Pb(Mg1/3Nb2/3)-0.37PbTiO3 single crystal

Author affiliations

Abstract

Domain engineering was performed on the [111]c-oriented tetragonal ferroelectric 0.63Pb(Mg1/3Nb2/3)-0.37PbTiO3 (PMN-0.37PT) single crystal in order to achieve better piezoelectric properties. Influences of the poling electric field (EP), poling temperature, and poling time on piezoelectric and electromechanical properties were investigated. The piezoelectric and dielectric constants increase with increasing the EP. In addition, the piezoelectric response increases with increasing the poling time but the crystal saturates after 10 min of poling at 30 °C or 20 min at 150 °C under EP = 2 kV mm−1. The piezoelectric strain coefficient d33 can be improved from 407 pC N−1 poled at 30 °C to 706 pC N−1 after poling at 150 °C near TC, which is 27.9% higher than the highest value reported before (d33 = 551.9 pC N−1). The enhancement of piezoelectric response results from the domain structure redistribution occurring near the ferroelectric to paraelectric phase transition temperature because the potential barrier is substantially lowered so that polarization switching becomes easier. Therefore, more domain walls appear to be beneficial for the enhancement of the piezoelectric response. Under the optimized poling conditions, a complete set of dielectric, elastic, and piezoelectric constants was measured for [111]c-poled PMN-0.37PT single crystal using a combined resonance and ultrasonic method (CRUM). Both the longitudinal (d33 = 706 pC N−1) and shear (d15 = 875 pC N−1) piezoelectric properties are outstanding for the [111]c-poled PMN-0.37PT single crystal due to domain wall motions.

Graphical abstract: Domain engineering and full matrix material constants of the [111]c-poled 0.63Pb(Mg1/3Nb2/3)-0.37PbTiO3 single crystal

Back to tab navigation

Publication details

The article was received on 20 May 2018, accepted on 11 Jul 2018 and first published on 11 Jul 2018


Article type: Paper
DOI: 10.1039/C8CE00831K
Citation: CrystEngComm, 2018,20, 4745-4751
  •   Request permissions

    Domain engineering and full matrix material constants of the [111]c-poled 0.63Pb(Mg1/3Nb2/3)-0.37PbTiO3 single crystal

    Z. Yuan, S. Sang, E. Sun, X. Qi, W. Chang, R. Zhang, B. Yang, X. Jiang and W. Cao, CrystEngComm, 2018, 20, 4745
    DOI: 10.1039/C8CE00831K

Search articles by author

Spotlight

Advertisements