Simple and sustainable synthesis of perovskite-based optoelectronic material: CsPbBr3 nanocrystals via laser ablation in alcohol

Simone Sansoni , Filippo M. Anoè and Moreno Meneghetti *
Department of Chemical Sciences, University of Padua, Padua 35131, Italy. E-mail: moreno.meneghetti@unipd.it

Received 4th September 2022 , Accepted 12th October 2022

First published on 12th October 2022


Abstract

All-inorganic lead halide perovskite nanocrystals (NCs) have shown great potential as emerging semiconducting materials due to their excellent optoelectronic properties. However, syntheses in solution commonly use high temperatures and toxic solvents, which are obstacles for safety and sustainability of the process. In this work, laser ablation in alcohol is proposed as a simple and sustainable, ligand-free, top-down approach to synthesize CsPbBr3 nanocrystals in ambient conditions. The effects of different low boiling point commercial alcohols used as solvents on the optical properties of CsPbBr3 NCs colloidal solutions are investigated. Although in traditional bottom-up synthesis alcohols are usually found to be not appropriate for the synthesis of perovskite NCs, here it is demonstrated that CsPbBr3 orthorhombic nanocrystals with narrow full width half maximum (FWHM < 18 nm), long photoluminescence lifetimes (up to 17.9 ns) and good photoluminescence quantum yield (PLQY up to 15.5%) can be obtained by selecting the dielectric constant and polarity of the alcohol employed for the synthesis.


Introduction

Lead halide perovskite nanocrystals (NCs) have drawn great attention in the last years and they found application in a variety of optoelectronic devices like light-emitting diodes, solar cells, transistors, laser, photo-detectors, quantum information and photocatalysis.1–3 Such a high versatility is attributable to their plethora of desirable properties: long carrier diffusion lengths, simple bandgap tunability, high absorption coefficients and exceptional defect tolerance.4,5 Defect tolerance is a very attractive property as it makes solution-processing a viable prospect.6 In addition to the relatively low cost of perovskite precursor salts, the perovskite-based optoelectronics have recently gained substantial commercial appeal. However, in-vacuum “hot-injection” synthesis is the most widely used approach to produce perovskite nanocrystals, although this is a challenging approach for a sustainable process.7 Recent approaches are based on free-amine syntheses obtained, however, at high temperature and with the usual solvents.8 Room temperature processes, performed without environmental problems, are more attractive9,10 and the identification of suitable green solvents is a relevant aspect to consider.11,12 Recently, several solvents have been selected on the basis of environmental, health and safety (EHS) evaluations and guides for their selection have been created.13 The innovative medicines initiative (IMI)-CHEM21 selection guide is used to select the solvents in the present approach.14 Small dimension nanocrystals and colloid stability are important to get stable and high-emissive inks. In bottom-up synthesis, perovskite NCs with small dimensions are usually obtained with a shell of organic ligands, which are crucial both for colloidal stability as well as for surface defect passivation.15–19 The low stability of lead halide perovskite NCs in such post-synthetic processes still limits their properties.20,21 Laser ablation synthesis in solution (LASiS) has proven to be a viable top-down method for the synthesis of ligand-free lead halide perovskite NCs in ambient conditions.22–24 In this work, LASiS process was optimized for the synthesis of all-inorganic CsPbBr3 perovskite NCs in eco-sustainable solvents at ambient condition. The effects of different commercially available alcohols, used as solvent for the LASiS process, on the optical properties of CsPbBr3 NCs colloidal solutions are investigated. Although in traditional bottom-up synthesis alcohols are usually found to be not beneficial for perovskite NCs,25,26 here it is demonstrated that orthorhombic CsPbBr3 nanocrystals with narrow FWHM down to 16 nm, long PL lifetimes up to 17.9 ns, and good PLQY up to 15.5% can be obtained by selecting the dielectric constant and polarity of the alcohol employed for the synthesis. The lower surface tension and higher vapor pressure of alcohols, compared to traditional high boiling toxic solvents used for LHP processing, can be exploited in sustainable and fast compatible processing.27,28

Materials and methods

Materials

Lead bromide (99.999%), cesium bromide (99.999%) and all the anhydrous solvents used for the synthesis were Sigma-Aldrich products and were used without further purification.

2-Step conversion of CsPbBr3 nanocrystals

Precursor solutions of PbBr2 NCs were obtained by LASiS using the third harmonic of a Nd:YAG laser at 355 nm, focused on the surface of a PbBr2 compressed powder round tablet with a fluence of 2 J cm−2. The target was placed into a glass vial (14 mm diameter) and immersed under 4.0 ml of alcohol (see Fig. 2b). LASiS were performed for 45 min, with 9 ns laser pulses at 20 Hz repetition rate. To ensure a uniform erosion of the target, the vial was continuously moved by an automated xy movement system, at a speed of 0.5 mm s−1. The concentration of PbBr2 NCs colloidal solutions, in the range of 0.5–0.7 mM, was estimated by optical extinction (see Fig. S1). CsPbBr3 NCs were produced as follows: 2.0 ml of 0.2 mM PbBr2 NCs diluted solution were mixed with 50 μl of 8 mM CsBr solution in ethanol for 30 min in a sonication bath. The solutions were then centrifuged for 4 min at 5000 RCF and redispersed in the same pure alcohol to get CsPbBr3 NCs colloidal solution without impurities.

1-Step in situ synthesis of CsPbBr3 nanocrystals

100 μl of 8 mM CsBr solution in ethanol were added to 4.0 ml ablation solvent and then vigorously mixed on a vortex for 5 min before synthesis. The ablation duration, between 60 and 90 min, was tuned for each sample to get a complete perovskite conversion with no unreacted CsBr in solution. All other experimental conditions/post-treatments were the same as for the “2-step conversion” samples.

Characterization

UV-visible spectra were registered with an Agilent Cary 5000 UV-Vis-NIR spectrometer using 0.2 cm quartz cuvettes. Edinburgh FLS 1000 UV/Vis/NIR photoluminescence spectrometer were employed for steady-state and time-resolved photoluminescence (SSPL and TRPL) measurements. SSPL spectra were collected exciting at 400 nm with a Xe lamp and using a PMT-850 detector. TRPL decays were registered following the time-correlated single photon counting (TCSPC) method, using a pulsed laser diode at 402.6 nm and a high-speed PMT-850 detector. Absolute PLQY were measured using an integrating sphere and exciting at 400 nm with a Xe lamp. All samples were diluted to get 0.1 Abs at the excitonic peak wavelength. TEM images were registered at 100 kV with a FEI TECNAI G2 electron microscope. XRD patterns were recorded at room temperature with a BRUKER AXS D8 ADVANCE Plus diffractometer in Bragg–Brentano geometry.

Results and discussion

EHS guidelines were followed to select the green solvents to be used for LASiS (see Fig. S2).14 Dielectric constant and relative polarity were considered as main parameters to evaluate the solvent- or antisolvent-like behavior towards perovskite nanocrystals.29,30 Aliphatic alcohols were chosen as class of non-hazardous solvents. Methanol (MeOH), ethanol (EtOH), isopropanol (IPA), tert-butanol (TBA), tert-pentanol (TPA) and triethyl carbinol (TEC) were selected to investigate a wide range of dielectric constant and polarity, moving from the solvent- to antisolvent-regime (see Fig. 1a). CsPbBr3 NCs were synthesized in these alcohols by following two different approaches, namely 2-step conversion and 1-step in situ synthesis (see Materials and methods).
image file: d2na00596d-f1.tif
Fig. 1 (a) Dielectric constant as a function of relative polarity of most used solvents (red) and antisolvents (blue) for perovskite synthesis. It is noticeable that, contrary to linear chain alcohols (yellow), the use of branched alcohols (green) enables to reach low values of both dielectric constant and polarity. (b) XRD patterns of orthorhombic CsPbBr3 perovskite NCs synthesized by LASiS in different alcohols. Contributes of non-perovskite phases at low angles are highlighted with red asterisk. Pattern of PbBr2 NCs obtained by LASiS in alcohol and of CsBr powders are also reported for comparison. The orthorhombic reference spectrum (ICSD 97851) of the CsPbBr3 orthorhombic phase is taken from ref. 32.

CsPbBr3 NCs by 2-step conversion were obtained by mixing a colloidal solution of PbBr2 precursors NCs, synthesized via laser ablation in alcohol (see Fig. S3), with an equimolar CsBr solution in EtOH. A scheme summarizing the whole process is reported in Fig. 2 with the TEM image of the synthesized nanocrystals. The best results were obtained by exploiting the alcohols with the lowest polarity and dielectric constant among those investigated, namely TPA and TEC, getting perovskite NCs with good optical and morphological properties. The typical CsPbBr3 perovskite excitonic peaks, around 515–520 nm, were observed in the UV-Vis spectra (see Fig. S4a). Narrow and intense PL emissions were registered in SSPL measurements, while average PL lifetimes of 10.2 and 12.6 ns were estimated from TRPL decays of NCs synthesized in TPA and TEC, respectively (see Fig. S4b and c). Cubic-shaped nanocrystals were observed by TEM analysis in both samples (see Fig. S5), with an average size of 120–200 nm. Poor optical and morphological properties were obtained with other solvents and particularly with MeOH and EtOH, (see Fig. S4 and S5). The XRD analysis, reported in Fig. 1b, confirmed the trend of optical and morphological properties deteriorating as the polarity of the alcohols employed for the synthesis increases.


image file: d2na00596d-f2.tif
Fig. 2 Scheme of PbBr2 nanocrystals synthesis by laser ablation in alcohol and their conversion into CsPbBr3 colloidal solution by the 2-step protocol. (a) PbBr2 compressed powder round pellet employed as target. (b) Picture of laser ablation in progress, showing the Nd:YAG laser beam focused on the surface of the target immersed in alcohol. (c) TEM image of PbBr2 precursor nanocrystals; the inset shows a picture of PbBr2 NCs solution under visible light. (d) TEM image of CsPbBr3 perovskite nanocrystals; the inset shows a picture of CsPbBr3 NCs solution under UV light.

A good crystallinity of orthorhombic CsPbBr3 perovskite phases were observed for the NCs synthesized in TPA and TEC,31,32 while unreacted precursors and Cs–Pb–Br non-perovskite phases (e.g., CsPb2Br5 (ref. 33 and 34)) were found in MeOH and EtOH, with still some residuals in IPA sample. The sharp double peaks observed for example at 15.1°, 21.5° and 30.4°, show that we obtained the orthorhombic phase. The peak at low angles indicated with an asterisk is for example characteristic of the CsPb2Br5 phase.33,34

CsPbBr3 NCs obtained by the 1-step in situ synthesis approach were produced during LASiS with CsBr already present in the solvent before the ablation process (see Fig. S6). Given the poor results obtained with CsPbBr3 NCs by 2-step conversion in MeOH and EtOH deriving from the different results obtained with the ablation of PbBr2 (see Fig. S4a), the 1-step in situ synthesis approach was used with the other alcohols. Compared to the 2-step samples synthesized in the same alcohols, the 1-step in situ syntheses showed important improvements of many parameters. Sharp CsPbBr3 excitonic peaks were observed in the UV-Vis spectra (Fig. 3a). PL emissions significantly increased in intensity (Fig. 3b) and long average PL lifetimes were obtained from TRPL measurements, which increased up to 12.5 and 17.9 ns in the case of CsPbBr3 NCs synthesized in TPA and TEC (Fig. 3c). A comparison between the optical properties of 2-step and 1-step in situ samples is reported in Fig. S7.


image file: d2na00596d-f3.tif
Fig. 3 Comparison of (a) UV-Vis spectra, (b) steady-state PL emissions, and (c) time-resolved PL decays of CsPbBr3 NCs synthesized by 1-step in situ synthesis in different alcohols (PL profiles are normalized to the intensity of the respective absorption peak). The intensity-averaged lifetimes reported in (c) were calculated by three-exponential fit of the respective PL decays, following previous indications (the reported values are intensity-averaged lifetime values, see Fig. 3a).25,35,36

Table in Fig. 4a summarizes all the optical characterization results of CsPbBr3 NCs. Both excitonic peaks and PL emissions of the 1-step in situ perovskite showed a slight blueshift. This observation is in line with results obtained with smaller nanocrystals.35,36 A more defined cubic shape of perovskite NCs was also noticed by decreasing alcohols polarity, moving from IPA to TEC, with an average size of 30–50 nm. A PLQY up to 15.5% was measured for the orthorhombic CsPbBr3 NCs synthesized in TPA, showing a good quantum yield stability over several days in ambient conditions (Fig. 4b).


image file: d2na00596d-f4.tif
Fig. 4 (a) Table summarizing the results of optical characterizations of CsPbBr3 NCs by laser ablation in alcohols. The excitonic peak positions (AbsMAX) observed in UV-Vis spectra, the PL emission wavelength (PLMAX) and FWHM given by SSPL measurements, and the intensity-averaged lifetime values (τAVG) calculated by three-exponential fit of the TRPL decays are listed. Data related to CsPbBr3 NCs by the 2-step conversion protocol are reported with light font. (b) PLQY values measured over time for the CsPbBr3 NCs by 1-step in situ synthesis method in different alcohols. All samples were kept in ambient conditions during aging.

The PLQY and lifetime values are consistent with previous works on orthorhombic CsPbBr3 nanocrystals,32 proving the good quality of the perovskite colloids synthesized with this methodology. Despite the absence of any ligands in the CsPbBr3 NCs solutions obtained by LASiS, a good colloidal stability was also observed in all samples. This is clearly related to the surface charge induced by LASiS,37,38 which produces high z-potential values for the nanocrystals obtained by the 1-step in situ synthesis (see Fig. S8) and therefore a stronger coulomb interaction among nanocrystals.

Conclusions

Laser ablation technique was used to produce colloidal solutions of all-inorganic CsPbBr3 perovskite nanocrystals in commercially available branched alcohols. By selecting alcohols with low polarity and dielectric constant it is demonstrated that, contrary to what is generally reported, orthorhombic CsPbBr3 nanocrystals can be synthesized at ambient conditions in this class of eco-sustainable, low-toxic solvents. Two protocols were used for the syntheses. The first protocol, called 2-step, is based on the ablation of PbBr2 and then the reaction of the obtained PbBr2 nanoparticles with CsBr, whereas the second one, called 1-step, is based on the reaction of the nanoparticles with CsBr at the same time of the ablation of PbBr2. It is found that the second protocol, the 1-step one, allows the synthesis of CcPbBr2 with better properties. Optimized samples showed good optical and morphological properties, good crystallinity and colloidal stability, intense and narrow PL emissions (FWHM down to 16 nm), long PL lifetimes (up to 17.9 ns), and good PLQY (up to 15.5%) which was stable over many days under ambient conditions. High emissive nanocrystals with cubic symmetry32 will be considered as a further step of this study. These results show that laser ablation in solution can be an effective alternative top-down method for the synthesis of ligand-free CsPbBr3 nanocrystals in “green” solvents at ambient condition, answering the call for more sustainable production and processing of halide perovskite nanomaterials.

Conflicts of interest

The authors declare no competing financial interest.

Acknowledgements

The Edinburgh FLS 1000 UV/Vis/NIR photoluminescence spectrometer and BRUKER AXS D8 ADVANCE Plus diffractometer at the PanLab department facility were founded by the MIUR-“Dipartimenti di Eccellenza” grant NExuS. Project P-DiSC#06BIRD2020-UNIPD of the University of Padova is acknowledged for supporting the present work.

References

  1. A. Dey, J. Ye, A. De, E. Debroye, S. K. Ha, E. Bladt, A. S. Kshirsagar, Z. Wang, J. Yin and Y. Wang, State of the Art and Prospects for Halide Perovskite Nanocrystals, ACS Nano, 2021, 15(7), 10775–10981,  DOI:10.1021/acsnano.0c08903.
  2. C. R. Kagan, L. C. Bassett, C. B. Murray and S. M. Thompson, Colloidal Quantum Dots as Platforms for Quantum Information Science, Chem. Rev., 2021, 121, 3186–3233,  DOI:10.1021/acs.chemrev.0c00831.
  3. M. Palabathuni, S. Akhil, R. Singh and N. Mishra, Charge Transfer in Photoexcited Cesium–Lead Halide Perovskite Nanocrystals: Review of Materials and Applications, ACS Appl. Nano Mater., 2022, 5, 10097–10117 CrossRef CAS.
  4. J. S. Manser, J. A. Christians and P. V. Kamat, Intriguing Optoelectronic Properties of Metal Halide Perovskites, Chem. Rev., 2016, 116(21), 12956–13008,  DOI:10.1021/acs.chemrev.6b00136.
  5. M. V. Kovalenko, L. Protesescu and M. I. Bodnarchuk, Properties and Potential Optoelectronic Applications of Lead Halide Perovskite Nanocrystals, Science, 2017, 358(6364), 745–750,  DOI:10.1126/science.aam7093.
  6. Y. Du, P. Liu, F. Li, X. Hou, H. Zhang, Y. Shi, S. Wang, Y. Wang, S. Guo and Q. Tai, Precursor Engineering for Performance Enhancement of Hole-Transport-Layer-Free Carbon-Based MAPbBr3 Perovskite Solar Cells, J. Alloys Compd., 2020, 154902,  DOI:10.1016/j.jallcom.2020.154902.
  7. J. Shamsi, A. S. Urban, M. Imran, L. De Trizio and L. Manna, Metal Halide Perovskite Nanocrystals: Synthesis, Post-Synthesis Modifications, and Their Optical Properties, Chem. Rev., 2019, 119(5), 3296–3348,  DOI:10.1021/acs.chemrev.8b00644.
  8. S. Akhil, V. G. V. Dutt and N. Mishra, Amine-Free Synthesis of Colloidal Cesium Lead Halide Perovskite Nanocrystals, ChemNanoMat, 2021, 7, 342–353 CrossRef CAS.
  9. A. A. M. Brown, B. Damodaran, L. Jiang, J. N. Tey, S. H. Pu, N. Mathews and S. G. Mhaisalkar, Lead Halide Perovskite Nanocrystals : Room Temperature Syntheses toward Commercial Viability, Adv. Energy Mater., 2020, 2001349, 1–19,  DOI:10.1002/aenm.202001349.
  10. A. A. M. Brown, P. Vashishtha, T. J. N. Hooper, Y. F. Ng, G. V. Nutan, Y. Fang, D. Giovanni, J. N. Tey, L. Jiang and B. Damodaran, Precise Control of CsPbBr3 Perovskite Nanocrystal Growth at Room Temperature: Size Tunability and Synthetic Insights, Chem. Mater., 2021, 33, 2387–2397,  DOI:10.1021/acs.chemmater.0c04569.
  11. M. Zhang, D. Xin, X. Zheng, Q. Chen and W. H. Zhang, Toward Greener Solution Processing of Perovskite Solar Cells, ACS Sustainable Chem. Eng., 2020, 8(35), 13126–13138,  DOI:10.1021/acssuschemeng.0c04289.
  12. R. Vidal, J. A. Alberola-Borràs, S. N. Habisreutinger, J. L. Gimeno-Molina, D. T. Moore, T. H. Schloemer, I. Mora-Seró, J. J. Berry and J. M. Luther, Assessing Health and Environmental Impacts of Solvents for Producing Perovskite Solar Cells, Nature Sustainability, 2021, 4(3), 277–285,  DOI:10.1038/s41893-020-00645-8.
  13. C. J. Clarke, W. C. Tu, O. Levers, A. Bröhl and J. P. Hallett, Green and Sustainable Solvents in Chemical Processes, Chem. Rev., 2018, 118(2), 747–800,  DOI:10.1021/acs.chemrev.7b00571.
  14. D. Prat, A. Wells, J. Hayler, H. Sneddon, C. R. McElroy, S. Abou-Shehada and P. J. Dunn, CHEM21 Selection Guide of Classical- and Less Classical-Solvents, Green Chem., 2016, 18(1), 288–296,  10.1039/c5gc01008j.
  15. S. R. Smock, T. J. Williams and R. L. Brutchey, Quantifying the Thermodynamics of Ligand Binding to CsPbBr3 Quantum Dots, Angew. Chem., Int. Ed., 2018, 57(36), 11711–11715,  DOI:10.1002/ANIE.201806916.
  16. B. Chen, P. N. Rudd, S. Yang, Y. Yuan and J. Huang, Imperfections and Their Passivation in Halide Perovskite Solar Cells, Chem. Soc. Rev., 2019, 48, 3842,  10.1039/c8cs00853a.
  17. Y. Yang, H. Qin, M. Jiang, L. Lin, T. Fu, X. Dai, Z. Zhang, Y. Niu, H. Cao and Y. Jin, Entropic Ligands for Nanocrystals: From Unexpected Solution Properties to Outstanding Processability, Nano Lett., 2016, 16, 2127–2132,  DOI:10.1021/acs.nanolett.6b00737.
  18. L. M. Wheeler, E. M. Sanehira, A. R. Marshall, P. Schulz, M. Suri, N. C. Anderson, A. Christians, D. Nordlund, D. Sokaras and T. Kroll, Targeted Ligand-Exchange Chemistry on Cesium Lead Halide Perovskite Quantum Dots for High-Efficiency Photovoltaics, J. Am. Chem. Soc., 2018, 140, 10504–10513,  DOI:10.1021/jacs.8b04984.
  19. J. Yuan, C. Bi, S. Wang, R. Guo, T. Shen, L. Zhang and J. Tian, Spray-Coated Colloidal Perovskite Quantum Dot Films for Highly Efficient Solar Cells, Adv. Funct. Mater., 2019, 1906615, 1–7,  DOI:10.1002/adfm.201906615.
  20. K. Hills-Kimball, H. Yang, T. Cai, J. Wang and O. Chen, Recent Advances in Ligand Design and Engineering in Lead Halide Perovskite Nanocrystals, Adv. Sci., 2021, 8, 2100214–2100258,  DOI:10.1002/advs.202100214.
  21. S. Cho, J. Kim, S. M. Jeong, M. J. Ko, J.-S. Lee and Y. Kim, High-Voltage and Green-Emitting Perovskite Quantum Dot Solar Cells via Solvent Miscibility-Induced Solid-State Ligand Exchange, Chem. Mater., 2020, 32, 8808–8818,  DOI:10.1021/acs.chemmater.0c02102.
  22. F. Lamberti, L. Litti, M. De Bastiani, R. Sorrentino, M. Gandini, M. Meneghetti and A. Petrozza, High-Quality, Ligands-Free, Mixed-Halide Perovskite Nanocrystals Inks for Optoelectronic Applications, Adv. Energy Mater., 2017, 1601703–1601707,  DOI:10.1002/aenm.201601703.
  23. A. Rizzo, F. Lamberti, M. Buonomo, N. Wrachien, L. Torto, N. Lago, S. Sansoni, R. Pilot, M. Prato and N. Michieli, Understanding Lead Iodide Perovskite Hysteresis and Degradation Causes by Extensive Electrical Characterization, Sol. Energy Mater. Sol. Cells, 2019, 189, 43–52,  DOI:10.1016/j.solmat.2018.09.021.
  24. S. Sansoni, M. De Bastiani, E. Aydin, E. Ugur, F. H. Isikgor, A. Al-Zahrani, F. Lamberti, F. Laquai, M. Meneghetti and S. De Wolf, Eco-Friendly Spray Deposition of Perovskite Films on Macroscale Textured Surfaces, Adv. Mater. Technol., 2020, 5(2), 1901009–1901014,  DOI:10.1002/admt.201901009.
  25. A. Zhao, Y. Sheng, C. Liu, S. Yuan, X. Shan, Y. Di and Z. Gan, Fluorescent Dynamics of CsPbBr3 Nanocrystals in Polar Solvents: A Potential Sensor for Polarity, Nanotechnology, 2021, 32(13), 135701,  DOI:10.1088/1361-6528/abd2e9.
  26. L. Rao, Y. Tang, C. Song, K. Xu, E. T. Vickers, S. Bonabi Naghadeh, X. Ding, Z. Li and J. Z. Zhang, Polar-Solvent-Free Synthesis of Highly Photoluminescent and Stable CsPbBr3 Nanocrystals with Controlled Shape and Size by Ultrasonication, Chem. Mater., 2019, 31(2), 365–375,  DOI:10.1021/acs.chemmater.8b03298.
  27. Y. Deng, C. H. van Brackle, X. Dai, J. Zhao, B. Chen and J. Huang, Tailoring Solvent Coordination for High-Speed, Room-Temperature Blading of Perovskite Photovoltaic Films, Sci. Adv., 2019, 5(12), 1–9,  DOI:10.1126/sciadv.aax7537.
  28. Y. Y. Kim and J. Seo, Roll-to-Roll Gravure-Printed Flexible Perovskite Solar Cells Using Eco-Friendly Antisolvent Bathing with Wide Processing Window, Nat. Commun., 2020, 11, 5146–5156,  DOI:10.1038/s41467-020-18940-5.
  29. T. Bu, L. Wu, X. Liu, X. Yang, P. Zhou, X. Yu, T. Qin, J. Shi, S. Wang and S. Li, Synergic Interface Optimization with Green Solvent Engineering in Mixed Perovskite Solar Cells, Adv. Energy Mater., 2017, 7(20), 1–10,  DOI:10.1002/aenm.201700576.
  30. Y. Li, H. Huang, Y. Xiong, A. F. Richter, S. V. Kershaw, J. Feldmann and A. L. Rogach, Using Polar Alcohols for the Direct Synthesis of Cesium Lead Halide Perovskite Nanorods with Anisotropic Emission, ACS Nano, 2019, 13(7), 8237–8245,  DOI:10.1021/acsnano.9b03508.
  31. S. Sun, D. Yuan, Y. Xu, A. Wang and Z. Deng, Ligand-Mediated Synthesis of Shape-Controlled Cesium Lead Halide Perovskite Nanocrystals via Reprecipitation Process at Room Temperature, ACS Nano, 2016, 10(3), 3648–3657,  DOI:10.1021/acsnano.5b08193.
  32. L. Wang, K. Fu, R. Sun, H. Lian, X. Hu and Y. Zhang, Ultra-Stable CsPbBr3 Perovskite Nanosheets for X-Ray Imaging Screen, Nano-Micro Lett., 2019, 11(52) DOI:10.1007/s40820-019-0283-z.
  33. J. Feng, X. Han, H. Huang, Q. Meng, Z. Zhu, T. Yu, Z. Li and Z. Zou, Curing the Fundamental Issue of Impurity Phases in Two-Step Solution-Processed CsPbBr3 Perovskite Films, Sci. Bull., 2020, 65(9), 726–737,  DOI:10.1016/j.scib.2020.01.025.
  34. L. Nasi, D. Calestani, F. Mezzadri, F. Mariano, A. Listorti, P. Ferro, M. Mazzeo and R. Mosca, All-Inorganic CsPbBr3 Perovskite Films Prepared by Single Source Thermal Ablation, Front. Chem., 2020, 8, 1–10,  DOI:10.3389/fchem.2020.00313.
  35. J. Chen, C. Zhang, X. Liu, L. Peng, J. Lin and X. Chen, Carrier Dynamic Process in All-Inorganic Halide Perovskites Explored by Photoluminescence Spectra, Photonics Res., 2021, 9(2), 020151–020170,  DOI:10.1364/prj.410290.
  36. I. Lignos, R. M. MacEiczyk, M. V. Kovalenko and S. Stavrakis, Tracking the Fluorescence Lifetimes of Cesium Lead Halide Perovskite Nanocrystals during Their Synthesis Using a Fully Automated Optofluidic Platform, Chem. Mater., 2020, 32(1), 27–37,  DOI:10.1021/acs.chemmater.9b03438.
  37. D. Zhang, B. Gökce and S. Barcikowski, Laser Synthesis and Processing of Colloids: Fundamentals and Applications, Chem. Rev., 2017, 117(5), 3990–4103,  DOI:10.1021/acs.chemrev.6b00468.
  38. H. Zeng, X. W. Du, S. C. Singh, S. A. Kulinich, S. Yang, J. He and W. Cai, Nanomaterials via Laser Ablation/Irradiation in Liquid: A Review, Adv. Funct. Mater., 2012, 22(7), 1333–1353,  DOI:10.1002/adfm.201102295.

Footnote

Electronic supplementary information (ESI) available: Details of the ablation setup; PbBr2 molar extinction coefficient; environmental, health and safety guidelines for solvents; optical, structural, and morphological characterization of PbBr2 and CsPbBr3 nanocrystals; Z-potential and DLS measurements of CsPbBr3 nanocrystals. See DOI: https://doi.org/10.1039/d2na00596d