Zeolite microspheres with hierarchical structures: formation, mechanism and catalytic performance

Abstract

An improved polymerization-induced colloid aggregation (im-PICA) method was developed to prepare zeolite microspheres (ZMSs) with a hierarchical porous structure and a uniform size, which could easily be carried out within half an hour by simply adding urea and formaldehyde into an acidic pH-pre-controlled colloidal solution as-obtained from a hydrothermal crystallization process. This procedure successfully avoided the repeated ultrasonic washing and high-speed centrifugation of the nanozeolite colloid during the traditional PICA method, and thereby became energy and time-economical. After removing the polymeric component, solid and hollow ZMSs as well as the mono-dispersed nanozeolite can be obtained under different preparation conditions. The structural transformation could be attributed to the correlation of the polymerization velocity on the zeolite nanocrystal surface and in the bulk solution with variation of acidity. Due to the short diffusion routes and abundant exposed active sites of nanozeolites as well as their unique secondary mesopore architecture, ZMSs displayed a clear advantage on catalysis reactions compared to commercial zeolite catalysts, such as the dehydration of fructose into 5-hydromethyl furfural.

Graphical abstract: Zeolite microspheres with hierarchical structures: formation, mechanism and catalytic performance

Supplementary files

Article information

Article type
Paper
Submitted
18 Apr 2011
Accepted
11 Aug 2011
First published
14 Sep 2011

J. Mater. Chem., 2011,21, 16223-16230

Zeolite microspheres with hierarchical structures: formation, mechanism and catalytic performance

Y. Shi, X. Li, J. Hu, J. Lu, Y. Ma, Y. Zhang and Y. Tang, J. Mater. Chem., 2011, 21, 16223 DOI: 10.1039/C1JM11669J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements