Synthesis of high-purity, layered structured K2Ta4O11 intermediate phase nanocrystals for photocatalytic water splitting

Abstract

High-purity K2Ta4O11 (kalitantite) intermediate phase with a layered structure, as a new family member of alkali-metal tantalate semiconductors, was successfully prepared via a simple and cost-effective flux growth technique using potassium chloride (KCl) at a low temperature of 800 °C for only 4 h. The as-synthesized K2Ta4O11 was characterized by XRD, SEM, TEM, STEM/EDS, and UV-Vis DRS, etc. It was found that the K2Ta4O11 single nanocrystals were non-stoichiometric in the size range of 100–500 nm, and the indirect band gap of K2Ta4O11 was correctly determined to be 4.15 eV. The K2Ta4O11 not only exhibited a high and stable photocatalytic H2 generation rate of ∼45.3 μmol h−1 g−1 in an aqueous methanolic solution with the photodeposition of Pt as co-catalysts, but also possessed the photocatalytic ability for simultaneous evolution of H2 and O2 in a stoichiometric ratio, with loading of NiO particles as cocatalysts. Thus, it can be mainly attributed to the benefits of KCl flux lowing the reaction temperature, and increasing the surface area and crystallinity of K2Ta4O11, that the charge efficiency and enhancement of the photoreactivity for water splitting are improved.

Graphical abstract: Synthesis of high-purity, layered structured K2Ta4O11 intermediate phase nanocrystals for photocatalytic water splitting

Article information

Article type
Paper
Submitted
29 Apr 2016
Accepted
01 Jul 2016
First published
04 Jul 2016

Phys. Chem. Chem. Phys., 2016,18, 25831-25836

Synthesis of high-purity, layered structured K2Ta4O11 intermediate phase nanocrystals for photocatalytic water splitting

P. Wang, F. Sun, J. H. Kim, J. H. Kim, J. Yang, X. Wang and J. S. Lee, Phys. Chem. Chem. Phys., 2016, 18, 25831 DOI: 10.1039/C6CP02868C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements