Correction: Nanoarchitectonics of p-type BiSbTe with improved figure of merit via introducing PbTe nanoparticles
Yuanyue Li,
Mengna Ren,
Zhongsen Sun* and
Zhao Yao*
College of Electronic and Information, Qingdao University, Qingdao 266071, China. E-mail: sunzs@qdu.edu.cn; yao9074@hotmail.com
First published on 2nd December 2021
Abstract
Correction for ‘Nanoarchitectonics of p-type BiSbTe with improved figure of merit via introducing PbTe nanoparticles’ by Yuanyue Li et al., RSC Adv., 2021, 11, 36636–36643, DOI: 10.1039/D1RA07138F.
The authors regret that affiliation a was incorrectly given in the original article. The correct affiliation is shown here.
In the sentence beginning “For instance, PF of the sample with χ = 0.5 wt% is 33.8…” incorrect units were given. The corrected sentence is as follows: For instance, PF of the sample with χ = 0.5 wt% is 33.8 μW cm−1 K−2 at 482 K, which is ∼33% larger than that of the BST matrix (25.5 μW cm−1 K−2).
In the sentence beginning “For instance, as to the sample with χ = 0.5 wt%, κ decreases from 1.10…” incorrect units were given. The corrected sentence is as follows: For instance, as to the sample with χ = 0.5 wt%, κ decreases from 1.10 to 0.99 W m−1 K−1 at 482 K (a ∼10% decline).
The Royal Society of Chemistry apologises for these errors and any consequent inconvenience to authors and readers.