Optimizing crystallinity and porosity of hierarchical Ni(OH)2 through conformal transformation of metal-organic framework template for supercapacitor applications

Abstract

MOFs (metal-organic frameworks) are recently widely utilized as both the templates and precursors to prepare nanomaterials as supercapacitor electrodes. However, traditional thermalysis routs are difficult to control and usually lead to collapse of the MOF skeletons, which hinders the widely applications. Herein, we describe a simple and facile strategy for fabricating Ni(OH)2 hierarchical structure through the “conformal transformation” of one particular Ni-MOF through hydrolysis in the KOH aqueous solution. By controlling the concentration of KOH solution and the soaking time, the obtained Ni(OH)2 nanomaterial possesses both optimized crystallinity and porosity, extremely beneficial for electron transportation and ion migration within the electrodes. Taking these advantages, the Ni(OH)2 electrode presents remarkable specific capacity of 830.6 C∙g-1, and the fabricated all-solid state asymmetric supercapacitor presents remarkable energy density of 37.8 W∙h∙kg-1 at the power density of 252.67 W∙kg-1, which surpasses most Ni(OH)2 based supercpacitor devices. After 10000 cycles, the capacitance maintains at over 98% of the initial value.

Back to tab navigation

Supplementary files

Publication details

The article was received on 06 May 2018, accepted on 29 Jun 2018 and first published on 03 Jul 2018


Article type: Paper
DOI: 10.1039/C8CE00741A
Citation: CrystEngComm, 2018, Accepted Manuscript
  •   Request permissions

    Optimizing crystallinity and porosity of hierarchical Ni(OH)2 through conformal transformation of metal-organic framework template for supercapacitor applications

    H. Zhang, B. Xu, Z. Xiao, H. Mei, L. Zhang, Y. Han and D. Sun, CrystEngComm, 2018, Accepted Manuscript , DOI: 10.1039/C8CE00741A

Search articles by author

Spotlight

Advertisements