Shintaro
Niwa
a,
Shuhei
Hashimoto
a,
Duotian
Chen
b,
Takashi
Toyao
b,
Ken-ichi
Shimizu
b and
Masaaki
Sadakiyo
*a
aDepartment of Applied Chemistry, Faculty of Science Division I, Tokyo University of Science, 1-3 Kagurazaka, Shinjuku-ku, Tokyo 162-8601, Japan. E-mail: sadakiyo@rs.tus.ac.jp
bInstitute for Catalysis, Hokkaido University, Sapporo, Hokkaido 001-0021, Japan
First published on 15th July 2024
We report on the synthesis and high ionic conductivity of a highly crystalline Mg2+-containing metal–organic framework (MOF) with Type A feature (i.e., anionic framework having Mg2+ as a counter cation). We synthesized Mg[Zr(C14H3O8)2] (SU-102-Mg) through ion exchange reaction. SU-102-Mg showed a high ionic conductivity of 3.6 × 10−5 S cm−1 (25 °C, under MeCN vapor).
Conversely, metal–organic framework (MOF)-based ionic conductors have recently been extensively developed because of their highly regular and designable pores, which could act as ion-conducting pathways for various ionic carriers.4,5 In the case of the Mg2+ carrier, we recently found that MOFs containing Mg2+ carriers in the pores exhibit drastic enhancement of ionic conductivity under the vapor of small organic guest molecules (e.g., MeCN), termed vapor-induced ionic conduction.6 It is also reported that the Mg2+-containing MOFs are classified into two types (i.e., Type A: Mg2+ carriers introduced as counter cations of the anionic framework; Type B: Mg2+ carriers introduced as Mg2+ salts).4 So far, several examples of Type B compounds showing superionic conductivity under the vapor of optimal guest molecules have been reported.6–8 Although Type A compounds, prepared through ion exchange reaction, potentially have advantages when applied to the secondary battery (e.g., high transport number), only one compound, MOF-688-Mg, which exhibits low crystallinity, has been reported to date.9 Because its conductivity (1.3 × 10−5 S cm−1, 25 °C)9 is still much lower than that of Type B compounds (e.g., MIL-101⊃{Mg(TFSI)2}1.6: 1.9 × 10−3 S cm−1, 25 °C),7 the further development of Type A compounds is highly desired.
Here, we report on a highly crystalline Mg2+-conducting MOF with Type A feature. We succeeded in preparing a Mg2+-containing porous MOF, Mg[Zr(C14H3O8)2] (SU-102-Mg), through a simple ion exchange reaction by employing a robust anionic framework, SU-102,10 as the mother framework (Fig. 1). We found that SU-102-Mg shows high crystallinity even after the ion exchange with Mg2+ and a high ionic conductivity of 3.6 × 10−5 S cm−1 at room temperature (RT) under MeCN vapor. Detailed analysis of the guest adsorption, ionic conductivity, and infrared (IR) spectroscopy revealed that the significant increase in ionic conductivity is derived from the formation of coordinated Mg2+ carriers, which is similar to the case of the previously reported Mg2+ salt-containing MOF.7
![]() | ||
Fig. 1 Synthetic scheme of the crystalline Mg2+-containing anionic MOF through ion-exchange reaction. |
Following previous literature,10 the mother MOF, SU-102 ((DMA)2[Zr(C14H3O8)2]), an anionic MOF with dimethyl ammonium (DMA+) as the counter cations in its pores, was synthesized by the typical solvothermal method with Zr4+ and ellagic acid as the ligand (details are shown in the ESI†). Samples were characterized with X-ray powder diffraction (XRPD) and N2 adsorption isotherms. As shown in Fig. 2 and 3, the porous mother MOF was successfully synthesized. For the prepared SU-102, Mg2+ carriers were introduced in the pores instead of the included DMA+ through an ion exchange reaction in MeCN solution of Mg salt, Mg(TFSI)2 (TFSI− = bis(trifluoromethanesulfonyl)imide) (see the ESI†). After the reaction, the sample was carefully washed with pure MeCN to remove the remaining Mg(TFSI)2.
The presence of Mg2+ in the ion-exchanged sample, SU-102-Mg, was confirmed by inductively coupled plasma-atomic emission spectroscopy (ICP-AES). The measurement revealed that the Mg2+ was stoichiometrically introduced (1.0 Mg2+ per formula, instead of two DMA+) in the pores to form Mg[Zr(C14H3O8)2]. The exchange of DMA+ was also confirmed by 1H NMR. As shown in Fig. S1,† the peaks from the DMA+ cations completely disappeared after the ion exchange reaction, indicating the absence of DMA+ in SU-102-Mg. The good agreement of the elemental analysis for SU-102-Mg also confirmed the stoichiometric ion exchange (see the ESI†).
The crystal structure of the Mg2+-containing MOF, SU-102-Mg, was characterized with XRPD measurements. As shown in Fig. 2, SU-102-Mg showed sharp peaks, evidencing its high crystallinity even after inclusion of Mg2+. The XRPD pattern of SU-102-Mg is almost the same as that of SU-102, clearly indicating that SU-102-Mg had no significant changes in its fundamental framework structure. Note that the intensity ratio is slightly different between the samples before and after the ion exchange reaction. This should be due to the change in electron density inside the pores of the MOF, which is consistent with the fact that the stoichiometric ion exchange from DMA+ to Mg2+ occurred in the pores of the sample. As shown in Fig. S2,† the thermal stability of SU-102-Mg is also similar to that of SU-102.
To confirm the porosity of the prepared MOF, we measured adsorption isotherms at 77 K. Fig. 3 shows the adsorption isotherms of the samples before and after the ion exchange. SU-102-Mg showed a large amount of adsorption at the low-pressure region, resulting in a typical Type I isotherm. This clearly indicates that the SU-102-Mg has apparent porosity even after the inclusion of Mg2+ ions in the pores. The BET surface area of SU-102-Mg was estimated to be 461 m2 g−1, which is similar to that of SU-102 (519 m2 g−1), indicating that the high porosity remained after the ion exchange. This is consistent with the fact that SU-102-Mg has fundamentally the same framework structure, as shown in the XRPD results. As mentioned, we previously reported an example of a Mg2+-containing MOF with Type A feature (MOF-688-Mg). However, it showed low crystallinity and no apparent porosity in the N2 adsorption measurements. In this study, we succeeded in creating a crystalline porous Mg2+-containing MOF with Type A feature through ion exchange reaction. Since the crystalline nanopores often act as excellent ion-conducting pathways, the ionic conductivity is strongly expected to be promoted. In addition, the high porosity would be advantageous in vapor-induced ionic conduction because of the high capability to accept the guest molecules that enhance the migration of Mg2+.
To reveal the ionic conductivity of the crystalline MOF containing only Mg2+ in its pores, we performed alternating current impedance measurements under various conditions (Fig. 4, S3, and Table S1†). Fig. 4 shows the temperature dependence of ionic conductivity under various guest vapors of small organic molecules or dry N2. As with a previous report (MOF-688-Mg),9 SU-102-Mg exhibited insulating character under dry N2, clearly indicating that Mg2+ located in the pores are strongly bound by the framework and thus cannot be migrated. Conversely, small guest molecules such as MeOH and MeCN drastically enhance its ionic conductivity. This is also similar to the case of MOF-688-Mg. The ionic conductivity of SU-102-Mg reaches 3.6 × 10−5 S cm−1 at 25 °C under the optimal guest (MeCN) vapor, which is almost three times higher than that of MOF-688-Mg (1.3 × 10−5 S cm−1 at 25 °C under MeCN vapor) and is the highest value among the Mg2+-containing MOFs with the Type A feature. The result suggested that the crystalline pores or regular channels of SU-102-Mg deeply contribute to the efficient migration of the included Mg2+. As listed in Table S1,† the activation energy of SU-102-Mg under each guest is also similar to that of MOF-688-Mg,9 suggesting the similar conducting mechanisms under the guest vapors.
![]() | ||
Fig. 4 Temperature dependence of the ionic conductivity of SU-102-Mg under (green) MeCN, (red) MeOH, (pink) EtOH, and (blue) THF vapors, compared to (black) dry N2. |
Previously, we reported that the drastic increase of ionic conductivity in Mg2+-containing MOFs under guest vapor (i.e., vapor-induced Mg2+ conduction) is derived from the formation of coordinated Mg2+ carriers with high mobility. To gain information about the mechanism of the vapor-induced Mg2+ conduction in SU-102-Mg, firstly, we evaluated the guest adsorption property of SU-102-Mg for the optimal guest, MeCN. As shown in Fig. S4,† SU-102-Mg adsorbed a large amount of MeCN from the low-pressure region, finally reaching approximately six molecules per formula. Next, we evaluated the vapor pressure dependence of ionic conductivity (Fig. S5†). The ionic conductivity deeply depends on MeCN vapor pressure and increased with increasing pressure, confirming that the adsorbed MeCN molecules truly enhanced the Mg2+ conduction in SU-102-Mg. By combining these data, we could reveal the relationship between ionic conductivity and the number of adsorbed guest molecules (Fig. S6†). Fig. S6† clearly indicates that the ionic conductivity did not obviously increase at low MeCN content, but started to slightly increase at around 4 adsorbed MeCN molecules per formula (i.e., per one Mg2+). It continuously increased to reach the maximum conductivity above 10−5 S cm−1 at around the maximum MeCN content of approximately 6 molecules per formula. Compared with our previous study on the Type B compound, Mg2+ salt-containing MOF (MIL-101⊃{Mg(TFSI)2}1.6),7 the tendency of this relationship is actually very similar. In the case of MIL-101⊃{Mg(TFSI)2}1.6, the conductivity is drastically increased at around 9.6 MeCN molecules per formula, which corresponds to 6-coordination to Mg2+, forming the highly mobile coordinated carriers.7 Considering this fact, the similar behavior of SU-102-Mg (Fig. S6†) is indicative that the increase of ionic conductivity in SU-102-Mg was caused by the change in mobility of the included Mg2+ due to the formation of the coordinated carriers. It is also suggested that one of the main reasons for the relatively low ionic conductivity of SU-102-Mg (≳10−5 S cm−1) compared to MIL-101⊃{Mg(TFSI)2}1.6 (≳10−3 S cm−1)7 is the limited pore capacity of SU-102-Mg: 6 MeCN molecules per Mg2+ does not seem enough to make the formed carriers highly mobile (i.e., still not free from the electrostatic interaction from the anionic framework). We believe that the additional guest molecules (i.e., more than 6), coordinating to the framework, play a critical role in reducing the remaining electrostatic interaction to allow the formed carriers to migrate more freely.
To confirm the formation of the coordinated Mg2+ carriers in SU-102-Mg, we measured the in situ Fourier transform infrared (FT-IR) spectra under MeCN vapor (Fig. S7†). In the case of SU-102 (without Mg2+), the main peaks at around 2255 and 2283 cm−1 are attributable to CN stretching mode (ν2) and the combination of CH3 bending and CC stretching mode (ν3 + ν4), respectively.11 In contrast, SU-102-Mg showed apparently shifted peaks at around 2289 and 2315 cm−1, which should be attributed to ν2 and ν3 + ν4 bands, derived from the MeCN molecules coordinating to metal ions (Mg2+).11 This behaviour is similar to the previously reported Mg2+ salt-containing MOF,7 although SU-102-Mg shows some extra peaks that would be attributed to MeCN molecules with various coordination forms (e.g., other than the typical octahedral six-coordination). This result clearly confirmed the existence of the coordinated Mg2+ carriers in the pores under MeCN vapor and is consistent with the results of conductivity and adsorption measurements described above. These results confirm that the adsorbed small guest molecules act as the conducting media for Mg2+ conduction and indeed help the migration of Mg2+ carriers located in the MOF pores.
Footnote |
† Electronic supplementary information (ESI) available: Details of synthesis and physical measurements; NMR spectra; TGA curves; Nyquist plots; adsorption isotherms; conductivity; IR spectra. See DOI: https://doi.org/10.1039/d4dt01331j |
This journal is © The Royal Society of Chemistry 2024 |