Tim P.
Seifert
,
Vanitha R.
Naina
,
Thomas J.
Feuerstein
,
Nicolai D.
Knöfel
and
Peter W.
Roesky
*
Institute of Inorganic Chemistry, Karlsruhe Institute of Technology (KIT), Engesserstr. 15, 76131 Karlsruhe, Germany. E-mail: roesky@kit.edu
First published on 1st October 2020
This review covers the compound class of one-dimensional gold strings. These compounds feature a formally infinite repetition of gold complexes as monomers/repeating units that are held together by aurophilic interactions, i.e. direct gold–gold contacts. Their molecular structures are primarily determined in the solid state using single crystal X-ray diffraction. The chemical composition of the employed gold complexes is diverse and furthermore plays a key role in terms of structure characteristics and the resulting properties. One of the most common features of gold strings is their photoluminescence upon UV excitation. The emission energy is often dependent on the distance of adjacent gold ions and the electronic structure of the whole string. In terms of gold strings, these parameters can be fine-tuned by external stimuli such as solvent, pH value, pressure or mechanical stress. This leads to direct structure–property correlations, not only with regard to the photophysical properties, but also electric conductivity for potential application in nanoelectronics. Concerning these correlations, gold strings, consisting of self-assembled individual complexes as building blocks, are the ideal compound class to look at, as perturbations by an inhomogeneity in the ligand sphere (such as the end of a molecule) can be neglected. Therefore, the aim of this review is to shed light on the past achievements and current developments in this area.
EAu–Au = 1.27 × 106e−3.5d(Au–Au) | (1) |
Fig. 1 Schematic drawings of different subtypes of aurophilic interactions. L = neutral donor ligand; A = anionic ligand.68 |
While it is assumed that fully supported interactions are maintained in solution, the bonding situation of semi- and unsupported interactions in solution cannot be generalized and has to be evaluated in each case individually, because the solvation energy can compensate the comparably weak energy gain resulting from aurophilic interactions.67,69–73
The upcoming of aurophilicity attracted interest in similar interactions of other closed-shell ions as well. For example, R. Hoffmann and M. Jansen observed very short intermetallic distances for the lighter d10 configured homologues Cu(I) and Ag(I) in 1978 and 1987, respectively.74,75 Today, numerous elements, including open-shell ions like Au(III), Pt(II), Pd(II), Ir(I) or Ru(0), are known to interact with other heavy metal ions, expanding the concept to ‘metallophilic interactions’, even though pure aurophilic interactions are typically the strongest among them and therefore still take a special place.36,39,76–83
Fig. 2 Schematic representation of orbital splittings induced by to aurophilic interactions in dinuclear gold(I) thiolate complexes. Adapted with permission.88 Copyright 2004 American Chemical Society. |
It has been predicted that the alteration from LMCT towards LMMCT states further enhances when three gold(I) ions interact linearly, due to a δ combination of three instead of two dx2−y2 orbitals (Fig. 3). This interesting phenomenon is particularly anticipated for ‘infinite’ 1D gold(I) chains.92 Moreover, as unsupported aurophilic interactions are the main assembly motif of 1D gold chains, a perturbation via different environmental stimuli is readily achieved in many cases and often goes along with a significant change of the structural and photophysical properties.
Fig. 3 Molecular-orbital interactions for stacking of d10 AuP2 units in D2h symmetry.93 |
From a photophysical point of view, this represents the most important aspect of the herein presented 1D structures, as diverse slight stimuli already have an impact on the rather weak aurophilic interactions. Possible stimuli include solvent, pH value, pressure, and mechanical stress as well as temperature.84 This makes them a promising compound class towards an application as luminescent sensors and has already been remarkably demonstrated in recent reports, in which 1D gold(I) chains were found to show unique properties like solvatochromism,94 mechanochromism95 and luminescence tribochromism.96 In addition, this compound class is especially valuable to gain a better understanding of metallophilic interactions in general.
Fig. 4 Schematic drawing of gold strings consisting of Au(I) chain links with neutral or ionic building blocks (A = anion, C = cation, L = neutral ligand). |
Already in 1974, the Balch group introduced a synthetic procedure for cationic bis(carbene) gold(I) complexes by addition of isocyanides and primary amines to aqueous solutions of [AuCl4]− salts. The reaction readily yields compounds of the type [Au{C(NR2)(NR′H)}2]+.107 Following this procedure, using methylisocyanide and methylamine, a series of symmetrically substituted bis(carbene) gold(I) complexes [Au{C(NHMe)2}2]+ with varying anions (PF6− (1a), BF4− (1b), AsF6−, SbF6−) were presented in 2002 and 2008 by the same group (Scheme 1).108–110
As observed in the crystal structure, the PF6− salt 1a consists of a linear coordinated gold(I) center with the ligands being arranged coplanarly. The cations form a linear gold chain along a crystallographic 42 axis comprising relatively short Au–Au contacts (3.1882(1) Å). Furthermore, the carbene ligands are linked to the PF6 ion via hydrogen bonds from the NH-moieties (Fig. 5, left). For 1b (anion = BF4−), the Au–Au bond lengths are elongated (dAu–Au = 3.4615(2) Å), while the angles are in a comparable range to 1a (angleC–Au–C = 178.42(12)°). In addition, the relative ligand orientation differs in a way that the outer methyl groups face one another. The same applies for the N–H groups, which allow the formation of hydrogen bonds from one cation to two different fluorine atoms of the BF4 ion (Fig. 5, right). Both 1a and 1b are colourless solids and display photoluminescence behaviour. Exemplarily, 1a shows green-blue (λmax = 460 nm) luminescence upon UV irradiation at 300 K. Upon cooling to 77 K, two emission bands are observed, whereby the maximum of the more intense emission is significantly red shifted. When dissolved in solvents like acetone, pyridine, dimethylsulfoxide (DMSO), dimethylformamide (DMF) or acetonitrile, the resulting colourless solutions are not luminescent anymore. However, upon freezing in liquid N2, the solutions become intensely luminescent again and strikingly, the emission colours differ in varying solvents (Fig. 6). This process is entirely reversible as the thawed solutions lose their photoluminescence properties. Note that the luminescence of 1b is affected in a similar fashion by dissolution in the aforementioned solvents and the freezing procedure.
Fig. 5 Left: A portion of the structure of crystalline [Au{C(NHMe)2}2][PF6]·0.5acetone (1a). Solvent molecules (acetone) are omitted. Right: A portion of the structure of crystalline [Au{C(NHMe)2}2][BF4] (1b).108 |
Fig. 6 Left: Emission spectra obtained from 6 mM solutions of 1a, frozen at 77 K. Top right: Emission spectra obtained from 0.06 mM solutions of 1a frozen at 77 K and crystalline 1a at 77 K. Bottom right: Photograph of the luminescence from 6 mM solutions of 1a at 77 K. From left to right: MeCN, DMSO, DMF, pyridine, acetone. Reprinted (adapted) with permission.108 Copyright 2002 American Chemical Society. |
The absence of luminescence in solutions of 1a is presumably due to a breakdown of the polymeric structure into smaller units or monomers. The fact that the emission spectra of the frozen solutions strongly resemble the spectrum of polycrystalline 1a suggests similarities in the respective molecular structures. In this regard, it is reasonable that oligomeric forms of [Au{C(NHMe)2}2][PF6], generating species similar in structure to the arrangement of crystalline 1a, do form upon freezing the different solutions. The detailed molecular structures that are present in the frozen solutions could not be resolved, but it is apparent that the luminescence behaviour is affected by the number of gold ions, the Au–Au distance, the orientation of the ligands, hydrogen bonding interactions, the anion itself and the coordination of solvent molecules to the metal centers.111 A detailed understanding of these aspects might play a crucial role, e.g. in the development of sensors for different chemical environments.
Other examples for purely cationic chain links paired with weakly coordinating anions (WCA) were presented by the Krossing group in 2016.112 A series of [Au(MeCN)2][WCA] salts was prepared by direct oxidation of elemental gold in acetonitrile (MeCN) with nitrosyl salts of the type [NO]+[WCA]− ([WCA]− = [BF4]−, [GaCl4]−, [B(CF3)4]−, [Al(OC(CF3)3)4]− and [B(CF3)3CN]−). The resulting complexes [Au(MeCN)2][BF4] (2a) and [Au(MeCN)2][GaCl4] (2b) contain gold strings only composed of [Au(MeCN)2]+ cations that are interconnected by aurophilic interactions in the solid state, whereas the corresponding [B(CF3)4]− and [Al(OC(CF3)3)4]− salts form dimers and monomers, respectively (Scheme 2).
Scheme 2 Synthesis and molecular structures of compounds 2a and 2b in the solid state.112 |
In both 2a and 2b, a weak interaction to the fluoride and chloride atoms of the respective anions BF4− and GaCl4− is observed in a trans ‘coordination’, although the atomic distances are outside of their van der Waals distance. In 2a, the contact lengths between adjacent gold atoms follow a repeating medium–short–short–medium–long–long pattern with the shortest contact being 3.113 Å. The respective Au–Au distances in 2b are equidistant (3.540 Å). Interestingly, Au–Au contact lengths are correlated with the coordination strength of the anions, which follows a [BF4]− > [GaCl4]− > [B(CF3)4]− > [Al(OC(CF3)3)4]− sequence.113,114 The cations thus appear in four forms: (a) as a chain with strong contacts (2a), (b) as a chain with weak contacts (2b), (c) as a dimer ([WCA]− = [B(CF3)4]−) and (d) as a monomer ([WCA]− = [Al(OC(CF3)3)4]−). This leads to the hypothesis that more electron-rich gold(I) centers feature stronger aurophilic interactions.
The assumption that the respective anion plays a decisive role regarding the molecular structure and resulting properties of cationic gold strings is further supported by a series of [(C6H11NC)2Au][XF6] salts (X = P (3a), As (3b), Sb (3c)) published by the Balch group.115–117 The hexafluoropnictogenates PF6−, AsF6− and SbF6−, although being weakly coordinating anions, alter the structure and thus the photophysical properties (including vapochromism and thermochromism) of the cationic string consisting of the two-coordinate [(C6H11NC)2Au]+. The term ‘thermochromism’ is used to describe a (typically reversible) temperature dependent change in the photophysical properties (e.g. colour or emission wavelength) of a sample. This phenomenon can be attributed to a change in the molecular or crystal structure.118,119 Both compounds 3a and 3b crystallize either as colourless, blue-emitting crystals or as yellow, green emitting crystals. Interestingly, the colourless crystals of 3a and 3b are isostructural (Fig. 7, P21/c), whereas the yellow crystals exhibit different solid state structures (Fig. 7, P212121 and P). The SbF6− derivative 3c is obtained as pale-yellow crystals as well, exhibiting a blue luminescence, yet its molecular structure is entirely different from that of 3a and 3b. Two different chains of cations are observed and both run parallel along the same crystallographic axis (Fig. 7). The Au–Au separations of 3a–c are summarized in Table 1.
Fig. 7 Comparison of the columnar structures of the different forms of [(C6H11NC)2Au][XF6] (X = P (3a), As (3b), Sb (3c)). For clarity, only the gold ions and the CNC portion of the ligands attached to the metals are indicated. Aurophilic interactions are shown as dashed lines. Anions are not shown. There are no solvate molecules in any of the crystal structures. Reprinted (adapted) with permission.115 Copyright 2020 American Chemical Society. |
Sample | Colourless polymorph | Yellow polymorph |
---|---|---|
3a | 3.1822(3) Å | 2.9803(6) Å |
2.9790(6) Å | ||
2.9651(6) Å | ||
2.9643(6) Å | ||
3b | 3.1983(8) Å | 3.0230(5) Å |
3.0097(6) Å | ||
3c | Chain 1: | |
3.0252(7) Å | ||
3.0858(7) Å | ||
Chain 2: | ||
3.0424(9) Å | ||
3.0782(9) Å |
Although being intensely luminescent in the solid state, solutions of 3a–c are not emissive, which is consistent with a breakdown of the polymeric structure into monomers. However, upon exposure of the yellow, green-emitting polymorphs of 3a and 3b to vapours of selected solvents (dichloromethane, acetone, methanol or acetonitrile), a conversion to their respective colourless, blue-emitting polymorphs is observed (Fig. 8). In contrast, no change in colour or luminescence was observed in similar experiments with 3c.
Fig. 8 Photographs of crystalline 3b: (A) at ambient light, (B) upon UV irradiation, (C) after exposure to dichloromethane vapour upon UV irradiation, and (D) after crushing the crystal upon UV irradiation. Reprinted (adapted) with permission.115 Copyright 2020 American Chemical Society. |
Crystalline samples of 3a–c can be melted upon rising the temperature to a range of 113–126 °C. Independent of the polymorph type, the resulting melts of all samples are colourless and exhibit a bluish-white emission. Upon cooling, the respective yellow polymorphs of 3a and 3b are eventually formed, indicating that these are the thermodynamically more stable forms. Cooling the melt of 3c results in the reformation of crystalline 3c. However, a peculiarity is observed regarding the colourless polymorph of the AsF6− derivative 3b, which, upon rising the temperature to 100 °C, transforms into a yellow solid without melting. The emission spectrum of this solid is nearly identical to that of the respective yellow polymorph. A similar yellow solid is formed by cooling the melt of 3b, but in this case, the emission spectrum of this amorphous sample does not resemble the spectra of either the colourless or the yellow polymorph, indicating the formation of a new phase. The colourless polymorph of 3b is the only sample that shows this thermochromic behaviour. In addition, the mixed-anion salts [(C6H11NC)2Au][PF6]0.5[AsF6]0.5, [(C6H11NC)2Au] [PF6]0.5[SbF6]0.5, [(C6H11NC)2Au][AsF6]0.5[SbF6]0.5, [(C6H11NC)2Au][PF6]0.25[AsF6]0.75 and [(C6H11NC)2Au] [PF6]0.75[AsF6]0.25 were prepared by co-crystallization. Similar to 3a and 3b, colourless, blue-emitting and yellow, green-emitting polymorphs were found for all mixed-anion salts. Remarkably, all of the colourless crystals formed from a mixture of two anions show luminescence thermochromism below their melting points, similar to the colourless polymorph of 3b. In the interest of an overall view, we would like to dispense a further detailed discussion about the mixed-anion salts, yet an in-depth investigation of these compounds can be found in the original work.115 The thermochromic and melting point ranges are summarized in Table 2. A picture of the thermochromic behaviour is shown in Fig. 9.
Fig. 9 Photographs of the luminescence from a crystal of [(C6H11NC)2Au][PF6]0.5[AsF6]0.5. Top: Blue luminescence at ambient temperature. Bottom: Green luminescence after heating to 104–108 °C. Reprinted (adapted) with permission.115 Copyright 2020 American Chemical Society. |
Compound | Thermochromic range [°C] | Melting point range [°C] |
---|---|---|
Colourless form | ||
[(C6H11NC)2Au][PF6] | None | 115–120 |
[(C6H11NC)2Au][AsF6] | 98–102 | 123–125 |
[(C6H11NC)2Au][PF6]0.5[SbF6]0.5 | 87–95 | 114–116 |
[(C6H11NC)2Au][AsF6]0.5[SbF6]0.5 | 88–92 | 113–114 |
[(C6H11NC)2Au][PF6]0.5[AsF6]0.5 | 104–108 | 118–119 |
[(C6H11NC)2Au][PF6]0.75[AsF6]0.25 | 105–111 | 118–121 |
[(C6H11NC)2Au][PF6]0.25[AsF6]0.75 | 100–105 | 118–121 |
Yellow form | ||
[(C6H11NC)2Au][PF6] | None | 110–115 |
[(C6H11NC)2Au][AsF6] | None | 123–126 |
[(C6H11NC)2Au][SbF6] | None | 113–115 |
These results show the significant impact of the respective anion on the aurophilic interactions, even though being weakly coordinating and well separated from the chains of gold ions that form the 1D molecular structure. Most likely, the differences in the volume of the anions are responsible for the variations in the solid state structures and ultimately, in the thermochromic and vapochromic responses.
Fig. 10 Representation of the crystal structure of 4.121 |
Another fascinating example for negatively charged chains is a series of bis(thiocyanato)aurates [Au(SCN)2]− with varying countercations including Na+ (5a), K+ (5b), Rb+ (5c), Cs+ (5d), NH4+ (5e), NMe4+ (5f), N(nBu)4+ (5g) and PPh4+, introduced in 2004 and 2006 by the Elder group.122,123 The phosphonium salt consists of isolated monomers, whereas the nearly isostructural alkali salts, as well as the NH4+ salt, form infinite linear gold strings with alternating long and short Au–Au distances along the chain. The NMe4+ salt forms a kinked chain of trimers and the N(nBu)4+ salt consists of isolated dimers (Fig. 11).
Fig. 11 Representation of the anion-arrangement in compounds 5a–g.122,123 |
Polycrystalline samples of 5a–g show photoluminescence upon UV excitation at cryogenic temperature (77 K) with emission maxima ranging from 506 to 710 nm (Table 3).
Sample | Au–Au [Å] | Exc [nm] | Em [nm] | E [cm−1] |
---|---|---|---|---|
5b | 3.0064(5) | 320 | 516 | 19379 |
3.0430(5) | ||||
5g | 3.0700(8) | 360 | 539 | 18552 |
5c | 3.0821(4) | 320 | 506 | 19762 |
3.1144(5) | ||||
5e | 3.1409(3) | Not stated | 627 | 15949 |
3.1723(3) | ||||
5f | 3.1794(2) | 325 | 635 | 15748 |
3.2654(2) | ||||
5d | 3.2128(11) | 320 | 670 | 14925 |
3.2399(11) | ||||
5a | Unknown | 320 | 710 | 14084 |
In the crystal structures of the gold string compounds 5b–5f, alternating short and long Au–Au distances can be observed. Thus, their molecular structures can be described as a polymer of dimers (or trimers in the case of 5f). Interestingly, when the emission energy (cm−1) is plotted against the reciprocal of the short Au–Au bond lengths (Å−1), a strong correlation can be observed (Fig. 12), which is in accordance with theoretical predictions.124
Fig. 12 Energy [cm−1] versus 1/d [Å−1] of the short Au–Au interaction of [Au(SCN)2]nn−. Reprinted (adapted) with permission.122 Copyright 2004 American Chemical Society. |
The overall length of the gold chains appears not to be a crucial factor in this case, as the dimeric complex 5g and the assembly of trimers in 5f fall in line with the data for the ‘infinite’ chains. Instead, it is very likely that not only the supramolecular string, but also single gold–gold pairs or ‘Au3’ trimers with equidistant gold–gold contacts serve as the source of the emission.
A different picture emerges in ionic liquids containing [Au(SCN)2]− moieties, when differently substituted imidazolium cations instead of ‘inorganic’ cations are used, as presented by Aoyagi and co-workers in 2015.125 In this case, ionic liquids of the type [Cnmim][Au(SCN)2] (mim = methylimidazolium) are formed (Scheme 3).
Scheme 3 Synthesis of 6a and metal-containing ionic liquids (M-IL) 6b–d.125 |
The imidazolium salts 6b–d are ionic liquids at ambient temperatures with very low glass transition temperatures around 200 K. An exception is compound 6a, which forms a solid at room temperature. Compound 6a consists of [Au(SCN)2]nn− gold strings with Au–Au distances of 3.1773(3) Å, as observed in the corresponding crystal structure (Fig. 13). Interestingly, using photocrystallography, it was possible to resolve the structural changes induced upon UV light irradiation. Besides a change in the unit cell parameters, an excimeric contraction of the (Au–Au)* distance is observed as well. A list of changes regarding bond lengths is summarized in Table 4.
Fig. 13 Excerpt of the crystal structure of 6a.125 |
Bond | Lamp off [Å] | Lamp on [Å] | Δoff–on [Å] |
---|---|---|---|
Au1–S1 | 2.304(3) | 2.319(5) | −0.015(6) |
Au2–S2 | 2.294(2) | 2.300(5) | −0.006(5) |
S2–C2 | 1.680(10) | 1.66(2) | 0.02(2) |
S1–C1 | 1.668(10) | 1.65(2) | 0.018(10) |
Au1–Au2 | 3.1773(3) | 3.1659(3) | 0.0114(4) |
Furthermore, for the M-ILs 6b–d, time-resolved laser fluorescence spectroscopy (TRLFS) was performed. The spectra of the crude products are shown in Fig. 14. After a delay time of 100 μs to the excitation pulse, the peaks between 519 and 526 nm disappear, indicating fluorescence from the S1 state, and all envelopes of the spectra undergo a blue-shift. The data indicate a colour change in a single luminescence decay event. The existence of multiple different aggregates of [Au(SCN)2]nn−, possessing individual spectral features and luminescence lifetimes, is therefore suggested. For example, since the band gap of the T1 phosphorescent state to the S0 state is reduced by the number of metal ions involved, the peak in the deconvolution curves (green) at around 548 nm (Fig. 14, inset (a)) is attributed to a small aggregate, presumably a dimer [Au(SCN)2]22−, since the monomer (with no aurophilic interaction) shows no luminescence behaviour.
Fig. 14 Time-resolved luminescence spectra of 6b (a), 6c (b) and their deconvolution curves (green) at 77 K (λex = 355 nm). Reprinted (adapted) with permission.125 Copyright 2015 American Chemical Society. |
The dicyanoaurate anion [Au(CN)2]− is a highly stable ion and is therefore used or observed in many different processes, such as cyanide leaching,126 gold electroplating127 or in protein crystallography as a phasing agent.128 A number of crystallographically investigated compounds containing [Au(CN)2]− are described in the literature. However, the aggregation of multiple [Au(CN)2]− units seems disfavoured in terms of Coulomb repulsion. On the other hand, the low steric demand, the simple linear structure and not least the hydrogen bond acceptor ability of the cyanides facilitate a self-aggregation process.129,130 In this context, the Attar and Balch groups investigated the formation and luminescence of dicyanoaurate strings comprising common ammonium counter cations.131 Among the presented piperidinium [C5H10NH2][Au(CN)2] (7a), pyrrolidinium [C4H8NH2][Au(CN)2] (7b), 1,1-diphenylhydrazinium [Ph2NNH3][Au(CN)2] (7c) and tetrapropylammonium [(C3H7)4N][Au(CN)2] (7d) salts, only the latter does not form a polymeric string in the solid state, presumably due to a lack of N–H groups suitable for hydrogen bonding to the cyanide moieties of the anions. Exemplarily, the crystal structure of 7c is shown in Fig. 15.
Fig. 15 Excerpt of the crystal structure of 7c·H2O.131 |
In compound 7c, the aurates form an infinite gold string with equidistant Au–Au separations of 3.0866(4) Å. It is noteworthy that hydrogen bonds between the cyanides and the 1,1-diphenylhydrazinium cations and additional water molecules stabilize and support the formation of the string compound. The crystal structures of the analogues 7a and 7b are comparable to that of 7c, although hydrogen bonds are exclusively formed between the cyanide and the ammonium moieties.
In general, the Au–Au distances of 7a–c are remarkably short and lie in a narrow range of 3.0795(4)–3.0969(3) Å, whereas the shortest metal–metal distance in the tetrapropylammonium derivative [(C3H7)4N][Au(CN)2] (7d) is 7.526(1) Å and therefore far outside the aurophilic range. In consequence, crystalline 7a–c show intense blue luminescence, even at ambient temperature. The small range of the emission maxima (436 nm (7a), 451 nm (7b) and 400 nm (7c)) reflects the fact that their molecular structures in the solid state and their respective Au–Au separations are similar. In contrast, the charge separated salt [(C3H7)4N][Au(CN)2] without aurophilic contacts is non-luminescent at ambient and cryogenic (77 K) temperatures.
Purely anionic chains often include heterometallic compounds in which the chains are cross-linked by additional metal ions. By using dicyanoaurates [Au(CN)2]− as anions, similar to compounds 7a–c, but employing a metal complex as a [cation]+, (hetero)bimetallic coordination polymers are obtained.132 In this compound class, the bidentate character of the cyanide ligand is the driving force for the formation of supramolecular architectures. Representative compounds consist of [M(L)n]x[Au(CN)2]y (M = Cu, Mn, Zn, Ni, Co, Cd, Au; L = multidentate N-donor ligand).133–148 The general connectivity is illustrated in Scheme 4.
In many cases, the respective cationic [M(L)n] block consists of a divalent transition metal paired with a neutral multidentate ligand like phenanthroline, bipyridine or TMEDA. Additionally, +2 charged metal complex cations [M(L)n]2+, which consist of metal ions in higher oxidation states and negatively charged ligands, were employed for the construction of bimetallic coordination polymers, which tend to grow in two or three dimensions. The properties of the compounds, e.g. magnetism142 or biological activity,141 are mainly derived from the cationic [M(L)n]2+ building block. As an example, the first uranium-containing [Au(CN)2]− coordination polymer [UO2(bipy)(MeO)(MeOH)]2[(μ-Au(CN)2)(Au(CN)2)] (8) was presented by Leznoff and co-workers in 2017 (Fig. 16).149
Fig. 16 Excerpt of the crystal structure of 8.149 |
Compound 8 was synthesized by the reaction of [NBu4][Au(CN)2]·0.5H2O, UO2(NO3)2·6H2O and 2,2′-bipyridine in methanol. The molecular structure in the solid state consists of a one-dimensional gold chain structure of trinuclear [UO2(bipy)(MeO)(MeOH)]2[Au(CN)2] units linked by aurophilic contacts of 3.0528(5) Å to adjacent, unbound [Au(CN)2]− units. The dicyanoaurate anions are staggered, with a C–Au–Au–C torsion angle of 75.1(6)°. The different stretching frequencies of the cyanide ligands can be observed in the IR spectrum (CN = 2169 and 2133 cm−1) as well as in the corresponding Raman spectrum (CN = 2187 and 2148 cm−1). The blue-shifted bands can be assigned to the uranyl-bound [Au(CN)2]− units, whereas the resonance at lower energy is assigned to the free [Au(CN)2]− units.
In 2018, Lu, Chen and co-workers presented a library of 35 different combinations of [Au(NHC)2][MX2] (NHC = N-heterocyclic carbene; M = Au or Cu; X = halide, cyanide or arylacetylide) complex salts (Fig. 17), outlining the large diversity of the double-salt approach.15,150,151 Although not every compound was analysed by single crystal X-ray diffraction, it is assumed that all double salts feature infinite metal strings in the solid state. A representative crystal structure (C3–A8) is shown in Fig. 17. The intermetallic distances of the double salts, of which crystal structures were determined, are in the range of 3.182–3.384 Å (Au–Au) and 3.373–3.398 Å (Au–Cu). The prepared complex salts are emissive in the solid state upon UV irradiation with emission maxima ranging from 448 nm (C1–A1) to 785 nm (C3–A14), emission lifetimes ranging from 0.1 μs (C3–A13) to 7.1 μs (C1–A2) and quantum yields ranging from 10% (C3–A10) to 99% (C1–A5 and C2–A5). A picture of selected double salts upon UV-irradiation and representative emission spectra are shown in Fig. 18.
Fig. 17 Left: Chemical structures of four cationic (C1–C4) and fourteen anionic (A1–A14) precursors. Right: Representation of the crystal structure of the double salt C3–A8.15 |
Fig. 18 (a) The images of the 35 complex salts dispersed in water or acetonitrile observed under a 365 UV lamp; (b) normalized solid-state emission spectra of selected complex salts showing the multi-colour luminescence. Adapted with permission from John Wiley & Sons, copyright 2018.15 |
The following structure–property relationships can be derived from in-depth analysis of the photophysical properties: (1) Maintaining the anion, the emission energy of the resulting double salt red-shifts with more electron withdrawing NHCs on the cations. (2) Maintaining the cation, the emission energy of the resulting double salt red-shifts with more electron donating ligands on the anion series of [AuX2]−, yet it remains constant for the respective [CuX2]− salts. (3) The double salts of the form [Au(NHC)2][CuCl2] generate the highest quantum yields.
Interestingly, the combinatorial pool of double salts allows for multi-colour emission by combining two phosphors with different emission colour. Therefore, co-crystallization of C2, A1 and A4 (molar ratio 2:1:1) results in the formation of the triple salt C2–A1/A4 (Fig. 19).
Fig. 19 Representation of the crystal structure of the triple salt C2–A1/A4.15 |
The triple salt C2–A1/A4 indeed shows dual emission at 586 and 652 nm. The latter is significantly red-shifted compared to the corresponding parent complex salts C2–A1 (469 nm) and C2–A4 (570 nm), which can be explained by a simultaneous, yet not equal raise in energy of the HOMO and LUMO. This is due to a stronger σ-donating and weaker π-accepting capability of the iodide ligand in comparison with that of cyanide. The emission colour of C2–A1/A4 can further be fine-tuned by varying the molar ratios of A1 and A4 upon co-crystallization (Fig. 20). By screening the combinatorial pool, Lu, Chen and co-workers impressively demonstrated that metallophilic interactions, in the form of 1D chains, provide an easy access to new phosphorescent materials with high quantum yields and versatile colour tunability.
Fig. 20 (a) A sketch for the co-crystallization process; (b) fluorescence micrographs of C2–A1/A4 microcrystals prepared via co-crystallization; (c) excitation and emission spectra of C2–A1/A4 microcrystals with a variety of A1:A4 ratios. Adapted with permission from John Wiley & Sons, copyright 2018.15 |
Besides the combination of the typical monovalent cationic and anionic gold complexes152,153 that were highlighted above, this concept can be readily expanded to mixed-valence gold(I/III) complexes,154,155 as shown e.g. by Heck and co-workers.156 A reaction of AuCl, AuCl3 and cyclohexylcarbonitrile (NC-Cy) yielded the complex [Au(NC-Cy)2][AuCl4] (9).
The crystal structure consists of linear gold strings with alternating [Au(NC-Cy)2]+ and [AuCl4]− units (Fig. 21). The distances between the Au(I) and Au(III) centers are equidistant (polymorph A: 3.2382(4) Å; polymorph B: 3.2499(2) Å) and furthermore display the shortest unsupported Au(I)–Au(III) interactions that have been observed to date.
Fig. 21 Representation of the crystal structure of 9.156 |
Fig. 22 Representation of the crystal structure of 10b.172 |
Sample | Intra Au–Au [Å] | Inter Au–Au [Å] | Solid-state structure |
---|---|---|---|
(o-xylylNC)AuCl (10a) | 3.3570(11) | 4.0225(12) | Dimers |
(o-xylylNC)AuBr (10b) | 3.3480(5) | 3.7071(10) | Slightly kinked chain |
(o-xylylNC)AuI (10c) | 3.4602(3) | 3.4602(3) | Slightly kinked chain |
(o-xylylNC)AuCN (10d) | 3.4220(6) | 3.4615(6) | 2D structure |
3.1706(4) |
In accordance, Scheer and co-workers studied Au(I) complexes containing phosphanyl and arsanyl borane ligands and concluded that softer co-ligands coordinated to Au(I) tend to form extended polymeric structures due to multiple Au–Au interactions when compared to hard Lewis bases.176 In fact, gold in its +I oxidation state is a very soft Lewis acid and therefore has a pronounced affinity towards soft bases such as sulfur or selenium,177–180 which is in accordance with Pearson's principle of hard and soft acids and bases (HSAB).181–184 In this context, many gold string compounds are supported by bidentate dithiophosphate,185–189 dithiocarboxylate,190,191 diselenophosph(in)ate192,193 or related ligand systems.194–199 The Ch-X-Ch donor sites (Ch = chalcogenide, X = C, P) exhibit a low steric demand, which allows for the formation of gold strings comprising intermolecular connected homoleptic digold complexes (Fig. 23).
Fig. 23 General connectivity of gold strings comprising Ch-X-Ch ligand systems (Ch = chalcogenide, X = C, P). |
In 2014, Katrusiak and co-workers studied the behaviour of a dithiocarbamate-ligated one-dimensional gold string towards the application of pressure.200 The two known polymorphs of [Au(Et2DTC)]2 (11) (DTC = dithiocarbamate) differ in their respective crystal structures as shown in Fig. 24. The α-phase consists of repeating identical units of [Au(Et2DTC)]2, whereas the β-phase exhibits an interval two times longer. For both, the intramolecular Au–Au bond lengths are about 2.78 Å, while the respective unsupported intermolecular Au–Au distance is about 0.2 Å longer.
Fig. 24 Representation of the crystal structure of 11. The brackets indicate the repeating unit of the two different polymorphs.200 |
The selective formation of either the α- or the β-phase can be controlled by varying the crystallization conditions or by the application of pressure. It is observed that above 50 MPa, the tetragonal crystals of the α-phase transform to an orthorhombic β-phase. Interestingly, the Au–Au distances can be further compressed by increasing the pressure. Thereby, the intermolecular Au–Au bonds are shortened at an average rate of −0.1006 Å per applied GPa. The average compressibility of the fully supported intramolecular Au–Au bonds, measured between 0.1 MPa and 1.0 GPa, is −0.0435 Å GPa−1 (Fig. 25). Thus, the fully supported bond is more than two times harder (i.e. deforms twice less). At 0.1 GPa, the supported Au–Au bonds are similar in length to that in metallic gold, whereas a pressure of 1.0 GPa diminishes the contact length to 2.72 Å, which therefore is about 0.05 Å shorter in comparison with that for the metal.
Fig. 25 Compression of the Au–Au distances in phases α (open circles) and β (full symbols) of 11. The pressure dependence of the Au–Au distance (hardly changing to 1.0 GPa) in metallic gold is shown as the dashed line. Intramolecular and intermolecular bonds are shown. Reprinted with permission.200 Further permissions to this material should be directed to the ACS. |
Another example for dithiocarbamate ligated gold strings involves the report of solvochromic luminescence regarding a dinuclear gold(I)-(aza-[18]crown-6)dithiocarbamate (12), as presented by Chao and co-workers.201 The study investigates the effect of different solvates on the Au–Au distance of 12 and its resulting luminescence behaviour. Initially, the title compound was synthesized in the presence of MeCN to obtain 12·2MeCN (Fig. 26).
Fig. 26 Representation of the crystal structure of 12·2(MeCN). Solvent molecules are omitted.201 |
Immersing the crystals of 12·2MeCN in a tert-butylbenzene or m-xylene solution yielded 12·tert-butyl-benzene·H2O and 12·0.5m-xylene respectively through single-crystal-to-single-crystal (SCSC) phase transformation. Hereby, 12 forms 1D chains irrespective of the presence of the aforementioned solvates. The Au–Au distances in 12, when crystallized with different solvates and their corresponding emission wavelengths, are summarized in Table 6. From the values, a direct correlation between the Au–Au distance and the emission wavelength is observed. The study was extended to other aromatic solvates with electron donating groups and it was observed that the emission energies vary in the following order: tert-butylbenzene (546 nm) > dry (553 nm) > benzene (566 nm) > p-xylene (568 nm) > m-xylene (583 nm) > o-xylene, anisole, toluene (595 nm) > MeCN (602 nm). It is suggested that even though the electron-donating substituents in the solvates do not interact with the complexes, they influence stacking in the crystal lattice, affecting i.e. the Au–Au distance. As a result, the complexes exhibit distinct emission wavelengths as shown in Fig. 27. In a similar study, Ito and co-workers presented the formation of crystals comprising gold isocyanides as a versatile host system with guest-dependent luminescence.202
Fig. 27 Solvochromic luminescence (λexc = 380 nm) of (a) dry samples of 12·2MeCN and upon grinding with (b) tert-butylbenzene, (c) benzene, (d) p-xylene, (e) m-xylene, (f) o-xylene, (g) anisole, (h) toluene, and (i) MeCN. Adapted with permission from John Wiley & Sons, copyright 2014.201 |
Sample | Intra Au–Au [Å] | Inter Au–Au [Å] | Em [nm] |
---|---|---|---|
12·2MeCN | 2.7186(3) | 2.8355(3) | 602 |
2.7249(3) | |||
12·0.5m-xylene | 2.755(2) | 2.890(2)–2.902(2) | 583 |
2.764(2) | |||
12·tBu-benzene·H2O | 2.7713(4) | 2.9420(5) | 546 |
12 (dry sample) | Unknown | Unknown | 553 |
In 2016, Ito and co-workers reported the synthesis of phenyl(phenylisocyanide)gold(I) (13a) and phenyl(3,5-dimethylphenylisocyanide)gold(I) (13b), which exhibit mechano triggered SCSC phase transformations and possess interesting optical and electronic properties.23,203–205 Complexes 13a and 13b were obtained as blue- and green-emitting single crystals respectively. However, a rapid phase transition was observed when the crystals were mechanically triggered. The phase transition of 13a and 13b propagated to the entire crystal to yield the daughter phases 13aSCSC and 13bSCSC. The values determining the photoluminescence properties of the corresponding crystals are summarized in Table 7 and their respective PL spectra are displayed in Fig. 28. The PL spectra indicate that the phase transition induces a red- and blue-shift of the emission bands of 13a and 13b, respectively.
Fig. 28 Top: Mechano-triggered SCSC phase transition of 13a to 13aSCSC and 13b to 13bSCSC over time. Bottom: PL spectra of crystals 13a and 13b in comparison with their daughter phases obtained upon slight mechanical stimulation. Excitation wavelength: 365 nm. Adapted with permission from John Wiley & Sons, copyright 2016.23 |
Sample | Em [nm] | Φ em [%] | τ av [μs] |
---|---|---|---|
13a | 460 | 4 | 108 |
490 | |||
13aSCSC | 566 | 16 | 5.33 |
13b | 540 | 84 | 0.97 |
13bSCSC | 535 | 6 | 13.8 |
The changes in the emission properties were rationalized by the formation of different crystal structures (shown in Fig. 29).23 The crystal structure of 13a comprises dimeric units (formed by CH/π interactions) which are further stacked into 1D columns through additional CH/π interactions. The shortest Au–Au distance of 5.733 Å indicates the absence of aurophilic interactions. However, on mechanical stimulation, the monomeric units are twisted and aurophilic contacts of 3.177 Å are formed within the dimeric units of 13aSCSC, which is in accordance with the red-shift of the emission band of 13a. The crystal structure of 13b consists of hexamers held together by aurophilic interactions, which are in the range of 3.274–3.112 Å. The hexamers are stacked into 1D columns supported by π–π interactions. Mechanical stimulation of the green-emitting species 13b leads to the formation of the blue-emitting daughter phase 13bSCSC (the Au–Au distance is 4.784 Å) by disconnecting the aurophilic interactions. Additionally, weak CH/π interactions are formed in the daughter phase.
Fig. 29 Crystal structures of (a) 13a (b) 13aSCSC (c) 13b and (d) 13bSCSC. Dotted lines and solid lines indicate CH/π interactions and aurophilic interactions, respectively.23 |
Furthermore, intergrowth (IG) crystals comprising multiple crystal domains of different polymorphs were prepared by mechanical stimulation. Quantitatively, SEM images show the difference between the IG crystals and their respective daughter phases in terms of charging ability which is demonstrated in Fig. 30. Moreover, the conductive properties of the samples were analysed quantitatively. The evaluation of conductive properties typically requires an electrode–sample contact, which is not very effective for 13a and 13b, because such a contact would trigger SCSC phase transition. For this reason, flash-photolysis time-resolved microwave conductivity (FP-TRMC) measurements were performed. Although this method only gives insight into short-range (approx. 10 nm) conductivity, it is contactless and therefore suitable to increase the knowledge about the electronic properties of the polymorphs.
Fig. 30 Photoluminescence microscopy images of (a) 13aIG and (c) 13bIG upon excitation at 365 nm and sputtering-free SEM images of (b) 13aIG and (d) 13bIG. Schematic representations of charging in (e) 13aIG and (f) 13bIG, when observed by SEM. Adapted with permission from John Wiley & Sons, copyright 2018.23 |
The maximum transient conductivity of species 13a was determined to be φ∑μ = 1.3 × 10−5 cm2 V−1 s−1, while the conductivity of species 13aSCSC was significantly higher at φ∑μ = 1.3 × 10−4 cm2 V−1 s−1. This increase of conductivity is most likely attributed to the formation of aurophilic interactions, as observed in the respective crystal structures (Fig. 29). For 13b and 13bSCSC, maximum transient conductivities of 3.2 × 10−5 and 2.8 × 10−6 cm2 V−1 s−1 were determined. The fact that the conductivity of 13bSCSC is one order of magnitude lower than that for 13b supports the assumption that the difference in conductivity of the samples is directly attributable to the presence or absence of aurophilic interactions in each species.
Another example focussing on the correlation between a change in the crystal structures and the photophysical properties due to external stimulation was presented by Eisenberg and co-workers in their report on luminescence tribochromism.206 It describes the phenomenon that luminescence of suitable solid samples can be turned on by gentle grinding. Their work focussed on Au(I) thiouracilate complexes which were synthesized by reacting [Au2Cl2(μ-dppm)] and AgCO2CF3 with 2-thiouracil (TU) and 6-methyl-2-thiouracil (Me-TU) to give [Au2(μ-TU)(μ-dppm)]CF3COO (14a) and [Au2(μ-Me-TU)(μ-dppm)]CF3COO (14b), respectively (Scheme 5).
Scheme 5 Synthesis of 14a and 14b.206 |
The obtained complex 14a is a monocationic dinuclear Au(I) complex, which forms a helical structure in the solid state. A head to tail arrangement of the TU moieties is observed and an intramolecular Au–Au distance of 2.8797(4) Å and an intermolecular Au–Au distance of 3.3321(5) Å were determined. The structure of 14b is similar to that of 14a, except that the helix is discontinuous for head to head arrangement with an inter Au–Au distance of 4.344 Å and for the head to tail arrangement, the average Au–Au distance is 3.236–3.354 Å. 14a and 14b are either weakly luminescent or non-emissive. However, on gently grinding the solids, a bright cyan coloured luminescence was observed at room temperature. Recrystallization of the emissive forms in the presence of CF3COOH again results in the formation of 14a or 14b. However, the emissive forms (15a and 15b) can be selectively prepared by stirring CH2Cl2/MeOH solutions of 14a or 14b over Na2CO3 followed by filtration. The changes seen in the presence of the base/acid might be due to the deprotonation/protonation of the pyrimidine N–H moiety of thiouracil. The PL spectra of both emissive (15b) and non-emissive (14b) forms are displayed in Fig. 31.
Fig. 31 Emission spectra of 14b (black line) and ground crystals of 14b (blue line), CH2Cl2 solution of 14b (---) and crystals of 15b (⋯) (prepared by reaction with Na2CO3) at room temperature (at λex = 375 nm). Reprinted (adapted) with permission.206 Copyright 2003 American Chemical Society. |
The emissive compound 15b has a similar structure to 14a and 14b but different packing arrangements, and comprises strong intermolecular aurophilic interactions between the dimers with a distance of 2.9235(4) Å (Fig. 32). Hence, it can be concluded that the delicate balance between changes in the Au–Au interactions and acidity of the sample results in this fascinating luminescence tribochromism.
Fig. 32 Top: (a) View of cationic 14a with phenyl rings omitted; (b) helical arrangement of the gold ions in 14a with ligands omitted for clarity. Bottom: Perspective view of 15b with phenyl rings omitted.206 |
Among the compound class of neutral gold strings, cyclic trinuclear gold complexes represent a special case as they exhibit unique electronic properties.207 Their properties are majorly impacted by intermolecular interactions in the solid state that involve aurophilic contacts between the trimers.208 Balch and co-workers have reported on the synthesis and intermolecular interactions in the polymorphs of [Au3(MeNCOMe)3] (16a), [Au3(n-PentNCOMe)3] (16b) and [Au3(i-PrNCOMe)3] (16c) in 2005 (Fig. 34).209 The trinuclear gold complexes of the form [Au3(RNCOR′)3] stack in four different arrangements, dependent on the bulkiness of the ligand substituents (R, R′), which retard or enhance intertrimer interactions, as reported by Omary and co-workers (Fig. 33). The stacking arrangements mainly differ regarding the nature of relative disposition of trimers with respect to each other.24
Fig. 33 Different stacking arrangements of trimers, in which the dashed lines and solid lines indicate inter and intramolecular Au–Au interactions. I, II, III and IV represent eclipsed, disorder staggered, chair and staircase stacking arrangements.24 |
Fig. 34 Chemical structure of trinuclear Au(I) carbeniate complexes.209 |
16a forms three polymorphs, namely hexagonal, monoclinic and triclinic. The hexagonal polymorph forms the stack arrangements I and II, while the triclinic and monoclinic polymorphs are present in the structural motifs III and IV, respectively. The Au–Au distances of the different polymorphs are summarized in Table 8. The hexagonal polymorphs of 16a, in which extended, linear chains of gold ions are present, show some remarkable photophysical properties. Upon irradiation with near-UV light, a dual emission, consisting of a short-lived (t ≈ 1 ms) emission at 446 nm and a broad long-lived (triexponential, t ≈ 1.4, 4.4 and 31 s) emission at 552 nm, is observed. The yellow emission at 552 nm is readily detected by the human eye even seconds after the irradiation has stopped. Interestingly, if a suitable solvent (chloroform, dichloromethane, toluene, methanol, hexane, water) is dropped onto previously irradiated and still glowing crystals of 16a, a bright burst of yellow light is observed. No overall chemical transformation appears to be involved in this solvoluminescence process. This phenomenon can be reproduced until the sample is entirely dissolved. For comparison, the sterically more demanding derivative [Au3(C6H5CH2NCOMe)3], which consists of separated individual molecules in the solid state, does not show long-lived luminescence behaviour. Consequently, the extended supramolecular aggregation of 16a is believed to be important for the energy storage within the solid and may be involved in the solvoluminescence process. In this context, the recombination of a charge or electron separation may be responsible for the emission that occurs by exposure to the solvent.94
Polymorph of 16a | Intra Au–Au [Å] | Inter Au–Au [Å] | Em [nm] |
---|---|---|---|
Hexagonal I | 3.308 | 3.346 | 450 |
Hexagonal II | 3.280 | 3.384 | 520 |
Triclinic III | 3.339 | 3.528 | 444 |
Monoclinic IV | 3.323 | 3.653 | 431 |
Moreover, the unique electronic characteristics of hexagonal 16a are further demonstrated by the successive oxidation with molecular bromine or iodine, yielding in [Au3Xn(MeNCOMe)3] (X = Br, I), where n is 2, 4 or 6.210 A study of the electrochemical oxidation of this compound was presented as well.211 In a 0.1 M N(nBu)4ClO4 dichloromethane solution as the supporting electrolyte, 16a was oxidized at +650 mV, accompanied by the formation of fine, needle-like crystals on the electrode. Not suitable for single crystal XRD measurements, their composition was determined by bulk electrolysis and quartz crystal microbalance techniques to be [Au3(MeNCOMe)3][ClO4]0.34, being the first partially oxidized extended linear chain gold complex. It is assumed that the molecular structure of [Au3(MeNCOMe)3][ClO4]0.34 resembles the hexagonal polymorph of 16a. Chronoamperometric studies confirmed this new phase to be conductive, which offers further insight into the solvoluminescence, energy storage and electron mobility along chains of gold complexes.
The n-pentyl substituted compound 16b crystallizes in an orthorhombic (16b-1) and a triclinic polymorph (16b-2). 16b-1 exhibits a stair case arrangement, in which the intermolecular Au–Au distance between the trimers is 3.618 Å, whereas the intramolecular Au–Au distances are 3.315(3), 3.260(2) and 3.332(2) Å. 16b-2 comprises four independent trimers in the asymmetric unit linked by aurophilic interactions (Au–Au: 3.4614(6), 3.3458(6), 3.6126(6) Å). The shortest Au–Au distance between the asymmetric units is 3.8125(6) Å. Among both polymorphs only 16b-2 is luminescent at room temperature with an emission band at 654 nm (excitation at 326 nm), resulting in a large Stokes shift. This indicates the possible occurrence of a metal-centered excimeric emission due to the contraction of the ground-state aurophilic association.24 The structure of 16c comprises only one trinuclear unit in the asymmetric unit. However, the shortest Au–Au distance in the trimers is 6.417 Å, which is far outside the aurophilic range. Moreover, 16c is not luminescent at ambient temperature, most likely due to the absence of aurophilic interactions. Furthermore, it is suggested that steric effects of the side groups (R, R′) influence the formation of Au–Au interactions and thereby the photophysical properties.
Omary and co-workers have also reported their research on cyclotrimeric gold(I) carbeniates, [Au3(RNCOR′)3] (17a: R = Me, R′ = nBu; 17b: R = nBu, R′ = Me; 17c: R = R′ = nBu and 17d: R = cyclo-pentyl, R′ = Me).24 The crystal structure of [Au3(MeNCOnBu)3] (17a) is exemplarily shown in Fig. 35.
Fig. 35 Excerpt of the crystal structure of 17a with n-butyl groups omitted for clarity.24 |
Their study revealed that a substitution of R or R′ leads to an alteration in solid-state stacking of the trinuclear units and thereby affecting opto-electronic and electronic properties. Bulky R and R′ groups tend to lie above or below the plane of the trinuclear units, which makes stacking of trinuclear Au units into 1D polymeric chains difficult. Molecular simulations of [Au3(HNCOH)3] reveal that infinitely extended chains of eclipsed trinuclear units with head to tail arrangement tend to have smaller Stokes shifts and lower band gaps and reorganization energies (λ), which are ideal characteristics required for the design of semiconducting materials for molecular electronic devices.
Charge transport properties of organic semiconductors in principle depend on the coupling between the geometric and electronic structures of the respective molecules.212 The degree of chain orders in polymers and solid-state stacking in crystals majorly impact the charge transport ability in the organic molecules.213,214 According to Marcus theory, the electron transfer rate (ket) can be expressed as
(2) |
Sample | λ [eV] |
---|---|
[Au3(NHCOH)3] | 0.448 |
[Au3(MeNCOMe)3] | 0.664 |
[Au3(MeNCOnBu)3] | 0.696 |
The molecular simulations predict that, if extended chains of [Au3(RNCOR′)3] with non-bulky groups can be synthesized, they can probably act as ideal semiconductor materials for fabricating molecular electronic devices.
The DFG funded Research Training Group (RTG) 2039 (Molecular architecture for fluorescence cell imaging) is acknowledged for financial support.