An ETFE-(poly(ethylene-co-tetrafluoroethylene))-based radiation-grafted anion-exchange membrane (AEM) containing a butyl-spacer between the benzene and the methylpyrrolidinium groups (C4-AEM) had double the ex situ alkali stability at 80 °C compared to a methylene benchmark (C1-AEM). H2/O2 fuel cells containing C4-AEM still achieved a peak power density of >1 W cm−2.
High performance AEMs containing a methylene-(C1)-group between the benzene ring and the cationic head-group have already been prepared by radiation-induced grafting of vinylbenzyl chloride (VBC) monomer onto commodity ETFE polymer films.14 The treatment of such films in air with an e−-beam source leads to the functionalisation of the films with peroxide groups (Scheme 1).15 Heating these radiation-activated polymer films in the presence of VBC (the grafting step) produces graft copolymers,‡ which can be subsequently functionalised with amines to yield pendant quaternary ammonium groups. These AEMs give high performances in H2/O2 anion-exchange membrane fuel cells (AEMFCs) but they also degrade during ex situ treatment in aqueous alkali solutions at >70 °C.16–18
Scheme 1 An outline of the synthesis of the pyrrolidinium-grafted-ETFE-based C4-AEM developed in this study.‡ The C1-AEM benchmark contains a single –CH2– group between the benzene ring and the cationic pyrrolidinium N-atom. |
We recently found that the efficiency of the grafting step could be increased by the use of water in the grating mixture.17 However, it still remained impossible to radiation-graft linear aliphatic monomers, such as 6-chloro-1-hexene, onto ETFE, which would have eliminated the presence of base-labile benzylic groups in the resultant AEMs: radiation-grafting is a radical polymerisation process, which enables polymerisation of styrenic monomers but not linear aliphatic vinyl monomers. As a compromise solution, a styrenic monomer was selected for use that contains an alkyl-spacer-chain located between the vinylbenzene group and the cationic quaternary ammonium group: this eliminates the presence of (alkali-susceptible) benzylic quaternary ammonium groups while retaining the availability of readily-polymerizable vinylbenzene groups.
In this study, we report the synthesis of a radiation-grafted AEM containing a (C4) butyl-spacer between the aromatic and quaternary ammonium groups (C4-AEM), which exhibits a reduced level of alkali degradation at 80 °C. Theoretical and experimental studies on small cationic molecules have found that trimethylalkylammoniums bearing alkyl chains containing 4–6 carbon atoms in length show higher alkaline resistance than those with shorter or longer alkyl chains.19,20 We opted for a monomer, 1-(4-chlorobutyl)-4-vinylbenzene, containing a butyl-spacer located at the para-aromatic position (C4-monomer, Scheme 1), as larger monomers (e.g. with a C6-spacer) risk impeded diffusion into the ETFE films in the grafting process. The bromide form of this monomer has been previously prepared by Tomoi et al. and converted into cross-linked quaternary ammonium anion-exchange resins.21 The hydroxide form of these resins retained their ion exchange capacities at 100 °C more than the (C1-linked) benzyltrimethylammonium analogues. Despite the presence of C–H bonds at the β-positions to the quaternary ammonium groups, these resins did not undergo high levels of the anticipated degradation via Hoffman elimination.
Tomoi et al.'s monomer synthesis involved Cu-mediated cross-coupling of vinylbenzylmagnesium chloride with 1,3-dibromopropane.21 We applied the same method using 1-bromo-3-chloropropane to give 4-(1′-chlorobutyl)styrene in 58% yield after distillation (details in the ESI†). A divinyl by-product (Fig. S1 in the ESI†), resulting from homocoupling of the vinylbenzylmagnesium chloride, was also present in 23% molar ratio in the crude reaction mixture: this could be reduced to 2% on distillation (calculated from the 1H NMR spectra, Fig. S2 in the ESI†). This by-product can act as a crosslinker during the grafting step. Finally, 50 ppm of 4-tert-butylcatechol (radical polymerisation inhibitor) was added to the monomer (+2% crosslinker) mixture before use in the grafting step: this matched the inhibitor concentration in the commercially available VBC monomer (supplied as a mixture of para- and meta-isomers) used to produce the C1-AEM benchmark.
The grafting conditions employed were comparable to those described previously17 but with the additional use of an ultrasound bath during the grafting step. Nasef et al. recently reported that the yield and kinetics of radiation-grafting could be enhanced by the use of sonication and that this additionally reduces the formation of undesired homopolymer by-products.22 With our synthetic protocol, a comparison between ultrasound-aided and ultrasound-free radiation-grafting of VBC indicated that the use of ultrasound did not improve grafting yield but did allow a reduction in grafting time (6 h with sonication vs. 16 h without) with the elimination of poly(VBC) homopolymer formation (previously observed as a white solid on the walls of the grafting vessel). The C4-monomer also underwent ultrasound-assisted radiation-grafting but resulted in lower grafting yields compared to the VBC, due to its higher molecular weight. Non-ultrasound grafting of C4-monomer was even less successful and led to high levels of undesired homopolymer (confirmed by Raman spectroscopy, see Fig. S3 in the ESI†).
The optimum conditions for grafting C4-monomer onto ETFE films (yielding ETFE-polyC4) involved immersion of pre-irradiated ETFE (40 kGy in air) in N2-purged monomer–water mixtures containing the wetting agent 1-octyl-2-pyrrolidone (1% vol) and heating for 6 h at 70 °C with sonication (35 kHz, 225 W). To account for the 28% higher molecular weight of C4-monomer, it was used at a concentration of 5% vol, while 4% vol VBC was used to synthesise the ETFE-polyVBC membrane that was then aminated to form the C1-AEM benchmark (all other grafting conditions were identical). Grafting was confirmed using Raman spectroscopy where significant differences were observed between the two monomers (Fig. 1). The benzylic CH2Cl deformation (1270 cm−1) was not visible in the spectrum of ETFE-polyC4. The bands characteristic of meta-disubstituted benzene rings (1000 cm−1 and 700 cm−1) were also absent,16,23 since the C4-monomer was synthesised from a para-disubstituted-only starting material. Homogeneous grafting, throughout the core of both pre-aminated membranes, was confirmed by cross-sectional Raman maps of the ratio between the areas of the 1615 cm−1/830 cm−1 bands, since these represent the aromatic ring/ETFE components, respectively (see Fig. S4 in the ESI†).16,24
For the amination of ETFE-polyVBC and ETFE-polyC4, to form C1-AEM and C4-AEM respectively, we selected N-methylpyrrolidine (MPY): this yields AEM cationic head-groups with superior alkaline stabilities and enhanced fuel cell performances compared to the traditional use of trimethylamine (TMA).16 We suspect that the reason behind the enhanced ex situ stability of MPY membranes is related to their higher λwater (average number of H2O molecules per anion), being around 1.5 times those of TMA-based AEMs.18 As recently published, the number of water molecules solvating the OH− anions has a substantial effect on AEM chemical stability.25,26 Furthermore, attempts to aminate ETFE-polyC4 at room temperature with TMA proved unsuccessful due to the higher activation energies required for SN2 reactions on non-benzylic primary alkyl chlorides (the high volatility of aqueous TMA solutions impedes the use of elevated temperatures on safety grounds). A prior optimisation study for the MPY amination of ETFE-polyVBC intermediates concluded that using 15% vol MPY in water for 6 hours at 60 °C was the mildest and cheapest effective option (details in the ESI†). However, this did not translate to ETFE-polyC4 (containing lower reactivity, non-benzyl head-groups): 70 °C and 24 h were required with the use of aqueous MPY (15% vol).
C4-AEM had 20% lower ion-exchange capacity (IEC) than the C1-AEM benchmark due to its lower Degree of Grafting (DoG) (Table 1). However, the Water Uptakes (WU) and λwater values were similar for both AEMs. Likewise, no major differences in the swelling degrees and the mechanical properties were seen between the two AEMs (Tables 1, S2, Fig. S6 and S7 in the ESI†). The Cl− conductivity of C4-AEM was lower than that of C1-AEM (Table 1 and Fig. S5 in the ESI†) but, as expected for AEMs containing similar pyrrolidinium chemistries and λwater values, the IEC-normalised conductivities27 were similar (Fig. 2).
C1-AEM | C4-AEM | |
---|---|---|
a Average number of H2O molecules per Cl− anion calculated as: λwater = WU (%)/(100 × 18.02 × IEC), where IEC is in mol g−1. b Swelling degree in the x–y (in-plane) direction. c Swelling degree in the z (through-plane, thickness) direction. d The Cl− anion conductivities at 60 °C of the fully hydrated AEMs (4-probe, in-plane measurements with the RG-AEM submerged in water). | ||
DoG (%) | 75 | 66 |
IEC/mmol g−1 | 1.92 ± 0.05(4) | 1.508 ± 0.005(4) |
WU (%) | 95 ± 12(4) | 85 ± 8(4) |
λ water | 28 ± 3(4) | 31 ± 3(4) |
SDxy (%)b | 51 ± 5(3) | 52 ± 1(3) |
SDz (%)c | 65 ± 6(3) | 59 ± 8(3) |
σ Cl (60 °C)/mS cm−1d | 41 ± 3(3) | 30.4 ± 1.3(3) |
Fig. 2 IEC-normalised Cl−-anion conductivities (4-probe, in-plane, measured in water). Errors bars are from repeat measurement on n = 3 samples of each AEM. |
The H2/O2 AEMFC performances at 60 °C of membrane electrode assemblies (MEA) comprising both AEMs were evaluated using gas diffusion electrodes (GDEs) that contained 20% wt ETFE-benzyltrimethylammonium-based anion-exchange ionomer powder28 and 80% wt electrocatalysts: the Pt/C cathodes and PtRu/C anodes (all 0.40 ± 0.01 mgPt cm−2) were prepared as previously reported (details in the ESI†).18 The low current performances of both AEMs were identical, confirming similar electrocatalytic activities (Fig. 3). However, the performance curves deviate at higher currents, where internal ohmic resistances and mass transport losses control performances. C1-AEM achieved a peak power density of 1.22 W cm−2, whereas C4-AEM obtained 1.02 W cm−2 (under identical test conditions): this 17% lower power density is still good considering C4-AEM was 26% lower in conductivity at 60 °C than C1-AEM. The peak power increased to 1.12 W cm−2 at 70 °C with C4-AEM but no further improvement was observed when raising the temperature to 80 °C (Fig. S8 in the ESI†).
Fig. 3 H2/O2 fuel cell performances at 60 °C with PtRu/C anodes and Pt/C cathodes (all 0.4 mgPt cm−2). The unpressurised gases were supplied at 1 SLPM and 68% RH. |
The ex situ chemical stabilities were tested by ageing individual samples of each AEM in aqueous KOH (1 mol dm−3) at 80 °C for 28 d. Post-aged samples were converted back into the Cl−-form and the IECs were re-measured (Table 2). The loss of IEC with C4-AEM was half that of the C1-AEM benchmark. For more insights into the degradation mechanisms, CHN + Cl elemental analyses were also performed (Fig. 4). The % Cl loss correlates with the % IEC loss as all degradation mechanisms lead to loss of Cl− anions. However, the differences between the % Cl and % N losses indicate multiple degradation mechanisms are operating (discussed previously:16 see Fig. S9 in the ESI†).
C1-AEM | C4-AEM | |
---|---|---|
IEC pre-aged AEM/mmol g−1 | 1.88 ± 0.03 | 1.44 ± 0.04 |
IEC post-aged AEM/mmol g−1 | 1.38 ± 0.01 | 1.25 ± 0.02 |
IEC loss (%) | 27 ± 2 | 13 ± 3 |
Around a third of the degradation of C1-AEM involves loss of the N atoms due to OH− derived displacement of complete MPY head-groups (SN2Bn). Degradation by this pathway is essentially eliminated with C4-AEM, as the partial negative charges on the α-C atom (attached to the quaternary ammonium N) are not stabilized by resonance with a phenyl ring (confirms the stabilising effect of the spacer-group).4 For C4-AEM, degradation via Hoffman elimination at the spacer-chain is also possible, which would lead to loss of N content: however, the near zero % N loss indicates that this, along with nucleophilic loss of MPY, does not occur to a significant extent (in accordance with Tomoi et al.).21 Adding a spacer-chain appears to have “switched off” the degradation mechanisms involving loss of N atoms (see the degradation mechanisms in Fig. S9 in the ESI†). Nevertheless, 13% degradation still occurs with C4-AEM, which is predominantly due to loss of positive charges (loss of Cl− anions) but with retention of N atoms on the polymer grafts. This can proceed via nucleophilic substitution on the N-methyl group (SN2NMe) or ring-opening of the 5-membered heterocyclic ring.29 A previous study of ETFE-based VBC-grafted AEMs, with different head-groups,16 observed 12–14% degradation that did not involve loss of N content (approximately constant for TMA-, MPY- and N-methylpiperidinium-based head-groups). To obtain further confirmation of the degradation mechanisms, solid-state 13C and 14N NMR spectra were recorded on the pre- and post-alkali-aged samples, but no discernible changes were observed on ageing (see Fig. S10 and S11 in the ESI†).
Footnotes |
† Electronic supplementary information (ESI) available: Additional experimental details and data in support of the main text. See DOI: 10.1039/c7ta10222d |
‡ It is not currently known whether an oxygen atom (C–O–C ether group) links the ETFE backbone and the pendent grafted polymer chains or if the link is a C–C bond.15 |