A conversion-based highly energy dense Cu2+ intercalated Bi-birnessite/Zn alkaline battery

Author affiliations


Manganese dioxide (MnO2)–zinc (Zn) batteries are cheap and environmentally benign and have sufficient theoretical energy density to be used as an energy storage device for the grid; however, they have been relegated to primary systems, where the complete energy is delivered in a single discharge, due to the irreversibility of their active materials. Until recently, rechargeable MnO2–Zn batteries have only been able to cycle ∼10% of MnO2's theoretical 2-electron capacity (617 mA h g−1), thus delivering significantly reduced energy density. In a recent paper from our group, we reversibly accessed the full theoretical 2-electron capacity of MnO2 for >6000 cycles by using a layered polymorph of MnO2 mixed with bismuth oxide (Bi2O3) called Bi-birnessite (Bi–δ-MnO2) intercalated with Cu2+ ions. This discovery highlighted the possibility of achieving very high energy densities from inexpensive aqueous batteries; however, a full-cell demonstration with Zn as the anode was not studied. Here we report for the first time the effect of Zn anodes on the cycle life and energy density of a full cell, where we observe that 15% depth-of-discharge (DOD) of the Zn's theoretical capacity (820 mA h g−1) creates a cell energy density of ∼160 W h L−1; however, this causes a drastic shape change and formation of irreversible zinc oxide (ZnO) at the anode, which ultimately causes cell failure after ∼100 cycles. A drop in energy density is also observed as a result of the interaction of dissolved Zn ions with the cathode, which forms a resistive Zn-birnessite compound in the early cycles, and then forms a highly resistive haeterolite (ZnMn2O4) in the later cycles, and ultimately causes cathode failure. A possible solution using a calcium hydroxide layer as a separator is presented, where the layer blocks the interaction of zinc ions through a complexing mechanism to obtain >900 cycles with >80% retention of MnO2 DOD.

Graphical abstract: A conversion-based highly energy dense Cu2+ intercalated Bi-birnessite/Zn alkaline battery

Back to tab navigation

Publication details

The article was received on 19 Jun 2017, accepted on 05 Jul 2017 and first published on 05 Jul 2017

Article type: Paper
DOI: 10.1039/C7TA05347A
Citation: J. Mater. Chem. A, 2017,5, 15845-15854

  •   Request permissions

    A conversion-based highly energy dense Cu2+ intercalated Bi-birnessite/Zn alkaline battery

    G. G. Yadav, X. Wei, J. Huang, J. W. Gallaway, D. E. Turney, M. Nyce, J. Secor and S. Banerjee, J. Mater. Chem. A, 2017, 5, 15845