Temperature-controlled synthesis, thermodynamics and field emission properties of β-SiC/SiO2 coaxial heterojunction emitters

Author affiliations

Abstract

β-SiC/SiO2 coaxial heterogeneous emitters composed of a SiC nanowire core and a uniform amorphous SiO2 coating have been fabricated via the chemical vapor deposition (CVD) technique. The effect of synthesis temperature on the yield, microstructure, and chemical composition of the products was systematically analysed. A rational explanation for the growth of the β-SiC/SiO2 emitter was proposed and analysed from the perspective of the reaction thermodynamics. The field emission behaviors of the β-SiC/SiO2 coaxial nanocables exhibit a strong dependence on the synthesis temperatures. Excellent performances with a low turn-on field (Eto) of 0.63 V μm−1 and threshold field (Eth) of 1.92 V μm−1 have been recorded at 1200 °C. Furthermore, the optimized cathode shows remarkable electron emission stability with the fluctuation of the current density being less than 5.7% after a 3 h long lifetime test.

Graphical abstract: Temperature-controlled synthesis, thermodynamics and field emission properties of β-SiC/SiO2 coaxial heterojunction emitters

Back to tab navigation

Article information


Submitted
17 Mar 2016
Accepted
06 Jun 2016
First published
07 Jun 2016

RSC Adv., 2016,6, 56489-56494
Article type
Communication

Temperature-controlled synthesis, thermodynamics and field emission properties of β-SiC/SiO2 coaxial heterojunction emitters

M. Zhang, Z. Li, J. Zhao, H. Yu, A. Meng and Q. Li, RSC Adv., 2016, 6, 56489
DOI: 10.1039/C6RA07053A

Social activity

Search articles by author

Spotlight

Advertisements