Ya-xin
Li
ab,
Huifang
Cheng
c,
Xiangbing
Zeng
b,
Yuan
Tao
c,
Xiaohong
Cheng
*cd and
Goran
Ungar
*ab
aState Key Laboratory for Mechanical Behaviour of Materials, Shaanxi International Research Center for Soft Materials, Xi’an Jiaotong University, Xi’an, P. R. China
bDepartment of Materials Sciences and Engineering, University of Sheffield, Sheffield, UK. E-mail: g.ungar@sheffield.ac.uk
cSchool of Chemical Science and Technology, Yunnan University, Kunming, P. R. China
dSchool of Chemistry and Chemical Engineering, Yangtze Normal University, Fuling, P. R. China. E-mail: xhcheng@ynu.edu.cn
First published on 12th May 2020
We introduce a new class of mesogens that are bird-like in shape and form honeycomb-type supramolecular liquid crystals. They have a bent pi-conjugated aromatic core as wings, a linear or branched chain as the tail and a selection of functional headgroups. Honeycombs of non-centrosymmetric trigonal type (p3m1) are obtained, along with two different complex honeycomb superlattices (p31m and p2gg) and a randomized hexagonal mesophase (p6mm). The key determinant of the self-assembled structure is the nature of interaction of the headgroup with the glycerols at the ends of the wings. The structure depends on whether the sub-columns lying along the edges of the prismatic cells contain pure or mixed headgroups and wing-end hydrogen-bonding groups. Its assembly is further controlled by reducing the tail-chain volume, inducing out-of-plane buckling of the honeycomb. These two modes of symmetry breaking lead to structural polarity both in- and out-of-plane, opening the way to applications in devices relying on properties such as ferroelectricity and second harmonic generation.
However, the aromatic cores do not have to be straight, and a few examples of honeycomb-generating bent core polyphiles have been reported. Their cores were bent at the centre, with the attached chain facing inward9,10 or outward11 at the bend, the two rigid arms subtending a 120° angle. Mesogens with inward-facing chains are referred to as anchor-shaped. They were found to assemble in hexagonal honeycombs with either 3 or 6 molecules in the cell circumference, depending on whether the pendant chain was small or large.10 At the time it was actually not clear if the 3-molecule honeycombs had trigonal or hexagonal (randomized) symmetry. Here we introduce a new way of controlling complexity in LC honeycombs; we add a functional headgroup Rh on the outside of the bend in anchor-shaped molecules, turning them into what can be described as bird-shaped. Rh groups interact in different ways between themselves and with the terminal hydrogen-bonding groups, resulting in a variety of new controllable honeycomb structures and superlattices. Furthermore, additional frustration is introduced by reducing the size of the pendant chain (the “tail”), depriving the honeycomb of adequate filler volume and forcing it to “buckle”, thus creating new opportunities. Most structures described are non-centrosymmetric, thus having interesting application potential.
Compound Rh–F/Ha | Rc | a (Å) [Acol (Å2)] | T /°C [ΔH/kJ mol−1] |
---|---|---|---|
a First part of compound name is the head group Rh, second part denotes the type of attached chain. b Lattice parameter [area per column in brackets]. c Peak DSC transition temperatures [and enthalpies] on 2nd heating (↑) and cooling (↓), all at 10 K min−1. d Transition temperatures of CO2CH3–F are determined by XRD, SHG and POM. Phase abbreviations: Cr = crystal, p6mm-ran = hexagonal columnar phase with random orientation of the local 3-fold axis with 6-fold p6mm overall symmetry; p3m1-reg = columnar phase with trigonal symmetry and one column per unit cell; p31m-sup = trigonal superlattice with three columns per unit cell; p2gg-sup = rectangular superlattice with p2gg symmetry and four columns per cell; Iso = isotropic melt. Transition temperatures in the bar chart are from 2nd DSC heating, except for Br–H where they were determined on cooling. | |||
CO2CH3–F | C6H12C4F9 | 29.8 [769] | r.t.↑p3m1-reg 42 Isod |
Br–H | CH2CH(C5H11)2 | 26.9 [627] | ↑Cr 113.7[33.3] Iso ↓91.8 [1.9] p3m1-reg 32.2[8.6] Cr |
CONH2–F | C4H8C6F13 | 30.1 [785] | ↑p3m1-reg 212.5[13.3] Iso ↓206.8[13.2] p3m1-reg |
CN–F | C6H12C4F9 | 51.7 [772] | ↑p31m-sup 82.9[0.1] Iso ↓78 (onset) p31m-sup |
CN–H | CH2CH(C5H11)2 | 24.5 [520] | ↑p6mm-ran 84.4[1.6] Iso ↓81.5[1.6] p6mm-ran |
NO2–F | C4H8C6F13 | a 63.3 b 50.6 [801] | ↑p2gg-sup 117[2.0] Iso ↓110.3[3.0] p2gg-sup |
POM images of the compounds in the mesophases are shown in Fig. 1 and Fig. S2 (ESI†). They are typical of columnar phases, with sizeable fraction of dark area indicating homeotropic alignment, where the optic axis, hence column axis, is normal to the glass substrate. Planar columns, parallel to the substrate, are prevalent in thicker samples. Bright fans are seen in Fig. 1c and e, where columns form concentric circles or arcs around the focal point. The same are seen as blue or pale-yellow in Fig. 1d and f recorded with a λ-plate retarder; these confirm that the slow (high-index) axis is radial, hence perpendicular to the column axis. This negative birefringence is also seen in the “tumbling” defects, especially in Fig. 1a and b, appearing as thin bright streaks, where bundles of vertical columns perform a U-turn. The slow axis is seen to be parallel to the streaks, and since the columns are perpendicular, the slow axis is again confirmed as normal to the columns. This is consistent with the situation in most honeycomb LCs where the π-conjugated aromatic rods are perpendicular to the axis of the prismatic cells, or columns.
SAXS patterns of unoriented (“powder”) samples and GISAXS patterns of thin films of the mesophases of all compounds except the nitro-compound NO2–F give Bragg peaks/spots indexable on a 2D hexagonal lattice with the ratio of squared reciprocal spacings d−2(10):d−2(11):d−2(20):d−2(21):d−2(30)… = 1:3:4:7:9… (Fig. 2a, b, 3a and Fig. S3a, S5a, ESI†). GISAXS patterns of films lying on a horizontal Si substrate confirm this indexing, giving sharp spots or arcs mainly on the equator, consistent with homeotropic alignment (Fig. 2c, d and 3e). Exceptionally, compound NO2–F displays a rectangular lattice, plane group p2gg (Fig. 3b, d, g and i). Its GISAXS pattern in Fig. 3d, coming from planar domains, shows two orientations, one in which the columns lie with the (010) plane on the substrate (green reciprocal net), the other with the diagonal (210) plane on the substrate (white net). Both (010) and (210) are planes of densely packed columns, supporting the viability of the proposed structural model. The rectangular phase with its 2b/a ratio of 1.60 is a distortion of a hexagonal lattice, where the equivalent ratio would be √3. WAXS contains only diffuse scatter centred around 2π/q = 4–5 Å, consistent with a true LC phase (Fig. S3b, ESI†). No peak around 3.5–4 Å is observed (Fig. S3b, ESI†), indicating that the benzene rings do not stack as in a discotic LC with parallel discs. The absence of a 3.5–4 Å peak suggests that the rings are inclined to the xy-plane and to each other.
Fig. 2 (a) Powder SAXS of CONH2–F and CN–F recorded at 130 and 70 °C upon cooling. (b) Temperature dependent intensity of the second harmonic (400 nm) normalized by dividing by the surrounding background level for 800 nm excitation, generated 20 μm above the substrate surface; for measurements at different heights see Fig. S7 and S8 (ESI†). (c) and (d) GISAXS patterns of CONH2–F and CN–F recorded at 100 and 60 °C upon cooling. (e) and (f) ED maps with schematic models of CONH2–F (p3m1-reg) and CN–F (p31m-sup). (g) and (h) Snapshot of dynamic simulation of CONH2–F (p3m1-reg) and CN–F (p31m-sup). |
Based on previous work on anchor-shaped molecules,10 it was reasonable to assume that the structures are based on hexagonal or, in the present case, possibly pseudo-hexagonal prismatic cells. Calculations based on unit cell area, expected average intracolumnar intermolecular distance and molecular volumes (Table S8, ESI†), suggest that in CO2CH3–F, Br–H, CONH2–F and CN–H there are 3 molecules circumscribing a column rather than 6. The fact that the unit cell areas were always close to an integer multiple m of the smallest cell implies that for m > 1 we have superlattices with m prismatic columns per unit cell. Specifically, for CO2CH3–F, Br–H, CONH2–F and CN–H m = 1 (“regular” columnar phase). Meanwhile the unit cell of the superlattice of CN–F contains m = 3 columns, whereas the rectangular cell in NO2–F contains m = 4 columns. Thus the number of molecules per unit cell 3m is, respectively, 3, 9 and 12 – Table S8 (ESI†).
The fact that a column stratum contains only 3 molecules raises the possibility that the structures have 3-fold rather than 6-fold symmetry. As Laue symmetry is hexagonal in both cases, X-ray diffraction alone cannot distinguish between the two. Therefore, we tested the mesophases for the presence of SHG signal. Only CN–H and NO2–F tested negative, while CO2CH3–F, Br–H, CONH2–F and CN–F all showed clear second harmonic emission above the background level caused by surface effects12 (Fig. 2b and Fig. S4, S6–S8, ESI†). Hence the columnar phases in these compounds are non-centrosymmetric, i.e. trigonal. In all trigonal compounds SHG intensity drops sharply to the background level near the isotropisation temperature Ti.
While for hexagonal CN–H the plane group is clearly p6mm, for trigonal phases the choice was between p3m1 and p31m.13 Since neither imposes any systematic extinctions, the choice was based on the following reasoning. The columns must be centred on the 3-fold axes, all three of which lie on the long diagonal of the rhombic unit cell in both plane groups – Fig. 4a and b. At the same time two conditions must be fulfilled. (i) To tessellate, the prismatic cells must face each other with their sides rather than edges. (ii) Since a column stratum contains three identical molecules, the mirror planes must pass through the opposing edges (apices) rather than bisecting the sides of the prisms; otherwise the prisms would acquire hexagonal rather than trigonal symmetry. For the “regular” m = 1 phase, conditions (i) and (ii) are satisfied only if the symmetry is p3m1, with the single column centred at (0,0) (Fig. 4a). Meanwhile, for the m = 3 superlattice of CN–F the symmetry must be p31m, with the three columns situated at (0,0), (1/3,2/3) and (2/3,1/3) (Fig. 4b). Accordingly, the regular 1-column trigonal phase is labelled “p3m1-reg”, and the 3-column superlattice as “p31m-sup”. In the same vein, the 4-column rectangular superlattice is labelled “p2gg-sup”.
With the knowledge of mesophase symmetry, electron density (ED) maps of the xy plane were constructed from Lorentz-corrected Bragg reflection intensities (Tables S2–S7, ESI†), bearing in mind that for trigonal mesophases the phase angles of certain reflections are not limited to 0° or 180° as in the usual centrosymmetric LCs. In choosing the correct map we were guided by the above reasoning and by the ED values calculated for the specific parts of the molecules (Table S10, ESI†). The map for CONH2–F, representative of the p3m1-reg phase, is shown in Fig. 2e, and that for the p31m-sup phase of CN–F in Fig. 2f. The structure factor phase angles are given in Tables S4 and S5, ESI.† While the aromatic and glycerol groups (“backbones”) have similar medium ED (green), the stand-out high-ED features are the three perfluoro chains in the centre of each column (blue-purple triangles). We associate the apices of the high-ED triangles with the positions of attached chains, close to the bay position on the aromatic cores. Schematic molecules at positions compatible with the maps are superimposed. In the p3m1-reg phase the implication is that there are separate glycerol and amide sub-columns at alternative honeycomb nodes, each having, respectively, either 6 glycerols (6Gly) or 3 headgroups (3Rh) in a stratum (Fig. 2e and 4a). As the former sub-columns will be wider than the latter, the hexagonal prisms are likely to be distorted as shown in an exaggerated way in Fig. 4a. Meanwhile in the p31m-sup phase of CN–F (Fig. 2f and 4b), the triangles follow an up-down-down sequence along any of the three {110} planes (labelled A, B, B in Fig. 2f and 4b). Hence there are again two types of sub-columns, but both are mixed, half of them containing 4Gly + 1CN and the other half 2Gly + 2CN.
To check the viability of the proposed structures, using experimental lattice parameters molecular models were built and subjected to NVT molecular dynamics annealing. As shown in Fig. 2g, h and Fig. S3d and S5d (ESI†), good space-filling is achieved with no overcrowding and no voids. The tessellating bird-like molecules, outlined in black in Fig. 2g and 3h, are reminiscent of some of the drawings of birds and bats by M. C. Escher.14
As mentioned, CN–H is the only compound with hexagonal Laue symmetry that shows no SHG signal. This means that, even if it still has only 3 molecules in the unit cell, its honeycomb phase does have an inversion centre and therefore has plane group p6mm. Here electron density has a minimum rather than a maximum in the centre of the column (Fig. 3f), as the pendant chains are low-ED aliphatic (see Table S10, ESI†). Incidentally, a similar situation is seen in Br–H (Fig. S5c, ESI†). To explain the high symmetry of the p6mm phase in CN–H, we propose that the honeycomb actually contains small trigonal domains which are, however, randomized in orientation; hence the long-range order, as seen by SAXS, is hexagonal. Accordingly, the mesophase is denoted “p6mm-ran”. Accordingly, although there may still be some local partial separation of glycerols and cyano-groups, the average composition of all sub-columns is the same, namely 1/2(6Gly + 3CN) or 3Gly + 1.5CN (see models in Fig. 3f and 4c), where empty circles and dashed-lined chains indicate half occupancy. Note that the pale-blue ED maxima in Fig. 3f indicate the positions of chain attachment and branching points. A snapshot of annealed molecular model is shown in Fig. 3h.
The only mesophases with the ratio of d−2 values not obeying the hexagonal rule is the rectangular p2gg-sup phase in NO2–F. The plane group p2gg is determined based on the absence of (h0) and (0k) Bragg reflections with odd h, k (Fig. 3b and d). The schematic depiction of the xy plane is shown in Fig. 4d. The apices of the distorted triangular high-ED fluoroalkyl regions in Fig. 3g again mark the chain attachment points, hence the positions of the centres of molecules. They reveal that there are four different orientations of the distorted hexagonal columns in a unit cell, labelled A, B, C, D in Fig. 3g and 4d. As in the trigonal superlattice of CN–F but replacing the CN headgroup with NO2, there are two types of sub-columns, one containing 4Gly + 1NO2 and the other 2Gly + 2NO2. If we call the 4Gly + 1Rh sub-column “large” (L) and the 2Gly + 2Rh sub-column “small” (S), then the difference between the two superlattices is in that going around a distorted hexagon the apex sequence in p31m-sup of CN–F is LSLSLS, while in p2gg-sup of NO2–F it is LLSSLS.
A further notable feature of the present mesophases is the significantly smaller cross-sectional area of columns filled with branched aliphatic chains compared to those filled with semiperfluoroalkyls – Table 1 and Fig. S9 (ESI†). The average area of columns in Br–H and CN–H is 573 Å2, while in fluorinated compounds it is 782 Å2. At the same time the estimated average intracolumnar spacings (c) between molecules are, respectively, 5.5 Å and 4.2 Å (Table S8, ESI†). Since the bent core backbones are the same, we conclude that in Br–H and CN–H their long axis is inclined to the xy plane instead of being parallel to it. This conclusion is further supported by the observed lower birefringence of H-compounds compared to that of the F-compounds. This is apparent already by qualitative POM inspection of a contact preparation in Fig. 3c, showing a film of uniform thickness, with CN–H on the left and CN–F on the right. While CN–F is coloured, CN–H is not. Optical retardation (Γ) of CN–F and CN–H is also measured quantitatively by Berek compensator, giving Γ as −436 and −174 nm, respectively. As Γ is proportional to the order parameter S, where
S = (3〈cos2θ〉 − 1)/2 |
It should be mentioned that this is not the first example of tilted backbones in honeycomb LCs. Examples were reported in a hexagonal facial amphiphile15 and a square honeycomb of a straight rod-like glycerol-terminated bolaamphiphile,16 both with a laterally attached flexible chain. In both cases θ changed steeply with temperature with S passing through zero causing birefringence inversion. However, in vast majority of honeycombs θ = 0, presumably to maximize entropy by allowing transverse self-diffusion. If filler volume is reduced and θ remains 0°, in most cases the system chooses a smaller polygon. Thus hexagonal gives way to pentagonal or square.4b However a change from square to triangle reduces the area to √3/4 = 0.43, evidently too drastic a jump for the system in ref. 16, which chooses the tilt alternative. Other systems have opted for a combination of squares and triangles.5 However, in the present case what prevents CN–H and Br–H from switching from hexagons to pentagons or squares must be the fixed 120° bend in the aromatic core.
Finally, we propose an explanation for the key effect of headgroup on phase structure and stability. Compared to compound 2b in ref. 10 with no headgroup (Rh = H) and with a (CH2)4C6F13 chain, having a Ti of 190 °C, all current compounds except the amide have lower Ti. This reflects the packing disturbance caused by the headgroup, also notable by the, on average, 9% larger area per column in F-compounds compared to that in the headless 2b (Table S9, ESI†). The disturbance is partially compensated or even overcompensated by hydrogen bonding and/or dipolar interaction of the headgroups. The lowest Ti, 40 °C, is found in the ester, where such interactions are at best weak, while the amide's H-bonds overcompensate lifting Ti to 212 °C (Table 1).
One would expect the headgroups and glycerols to segregate in separate sub-columns, which is what indeed happens in the p3m1-reg phase of CO2CH3–F, Br–H and CONH2–F. But clustering together all the bulky glycerol endgroups carries an energy penalty of distortion of the hexagons (Fig. 4a). We propose that avoiding such distortion is responsible for mixed rather than chemically pure sub-columns in CN–F and NO2–F. In these two compounds the energies of mutual dipolar interaction between the headgroups and their H-bonding interaction with the glycerols are of the same order of magnitude. The driving force for segregation is thus weaker, so that by mixing and keeping the subcolumn volumes similar, distortion is reduced. This results in the formation of p31m and p2gg superlattices. Data in Table S11 (ESI†) indeed suggest that AB cross-interactions of CN and NO2 groups with glycerol are similar in energy to AA and BB homo-interactions within their own species.
Returning to compounds CO2CH3–F, Br–H and CONH2–F that do not form a superlattice and where headgroups and glycerols do not mix, we may ask what these three compounds have in common. We propose that since the ester and bromo groups do not interact strongly with hydroxyl groups, mixing them with glycerol would only dilute the H-bonding within the glycerol sub-columns. The resulting energy penalty would outstrip the benefit of reduced lattice and molecular distortion. In sharp contrast, amide groups in CONH2–F H-bond more strongly among themselves than with the glycerols (Table S11, ESI†). So in CONH2–F it is the amide H-bonds that would lose out most by mixing. Again, the accompanying reduction in distortion would not be sufficient to compensate.
Regarding compound CN–H, we refrain from speculating about the situation in its p6mm-ran phase as the detailed short-range configuration in its randomized clusters is not known.
Footnote |
† Electronic supplementary information (ESI) available: Experimental methods, DSC thermograms, additional POM images, additional X-ray diffraction data, SHG and molecular modelling/simulation results on individual compounds, estimation of number of molecules per columnar stratum, electron densities of functional groups, non-bonded interaction energies and dipole moments of headgroups, synthesis and analytical data and NMR spectra. See DOI: 10.1039/d0tc01879a |
This journal is © The Royal Society of Chemistry 2020 |