From solid to core@shell to hollow Pt–Ag nanocrystals: thermally controlled surface segregation to enhance catalytic activity and durability

Author affiliations

Abstract

Hollow bimetallic nanostructures exhibit increased durability and utilization efficiency compared to their solid counterparts, and therefore have become promising new candidates for catalytic applications. Here we demonstrate that hollow structured Pt–Ag nanocrystals can be fabricated through a simple one-pot synthesis by employing thermal treatment. During the reaction, Ag-rich Pt–Ag alloy nanocrystals were obtained shortly after co-reduction of Pt and Ag precursors. Subsequent reduction of Pt on the surface of the nanocrystals induced the alloyed Pt atoms to migrate outward to form Ag@Pt core@shell nanocrystals. They finally evolved into hollow alloy structures at an elevated temperature due to the surface energy difference of the metals and the Kirkendall effect. The hollow Pt–Ag nanocatalysts exhibited a substantial enhancement in the current density at 0.9 V and CO-tolerance toward the methanol oxidation reaction, and also showed excellent durability in acid media for methanol oxidation and in alkaline media for p-nitrophenol reduction. This new method of synthesizing hollow nanocrystals can be used towards the design and fabrication of a wide range of Pt-based bimetallic hollow nanostructures.

Graphical abstract: From solid to core@shell to hollow Pt–Ag nanocrystals: thermally controlled surface segregation to enhance catalytic activity and durability

Back to tab navigation

Supplementary files

Publication details

The article was received on 08 Apr 2016, accepted on 03 May 2016 and first published on 04 May 2016


Article type: Paper
DOI: 10.1039/C6TA02914K
J. Mater. Chem. A, 2016,4, 9038-9043

  •   Request permissions

    From solid to core@shell to hollow Pt–Ag nanocrystals: thermally controlled surface segregation to enhance catalytic activity and durability

    S. Chen, S. Thota, X. Wang and J. Zhao, J. Mater. Chem. A, 2016, 4, 9038
    DOI: 10.1039/C6TA02914K

Search articles by author

Spotlight

Advertisements