Open Access Article
This Open Access Article is licensed under a Creative Commons Attribution-Non Commercial 3.0 Unported Licence

Study on water resistance and tribological behaviours of basalt fibre/acrylonitrile-butadiene rubber composites under water lubrication at various temperatures

Zhuo Li*, Yingzhe Li, Yue Xiao, Yihan Yang and Lin Li
Key Laboratory of Rubber-Plastics, Ministry of Education/Shandong Provincial Key Laboratory of Rubber-Plastics, Qingdao University of Science & Technology, Qingdao 266042, China. E-mail: lizhuoqust@126.com

Received 20th September 2019 , Accepted 21st October 2019

First published on 29th October 2019


Abstract

In this study, the effects of water ageing on characteristics and properties of basalt fibre (BF)/acrylonitrile-butadiene rubber (NBR) composites were investigated, and the tribological behaviours of the composites that slide against the stainless-steel counterpart under water lubrication at 30–70 °C were the main focus. Results showed that with the water temperature increase, the hardness and tear strength of the water-aged samples decreased. Furthermore, both the friction coefficient (COF) and specific wear rate (Ws) of the composites increased with the temperature. The content and the orientation of BFs had no obvious effect on the COF, whereas the parallel-aligned BFs were effective at improving the wear resistance of the composites at both 30 °C and 70 °C.


1. Introduction

Traditionally, the marine stern tube bearing is lubricated by lubricating oils and grease, and the water environmental pollution caused by its leakage has provoked worries, especially with the sharp increase of its applications.1–3 To solve this problem, water-lubricated bearings were proposed to replace the oil-lubricated bearings and have attracted more attention in recent decades.4–10 For optimal lubricating effect, a continuous water film should be formed between the shaft and the bearing. Rubber is a type of material well lubricated by water, and acrylonitrile-butadiene rubber (NBR) is widely used for water-lubricated bearings thanks to its chemical stability, vibration absorption ability and relatively high resistance to fatigue and wear.1,11–13 The wear behaviour of the rubber materials under actual service conditions requires great attention, since excessive wear on the rubber stern tube bearings is one of the most important reasons for the loss of workability.14–16 Some literatures have reported the effects of actual working conditions, such as sand in the water and improper lubrication and cooling,1,12 on the tribological properties of NBR composites. Another environmental factor which affects the tribological behaviours of the water-lubricated bearings is the temperature. The bearings may experience various temperatures due to the environmental conditions and heat generation by friction. Some researchers have mentioned the increase of the friction coefficient (COF) with the temperature.17–19 However, the effect and mechanism of temperature changes on tribological behaviours of NBR composites have not been systematically studied.

To improve the tribological performance (especially at relatively high temperature) of the NBR composites, one of the options is introducing high-performance fibres. In recent years, basalt fibre (BF), which is a novel type of eco-friendly mineral fibre with excellent comprehensive properties and relatively low cost, has been introduced as reinforcement of the composites and its effects on the tribological properties were mentioned in several publications.4,20–24 Zhang et al.23 reported that the addition of BFs improved the hardness, compressive strength and creep resistance of the polyetheretherketone (PEEK)-based composites, and a BF/PEEK composite with 2.5–7.5 phr BFs possessed a low COF and excellent wear resistance. In our previous work,25,26 BFs were mixed into the NBR as reinforcement, and it was demonstrated that when sliding against the stainless steel counterface under dry condition, the addition of BFs could decrease both the COF and the wear rate. For the water-lubricated bearing application, understanding the tribological performance of the material under water lubrication is very important for the property assessment and life prediction of the product. In this study, the tribological behaviour of BF/NBR composites under water-lubricated conditions at 30–70 °C was investigated using a block-on-ring test, which has been widely applied to study the tribological performance of polymer composites for bearing application.27–30 To discuss the effect mechanism, the influences of water ageing on the properties of BF/NBR composites were also evaluated.

2. Experimental

2.1. Materials

The NBR (NANCAR1051, acrylonitrile content 41%) was purchased from the Nantex Industry Co., Ltd., Zhenjiang, China. The NBR was plasticated before use (Mooney viscosity ML (1 + 4) 100 °C: 60–63). Continuous BF (BC11-200, filament diameter 11 μm ± 2 μm) was supplied by the Sichuan Aerospace Tuoxin Industrial Co., Ltd., China, and cut into 4 mm lengths by a cutting machine in our laboratory. The chopped BFs were soaked in acetone for 50 min, washed with distilled water three times and vacuum dried at 105 °C for 6 h before use. Carbon black (CB) N550 was supplied by the Kabote (China) Investment Co., Ltd. N-Cyclohexyl-2-benzothiazole sulphonamide (CBS) was supplied by Puyang Willing Chemicals, China. Other reagents, including ZnO, stearic acid (SA), polymerized 1,2-dihydro-2,2,4-trimethylquinoline (TMQ), dioctyl phthalate (DOP) and insoluble sulphur, were commercially available and used as received.

2.2. BF/NBR composites preparation

The components of the BF/NBR composites are shown in Table 1, and the following mixing process was used to prepare the composites with various BF contents and orientation. NBR, ZnO, SA, TMQ, CB and DOP were first mixed in an internal mixer at an initial temperature of 90 °C for 8 min. Then, the compound was moved to a two-roll mill. CBS and insoluble sulphur were added into the blends first, and after the blends were fully mixed, the BFs (0, 3, 12, 20, 30 phr, separately) were added into the compounds and further rolled for 5 min 40 s to ensure that the BFs were sufficiently oriented along the rolling direction. To obtain the cured samples with BF parallel and perpendicular orientation, the blends were cut parallel and perpendicular to the rolling direction, respectively, and then were vulcanized at 155 °C at a pressure of 10 MPa for 15 min. The samples were denoted according to the BF content and orientation. For example, the samples with 12 phr BFs oriented in the parallel and perpendicular directions were named as BF12-pa and BF12-per, respectively. The vulcanized samples were stored at room temperature for 16 h before further ageing or performance evaluation.
Table 1 Composition of the BF/NBR composites
Component Content (phr)    
NBR 100    
ZnO 5    
SA 1    
CB N550 50    
TMQ 1.2    
DOP 10    
CBS 1    
Insoluble sulphur 1.5    
BF 0/3/12/20/30    


2.3. Water ageing

According to GB/T 1690-2010, the BF/NBR composites prepared in Section 2.2 were soaked in water and were aged at 30 °C, 50 °C and 70 °C for 72 h, respectively. For the water absorption ratio test, the samples (25 × 25 × 2 mm3) were weighed before ageing to obtain M1, and after ageing, the samples were wiped by a blotter and weighed immediately to obtain M2; the water absorption ratio was calculated according to eqn (1):
 
image file: c9ra07623a-t1.tif(1)

Three specimens were tested for each type of samples.

2.4. Measurements

The hardness of the rubber vulcanizates was evaluated using a Shore A hardness tester (GT-GS-MB, Gotech Testing Machines Co., Ltd.) according to GB/T 531.1-2008, and 3 points were measured for each sample. The density of the rubber vulcanizates was tested according to GB/T 533-2008, and 3 specimens were tested for each sample type. The tensile and tear properties of the vulcanized rubber were tested using a Z005 universal testing machine (Germany) at a drawing rate of 500 mm min−1 according to the standards GB/T 528-2009 and GB/T 529-2008, respectively. The T2 (transverse relaxation time) of the vulcanizates before and after water ageing was tested using nuclear magnetic resonance (NMR, MR-CDS3500) from IIC Innovative Imaging Co., Ltd., Germany. The measured values were fitted with the Gauss-exponential magnetization decay equation (eqn (2)) and the T2 (transverse relaxation time) was obtained.
 
image file: c9ra07623a-t2.tif(2)
in which qM2 means the residual dipole moment; A, B, and C are the parameters without special definition. The samples were dried in a dryer for 24 h before the test.

The friction and wear tests were performed on a high-speed block-on-ring wear testing machine (MR-H3B, Jinan Time Shijin Testing Machine Co., Ltd., China), under water lubrication at 30 °C, 50 °C and 70 °C, respectively. The BF/NBR block, the 304# stainless steel ring and the test apparatus are as shown in Fig. 1(a), (b) and (c), respectively. The test was carried out with a sliding speed of 1.03 m s−1 and a normal load of 40 N for 90 min. The Ws was calculated according to eqn (3), and the volume of wear scar (Vs) was obtained according to eqn (4).27

 
image file: c9ra07623a-t3.tif(3)
 
image file: c9ra07623a-t4.tif(4)
where F is the normal load (N), R is the radius of the steel ring (mm), b is the width of the wear scar (mm), B is the width of the rubber block (mm), n is the sliding speed (rpm), and t is the steady duration of the friction (min). The mean value of the COF and Ws was calculated based on the results of 3 specimens.


image file: c9ra07623a-f1.tif
Fig. 1 Images of the (a) BF/NBR block, (b) stainless steel ring and (c) the main part of the test apparatus.

The worn surfaces of the BF/NBR composites in the block-on-ring tests were observed using a JEOL JSM-7500F scanning electron microscope (SEM), and the worn surfaces of the steel counterparts were observed using a stereomicroscope (SMZ1500, Nikon, Japan).

3. Results and discussion

3.1 Water ageing

Table 2 shows the water absorption ratio and variations in the density of BF/NBR composites before and after 72 h water immersion at 30 °C, 50 °C and 70 °C, respectively. With the temperature increase, the water absorption ratio of the composites increased and was independent of the BF content. In our previous study,25 the NMR test showed that the T2 of the thermal-oxidative-aged NBR samples was lower than that of the initial one, which indicated further crosslinking during the ageing process. However, water ageing at temperatures above 50 °C led to an increase of the T2 of the samples (the typical magnetization intensity curves of the NBR vulcanizates are as shown in Fig. 2); the T2 of the initial NBR vulcanizate and the samples after water ageing at 30 °C, 50 °C and 70 °C were 1.11, 1.08, 1.29 and 1.24 ms, respectively. The increase of the T2 reflected the move ability improvement of the H in the system, which may be caused by hydrolysis of –CN and the generation of –CONH2 and –COOH when the sample was immersed in the water at temperatures above 50 °C. Furthermore, as shown in Table 3, the hardness of the samples decreased after ageing, and the addition of BFs failed to enhance the hardness of the water-aged composites, especially at 50 °C and 70 °C. The decrease of the hardness should be attributed to the water absorption, and as concluded by Wang et al.,4 diffusion through fibre/matrix interface is the predominant water absorption mechanism of fibre-reinforced polymer composites. According to this mechanism, the weak connection between the BF and the NBR matrix, which produced extensive interfacial free space around the fibre (Fig. 3), led to water aggregation and weakened the BF enhancement in hardness; when ageing in higher temperature, the water absorption was increased, and the aggregation of water in the BF/NBR interface was aggravated. However, after being fully dried, the hardness of the aged samples was basically the same as that of the untreated samples, which indicated that no crosslinking density change of the NBR matrix had occurred. The hardness of the composites under various temperatures in air is shown in Fig. 4. As the temperature increased, the hardness of the composites decreased due to the softening of the matrix.
Table 2 Water absorption ratio and density of BF/NBR composites before and after 72 h water immersion at various temperatures
  Water absorption ratio/% Density/g cm−3
30 °C 50 °C 70 °C Before aging 30 °C 50 °C 70 °C
BF0 1.29 ± 0.083 4.63 ± 0.125 7.10 ± 0.053 1.19 1.19 1.18 1.18
BF3 1.32 ± 0.040 4.58 ± 0.062 6.97 ± 0.111 1.20 1.20 1.19 1.19
BF12 1.30 ± 0.036 4.59 ± 0.028 7.19 ± 0.140 1.23 1.22 1.23 1.22
BF20 1.24 ± 0.082 4.58 ± 0.047 7.16 ± 0.068 1.26 1.26 1.24 1.24
BF30 1.40 ± 0.066 4.74 ± 0.016 7.32 ± 0.074 1.28 1.28 1.28 1.26



image file: c9ra07623a-f2.tif
Fig. 2 The magnetization intensity curves of the NBR vulcanizates before and after water ageing for 72 h at 30 °C, 50 °C and 70 °C.
Table 3 Hardness of BF/NBR composites before and after 72 h water immersion at various temperatures
  Shore A hardness
BF0 BF3 BF12 BF20 BF30
a The aged samples were dried in a drier for 24 h before the test.
Before ageing 63 64 66 67 70
[thin space (1/6-em)]
30 °C water ageing
Aged sample 61 62 62 62 64
Aged-dried samplea 63 64 66 66 69
[thin space (1/6-em)]
50 °C water ageing
Aged sample 60 60 60 61 61
Aged-dried sample 63 64 66 66 68
[thin space (1/6-em)]
70 °C water ageing
Aged sample 58 58 57 58 58
Aged-dried sample 63 63 65 65 69



image file: c9ra07623a-f3.tif
Fig. 3 The SEM image of the BF/NBR interface (the brittle fracture sample, 3000×).

image file: c9ra07623a-f4.tif
Fig. 4 Effects of the temperature on the Shore A hardness of BF/NBR composites in air.

The effects of water ageing on the rebound resilience, tensile properties and tear strength of the BF/NBR composites are as shown in Fig. 5, 6 and 7, respectively. With the water temperature rising, the rebound resilience of the aged composites obviously improved due to the increase of the water absorption. Furthermore, with regard to the mechanical properties, the influences of the water ageing on the tensile properties were relatively low. For example, the tensile strength, elongation at the break and modulus at 300% of BF12-pa water-aged for 72 h at 70 °C, were 92%, 103%, and 105% of that of the initial reading, respectively. However, the tear strength of the BF/NBR composites with a high BF content were more sensitive to the water ageing.


image file: c9ra07623a-f5.tif
Fig. 5 Effects of (a) the BF content and (b) the temperature of water ageing on the rebound resilience of BF/NBR composites.

image file: c9ra07623a-f6.tif
Fig. 6 Effects of the BF content and the temperature of water ageing on the tensile properties of the BF/NBR composites. (a) Tensile strength and elongation at break vs. content of the BF; (b) tensile strength and elongation at break vs. temperature of water ageing; (c) tensile strength at 300% elongation vs. content of BF; and (d) tensile strength at 300% elongation vs. temperature of water ageing.

image file: c9ra07623a-f7.tif
Fig. 7 Effects of (a) the BF content/orientation and (b) the temperature of water ageing on the tear strength of BF/NBR composites.

3.2 Friction and wear

3.2.1 COF. The typical variations of COFs for the NBR block and 304# stainless steel ring rubbing pairs as a function of the sliding time under water-lubricated conditions at 30 °C, 50 °C and 70 °C are as shown in Fig. 8, and the COFs obtained under dry sliding conditions in our previous work26 are also included as a reference. In general, the COF of the NBR/stainless steel stayed relatively stable throughout the sliding under water-lubrication at various temperatures and was much lower than that obtained under dry sliding conditions due to the formation of the water film between the rubbing pairs. Furthermore, the COF increased with the temperature from 30 °C to 70 °C. This variation should be attributed to the effect of the temperature on the water viscosity. The viscosity of water is 0.7977, 0.5470 and 0.4040 mN s m−2 at 30 °C, 50 °C and 70 °C, respectively,31 which shows a sharp decrease with the temperature rise. The decrease of water viscosity was not conducive to the formation of the continuous water film between the rubbing pairs, and as a result, the lubricating capacity of the water decreased. By comparison, as shown in Fig. 9, the BF content showed less impact on the COF. Although the hardness of water-absorbed NBR decreased, especially at high temperatures (as discussed in Section 3.1), and led to an increase of the contact area between the block and the ring during the sliding and inclined to increase the friction force, the lubrication condition played a critical role in determining the COF.
image file: c9ra07623a-f8.tif
Fig. 8 Typical COFs of the NBR as a function of sliding time under dry sliding and water lubrication at various temperatures.

image file: c9ra07623a-f9.tif
Fig. 9 (a) The COFs of the BF/NBR composites with 12 phr BFs under water lubrication at various temperatures, and (b) the COFs of the BF/NBR composites with various contents and orientation of BFs under water lubrication at 70 °C.
3.2.2 Ws. The effects of the temperature, the BF content and the orientation on the Ws of the BF/NBR composites abraded under water-lubricated conditions are shown in Fig. 10. The water lubrication showed a significant effect on decreasing the wear loss of the BF/NBR composites. Furthermore, as shown in Fig. 10a, for the friction system that is lubricated by 30 °C water, when the BFs were parallel oriented, the Ws obviously decreased with the BF content increase, whereas the Ws was kept approximately constant when the BFs were perpendicularly-aligned. When the system was lubricated by 70 °C water, the addition of BFs with either parallel or perpendicular orientation was effective in improving the wear resistance; after sliding at 70 °C, the Wss of BF30-pa and BF30-per were 1.3 and 1.6 × 10−7 mm3 N−1 mm−1, which were 62% and 73% of the BF0-pa and BF0-per, respectively. The efficiency improvement of the perpendicularly orientated BFs should be due to the insufficient water lubrication at high temperature, and the effects of the BFs were similar to those under dry sliding conditions, to some extent. Wang et al.4 reported that the addition of the BFs significantly increased the wear rate of the PTFE-based composites due to poor adhesion between the BF and the matrix, but this increase did not happen in the BF/NBR composites. This is because, as shown in Section 3.1, the water absorption ratio was not mainly affected by the BF content, and furthermore, mechanical properties of the BF/NBR composites did not significantly change after water absorption, which means that the water absorption did not lead to significant plasticization of the NBR matrix, as it did in the PTFE. In this study, the orientation of the BFs, besides the water temperature, was the primary factor in determining the Ws.
image file: c9ra07623a-f10.tif
Fig. 10 Effects of (a) the BF content/orientation and (b) the water temperature on the Ws of BF/NBR composites.

To further investigate the wear mechanism, the worn surfaces of BF/NBR blocks and the steel rings were observed by an SEM and stereomicroscope, respectively. As shown in Fig. 11, there is no visible rubber transfer film on the counterface, which should be attributed to the isolation effect of the water film. Furthermore, after friction occurred with water lubrication at 30 °C, only a few scratches could be observed on the steel counterface, whereas the friction that occurred with 70 °C water lubrication led to severe scratches along the sliding direction, which should be attributed to insufficient water lubrication.


image file: c9ra07623a-f11.tif
Fig. 11 Typical morphologies (40×) of (a) the initial steel counterpart surface and the steel counterpart surface after rubbing with the block of (b) BF12-pa-30 °C; (c) BF-12-per-30 °C; (d) BF12-pa-70 °C; (e) BF12-per-70 °C under water lubrication.

Similar to the steel ring, the temperature of the system, rather than the BF content/orientation, had a major effect on the wear morphologies of the BF/NBR. Fig. 12 and 13 show the SEM images of the surfaces of the BF/NBR composites with various BF contents worn under 30 °C and 70 °C water lubrication, respectively. In general, the wear degree of the BF/NBR blocks under water-lubricated conditions was much lower than that of the block friction under dry sliding conditions (in ref. 25 and 26). Fig. 14 illustrates the influences of the water during the sliding process. First, the water film formed between the rubbing pair and effectively reduced the friction, and second, the debris was taken away by water and the abrasive wear was reduced. For the samples that were rubbed under water lubrication at 30 °C, the BF30-per had a rougher surface than the others did. Compared with the parallel-oriented BFs, the perpendicularly oriented fibres were more easily crushed under a relatively high load (40 N in this study) because of the larger contact area with the steel counterpart during the rubbing. It has been speculated that the stripping and the rubbing of the BFs with high content and perpendicular orientation may have led to a relatively high heat production and, as a result, the adhesive wear was aggravated.


image file: c9ra07623a-f12.tif
Fig. 12 SEM images of the surfaces of the BF/NBR blocks (2000×) worn under water lubrication at 30 °C: (a) BF0-pa; (b) BF12-pa; (c) BF30-pa; (d) BF0-per; (e) BF12-per; (f) BF30-per.

image file: c9ra07623a-f13.tif
Fig. 13 SEM images of the surfaces of the BF/NBR blocks worn under water lubrication at 70 °C: (a) BF0-pa (2000×); (b) BF12-pa (2000×); (c) BF30-pa (2000×); (d) BF0-per (2000×); (e) BF12-per (2000×); (f) BF30-per (2000×); and (g) BF30-per (10[thin space (1/6-em)]000×).

image file: c9ra07623a-f14.tif
Fig. 14 Schematic of the rubbing between the BF/NBR block and the steel ring under the water-lubricated condition.

Furthermore, in comparing with the images in Fig. 12 and 13, it was revealed that the surface of the BF/NBR block worn under water lubrication at higher temperatures was much rougher, and delamination and cracks can be observed after zooming in 10[thin space (1/6-em)]000 times (Fig. 13g). This aggravated wear of the composite block at high temperatures could be attributed to: (1) the insufficient lubrication of the water at 70 °C because of the viscosity decrease; (2) the loss of the effect of the water on reducing the heat that is produced by the rubbing process, which could lead to an increase in the adhesive wear; and (3) the decrease of the hardness and the tear strength of the BF/NBR surface after absorbing water at 70 °C, which led to the increase of the contact area and aggravation of the surface fracture, respectively. These disadvantages led to an increase of the Ws of the composite block with temperature under the water lubrication condition, which is as shown in Fig. 10b.

4. Conclusions

To understand the water lubrication effect on the NBR-based composite at various temperatures and improve its wear resistance for the water-lubricated bearing application, this study investigated the tribological properties of the BF/NBR composites and 304# stainless steel rubbing pairs under water lubrication at various temperatures. Based on our results, the conclusions are as follows:

(1) With the water temperature increase, the water absorption ratio and rebound resilience of the aged BF/NBR composites significantly increased, whereas the hardness and tear strength decreased. For the composites with high BF content, the hardness and tear strength were more sensitive to the water temperature.

(2) Water provided excellent lubrication for the NBR-based composites at low temperature. With the increase of temperature from 30 °C to 70 °C, the COFs for the BF/NBR composites and the stainless steel rubbing pairs increased, whereas the content and the orientation of the BFs had less effect on the COF of the composites under water-lubricated conditions.

(3) With the temperature increase, the Ws of the BF/NBR composites increased. The parallel-oriented BFs showed an obvious effect on the wear resistance improvement under water-lubricated conditions at both 30 °C and 70 °C, whereas the addition of perpendicularly-aligned BFs showed a lower effect.

Generally speaking, NBR-based composites with parallel-aligned BFs showed good wear resistance under water lubrication at a wide range of temperatures, and has potential to be applied in the water-lubricated bearing field.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

The authors acknowledge the financial support from the National Natural Science Foundation of China (grant number 51603110).

References

  1. C. L. Dong, C. Q. Yuan, X. Q. Bai, Y. Yang and X. P. Yan, Study on wear behaviours for NBR/stainless steel under sand water-lubricated conditions, Wear, 2015, 332–333, 1012–1020 CrossRef CAS.
  2. H. L. Qin, X. C. Zhou, X. Z. Zhao, J. T. Xing and Z. M. Yan, A new rubber/UHMWPE alloy for water-lubricated stern bearings, Wear, 2015, 328–329, 257–261 CrossRef CAS.
  3. D. Hu, Z. W. Guo, X. Xie and C. Q. Yuan, Effect of spherical-convex surface texture on tribological performance of water-lubricated bearing, Tribol. Int., 2019, 134, 341–351 CrossRef CAS.
  4. J. Z. Wang, B. B. Chen, N. Liu, G. F. Han and F. Y. Yan, Combined effects of fiber/matrix interface and water absorption on the tribological behaviors of water-lubricated polytetrafluoroethylene-based composites reinforced with carbon and basalt fibers, Composites, Part A, 2014, 59, 85–92 CrossRef CAS.
  5. C. L. Dong, C. Q. Yuan, L. Wang, W. Liu, X. Q. Bai and X. P. Yan, Tribological properties of water-lubricated rubber materials after modification by MoS2 nanoparticles, Sci. Rep., 2016, 6, 35023 CrossRef.
  6. Z. L. Xie, N. Ta and Z. S. Rao, The lubrication performance of water lubricated bearing with consideration of wall slip and inertial force, J. Hydrodyn., 2017, 29, 52–60 CrossRef.
  7. S. B. Liu and B. G. Yang, Optimal placement of water-lubricated rubber bearings for vibration reduction of flexible multistage rotor systems, J. Sound Vib., 2017, 407, 332–349 CrossRef.
  8. W. Litwin, Influence of local bush wear on water lubricated sliding bearing load carrying capacity, Tribol. Int., 2016, 103, 352–358 CrossRef.
  9. X. Liang, Z. W. Guo, T. Jun and C. Q. Yuan, Effect of modified glass fiber on tribological performance of water-lubricated bearing, Polym. Test. DOI:10.1016/j.polymertesting.2019.106153.
  10. H. H. Feng, S. Y. Jiang and A. M. Ji, Investigations of the static and dynamic characteristics of water-lubricated hydrodynamic journal bearing considering turbulent, thermohydrodynamic and misaligned effects, Tribol. Int., 2019, 130, 245–260 CrossRef.
  11. H. J. Wang, Z. L. Liu, L. Zou and J. Yang, Influence of both friction and wear on the vibration of marine water lubricated rubber bearing, Wear, 2017, 376–377, 920–930 CrossRef CAS.
  12. W. Litwin and C. Dymarski, Experimental research on water-lubricated marine stern tube bearings in conditions of improper lubrication and cooling causing rapid bush wear, Tribol. Int., 2016, 95, 449–455 CrossRef.
  13. J. Yang, Z. L. Liu, Q. C. Cheng, X. K. Liu and T. Y. Deng, The effect of wear on the frictional vibration suppression of water-lubricated rubber slat with/without surface texture, Wear, 2019, 426–427, 1304–1317 CrossRef CAS.
  14. H. Hirani and M. Verma, Tribological study of elastomeric bearings for marine propeller shaft system, Tribol. Int., 2009, 42, 378–390 CrossRef CAS.
  15. S. W. Zhang, Green tribology: fundamentals and future development, Friction, 2013, 1, 186–194 CrossRef.
  16. F. M. Kuang, X. C. Zhou, J. Huang, H. Wang and P. F. Zheng, Machine-vision-based assessment of frictional vibration in water-lubricated rubber stern bearings, Wear, 2019, 426–427, 760–769 CrossRef CAS.
  17. Y. Q. Wang, X. J. Shi and L. J. Zhang, Experimental and numerical study on water-lubricated rubber bearings, Ind. Lubr. Tribol., 2014, 66, 282–288 CrossRef.
  18. Z. M. Yan, X. C. Zhou, H. L. Qin, W. Y. Niu, H. Wang, K. Liu and Y. M. Tang, Study on tribological and vibration performance of a new UHMWPE/graphite/NBR water lubricated bearing material, Wear, 2015, 332–333, 872–878 CAS.
  19. J. Huang, X. C. Zhou, J. Wang, X. W. Tang and F. M. Kuang, Influence of temperature on friction of polymeric materials in water, Wear, 2019, 426–427, 868–876 CrossRef CAS.
  20. S. Mahanta, S. Samanta and M. Chandrasekaran, Processing and investigation of tribological properties of basalt epoxy composites, Mater. Today: Proc., 2017, 4, 8185–8191 CAS.
  21. A. A. J. Kumar and V. Srinivasan, Wear behavior of chitosan-filled polylactic acid/basalt fiber hybrid composites, Adv. Polym. Technol., 2018, 37, 898–905 CrossRef.
  22. S. F. Zhou, J. J. Wang, S. Z. Wang, X. Z. Ma, J. Huang, G. Z. Zhao and Y. Q. Liu, Facile preparation of multiscale graphene-basalt fiber reinforcements and their enhanced mechanical and tribological properties for polyamide 6 composites, Mater. Chem. Phys., 2018, 217, 315–322 CrossRef CAS.
  23. T. Zhang, H. T. Liu, D. K. Zhang and K. Chen, Mechanical and wear properties of polyetheretherketone composites filled with basalt fibres, Sci. Eng. Compos. Mater., 2019, 26, 317–326 Search PubMed.
  24. S. F. Zhou, J. J. Gao, J. J. Wang, S. Z. Wang, J. F. Yue, C. S. Dong, J. Huang, G. Z. Zhao and Y. Q. Liu, Polydopamine-coupling of carbon nanotubes onto microscaled basalt fiber to enhancing mechanical, thermal and tribological properties of composite materials, Mater. Res. Express, 2019, 6, 0850g6 CrossRef CAS.
  25. Y. Z. Li, Z. Li, J. J. Wan, Z. Q. Yan, J. T. Sun and S. G. Zhao, Mechanical and tribological performance of chopped basalt fiber/acrylonitrile-butadiene rubber composites, Polym. Compos., 2019, 40, 630–637 CrossRef CAS.
  26. Z. Li, Y. Z. Li, J. M. Cheng, X. Y. Lu and Y. H. Yang, Effects of fibre content and orientation on the wear resistance of basalt fibre/acrylonitrile-butadiene rubber composites under various friction conditions, Iran. Polym. J. Search PubMed , under review.
  27. Y. Q. Li, Q. H. Wang, T. M. Wang and G. Q. Pan, Preparation and tribological properties of graphene oxide/nitrile rubber nanocomposites, J. Mater. Sci., 2012, 47, 730–738 CrossRef CAS.
  28. B. B. Chen, J. Yang, J. Z. Wang, N. Liu, H. P. Li and F. Y. Yan, Fiber hybrid polyimide-based composites reinforced with carbon fiber and poly-p-phenylene benzobisthiazole fiber: tribological behaviors under sea water lubrication, Polym. Compos., 2016, 37, 1650–1658 CrossRef CAS.
  29. N. Liu, J. Z. Wang, J. Yang, G. F. Han and F. Y. Yan, Enhancement on interlaminar shear strength and water-lubricated tribological performance of high-strength glass fabric/phenolic laminate by the incorporation of carbon nanotubes, Polym. Adv. Technol., 2014, 25, 1572–1579 CrossRef CAS.
  30. S. Meicke and R. Paasch, Seawater lubricated polymer journal bearings for use in wave energy converters, Renewable Energy, 2012, 39, 463–470 CrossRef CAS.
  31. J. A. Dean, Lange's handbook of chemistry, McGRAW-HILL INC., New York, 15th edn, 1999 Search PubMed.

This journal is © The Royal Society of Chemistry 2019