Effects of water on low-overpotential CO2 reduction in ionic liquid studied by sum-frequency generation spectroscopy

Abstract

We used vibrational sum-frequency generation spectroscopy (SFG) to investigate low-overpotential CO₂ reduction on a polycrystalline Ag electrode using room temperature ionic liquid (RTIL), 1-ethyl-3-methylimidazolium tetrafluorborate (EMIM-BF₄) electrolyte mixtures with 0.3 mol%, 45 mol% and 77 mol% water. Adding water dramatically increases CO₂ reduction efficiency up to 87.5 mol%. We found added water reduces the (negative) threshold potential for CO₂ reduction from −1.33 V to −0.9 V. Added water also moved the potentials of the nonresonant (NR) SFG minima and caused the CO Stark shift to increase in concert with the reduction threshold. In previous work (N. García Rey and D. D. Dlott, J. Phys. Chem. C, 2015, 119, 20892–20899), with nearly-dry RTIL electrolyte (0.3 mol% water), we concluded a potential-driven structural transition of RTIL in the double layer controlled CO₂ reduction. At lower water concentrations, where CO₂ reduction was less efficient, CO product appeared primarily on Ag atop sites. At higher water concentrations where CO₂ reduction efficiency was greater, adsorbed CO was observed on multiply-bonded sites, which are likely more efficient catalytic sites.