A novel flux coating method for the fabrication of layers of visible-light-responsive Ta3N5 crystals on tantalum substrates

Abstract

Layers of well-developed crystals of Ta3N5 were successfully fabricated on Ta substrates by using a novel flux coating method in a flow of NH3. The flux coating method is a simple one: the Ta substrates were coated with aqueous solutions of sodium compounds (= fluxes) and subsequently heated in a flow of NH3, whereupon the surfaces of the Ta substrates were dissolved in the flux, resulting in Ta3N5 crystal layers. The Ta in Ta3N5 was provided by the substrate. Therefore, crystal layers with good adhesion could be grown directly on the substrates. The shape of the individual crystals as well as the surface morphology of the layers formed was determined by the flux used. The crystals fabricated using NaCl–Na2CO3 as the flux were prismatic and had relatively smooth faces, covering the surface of the Ta substrate uniformly. The crystal growth field resulting from the use of this method yielded well-formed crystals, which presumably grew from a solution. Finally, it was confirmed that a thus-synthesized Ta3N5 crystal layer modified using Co-Pi as the co-catalyst generated a photoanodic current under visible-light irradiation.

Graphical abstract: A novel flux coating method for the fabrication of layers of visible-light-responsive Ta3N5 crystals on tantalum substrates

Supplementary files

Article information

Article type
Paper
Submitted
07 Mar 2015
Accepted
21 May 2015
First published
22 May 2015

J. Mater. Chem. A, 2015,3, 13946-13952

Author version available

A novel flux coating method for the fabrication of layers of visible-light-responsive Ta3N5 crystals on tantalum substrates

S. Suzuki, H. Wagata, M. Komatsus, T. Minegishi, K. Domen, S. Oishi and K. Teshima, J. Mater. Chem. A, 2015, 3, 13946 DOI: 10.1039/C5TA01724F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements