Thiol–ene click reaction on cellulose sponge and its application for oil/water separation
Received
20th January 2017
, Accepted 23rd March 2017
First published on 6th April 2017
Abstract
Thiol–ene click reaction was employed to synthesize a flexible hydrophilic cellulose sponge. The reactive vinyl group was introduced by silanization treatment with vinyl-trimethoxysilicane (VTMO), and the resulting silylated cellulose sponge (SCS) can be subsequently functionalized with various thiol-containing compounds such as 3-mercaptopropionic acid, via temperature induced thiol–ene reactions. The hydrophilic cellulose sponge thus prepared displayed an excellent mechanical strength of 70 KPa at 80% compression strain. The prepared sponge features hydrophilic and underwater oleophobic properties and was used in gravity-driven removal of oil from oil-in-water emulsions and oil/water mixtures with a high separation efficiency. The separation efficiency remained 100% after 10 cycles for an oil/water mixture and 95% after 6 cycles for an oil-in-water emulsion.
1. Introduction
Water pollution from oil spillage and industrial discharge of organic solvents has become more and more serious, making oil/water separation of worldwide urgency. Adsorption-based oil/waster separation methods are attractive for being energy-efficient. Inorganic sorbents including silica aerogels,1,2 carbon aerogels,3,4 graphene aerogels5,6 and organic synthetic polymers such as polystyrene,7 polypropylene,8 polyurethane foam,9 and melamine sponges10 have been demonstrated to function as oil removal materials that adsorb oil from water. However, the widespread utilization of these sorbents are hindered by their complicated fabrication procedures and lack of biodegradability. Thus, there was great interest in developing eco-friendly materials as effective oil/water separation mediums.
Cellulose sponge, a porous material, has been developed for oil/water separation particularly via absorption due to their fascinating characters, such as sustainable origins, low-cost, and biocompatibility.11–16 However, these absorption materials easily fouled by oil due to theirs oleophilicity, which can reduce the absorption capacity.17–19 Therefore, it's necessary to explore hydrophilic porous cellulose materials for oil/water separation via filtration through chemical modifications. Batchelor et al.20 used polyamideamine-epichlorohydrin in preparing a hydrophilic cellulose aerogel, which they successfully applied in oil/water separation. Hu et al.21 prepared a hydrophilic cellulose-based filtering material crosslinked by citric acid for oil/water separation. However, neither of the above mentioned work further discussed the recyclability for oil/water emulsion separation of the materials.
The current study involves using thiol–ene click reaction to treat cellulose sponge with vinyl-trimethoxysilicane (VTMO), re-introduces hydrophilicity into the rather hydrophobic silane-crosslinked cellulose sponge. Thiol–ene click reactions22,23 are widely employed to introduce functional groups, such as –OH, –COOH, and –NH2 to cellulose. Tingaut et al.24 prepared three functional cellulose films using thiol–ene click reactions. Zhang et al.25 prepared different pH-responsive nanoparticles from novel ionic cellulose derivatives made by thiol–ene click reactions. Levkin et al.26 prepared functional nanocellulose films using photo-induced thiol–ene reactions.
Crosslinked cellulose sponge was prepared by treating cellulose fibrils with vinyl-trimethoxysilicane (VTMO), where O–Si crosslinking and the introduction of the reactive vinyl groups were achieved simultaneously. The resulted silylated cellulose sponge (SCS) was then reacted with 3-mercaptopropionic acid (MPA) and to get grafted with the hydrophilic carboxylate moieties via thiol–ene reaction (Scheme 1). The surface of the modified SCS sponge showed underwater oleophobicity. The sponge was demonstrated to rapidly separate oil from the oil/water mixtures, and also exhibited decent performance and excellent recyclability in separating oil-in-water emulsions.
![image file: c7ra00847c-s1.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-s1.gif) |
| Scheme 1 Scheme showing the preparation of thiol–ene modified silylate cellulose sponge (SCS-MPA) from cellulose microfibrils. | |
2. Experimental section
2.1. Materials
Cellulose microfibrils suspension (solid content 1.4%) was purchased from Tianjin Haojia Cellulose CO., Ltd, China. VTMO was supplied by Zhejiang Feidian Chemical Co., Ltd. 2,2′-Azobis[2-methylpropionamidine]dihydrochloride (AIBA), 3-mercaptopropionic acid (MPA) was obtained from Energy Chemical. Hydrochloric acid (HCl) (37%) was obtained from Pinghu Chemical Reagent, China. n-Hexane was purchased from Changshu Hongsheng Fine Chemical Co., Ltd. Acetone, ethanol was provided by ShangHai Yunli Economic and Trade Co., Ltd. Disperse blue SE-5R was produced by Zhejiang JiHua Group. Deionized water was used in all experiments.
2.2. Synthesis of silylated cellulose sponge (SCS)
140 mg VTMO was added dropwise into 10 g cellulose microfibrils suspension. The suspension was stirred for 2 h at room temperature under acidic conditions (pH = 4). The mixture was frozen in liquid nitrogen and freeze-dried in freeze-dryer (DGJT-10, Beijing Songyuan Huaxing Technology Development Co., Ltd.) for 48 h. Finally, dry sponge was cured at 120 °C for 10 min to promote the cross-linking between cellulose and VTMO.
2.3. Preparation of SCS-MPA sponge via thiol–ene click reaction
79.5 mg AIBA (0.293 mmol) was dissolved in water (5 mL). 10 mL ethanol and 1 g (9.42 mmol) MPA were added to the solution successively. The mixture was shaken in a vortex mixer. Upon thorough mixing, 200 mg SCS was added, the mixture was heated to 60 °C and maintained for 2 h. The sample was rinsed with water and ethanol sufficiently to remove the unreacted materials. Finally, the sample was dried at 80 °C for 4 h and stored in a desiccator.
2.4. Characterization
2.4.1. Analysis of structure and morphology. The chemical constitution of the original cellulose sponge (CS), SCS and SCS-MPA sponges were studied using Fourier transform infrared (FT-IR) spectrometry (PerkinElmer Spectrum Two, American). All spectra were recorded between 4000 and 600 cm−1 with a resolution of 4 cm−1 scans.The morphologies of the samples were investigated using scanning electron microscopy (SEM, TM-1000, HITACHI, Japan). The N2 adsorption–desorption isotherms and BET surface area were characterized by a TriStar II 3020M analyzer (Micrometrics instrument corp.).
The dynamic water contact angle (WCA) and oil contact angle on underwater (OCA) were collected with a DSA30 contact angle analyzer (Kruss, German). Optical microscopy images of the emulsions and filtrates were captured by a Nikon 80i optical microscope. The amounts of oil in the emulsion and the filtrate were determined by UV-Vis spectroscopy (UV-1800, Shimadzu corp., Japan).
2.4.2. Mechanical testings. The compression tests were performed on a HY-940F Universal Testing System (Shanghai). The samples were placed between the testing plates and compressed at a speed of 2 mm min−1 with the maximum compression strain (ε) set to 80%. Young's modulus and compression strength were obtained from the stress curves. The thickness recovery was calculated according to the following formula:14where εfinal was the residual strain and could be measured at the final position, where no stress was applied. An average of three replicates were used for each sample.
2.4.3. Evaluation of the density and porosity of SCS sponge. The porosity was calculated using the following equation: |
![image file: c7ra00847c-t1.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-t1.gif) | (2) |
Where ρb was the bulk density and ρs was the skeletal density of the SCS sponge. ρb was calculated from the weight and bulk volume of the sponge. Considering that the SCS material could be regarded as a composite of cellulose and VTMO, ρs was calculated according to eqn (3): |
![image file: c7ra00847c-t2.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-t2.gif) | (3) |
where Wcellulose was the weight fraction of cellulose and WVTMO was the weight fraction of VTMO in the sponge (Wcellulose + WVTMO = 1). ρcellulose and ρVTMO were obtained according to literatures.14,27–29
2.4.4. Evaluation of the oil rejection (R%) of SCS-MPA sponge. The oil/water mixture was prepared by vigorously stirring. To prepare the surfactant-stabilized oil-in-water emulsions, sodium dodecyl-benzenesulfonate (0.5 g) and n-hexane (5 mL) was added to 5 mL of water with intensive mixing. The mixture formed a homogeneous dispersion in about 1 min.The oil rejection (R%) was calculated as follow:20
|
![image file: c7ra00847c-t3.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-t3.gif) | (4) |
where
C0 and
C1 are the concentrations of oil in the emulsion and filtrate, respectively.
3. Results and discussion
3.1. Structure and morphology
As illustrated in Fig. 1, compared with unmodified CS, the IR spectrum of SCS shows new peaks at 3062 cm−1 (νas
CH2), 3026 cm−1 (ν
CH), 2969 cm−1 (νs CH2), 1601 (νC
C), 1408 cm−1 (δ
CH2 and δ
CH), all of which were attribute vibrations of the vinyls on VTMO.30,31 Moreover, the peak at 1276 cm−1 (νSi–C), and between 1180–690 cm−1 were due vibrations of silyl connections (νSi–C, νas Si–C, νas Si–O–Si, νs Si–O–Si).31 Upon modification with MPA, the sponge showed a characteristic carbonyl stretching vibration at 1715 cm−1 (νC
O), meanwhile the vinyl vibration bands at 3062, 3026, 1600, 1408 cm−1 were considerably weakened, indicating the vinyls have transformed to thioether linkages.24
![image file: c7ra00847c-f1.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-f1.gif) |
| Fig. 1 FTIR spectra of (a) unmodified CS and (b) SCS and (c) its thiol–ene coupling products SCS-MPA. | |
The morphology of SCS and SCS-MPA was studied by SEM (Fig. 2). Both SCS and SCS-MPA sponges displayed a porous structure composed of thin sheets interconnected with microfilaments. These thin sheets likely formed from the aggregation of cellulose microfibrils during freeze-drying step, when water within the sponge crystalized.32,33 After the thiol–ene chick reaction, the resulted SCS-MPA remained porous.34 The porosity of the cellulose sponges was calculated according to eqn (2) and (3), which is a common method to evaluate the porosity of nanocellulose sponge.11,35 Results (Table 1) showed that regardless of silane modification, the cellulose sponges were highly porous (porosity ≥ 99%).
![image file: c7ra00847c-f2.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-f2.gif) |
| Fig. 2 SEM image of (a) SCS, and (b) SCS-MPA sponge. | |
Table 1 Density, porosity of unmodified and silylated cellulose sponge
Sample |
Density/kg m−3 |
Porosity/% |
CS |
10.9 |
99.3 |
SCS |
12.3 |
99.4 |
3.2. Mechanical properties
The compressive stress–strain curves of the cellulose sponges compressed at 80% compression strain are presented in Fig. 3a. At 80% compression strain, the compressive stress of SCS-MPA was about 70 KPa. The thickness recovery of unmodified CS was calculated to be 39%, while that of the SCS-MPA was significantly increased to around 62% (Fig. 3b). SCS-MPA could recover to its original height in 30 min, while the unmodified CS remained compressed. In addition to being more flexible and resilient, the SCS-MPA sponge also showed higher compressive strength compared with unmodified CS. These observations were in line with the theory that crosslinking enhances the mechanical properties of cellulose sponge.36,37
![image file: c7ra00847c-f3.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-f3.gif) |
| Fig. 3 (a) Compressive stress–strain curves of unmodified CS, SCS and SCS-MPA compressed to 80% strain, (b) thickness recovery (S%) and Young's modulus of unmodified CS, SCS and SCS-MPA upon unloading from a compressed state (ε = 80%) was visualized by columns. | |
3.3. Hydrophilic and underwater oleophobic properties
SCS is highly hydrophobic with water contact angle of 160°. After the thiol–ene reaction, carboxyl groups were grafted onto SCS.38 The surface of the sponge changed from hydrophobic to hydrophilic and displayed underwater oleophobicity. Both surfaces of unmodified CS and SCS-MPA sponge were highly hydrophilic as demonstrated in Fig. 4a. However, the CS surface collapsed after absorbing the water-droplets, while the SCS-MPA surface remained intact. The SCS-MPA sponge also showed oleophobicity when immersed in water, exhibiting a high oil contact angle of 147°(Fig. 4b).10 Therefore, the present material was used for oil/water separation.
![image file: c7ra00847c-f4.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-f4.gif) |
| Fig. 4 (a) Photographs of dynamic measurements of water permeation on the surface of CS and SCS-MPA sponge, (b) oil contact angle on the SCS-MPA sponge underwater (contact angle: 147°). | |
3.4. Separation capacity and recyclability
As expected, the wetted cellulose sponge, which showed underwater oleophobic, facilitated the efficient separation of oil/water mixtures. The oil/water mixture separation experiment was performed as depicted in Fig. 5a. The water-removing process was driven by gravity. For oil/water mixture (50 mL, 1
:
1, v/v), stratification took place when it was poured into the glass graduated funnel. Water rapidly passed through the materials (<2 min), while hexane was intercept due to the hydrophilic and underwater oleophobic characteristics of the sponge. Consequently, SCS-MPA has unexpectedly high separation efficiencies for oil/water mixture. The oil rejection, calculated by eqn (4), was studied after every separation experiment and the results are summarized in Fig. 5b. The oil rejection was 100% for all ten repeated cycles, demonstrating a favorable reusability feature of the SCS-MPA sponge.
![image file: c7ra00847c-f5.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-f5.gif) |
| Fig. 5 (a) The photographs of hexane/water mixtures separation process (the disperse blue dye SE-5R was dissolved in the oil phase), (b) efficiency and reusability of the SCS-MPA on separating oil/water mixtures. | |
The separation efficiency of SCS-MPA was further evaluated using oil-in-water emulsions. Passing through the sponge caused the emulsion to demulsify and the coalesced oil phase was retained above the sponge.39 The optical microscopic images of the oil-in-water emulsion and the filtrate were shown in Fig. 6. The filtrate clearly contained no oil droplet, suggesting the SCS-MPA sponge was effective in removing oil from the surfactant-stabilized oil-in-water emulsion. The UV-Vis spectrum was also employed to analyze the filtrate, from which the rejection ratio of oil was determined to be as high as 98.6% (Fig. 6c). This was comparable to reported rejection ratio of cellulose nanofiber aerogels (98.6%)20 and that of cellulose membranes (99.6%).40 And these results were illustrated the high separation efficiency of the wetted cellulose sponge. The used sponge could be reused after rinsing with D.I. water repeatedly until free of any oil-dissolved disperse dyes. The rejection ratio of the oil-in-water emulsion remained over 95% up to six reuse cycles (Fig. 6d).
![image file: c7ra00847c-f6.tif](/image/article/2017/RA/c7ra00847c/c7ra00847c-f6.gif) |
| Fig. 6 (a) and (b) Photographs of surfactant-stabilized n-hexane-in-water emulsion before and after separation (scale bar: 100 μm). (c) UV-Vis spectrum of the oil in water emulsion before and after separation, (d) cyclic separation of the SCS-MPA to oil-to-water emulsion. | |
4. Conclusions
In summary, a novel hydrophilic sponge with enhanced mechanical properties was prepared by silylation of cellulose fibrils and subsequent modification by thiol–ene click reaction. The sponge was successfully utilized for oil removal from both oil/water mixture and an oil-in-water emulsion. The thiol–ene modification endowed the sponge with superb hydrophilicity and underwater oleophobicity (147°). The sponge also boasted high porousity (>99%), excellent compressive strength (70 KPa) and decent stability and flexibility, allowing it to be repeatedly used. The separation efficiency was as high as 100% after 10 cycles for oil/water mixture and over 95% after 6 cycles for oil-in-water emulsions. It is worth noting that the cellulose sponge gained high wet strength and durability underwater from crosslinking by VTMO. These results indicated that the hydrophilic material has great potential in separating oil/water emulsion.
Acknowledgements
This work was financially supported by National Natural Science Foundation of China (No. 51403035), and the Fundamental Research Funds for the Central Universities (No. 16D110510).
References
- A. Venkateswara Rao, N. D. Hegde and H. Hirashima, J. Colloid Interface Sci., 2007, 305, 124–132 CrossRef CAS PubMed
. - S. Yun, H. Luo and Y. Gao, RSC Adv., 2014, 4, 4535–4542 RSC
. - R. Zhang, L. Hu, S. Bao, R. Li, L. Gao, R. Li and Q. Chen, J. Mater. Chem. A, 2016, 4, 8412–8420 CAS
. - Y. Meng, T. M. Young, P. Liu, C. I. Contescu, B. Huang and S. Wang, Cellulose, 2014, 22, 435–447 CrossRef
. - H. Hu, Z. Zhao, W. Wan, Y. Gogotsi and J. Qiu, Adv. Mater., 2013, 25, 2219–2223 CrossRef CAS PubMed
. - S. Kabiri, D. N. H. Tran, T. Altalhi and D. Losic, Carbon, 2014, 80, 523–533 CrossRef CAS
. - S. Yu and H. Tan, ACS Appl. Mater. Interfaces, 2015, 7, 6745–6753 CAS
. - Q. F. Wei, R. R. Mather, A. F. Fotheringham and R. D. Yang, Mar. Pollut. Bull., 2003, 46, 780–783 CrossRef CAS PubMed
. - X. Zhang, L. Zhang, K. Liu and L. Jiang, Adv. Funct. Mater., 2013, 23, 2881–2886 CrossRef CAS
. - C. F. Wang, H. C. Huang and L. T. Chen, Sci. Rep., 2015, 5, 14294 CrossRef PubMed
. - D. Klemm, B. Heublein, H. P. Fink and A. Bohn, Angew. Chem., Int. Ed., 2005, 44, 3358–3393 CrossRef CAS PubMed
. - J. Feng, S. T. Nguyen, Z. Fan and H. M. Duong, Chem. Eng. J., 2015, 270, 168–175 CrossRef CAS
. - T. Zhai, Q. Zheng, Z. Cai, H. Xia and S. Gong, Carbohydr. Polym., 2016, 148, 300–308 CrossRef CAS PubMed
. - Z. Zhang, G. Sèbe, D. Rentsch, T. Zimmermann and P. Tingaut, Chem. Mater., 2014, 26, 2659–2668 CrossRef CAS
. - Q. Liao, X. Su, W. Zhu, W. Hua, Z. Qian, L. Liu and J. Yao, RSC Adv., 2016, 6, 63773–63781 RSC
. - N. T. Cervin, C. Aulin, P. T. Larsson and L. Wågberg, Cellulose, 2011, 19, 401–410 CrossRef
. - F. Wang, S. Lei, M. Xue, J. Ou and W. Li, Langmuir, 2014, 30, 1281–1289 CrossRef CAS PubMed
. - C. Su, Y. Xu, W. Zhang, Y. Liu and J. Li, Appl. Surf. Sci., 2012, 258, 2319–2323 CrossRef CAS
. - W. Zhang, Y. Zhu, X. Liu, D. Wang, J. Li, L. Jiang and J. Jin, Angew. Chem., 2014, 53, 856–860 CrossRef CAS PubMed
. - Z. He, X. Zhang and W. Batchelor, RSC Adv., 2016, 6, 21435–21438 RSC
. - K. Rohrbach, Y. Li, H. Zhu, Z. Liu, J. Dai, J. Andreasen and L. Hu, Chem. Commun., 2014, 50, 13296–13299 RSC
. - H. C. Kolb, M. G. Finn and K. B. Sharpless, Angew. Chem., Int. Ed., 2001, 40, 2004–2021 CrossRef CAS PubMed
. - A.
B. Lowe, Polym. Chem., 2010, 1, 17–36 RSC
. - P. Tingaut, R. Hauert and T. Zimmermann, J. Mater. Chem., 2011, 21, 16066 RSC
. - Y. Wang, T. Heinze and K. Zhang, Nanoscale, 2016, 8, 648–657 RSC
. - J. Guo, W. Fang, A. Welle, W. Feng, I. Filpponen, O. J. Rojas and P. A. Levkin, ACS Appl. Mater. Interfaces, 2016, 8, 34115–34122 CAS
. - A. P. Rao, A. V. Rao and G. M. Pajonk, Appl. Surf. Sci., 2007, 253, 6032–6040 CrossRef CAS
. - H. Guo, B. N. Nguyen, L. S. McCorkle, B. Shonkwiler and M. A. B. Meador, J. Mater. Chem., 2009, 19, 9054 RSC
. - T. Matias, C. Varino, H. C. de Sousa, M. E. M. Braga, A. Portugal, J. F. J. Coelho and L. Durães, J. Mater. Sci., 2016, 51, 6781–6792 CrossRef CAS
. - S. Smitha, P. Shajesh, P. Mukundan and K. G. K. Warrier, J. Sol-Gel Sci. Technol., 2007, 42, 157–163 CrossRef CAS
. - M. Zaharescu, A. Jitianu, A. Braileanu, J. Madarász and G. Pokol, J. Therm. Anal. Calorim., 2001, 64, 689–696 CrossRef CAS
. - H. Sehaqui, Q. Zhou and L. A. Berglund, Compos. Sci. Technol., 2011, 71, 1593–1599 CrossRef CAS
. - A. J. Svagan, M. A. S. A. Samir and L. A. Berglund, Adv. Mater., 2008, 20, 1263–1269 CrossRef CAS
. - H. Sai, R. Fu, L. Xing, J. Xiang, Z. Li, F. Li and T. Zhang, ACS Appl. Mater. Interfaces, 2015, 7, 7373–7381 CAS
. - C. Aulin, J. Netrval, L. Wågberg and T. Lindström, Soft Matter, 2010, 6, 3298 RSC
. - H. Huang, P. Chen, X. Zhang, Y. Lu and W. Zhan, Small, 2013, 9, 1397–1404 CrossRef CAS PubMed
. - X. Yang and E. D. Cranston, Chem. Mater., 2014, 26, 6016–6025 CrossRef CAS
. - Q. Fu, X. Wang, Y. Si, L. Liu, J. Yu and B. Ding, ACS Appl. Mater. Interfaces, 2016, 8, 11819–11829 CAS
. - Y. Si, Q. Fu, X. Wang, J. Zhu, J. Yu, G. Sun and B. Ding, ACS Nano, 2015, 9, 3791–3799 CrossRef CAS PubMed
. - Y. Cao, N. Liu, W. Zhang, L. Feng and Y. Wei, ACS Appl. Mater. Interfaces, 2016, 8, 3333–3339 CAS
.
|
This journal is © The Royal Society of Chemistry 2017 |