Polymer surface nano-structuring of reverse osmosismembranes for fouling resistance and improved flux performance

Author affiliations


A new class of surface-structured RO membranes was developed with a hydrophilic brush layer of terminally anchored polymer chains resulting in fouling resistant membranes of low mineral scaling propensity and high permeability. The approach is based on free-radical graft polymerization of a suitable monomer, onto the active polyamide (PA) layer of a thin film composite (PA-TFC) membrane, post-surface activation with an impinging atmospheric pressure plasma source. Two types of nano-structured (SNS) RO membranes (SNS-PA-TFC) were synthesized based on methacrylic acid (MAA-SNS-PA-TFC) and acrylamide (AA-SNS-PA-TFC) graft polymerization. The poly(methacrylic acid) and poly(acrylamide) brush layers, on the PA surface, resulted in RO membranes of significantly lower mineral scaling propensity, evaluated with respect to the mineral scalant calcium sulfate dihydrate, compared with commercial RO membrane (LFC1) of about the same salt rejection (∼95%) and surface roughness (∼70 nm). Direct membrane surface imaging indicated that the rate of nucleation and thus mineral scaling were reduced owing to the polymer brush layer. Fouling resistance of the SNS-PA-TFC membranes was also demonstrated with respect to model foulants (the protein BSA and alginic acid). The MAA-SNS-PA-TFC and AA-SNS-PA-TFC membranes had a negatively charged and near neutral surfaces, respectively, with water contact angles somewhat lower for the former and higher for the latter membranes relative to the LFC1 membrane. The AA-SNS-PA-TFC membrane displayed lower mineral scaling propensity than the MAA based membrane, although its alginic acid fouling resistance was inferior, despite its lower surface roughness (25–33 nm) relative to the MAA-SNS-PA-RFC (∼60–80 nm) and LFC1 (∼73 nm) membranes.

Graphical abstract: Polymer surface nano-structuring of reverse osmosis membranes for fouling resistance and improved flux performance

Back to tab navigation

Article information

22 Dec 2009
04 Mar 2010
First published
30 Mar 2010

J. Mater. Chem., 2010,20, 4642-4652
Article type

Polymer surface nano-structuring of reverse osmosis membranes for fouling resistance and improved flux performance

N. H. Lin, M. Kim, G. T. Lewis and Y. Cohen, J. Mater. Chem., 2010, 20, 4642
DOI: 10.1039/B926918E

Search articles by author