Efficient and stable polymer solar cells with annealing-free solution-processible NiO nanoparticles as anode buffer layers

Abstract

Annealing-free solution-processible nickel oxide (NiO) nanoparticles are prepared via sonochemical synthesis. In contrast to the common sol–gel route to prepare a NiOx film that had to undergo high-temperature post-annealing to be converted into NiO nanoparticles, herein, colloidal crystalline NiO nanoparticles with diameters of 4–8 nm are prepared with the metal salt at low temperature via ultrasonic irradiation. The colloidal crystalline NiO nanoparticles were directly used as the anode buffer layer in polymer solar cells (PSCs) without post-thermal annealing, which was compatible with flexible substrates and low-cost high-throughput fabrication. After O2-plasma treatment to the as-deposited buffer layer of NiO nanoparticles, the ITO/NiO contact work function was increased from −4.8 to −5.3 eV, providing superior contact with the highest occupied molecular orbital energy levels of polymer donors. Compared to PCDTBT:PC70BM PSCs with a PEDOT:PSS buffer layer, the power conversion efficiency of PSCs with an O2-plasma treated anode buffer layer of NiO nanoparticles was increased from 5.84% to 6.30% and the device stability was also enhanced.

Graphical abstract: Efficient and stable polymer solar cells with annealing-free solution-processible NiO nanoparticles as anode buffer layers

Article information

Article type
Paper
Submitted
19 Jun 2014
Accepted
06 Aug 2014
First published
03 Sep 2014

J. Mater. Chem. C, 2014,2, 8295-8302

Efficient and stable polymer solar cells with annealing-free solution-processible NiO nanoparticles as anode buffer layers

J. Zhang, J. Wang, Y. Fu, B. Zhang and Z. Xie, J. Mater. Chem. C, 2014, 2, 8295 DOI: 10.1039/C4TC01302F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements