A g-C3N4/WO3 photoanode with exceptional ability for photoelectrochemical water splitting

Author affiliations

Abstract

Herein, we report a photoanode of g-C3N4/WO3 heterojunctions with exceptional ability and stability for photoelectrochemical (PEC) water splitting which achieved a high photocurrent density of 1.92 mA cm−2 at +1.23 V versus (vs.) RHE which is about 2 times higher than that of the pristine WO3 photoanode (0.71 mA cm−2).

Graphical abstract: A g-C3N4/WO3 photoanode with exceptional ability for photoelectrochemical water splitting

Back to tab navigation

Supplementary files

Publication details

The article was received on 11 Apr 2016, accepted on 31 May 2016 and first published on 12 Aug 2016


Article type: Research Article
DOI: 10.1039/C6QM00009F
Mater. Chem. Front., 2017,1, 338-342

  •   Request permissions

    A g-C3N4/WO3 photoanode with exceptional ability for photoelectrochemical water splitting

    H. Li, F. Zhao, J. Zhang, L. Luo, X. Xiao, Y. Huang, H. Ji and Y. Tong, Mater. Chem. Front., 2017, 1, 338
    DOI: 10.1039/C6QM00009F